Surface and Structural Characterization of PVTMS Films Treated by Elemental Fluorine in Liquid Perfluorodecalin.

Poly(vinyl trimethylsilane) (PVTMS) films were subjected to direct surface fluorination in liquid medium (perfluorodecalin). The samples were investigated using several techniques: SEM-XEDS, XPS, ATR-IR, and contact angle measurement. The methods used allowed us to estimate chemical changes occurring because of the treatment. ATR-IR showed that most of the changes occurred in the Si(CH3)3 group. Monofluorinated Si(CH3)3 groups formed in the near-surface layer (Ge crystal, 0.66 µm penetration) after 30 min of fluorination, and then di- and trifluorinated groups appeared. Oxidation of the film with oxygen was also shown with the use of ZnSe crystal (2 µm penetration). The XPS method allowed an assessment of the ratio of the main elements at the surface of the fluorinated film. Two different exponential models were proposed to fit the experimental data of SEM-XEDS. Based on the model with the intercept, the depth of fluorination was estimated to be ≤1.1 µm, which is consistent with the result from the literature for the gas-phase fluorination. Contact angle measurements showed that oxidation of the PVTMS surface prevailed for the first 45 min of fluorination (surface hydrophilization) with a subsequent fluorine content increase and hydrophobization of the surface upon 60 min of fluorination.

Hydrophobic-Hydrophilic Properties and Characterization of PIM-1 Films Treated by Elemental Fluorine in Liquid Perfluorodecalin.

A direct fluorination technique was applied for the surface treatment of PIM-1 films in a liquid phase (perfluorodecalin). The fluorinated samples were analyzed by various instrumental techniques. ATR-IR spectroscopy showed that the fluorination predominantly takes place in methylene- and methyl-groups. Cyano-groups, aromatic hydrogens and the aromatic structure of the PIM-1 repeat unit were shown to be relatively stable at the fluorination conditions. XPS confirmed that the concentration of fluorine, as well as oxygen, in the near surface layer (~1 nm) increases with fluorination time. C1s and O1s surface spectra of the fluorinated PIM-1 samples indicated an appearance of newly-formed C-F and C-O functional groups. Scanning electron microscopy and X-ray energy-dispersive spectroscopy of the fluorinated PIM-1 samples showed an increase of the fluorine concentration at the surface (~0.1-1 µm) with the treatment duration. Analysis of the slices of the PIM-1 films demonstrated a decline of the fluorine content within several microns of the film depth. The decline increased with the fluorination time. A model of fluorine concentration dependence on the film depth and treatment duration was suggested. A change in the specific free surface energy as a result of PIM-1 fluorination was revealed. The fluorination time was shown to affect the surface energy (γSV), providing its shift from a low value (25 mJ∙m-2), corresponding to tetrafluoroethylene, up to a relatively high value, corresponding to a hydrophilic surface.

Effect of Direct Fluorination on the Transport Properties and Swelling of Polymeric Materials: A Review.

Fluorine-containing polymers occupy a peculiar niche among conventional polymers due to the unique combination of physicochemical properties. Direct surface fluorination of the polymeric materials is one of the approaches for the introduction of fluorine into the chemical structure that allows one to implement advantages of fluorinated polymers in a thin layer. Current review considers the influence of the surface interaction of the polymeric materials and membranes with elemental fluorine on gas, vapor and liquid transport as well as swelling and related phenomena. The increase in direct fluorination duration and concentration of fluorine in the fluorination mixture is shown to result mostly in a reduction of all penetrants permeability to a different extent, whereas selectivity of the selected gas pairs (He-H2, H2-CH4, He-CH4, CO2-CH4, O2-N2, etc.) increases. Separation parameters for the treated polymeric films approach Robeson's upper bounds or overcome them. The most promising results were obtained for highly permeable polymer, polytrimethylsilylpropyne (PTMSP). The surface fluorination of rubbers in printing equipment leads to an improved chemical resistance of the materials towards organic solvents, moisturizing solutions and reduce diffusion of plasticizers, photosensitizers and other components of the polymeric blends. The direct fluorination technique can be also considered one of the approaches of fabrication of fuel cell membranes from non-fluorinated polymeric precursors that improves their methanol permeability, proton conductivity and oxidative stability.

Direct Fluorination as Method of Improvement of Operational Properties of Polymeric Materials.

Direct fluorination of polymers is a widely utilized technique for chemical modification. Such introduction of fluorine into the chemical structure of polymeric materials leads to laminates with highly fluorinated surface layer. The physicochemical properties of this layer are similar to those of perfluorinated polymers that differ by a unique combination of chemical resistance, weak adhesion, low cohesion, and permittivity, often barrier properties, etc. Surface modification by elemental fluorine allows one to avoid laborious synthesis of perfluoropolymers and impart such properties to industrial polymeric materials. The current review is devoted to a detailed consideration of wetting by water, energy characteristics of surfaces, adhesion, mechanical and electrical properties of the polymers, and composites after the direct fluorination.