High performance of membrane capacitive deionization with ZnS/g-C3N4 composite electrodes.

ABSTRACT

Capacitive deionization (CDI) is considered a promising technology for desalination of sea or brackish water. In this study, a ZnS/g-C3N4 composite was synthesized through a one-step high-temperature method and used as the main material to fabricate CDI electrodes. The results of SEM and TEM showed that spherical-like nanoparticles of ZnS were uniformly distributed on the g-C3N4 sheet. The g-C3N4 phase facilitates the ZnS particles precipitate and restrain their agglomeration, which contributes to a high specific surface area of ZnS. Furthermore, the electrochemical test results indicated that ZnS/g-C3N4 composite had a good capacitance characteristic, low resistance, and high electrochemical stability. Finally, the desalinization performance of the ZnS/g-C3N4 composite electrodes was tested in traditional mode and membrane capacitive deionization (MCDI) mode. The results showed that ZnS/g-C3N4//ZnS/g-C3N4 (MCDI) exhibited an optimal desalination capacity. The adsorption amount was 27.65, 50.26, and 65.34 mg/g for NaCl initial concentration of 200, 400, and 600 mg/L, respectively, with the voltage of 1.2 V and flow rate of 5 mL/min. Increasing initial concentration enhanced the conductivity and ion migration rate so as to increase the NaCl adsorption amount. ZnS/g-C3N4 composite can be used as potential electrode material for high performance of MCDI.