Influence of different drying methods on microtensile bond strength of self-adhesive resin cements to dentin.
Acta Odontol Scand
; 72(8): 954-62, 2014 Nov.
Article
em En
| MEDLINE
| ID: mdl-24922092
ABSTRACT
OBJECTIVE:
This study investigated the effect of different drying methods of dentin surface on the bonding efficacy of self-adhesive resin cements (SRCs). MATERIALS ANDMETHODS:
Three SRCs (RelyX U200, RU; Maxcem Elite, ME; and BisCem, BC) and one resin-modified glass ionomer cement (RelyX Luting 2, RL) were used. The characteristics of the materials were evaluated using thermogravimetric analysis and surface roughness and contact angle measurements. Human dentin surfaces were finished with 600-grit silicon carbide paper and assigned to three groups according to these dryingmethods:
ethanol dehydration, drying by waiting for 10 s after blot-drying and blot-drying. The four cements were used for luting composite overlays to the dried dentin. After 24 h storage at 37°C and 100% relative humidity, stick-shaped specimens with a cross-sectional area of 0.8 mm(2) were prepared and stressed to failure in tension at a crosshead speed of 0.5 mm/min (n = 27). Failure modes of fractured specimens were assessed by optical and scanning electron microscopy.RESULTS:
RL was the most hydrophilic, followed by BC and ME and then RU. All the luting cements luted to ethanol-dehydrated dentin showed zero bond strengths. For the three SRCs, drying by waiting produced higher microtensile bond strengths than blot-drying. RU showed the best bonding performance in the above two dentin conditions. RL showed significantly higher bond strength in blot-drying condition than in drying-by-waiting (p < 0.001).CONCLUSIONS:
This study suggests that dentin surface moisture has a crucial effect on the bond strength of SRCs.Palavras-chave
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Assunto principal:
Colagem Dentária
/
Cimentos de Resina
/
Dentina
Limite:
Humans
Idioma:
En
Revista:
Acta Odontol Scand
Ano de publicação:
2014
Tipo de documento:
Article