Braz. j. oral sci ; 18: e191406, jan.-dez. 2019. tab
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-1094951

RESUMO

Aim: To evaluate the bond strength (BS) and failure mode of orthodontic tubes treated with different alloy primers at the interface among enamel, resin and orthodontic tubes. Methods: Orthodontic tubes were bonded to the enamel of 80 bovine incisors with the orthodontic resin (Transbond XT, 3M Unitek). Prior to bonding, the tubes were chemically treated with (n=20) Metal/Zirconia Primer (MZ, Ivoclar), Scothbond Universal (SB, 3M Espe); Orthoprimer (OP, Morelli) or left untreated (Control - C). Specimens were submitted to 5,000 thermal cycles (5 and 55o C) to age the bonded interface. A shear BS test and failure modes were conducted, and the results were analyzed using one-way analysis of variance and Fisher's exact test, respectively. Results: No differences were observed among groups regardless of the type of alloy primer used (p = 0.254). However, no differences were observed among the failure modes of the groups tested (p=0.694). The adhesive failure mode between the resin and enamel was the most prevalent failure (45%) for groups OP and C, whereas cohesive failure in the orthodontic resin was the most prevalent failure (40%) for groups SB and MZ. Conclusion: Alloy primers were unable to increase the BS of the orthodontic tubes to enamel


Assuntos
Animais , Bovinos , Ortodontia , Teste de Materiais , Colagem Dentária , Resistência ao Cisalhamento
2.
Braz. j. oral sci ; 18: e191649, jan.-dez. 2019. ilus
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-1095175

RESUMO

Aim: To evaluate the performance of three digital radiographic systems in the analysis of root canal filling quality using different intracanal materials for primary teeth. Methods: Twenty-five bovine teeth were divided into 5 groups: Calen® combined with iodoform; Calen® combined with zinc oxide; zinc oxide and eugenol; UltraCal®XS, and 2% chlorhexidine combined with Ca(OH)2 + zinc oxide. Periapical radiographs were obtained with the VistaScan, Express, and SnapShot systems. The quality of the images was evaluated objectively (radiopacity) and subjectively (apical sealing and filling homogeneity). As the reference standard, the teeth were scanned with a micro-CT device. Results: Radiopacity differed among the radiographic systems and materials tested. In general, the greatest difference was observed between the Express and VistaScan systems; Calen® combined with iodoform resulted in the highest radiopacity. The radiographic systems did not differ in terms of homogeneity. However, Calen® combined with iodoform differed from the other materials and exhibited the best results. Regarding apical sealing, the SnapShot system and Calen® combined with zinc oxide provided the best results. Conclusion: Direct digital systems show better performance in evaluating the quality of endodontic treatment in primary teeth and should be preferred for this purpose


Assuntos
Animais , Bovinos , Materiais Restauradores do Canal Radicular , Dente Decíduo , Radiografia Dentária Digital
3.
Ortho Sci., Orthod. sci. pract ; 45(12): 90-94, 2019. tab, graf
Artigo em Português | BBO - Odontologia | ID: biblio-994983

RESUMO

O objetivo neste estudo foi avaliar a influência da base de bráquetes cerâmicos na resistência de união ao esmalte bovino. Oitenta incisivos bovinos foram distribuídos em quatro grupos (n=20), de acordo com o tipo de base de retenção dos bráquetes ortodônticos: 1) Ceramic (Morelli): retenção por microcavidades; 2) Iceram (Orthometric): retenção por microcavidades; 3) Transcend Series 6000 (3M/ESPE): retenção por jateamento e 4) bráquetes 20/40 (American Orthododontics): retenção por canaletas. Os dentes foram condicionados com ácido fosfórico a 37% e os bráquetes colados com a resina composta Orthocem. Após 24 horas foi avaliada a resistência ao cisalhamento em máquina de ensaio Instron a uma velocidade de 0,5 mm/minuto. Após os testes, o índice de remanescente adesivo (IRA) foi analisado em lupa estereoscópica. Os dados foram analisados pelo teste de Kruskal-Wallis e Tukey com nível de significância de 5%. Os resultados mostraram que houve diferença significativa entre os bráquetes (p=0,003). Os bráquetes 20/40 (6,81 MPa) e Transcend 6000 (6,26 MPa) apresentaram resistência ao cisalhamento significativamente maior em relação aos Ceramic (4,00 MPa). Os bráquetes Iceram (5,83 MPa) não diferiram significativamente dos demais bráquetes. A avaliação do IRA mostrou que nos bráquetes com microcavidades houve predomínio de falhas entre a resina e o dente, diferentemente dos demais bráquetes. Pode-se concluir que os bráquetes com retenção de canaleta e jateados obtiveram melhores resultados comparados àqueles com retenção por microcavidades.(AU)


