Preparation and Characterization of Durian Husk-Based Biocomposite Films Reinforced With Nanocellulose From Corn Husk and Pineapple Leaf.

This research explores the integration of corn husk nanocellulose (CHNc) and pineapple leaf nanocellulose (PLNc) as reinforcing agents in a carboxymethyl cellulose-based film derived from durian husk (CMCDH). Through a solvent-casting method, composite films were fabricated with varying nanocellulose contents (15, 30, and 45 wt%). Analysis using Fourier transform infrared spectroscopy and x-ray diffraction confirmed the effectiveness of alkaline and bleaching treatments in eliminating noncellulosic components. Transmission electron microscopy image revealed the rod-like morphology of CHNc and PLNc, with dimensions approximately 206.5 × 7.2 nm and 150.7 × 6.5 nm, respectively. The inclusion of nanocellulose decreased the transparency of CMCDH films while enhancing their tensile strength, thermal stability, and water vapor transmission rate. Notably, CMCDH/PLNc(30%) exhibited the highest tensile strength at 5.06 ± 0.83 MPa, representing a remarkable 220% increase compared to CMCDH biofilm. Thermogravimetric analysis and differential scanning calorimeter results indicated that nanocellulose incorporation delayed the film's decomposition temperature by approximately 10°C. Moreover, CMCDH/PLNc(30%) demonstrated the lowest water vapor transmission rate, marking a 20% improvement. However, the film's properties were compromised at the highest nanocellulose content (45 wt%) due to observed fiber aggregation, as revealed by scanning electron microscopy analysis.

Bacterial cellulose as an ideal potential treatment for burn wounds: A comprehensive review.

Burn wound regeneration is a complex process, which has many serious challenges such as slow wound healing, secondary infection, and inflammation. Therefore, it is essential to utilise appropriate biomaterials to accelerate and guide the wound healing process. Bacterial cellulose (BC), a natural polymer synthesised by some bacteria, has attracted much attention for wound healing applications due to its unique properties including excellent physicochemical and mechanical properties, simple purification process, three-dimensional (3D) network structure similar to extracellular matrix, high purity, high water holding capacity and significant permeability to gas and liquid. BC's lack of antibacterial activity significantly limits its biomedical and tissue engineering application, but adding antimicrobial agents to it remarkably improves its performance in tissue regeneration applications. Burn wound healing is a complex long-lasting process. Using biomaterials in wound treatment has shown that they can satisfactorily accelerate wound healing. The purpose of this review is to elaborate on the importance of BC-based structures as one of the most widely used modern wound dressings in the treatment of burn wounds. In addition, the combination of various drugs, agents, cells and biomolecules with BC to expand its application in burn injury regeneration is discussed. Finally, the main challenges and future development direction of BC-based structures for burn wound repair are considered. The four most popular search engines PubMed/MEDLINE, Science Direct, Scopus and Google Scholar were used to help us find relevant papers. The most frequently used keywords were bacterial cellulose, BC-based biocomposite, wound healing, burn wound and vascular graft.

Bio-Polyethylene and Polyethylene Biocomposites: An Alternative toward a Sustainable Future.

Polyethylene (PE), a highly prevalent non-biodegradable polymer in the field of plastics, presents a waste management issue. To alleviate this issue, bio-based PE (bio-PE), derived from renewable resources like corn and sugarcane, offers an environmentally friendly alternative. This review discusses various production methods of bio-PE, including fermentation, gasification, and catalytic conversion of biomass. Interestingly, the bio-PE production volumes and market are expanding due to the growing environmental concerns and regulatory pressures. Additionally, the production of PE and bio-PE biocomposites using agricultural waste as filler materials, highlights the growing demand for sustainable alternatives to conventional plastics. According to previous studies, addition of ≈50% defibrillated corn and abaca fibers into bio-PE matrix and a compatibilizer, results in the highest Young's modulus of 4.61 and 5.81 GPa, respectively. These biocomposites have potential applications in automotive, building construction, and furniture industries. Moreover, the advancement made in abiotic and biotic degradation of PE and PE biocomposites is elucidated to address their environmental impacts. Finally, the paper concludes with insights into the opportunities, challenges, and future perspectives in the sustainable production and utilization of PE and bio-PE biocomposites. In summary, production of PE and bio-PE biocomposites can contribute to a cleaner and sustainable future.

