Flame-Retardant and Transparent Unsaturated Polyester Based on P/N Liquid Flame Retardants and Modified Halloysite Nanotubes.

Unsaturated polyester resin (UPR) with excellent flame retardant is mainly obtained by adding large amounts of flame retardants, usually at the expense of mechanical properties. In this work, a reactive flame retardant containing phosphorus and nitrogen (DOPO-N) was successfully synthesized and incorporated in UPR as a crosslinker. The mechanical and flame-retardant properties of UPR composites were enhanced. UPR/30DOPO-N passed a UL-94 V-1 rating with a limiting oxygen index (LOI) of 30.8%. The tensile strength of UPR/30DOPO-N increased by 24.4%. On this basis, a small amount of modified HNTs (VHNTs) was added to further improve the flame-retardant properties of the composite. With the introduction of 3 wt% VHNTs, the composite passed the UL-94 V-0 rating. The peak of heat release rate (PHRR) and total heat release (THR) of it decreased by 60.7% and 48.3%, respectively. Moreover, the detailed flame-retarding mechanism of DOPO-N and VHNTs was investigated by thermogravimetric infrared spectroscopy (TG-IR), Raman spectra, and X-ray photoelectron spectroscopy (XPS). It was found that DOPO-N played a role in quenching the flame in the gas phase and cooperated with VHNTs to enhance the barrier effect in the condensed phase.

A New Phosphorous/Nitrogen-Containing Flame-Retardant Film with High Adhesion for Jute Fiber Composites.

In this work, a novel P/N flame-retardant monomer (PDHAA) was synthesized through reacting phenyl dichlorophosphate (PDCP) with N-hydroxyethyl acrylamide (HEAA). The structure of PDHAA was confirmed using Fourier transform infrared (FTIR) spectroscopy and proton nuclear magnetic resonance (NMR) spectroscopy. PDHAA monomer and 2-hydroxyethyl methacrylate phosphate (PM-2) monomer were mixed at different mass ratios, to prepare UV-curable coatings, and then applied to the surface of fiber needled felts (FNFs), to improve their flame retardancy. PM-2 was introduced to reduce the curing time of the flame-retardant coatings and improve the adhesion between the coating and the fiber needled felts (FNFs). The research results indicated that the surface flame-retardant FNFs had a high limiting oxygen index (LOI) and rapidly self-extinguished in a horizontal combustion test and passed a UL-94 V-0 test. At the same time, the CO and CO2 emissions were greatly reduced, and the carbon residue rate was increased. In addition, the introduction of the coating improved the mechanical properties of the FNFs. Therefore, this simple and efficient UV-curable surface flame-retardant strategy has broad application prospects in the field of fire protection.