The aim of this study was to evaluate the influence of ceramic bracket bases on the bond strength to bovine enamel. Eighty bovine incisors were divided into four groups (n=20), according to the type of orthodontic bracket retention base: 1) Ceramic (Morelli): retention by means of microcavities; 2) Iceram (Orthometric): retention by means of microcavities; 3) Transcend Series 6000 (3M/ESPE): retention by sandblasting and 4) 20/40 brackets (American Orthododontics): retention by dovetail grooves. The teeth were etched with 37% phosphoric acid, and brackets were bonded with Orthocem composite resin. After 24 hours the shear bond strength was evaluated in an Instron test machine at speed of 0.5 mm/minute. After the tests, the adhesive remnant index (ARI) was analyzed under a stereoscopic magnifying glass. The data were analyzed by Kruskal-Wallis and Tukey test, significance level of 5%. The results showed statistically significant differences between the brackets (p=0.003). The 20/40 (6.81 MPa) and Transcend 6000 (6.26 MPa) brackets presented significantly higher shear bond strength than the Ceramic brackets (4.00 MPa). The Iceram brackets (5.83 MPa) did not differ significantly from other brackets. ARI evaluation showed that in brackets with microcavities there was a predominance of flawns between resin and the tooth, different from other brackets. It was concluded that brackets with dovetail grooves retention and sandblasted obtained better results than the brackets with microcavities. retention.(AU)


Assuntos
Bovinos , Cerâmica , Braquetes Ortodônticos , Esmalte Dentário , Resistência ao Cisalhamento
4.
Rio de Janeiro; s.n; 2019. 41 p. ilus, tab.
Tese em Português | BBO - Odontologia | ID: biblio-1021473

RESUMO

em polímeros, resulta em propriedades mecânicas satisfatórias para a adesão. Alterações na formulação dos materiais resinosos têm sido propostas com intuito de solucionar os problemas relacionados à polimerização desses sistemas, desta forma, fotoiniciadores diferentes da canforoquinona e que relatam maior grau de conversão têm sido utilizados. No entanto, o uso inadvertido de sistemas adesivos associados a compósitos odontológicos com diferentes sistemas de fotoiniciadores pode ocasionar uma redução na eficicácia da polimerização e, como consequência, da resistência adesiva. O objetivo deste estudo in vitro foi avaliar a influência dos fotoiniciadores na resistência à microtração de sistemas adesivos e resinas compostas na dentina bovina. Quarenta fragmentos dentais, com superfícies em dentina planificadas e lisas, obtidos da face vestibular coronária de incisivos bovinos hígidos, foram distribuídos aleatoriamente em 4 grupos experimentais (n=10) de acordo com os diferentes sistemas adesivos e resinas compostas utilizados: Grupo AAPS + VAPS (Ambar APS + Vittra APS); Grupo AAPS + O (Ambar APS + Opallis); Grupo A + VAPS (Ambar + Vittra APS); Grupo A + O (Ambar + Opallis). Após restauração com compósito, as amostras foram seccionadas para obtenção de palitos que foram submetidos ao teste de microtração (1,0 mm/min). Os dados obtidos foram submetidos à análise estatística. O teste de Kruskal-Wallis revelou não haver diferenças significativas entre os grupos (p<0,05). Valores em MPa foram: AAPS + VAPS - 19,56 MPa; AAPS + O - 19,77 MPa; A + VAPS - 17,78 MPa; A + O - 22,44 MPa. O resultado do teste de Mann-Whitney mostrou não haver diferenças significativas em função do adesivo (Ambar Universal- 19,11 MPa, Ambar APS Universal- 21,70 MPa) e da resina composta utilizada (Vittra APS- 18,75 MPa, Opallis- 23,75 MPa). Concluiu-se que a utilização de diferentes fotoiniciadores na composição dos sistemas adesivos e compósitos restauradores não influenciou seus valores de resistência adesiva devido à padronização dos fatores que influenciam o padrão de polimerização dos mesmos. (AU)