Remediation of acetamiprid pesticide from contaminated water by antibacterial biosorbent based on carboxymethyl tragacanth-grafted-poly(3-aminophenol) decorated with ZnO@Fe3O4.

Pesticides can have harmful impacts on the environment and living organisms. Thus, removing them from polluted water is crucial. In this study, a bionanocomposite of carboxymethyl tragacanth-grafted-poly(3-aminophenol)/zinc oxide@iron oxide (CMT-g-P3AP/ZnO@Fe3O4) synthesized by in situ copolymerization as an efficient adsorbent to eliminate the acetamiprid pesticide from polluted water. The CMT-g-P3AP/ZnO@Fe3O4 magnetic nanocomposite was analyzed utilizing various techniques including FTIR, EDX, FESEM, XRD, BET, CHNSO, and TGA. The results displayed that the resulting nanocomposite with maximum adsorption capacity (Qmax) successfully removed the acetamiprid pesticide from polluted water under optimal conditions such as pH of 7.00, 5.00 mg of adsorbent, 20.0 min duration, and 400 mg/L acetamiprid concentration. According to the linear Langmuir isotherm, the Qmax of the biosorbent was 833 mg/g. The experimental adsorption data fitted well with Temkin's nonlinear isotherm model. The adsorption kinetic data were closely related to the Weber-Morris intraparticle diffusion nonlinear model. After three repetitive cycles, CMT-g-P3AP/ZnO@Fe3O4 can be outstandingly renewed and recycled without significant reduction in its adsorption efficacy, as evidenced by the adsorption-desorption experiments. In addition, the CMT-g-P3AP/ZnO@Fe3O4 displayed the good antibacterial activity against E. coli and S. aureus.

Marine biofilm formation on flax fibre reinforced biocomposites.

Artificial reefs represent useful tools to revitalize coastal and ocean ecosystems. Their formulation determines the biofilm formation which is the prerequisite for the colonization process by marine micro- and macroorganisms. In comparison with concrete, biobased polymers offer improved characteristics, including architecture, formulation, rugosity and recycling. This article aims to explore a new scale of artificial reef made of biocomposites reinforced with a high flax fibre (Linum utilatissimum) content (30%). Cellular adhesion and resulting biofilm formation were assessed using two marine microorganisms: Pseudoalteromonas sp. 3J6 and Cylindrotheca closterium. The influence of flax fibre leachates and plastic monomers on the growth of those marine microorganisms were also evaluated. Results indicated that the introduction of flax fibres inside the polymer matrix modified its physicochemical properties thus modulating adhesion and biofilm formation depending on the microorganism. This study gives insights for further developments of novel functionalized artificial reefs made of biocomposites.

Human health risk assessment framework for new water resource recovery-based bio-composite materials.

A new type of bio-composite material is being produced from water-recovered resources such as cellulose fibres from wastewater, calcite from the drinking water softening process, and grass and reed from waterboard sites. These raw materials may be contaminated with pathogens and chemicals such as Escherichia coli, heavy metals, and resin compounds. A novel risk assessment framework is proposed here, addressing human health risks during the production of new bio-composite materials. The developed framework consists of a combination of existing risk assessment methods and is based on three main steps: hazard identification, qualitative risk mapping, and quantitative risk assessment. The HAZOP and Event Tree Analysis methodologies were used for hazard identification and risk mapping stages. Then, human health risks were quantitatively assessed using quantitative chemical risk assessment, evaluating cancer and non-cancer risk, and quantitative microbial risk assessment. The deterministic and the stochastic approaches were performed for this purpose. The contamination of raw materials may pose human health concerns, resulting in cancer risk above the threshold. Microbial risk is also above the safety threshold. Additional analysis would be significant as future research to better assess the microbial risk in biocomposite production. The framework has been effectively used for chemical and microbial risk assessment.

Chitosan Biocomposites with Variable Cross-Linking and Copper-Doping for Enhanced Phosphate Removal.

