Effect of Ti on the Structure and Mechanical Properties of TixZr2.5-xTa Alloys.
Zhang, Bin; Tang, Yu; Li, Shun; Ye, Yicong; Zhu, Li'an; Zhang, Zhouran; Liu, Xiyue; Wang, Zhen; Bai, Shuxin.
Affiliation
  • Zhang B; Department of Materials Science and Engineering, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha 410073, China.
  • Tang Y; Department of Materials Science and Engineering, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha 410073, China.
  • Li S; Department of Materials Science and Engineering, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha 410073, China.
  • Ye Y; Department of Materials Science and Engineering, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha 410073, China.
  • Zhu L; Department of Materials Science and Engineering, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha 410073, China.
  • Zhang Z; Department of Materials Science and Engineering, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha 410073, China.
  • Liu X; Department of Materials Science and Engineering, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha 410073, China.
  • Wang Z; Department of Materials Science and Engineering, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha 410073, China.
  • Bai S; Department of Materials Science and Engineering, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha 410073, China.
Entropy (Basel) ; 23(12)2021 Dec 04.
Article in En | MEDLINE | ID: mdl-34945938
To determine the effects of Ti and mixing entropy (ΔSmix) on the structure and mechanical proper-ties of Zr-Ta alloys and then find a new potential energetic structural material with good me-chanical properties and more reactive elements, TixZr2.5-xTa (x = 0, 0.5, 1.0, 1.5, 2.0) alloys were investigated. The XRD experimental results showed that the phase transformation of TixZr2.5-xTa nonequal-ratio ternary alloys depended not on the value of ΔSmix, but on the amount of Ti atoms. With the addition of Ti, the content of the HCP phase decreased gradually. SEM analyses revealed that dendrite morphology and component segregation increasingly developed and then weakened gradually. When x increases to 2.0, TixZr2.5-xTa with the best mechanical properties can be ob-tained. The yield strength, compressive strength and fracture strain of Ti2.0Zr0.5Ta reached 883 MPa, 1568 MPa and 34.58%, respectively. The dependence of the phase transformation and me-chanical properties confirms that improving the properties of Zr-Ta alloys by doping Ti is feasible.
Key words
Fulltext
Print
XML
PubMed Links
Search on Google

Full text: 1 Collection: 01-internacional Database: MEDLINE Language: En Journal: Entropy (Basel) Year: 2021 Type: Article Affiliation country: China
Fulltext
Print
XML
PubMed Links
Search on Google

Full text: 1 Collection: 01-internacional Database: MEDLINE Language: En Journal: Entropy (Basel) Year: 2021 Type: Article Affiliation country: China