An effective polymerization of the composite resin provides a higher monomer degree conversion into polymers, resulting in satisfactory mechanical properties for adhesion. Changes in the formulation of resinous materials have been proposed with the aim to solve the problems related to the polymerization of these systems. Thus, different photoinitiators from camphorquinone and that report higher degree of conversion have been used. However, the inadvertent use of adhesive systems associated with dental composites with different photoinitiators systems can lead to a reduction in the efficiency of the cure and, consequently, of the adhesive resistance. The objective of this in vitro was to evaluate the influence of photoinitiators on the microtensile strength of adhesive systems and composite resins to bovine dentin. Forty dental fragments with smooth and straightened dentin surfaces obtained from the coronary vestibular surface of healthy bovine incisors were randomly divided into 4 experimental groups (n = 10) according to the different adhesive systems and composite resins used: Group: AAPS + VAPS (Ambar APS + Vittra APS); Group: AAPS + O (Ambar APS + Opallis); Group: A + VAPS (Ambar + Vittra APS); Group: A + O (Ambar + Opallis). After composite restoration, the samples were sectioned to obtain sticks that were submitted to the microtensile test (1.0mm/min). The data were submitted to statistical analysis. The Kruskal-Wallis test revealed no significant diferences between groups (p<0.05). Values in MPa were: AAPS + VAPS - 19,56 MPa; AAPS + O - 19,77 MPa; A + VAPS - 17,78 MPa; A + O - 22,44 MPa. The result of the Mann-Whitney test showed no significant statistical difference as a function of adhesives (Ambar Universal- 19.11 MPa, Ambar Universal APS - 21,70 MPa) and the composite resin used (Vittra APS - 18.75 MPa, Opallis - 23.75 MPa). It was concluded that the use of different photoinitiators in the composition of adhesive systems and restorative composites did not influence their adhesive strength values due the standardization of the factors that influence the curing pattern of the adhesive systems. (AU)


Assuntos
Animais , Bovinos , Resistência à Tração/efeitos da radiação , Resinas Compostas/efeitos da radiação , Dentina/efeitos da radiação , Fotoiniciadores Dentários/normas , Técnicas In Vitro , Cura Luminosa de Adesivos Dentários/normas
5.
Rio de Janeiro; s.n; 2019. 46 p. ilus, graf.
Tese em Português | BBO - Odontologia | ID: biblio-1022948

RESUMO

O objetivo deste estudo foi avaliar a influência do momento da etapa de polimento, imediato ou após sete dias, na formação de fendas em restaurações de resina composta. Cavidades cilíndricas foram preparadas nas superfícies vestibulares de incisivos bovinos. Cada cavidade foi hibridizada com um dos dois sistemas adesivos: convencional (Adper Single Bond 2) ou autocondicionante (Single Bond Universal), e restaurada usando uma das três resinas compostas: nanoparticulada (Z350), micro-híbrida (P60) e bulk-fill (ONE). As cavidades restauradas foram divididas em dois subgrupos de acordo com o tempo de polimento, imediato ou postergado por 7 dias após a restauração. Por meio da combinação dos sistemas adesivos, resinas compostas e tempos de polimento, foram criados 12 grupos (n = 5). As porcentagens de fendas marginais (%FM) foram avaliadas quantitativamente com o microscópio confocal de varredura a laser. O módulo de elasticidade das resinas compostas foi obtido por meio do teste de flexão em três pontos. Os dados foram analisados por análise de variância e pelo teste de Tukey's HDS (α = 0,05). Em relação ao sistema adesivo, a %FM foi estatisticamente maior para as cavidades restauradas com Single Bond Universal (p<0,05). Com relação às resinas compostas, o resultado foi o seguinte: P60 > ONE > Z350 (p<0,05). O tempo de polimento imediato apresentou %FM estatisticamente menor que o tardio (p<0,05). P60 apresentou o maior módulo de elasticidade (p<0,05). Foi possível concluir que o polimento imediato gera menor formação de fendas em restaurações de resina composta. (AU)


The aim of this study was to analyze the influence of the polishing time, immediately or after seven days, in gap formation in composite resin restorations. Cylindrical cavities were prepared on buccal surfaces of bovine incisors. Each cavity was hybridized with one of the two adhesive systems: etch-and-rinse (Adper Single Bond 2) and self-etching (Single Bond Universal), and restored using one of the three composite resins: nanofilled (Z350), minifilled hybrid (P60) and bulk-fill (ONE). The cavities restored were divided in two subgroups according to polishing time, immediately or delayed by 7 days after specimen restoration. Through the combination of the adhesive systems, composite resins and polishing times, 12 groups were created (n=5). Percentages of marginal gaps (%MG) were quantitatively assessed with confocal laser scanning microscope. The flexural modulus of the composite resins was obtained from bar-shaped specimens submitted to three-point bending test. The data were analyzed by three-way ANOVA and Tukey's HSD test (α=0.05). Regarding adhesive system, %MG was statistically higher for cavities restored with Single Bond Universal (p<0.05). With respect to composite resins, the result was as follow: P60 > One > Z350 (p<0.05). Immediate polishing time presented statistically lower %MG than delayed one (p<0.05). P60 presented the highest flexural modulus (p<0.05). It was possible to conclude that immediate polishing generates less gap formation in composite resin restorations. (AU)


Assuntos
Animais , Bovinos , Resinas Compostas/normas , Cimentos Dentários/normas , Polimento Dentário/métodos , Restauração Dentária Permanente/métodos , Teste de Materiais , Incisivo
6.
Full dent. sci ; 10(38): 98-105, 2019.
Artigo em Português | BBO - Odontologia | ID: biblio-996540