The fabrication of chitosan (CH) biocomposite beads with variable copper (Cu2+) ion doping was achieved with a glutaraldehyde cross-linker (CL) through three distinct methods: (1) formation of CH beads was followed by imbibition of Cu(II) ions (CH-b-Cu) without CL; (2) cross-linking of the CH beads, followed by imbibition of Cu(II) ions (CH-b-CL-Cu); and (3) cross-linking of pristine CH, followed by bead formation with Cu(II) imbibing onto the beads (CH-CL-b-Cu). The biocomposites (CH-b-Cu, CH-b-CL-Cu, and CH-CL-b-Cu) were characterized via spectroscopy (FTIR, 13C solid NMR, XPS), SEM, TGA, equilibrium solvent swelling methods, and phosphate adsorption isotherms. The results reveal variable cross-linking and Cu(II) doping of the CH beads, in accordance with the step-wise design strategy. CH-CL-b-Cu exhibited the greatest pillaring of chitosan fibrils with greater cross-linking, along with low Cu(II) loading, reduced solvent swelling, and attenuated uptake of phosphate dianions. Equilibrium and kinetic uptake results at pH 8.5 and 295 K reveal that the non-CL Cu-imbibed beads (CH-b-Cu) display the highest affinity for phosphate (Qm = 133 ± 45 mg/g), in agreement with the highest loading of Cu(II) and enhanced water swelling. Regeneration studies demonstrated the sustainability and cost-effectiveness of Cu-imbibed chitosan beads for controlled phosphate removal, whilst maintaining over 80% regenerability across several adsorption-desorption cycles. This study offers a facile synthetic approach for controlled Cu2+ ion doping onto chitosan-based beads, enabling tailored phosphate oxyanion uptake from aqueous media by employing a sustainable polysaccharide biocomposite adsorbent for water remediation by mitigation of eutrophication.

Design and Evaluation of Inorganic/Organic Hybrid Bio-composite for Site-Specific Oral Delivery of Darifenacin.

Benign hyperplasia (BHP) is a common disorder that affects men over the age of 60 years. Transurethral resection of the prostate (TURP) is the gold standard for operative treatment, but a range of drugs are also available to improve quality of life and to reduce BHP-associated urinary tract infections and complications. Darifenacin, an anti-muscarinic agent, has been found effective for relieving symptoms of overactive bladder associated with BHP, but the drug has poor solubility and bioavailability, which are major challenges in product development. An inorganic/organic bio-composite with gastric pH-resistant property was synthesized for the targeted oral delivery of Darifenacin to the lower gastrointestinal tract (GIT). This development was accomplished through co-precipitation of calcium carbonate in quince seed-based mucilage. The FTIR, XRD, DSC, and TGA results showed good drug-polymer compatibility, and the SEM images showed calcite formation in the quince hydrogel system. After 72 h, the drug release of 34% and 75% were observed in acidic (0.1N HCl) and 6.8 pH phosphate buffer, respectively. A restricted/less drug was permeated through gastric membrane (21.8%) as compared to permeation through intestinal membrane (65%.) The developed composite showed significant reduction in testosterone-induced prostatic hyperplasia (2.39 ± 0.12***) as compared to untreated diseased animal group. No sign of organ toxicity was observed against all the developed composites. In this study, we developed an inorganic-organic composite system that is highly biocompatible and effective for targeting the lower GIT, thereby avoiding the first-pass metabolism of darifenacin.

Characterisation of Bambara groundnut (Vigna subterranea (L.) Verdc.) shell waste as a potential biomass for different bio-based products.

Efforts are ongoing to utilise agricultural waste to achieve a full resource use approach. Bambara groundnut is an important crop widely grown in the sub-Saharan Africa with potential future importance because of its resilience to thrive under heightened weather uncertainty and widespread droughts that have challenged food security. After harvesting, the edible nuts are separated from the shells which are discarded as waste. Therefore, this research is aimed at characterising the chemical composition and the structural properties of Bambara groundnut shells (BGS) in view of their potential application as a biomass for different bio-products. The chemical composition of BGS was found to be 42.4% cellulose, 27.8% hemicellulose, 13% lignin and 16.8% extractives. Proximate analysis showed a high amount of volatile matter (69.1%) and low moisture (4.4%). XRD analysis confirmed crystallinity of cellulose I polymer and FTIR analysis observed functional groups of lignocellulosic compounds. Thermal stability, maximum degradation temperature and activation energy were found to be 178.5 °C, 305.7 °C and 49.4 kJ/mol, respectively. Compared to other nutshells, BGS were found to have a relatively high amount of cellulose and crystallinity that may result in biocomposites with improved mechanical properties.

Sustainable Thermal Energy Batteries from Fully Bio-Based Transparent Wood.

