RESUMO
APAM was prepared under the action of composite initiator and UV irradiation, using acryl amide (AM), 2-acrylamido-2-methyl propane sulfonic acid (AMPS) and acrylic acid (AA) as raw materials. The paper studied the effect of proportion between monomers, monomer ratio, initiator concentration and other factors on intrinsic viscosity of the polymer, and optimized preparation conditions. The chemical structure and thermal stability of APAM were characterized by UV, FTIR, SEM and DTA-TGA respectively. The results showed that the APAM with the intrinsic viscosity 1.6 x 10(3) mL x g(-1) can prepared when the proportion between monomers was 70 : 10 : 10, the monomer ratio was 40%, initiator concentration was 0.20%, pH was 9 and the illumination time was 60 min.
RESUMO
Cationic degree has been investigated as an important factor in polyacrylamide materials. Diallyl dimethyl ammonium chloride and acrylamide (PDA) was grafted by free radical polymerisation of acrylamide monomer (AM) onto the cationic monomer dimethyl diallyl ammonium chloride (DMDAAC). In the present study, near infrared reflectance spectroscopy (NIRS) was used as a rapid and accurate method to determine the cationic degree in the PDA. In this experiment, the near infrared spectra of 37 PDA samples that were self-prepared in the laboratory from 900.00 to 1 700.00 were collected. The characteristic peaks and the entire spectrum segment as the input layer neurons in radical basis function (RBF) were investigated for establishing the mathematical conversion NIRS calibration mode. For reduction of the NIR spectrum noise, the wavelet analysis was used as pretreatment process. The measured value was determined by using precipitation titration and a comparison between the simulated value and measured value was made. It was found that the external validation determination coefficient was more than 0.9, and the simulation value is in good agreement with the measured value. The statistics analysis showed that there was no significant difference between simulated value and measured value. Therefore, the calibration model (RBF neural network) established in this paper exhibited a remarkable feasibility for predicting the cationic degree of PDA based on the near infrared spectroscopy.
RESUMO
In the presetn study, polymerized ferric sulphate (PFS) flocculant was prepared and tested. In the preparation of PFS flocculant, industrial by-product ferrous sulfate heptahydrate (FeSO4.7H2O) was reused as the main material. By composition with diatomite and drying up at certain temperature in vacuum drying oven, solid PFS flocculant was produced. Structural characteristics of the new flocculant product were examined through infrared spectroscopy and scanning electron microscopy (SEM), which showed that by compositing with diatomite, new group bridging emerged in the structure of PFS, which made the bond of groups stronger. In addition, part of the metalic contents in diatomite was polymerized with PFS, the product of which was polymerized ferric complex. Furthermore, the absorbing and agglomerating capacity of the diatomite carrier was significant. Considering the factors listed above, the new solid polymerized ferric sulphate (SPFS) flocculant was characterized with a larger molecule structure and enhanced absorbing, bridging and rolling sweep capacities. Through orthogonal experiment, optimum conditions of synthesis were as follows: the ratio of FeSO4.7H2O/diatomite in weight was 43/1, the reaction time is 1 h and the reaction temperature is 55 degrees C. By wastewater treatment experiment, it was found that the synthetic products showed good flocculation performance in the treatment of domestic sewage, the removal of COD was 80.00% and the removal of turbidity was 99.98%.