The sustainable development of functional energy-saving building materials is important for reducing thermal energy consumption and promoting natural indoor lighting. Phase-change materials embedded in wood-based materials are candidates for thermal energy storage. However, the renewable resource content is usually insufficient, the energy storage and mechanical properties are poor, and the sustainability aspect is unexplored. Here a novel fully bio-based transparent wood (TW) biocomposite for thermal energy storage, combining excellent heat storage properties, tunable optical transmittance, and mechanical performance is introduced. A bio-based matrix based on a synthesized limonene acrylate monomer and renewable 1-dodecanol is impregnated and in situ polymerized within mesoporous wood substrates. The TW demonstrates high latent heat (89 J g-1 ) exceeding commercial gypsum panels, combined with thermo-responsive optical transmittance (up to 86%) and mechanical strength up to 86 MPa. The life cycle assessment shows that the bio-based TW has a 39% lower environmental impact than transparent polycarbonate panels. The bio-based TW holds great potential as scalable and sustainable transparent heat storage solution.

Continuous removal of pharmaceutical drug chloroquine and Safranin-O dye from water using agar-graphene oxide hydrogel: Selective adsorption in batch and fixed-bed experiments.

In this work, Chloroquine diphosphate, and the cationic dye Safranin-O were selectively removed from water using the agar-graphene oxide (A-GO) hydrogel, produced via simple one-step jellification process. The morphology of the A-GO biocomposite was characterized and batch experiments were performed, with adsorption isotherms satisfactorily fitting (R2 > 0.98) Sips (Safranin-O) and Freundlich (Chloroquine) isotherms. Driving force models and Fick's diffusion equation were applied to the modeling of kinetic data, and a satisfactory fit was obtained. Selective adsorption carried out in batch indicated that competitive adsorption occurs when both components are mixed in water solution - the adsorptive capacities dropped ∼10 mg g-1 for each component, remaining 41 mg g-1 for safranin-O and 31 mg g-1 for chloroquine. Fixed-bed breakthrough curves obtained in an adsorption column showed adsorption capacities over 63 mg g-1 and 100 mg g-1 for chloroquine and safranin-O, respectively, also exhibiting outstanding regenerative potentials. Overall, the biocomposite produced using graphene oxide proved to be a viable and eco-friendly alternative to continuously remove both contaminants from water.

Transforming municipal cotton waste into a multilayer fibre biocomposite with high strength.

We analyzed the problematic textile fiber waste as potential precursor material to produce multilayer cotton fiber biocomposite. The properties of the products were better than the current dry bearing type particleboards and ordinary dry medium-density fiberboard in terms of the static bending strength (67.86 MPa), internal bonding strength (1.52 MPa) and water expansion rate (9.57%). The three-layer, four-layer and five-layer waste cotton fiber composite (WCFC) were tried in the experiment, the mechanical properties of the three-layer WCFC are insufficient, the five-layer WCFC is too thick and the four-layer WCFC had the best comprehensive performance. The cross-section morphology of the four-layer WCFC shows a dense structure with a high number of adhesives attached to the fiber. The hardness and stiffness of the four-layer cotton fiber composite enhanced by the high crystallinity of cellulose content, and several chemical bondings were presence in the composites. Minimum mass loss (30%) and thermal weight loss rate (0.70%/°C) was found for the four-layer WCFC. Overall, our findings suggested that the use of waste cotton fiber (WCF) to prepare biocomposite with desirable physical and chemical properties is feasible, and which can potentially be used as building material, furniture and automotive applications.

Physicochemical and Functional Properties and Storage Stability of Chitosan-Starch Films Containing Micellar Nano/Microstructures with Turmeric and Hibiscus Extracts.

The dynamic development of the food industry and the growing interest of consumers in innovative solutions that increase the comfort and quality of life push the industry towards seeking pioneering solutions in the field of food packaging. Intelligent and active packaging, which affects the quality and durability of food products and allows one to determine their freshness, is still a modern concept. The aim of our study was to obtain two types of films based on chitosan and starch with micellar nanostructures containing extracts from turmeric rhizomes and hibiscus flowers. The presence of spherical nanostructures was confirmed using a scanning electron microscope. The structural and optical properties of the obtained composites were characterised by Fourier-transform infrared (FTIR), UltraViolet-Visible (UV-VIS), and photoluminescence (PL) spectroscopy. Scanning electron microscopy (SEM) analysis confirmed the presence of spherical micellar structures with a size of about 800 nm in the obtained biocomposites. The presence of nano-/microstructures containing extracts affected the mechanical properties of the composites: it weakened the strength of the films and improved their elongation at break (EAB). Films with nano-/microparticles were characterised by a higher water content compared to the control sample and lower solubility, and they showed stronger hydrophilic properties. Preliminary storage tests showed that the obtained biocomposites are sensitive to changes occurring during the storage of products such as cheese or fish. In addition, it was found that the film with the addition of turmeric extract inhibited the growth of microorganisms during storage. The results suggest that the obtained bionanocomposites can be used as active and/or intelligent materials.

Biosynthesis of bionanomaterials using Bacillus cereus for the recovery of rare earth elements from mine wastewater.

The growing demand for rare earth elements (REEs) increasingly requires secondary resources such as mine wastewater containing high concentrations of REEs, to be used as a source of REEs. The current challenge is how to efficiently recover REEs from this feed source. In this paper, a functional bionanomaterial (FeNPs-EPS) was biosynthesized using Bacillus cereus as a possible means of recovering REEs. This composite was composed of both synthesized iron nanoparticles (FeNPs) and extracellular polymeric substances (EPS). Synthesis of the FeNPs-EPS composite via a one-step biosynthesis was confirmed by materials characterization. The peak in the material's UV-Vis spectra at 511 nm demonstrates the formation of FeNPs-EPS, where 3D-EEM showed that FeNPs-EPS was wrapped predominantly with tryptophan protein-like and humic acid-like substances. In addition, while FTIR indicated that the functional groups present in EPS where virtually identical to those observed in FeNPs-EPS, XPS demonstrated that Fe and O were the major elemental present as both FeO and Fe2O3. Zeta potential measurements indicated that FeNPs-EPS had good stability under different pH conditions, where BET analysis supported multilayer adsorption. Finally, on exposure to high concentrations of Eu(III) and Tb(III) in mine wastewater, the synthesized FeNPs-EPS demonstrated strong potential to remove two cations from the wastewater and hence a potentially practical way to efficiently recover REEs from such waste streams.

Recycling of Waste Bamboo Biomass and Papermaking Waste Liquid to Synthesize Sodium Lignosulfonate/Chitosan Glue-Free Biocomposite.

The development of the paper industry has led to the discharge of a large amount of papermaking waste liquid containing lignosulfonate. These lignin black liquids cause a lot of pollution in nature, which runs counter to the current environmental protection strategy under the global goal. Through the development and use of lignosulfonate in papermaking waste liquid to increase the utilization of harmful substances in waste liquid, we aim to promote waste liquid treatment and reduce environmental pollution. This paper proposes a new strategy to synthesize novel glue-free biocomposites with high-performance interfacial compatibility from papermaking by-product sodium lignosulfonate/chitosan (L/C) and waste bamboo. This L/C bamboo biocomposite material has good mechanical properties and durability, low formaldehyde emissions, a high recovery rate, meets the requirements of wood-based panels, and reduces environmental pollution. This method is low in cost, has the potential for large-scale production, and can effectively reduce the environmental pollution of the paper industry, promoting the recycling of biomass and helping the future manufacture of glue-free panels, which can be widely used in the preparation of bookcase, furniture, floor and so on.

Effects of Wood Content and Modification on Properties of Wood Flour/Polybutylene Adipate Terephthalate Biocomposites.

Biodegradable polymers have recently become attractive and have been increasingly used as matrix materials to replace fossil plastics due to concerns about the environmental issue. However, their application areas are limited due to their high costs and natural properties. In this study, we fabricated ecofriendly and economical polybutylene adipate terephthalate (PBAT) composites loaded with various concentrations of wood flour (WF) to investigate the effects on the PBAT and WF interfaces as well as the physical properties of the WF/PBAT biocomposites. Then, WF was acetylated with acetic anhydride, and the effect of WF acetylation on the mechanical and thermal properties of the biocomposites were investigated. The results showed that the tensile strength, tensile modulus, flexural strength and flexural modulus increased with WF loading in the composites, and acetylation could not only further increase these properties, but also increase the impact strength and elongation at break. The incorporation of WF would weaken the thermal stability of PBAT, but the thermal stability of the biocomposite could be improved after WF acetylation. The cold crystallization temperature and hydrophobicity of the WF/PBAT samples would be increased with the increasing load of the WF, while the melting enthalpy and the crystallinity of the samples reduced gradually. A morphological analysis of the modified composites revealed that the matrix exhibited greater interfacial interactions with the WF compared to the WF/PBAT. Considering the much lower cost of WF compared to PBAT, the improved properties of WF/PBAT biocomposites will make it economically competitive with other commercial polymers, and these biocomposites should have much wider application areas.

Newly developed nano-biocomposite embedded hydrogel to enhance drug loading and modulated release of anti-inflammatory drug.

A newly developed iron-based nano-biocomposite (nano Fe-CNB) impregnated alginate formulation (CA) is proposed to improve drug loading and exhibit pH-responsive behavior of model anti-inflammatory drug-ibuprofen for controlled release applications. The proposed formulation is investigated with conventional ß-CD addition in CA. The nano Fe-CNB-based formulations with and without ß-CD, (Fe-CNB ß-CD CA and Fe-CNB CA) are compared with only CA and ß-CD incorporated CA formulations. The results indicate the incorporation of nano-biocomposite or ß-CD into CA enhances the drug loading (>40%). However, pH-responsive controlled release behavior is observed for nano Fe-CNB based formulations only. The release studies from Fe-CNB ß-CD CA indicate ∼ 45% release in stomach pH (1.2) within 2 h. In contrast, Fe-CNB CA shows ∼20% release only in stomach pH and improved release (∼49%) at colon pH (7.4). The rheology and swelling studies indicate Fe-CNB CA remains intact in stomach pH with a minimal drug release, but it disintegrates at colon pH due to charge reversal behavior of nano-biocomposite and ionization of polymeric chains. Thus, Fe-CNB CA formulation is found to be a potential candidate for targeting colon delivery, inflammatory bowel disease, and post-operative conditions.

Formulation and Evaluation of Chitosan-PLGA Biocomposite Scaffolds Incorporated with Quercetin Liposomes Made by QbD Approach for Improved Healing of Oral Lesions.

The current research aims to develop and evaluate chitosan-PLGA biocomposite scaffolds in combination with quercetin liposomes to accomplish the desired impact in oral lesions where pharmacotherapeutic agent treatment through circulation could only reach the low content at the target. Optimization of quercetin-loaded liposomes was carried out using 32 factorial design. The preparation of porous scaffolds comprising produced quercetin-loaded liposomes by thin-film method was carried out in the current study using a unique strategy combining solvent casting and gas foaming procedures. The prepared scaffolds were tested for physicochemical properties, in vitro quercetin release study, ex vivo drug permeation and retention research using goat mucosa, antibacterial activity, and cell migration studies on fibroblast L929 cell lines. Improved cell growth and migration were seen in the order control < liposomes < proposed system. The proposed system has been examined for its biological and physicochemical features, and it has the potential to be utilized as an efficient therapy for oral lesions.

Multiscale micromechanics modeling of plant fibers: upscaling of stiffness and elastic limits from cellulose nanofibrils to technical fibers.

The mechanical properties of natural fibers, as used to produce sustainable biocomposites, vary significantly-both among different plant species and also within a single species. All plants, however, share a common microstructural fingerprint. They are built up by only a handful of constituents, most importantly cellulose. Through continuum micromechanics multiscale modeling, the mechanical behavior of cellulose nanofibrils is herein upscaled to the technical fiber level, considering 26 different commonly used plants. Model-predicted stiffness and elastic limit bounds, respectively, frame published experimental ones. This validates the model and corroborates that plant-specific physicochemical properties, such as microfibril angle and cellulose content, govern the mechanical fiber performance.

Polyhydroxyalkanoates biopolymers toward decarbonizing economy and sustainable future.

Polymers are synonymous with the modern way of living. However, polymers with a large carbon footprint, especially those derived from nonrenewable petrochemical sources, are increasingly perceived as detrimental to the environment and a sustainable future. Polyhydroxyalkanoate (PHA) is a microbial biopolymer and a plausible alternative for renewable sources. However, PHA in its monomeric forms has very limited applications due to its limited flexibility, tensile strength, and moldability. Herein, the life cycle of PHA molecules, from biosynthesis to commercial utilization for diverse applications is discussed. For clarity, the applications of this bioplastic biocomposite material are further segregated into two domains, namely, the industrial sector and the medical sector. The industry sectors reviewed here include food packaging, textiles, agriculture, automotive, and electronics. High-value addition of PHA for a sustainable future can be foreseen in the medical domain. Properties such as biodegradability and biocompatibility make PHA a suitable candidate for decarbonizing biomaterials during tissue repair, organ reconstruction, drug delivery, bone tissue engineering, and chemotherapeutics.