RESUMO

Este estudo objetivou avaliar o poder branqueador de diferentes dentifrícios branqueadores. Sessenta e quatro blocos de dentes bovinos (7x7 mm) foram distribuídos aleatoriamente em 8 grupos, estruturados conforme os diferentes dentifrícios clareadores utilizados: G1 (Controle): Colgate Total 12; G2: Sorriso Xtreme White; G3: Oral B 3D White Brilliant Fresh; G4: Oral B 3D White Perfection; G5: Colgate Whitening; G6: Sensodyne Branqueador Extra Fresh; G7: Closeup Extra Whitening e G8: Colgate Luminous White. Inicialmente, os espécimes foram corados por vinho tinto durante 24 horas. Na sequência, mensurou-se a cor desses com espectrofotômetro (Easyshade Compact DEASYC220; VITA, Bad Sackingen, Alemanha). Seguiu-se, então, a escovação dos corpos de prova seis vezes ao dia por um período de 14 dias, totalizando 84 ciclos. A mensuração da cor foi novamente aferida após 42 e 84 ciclos. Os resultados foram submetidos à análise de variância (ANOVA), teste de Friedman para comparações intragrupos e teste Kruskal-Wallis para comparações intergrupos (α = 0,05). Observou-se aumento do valor de L em todos os grupos, retomando aos valores da baseline, com exceção dos Grupos 4 e 5. Quanto ao valor de a*, foi verificado que todos os grupos reduziram, retomando aos valores da baseline, com exceção do Grupo 4, que ficou estatisticamente menor. Em referência ao valor de b*, foi constatado que todos os grupos reduziram, ficando inferiores aos valores da baseline e que o Grupo 8 obteve uma redução ainda maior após 84 ciclos de escovação. Os dentifrícios clareadores Sorriso Xtreme White, Closeup Extra Whitening e Colgate Luminous White apresentaram melhores resultados no branqueamento dentário (AU)


This study aimed to evaluate the whitening power of different tooth whitening products. Sixty four blocks of bovine teeth (7x7 mm) were randomly distributed in 8 groups, structured according to the different whitening dentifrices used: G1 (Control): Colgate Total 12; G2: Sorriso Xtreme White; G3: Oral B 3D White Brilliant Fresh; G4: Oral B 3D White Perfection; G5: Colgate Whitening; G6: Sensodyne Branqueador Extra Fresh; G7: Closeup Extra Whitening; and G8: Colgate Luminous White. Initially, the specimens were stained with red wine for 24 hours. The color was then measured with a spectrophotometer (Easyshade Compact DEASYC220; VITA, Bad Sackingen, Germany). The brushing of the specimens was carried out six times a day for a period of 14 days, totaling 84 cycles. Color measurement was again measured after 42 and 84 cycles. The results were submitted to analysis of variance (ANOVA), Friedman test for intragroup comparisons and Kruskal-Wallis test for intergroup comparisons (p; = 0.05). We observed an increase in the L value in all groups, returning to the baseline values, with exception of Groups 4 and 5. As for the value of a*, we verified that it was reduced in all groups, returning to baseline values, with exception of Group 4, which was statistically lower. Regarding the value of b*, we observed that it was reduced in all groups, being lower than baseline values, and that Group 8 obtained an even greater reduction after 84 brushing cycles. Whitening toothpastes Sorriso Xtreme White, Closeup Extra Whitening, and Colgate Luminous White showed better results for tooth whitening (AU).


Assuntos
Animais , Bovinos , Clareamento Dental/métodos , Técnicas In Vitro/métodos , Esmalte Dentário , Dentifrícios , Brasil , Análise de Variância , Estatísticas não Paramétricas , Incisivo
7.
Full dent. sci ; 10(38): 112-122, 2019.
Artigo em Português | BBO - Odontologia | ID: biblio-996561

RESUMO

O objetivo desta pesquisa foi avaliar a resistência da união, pelo método depush out, de pinos de fibra de vidro cimentados com cimento resinoso dual associado ao sistema adesivo Single Bond Universal, através de diferentes estratégias adesivas. Em 40 incisivos bovinos, um pino de fibra de vidro (Whitepost DC nº3) foi cimentado com cimento resinoso dual (RelyX ARC) e adesivo (Single Bond Universal). Os dentes foram divididos em 4 grupos (n = 10), de acordo com a estratégia de união. No Grupo 1 não se realizou nenhum tratamento do substrato dentinário. O Grupo 2 recebeu condicionamento com ácido fosfórico 37%. O Grupo 3 recebeu a aplicação de clorexidina 2% e o Grupo 4 recebeu condicionamento com ácido fosfórico 37% e aplicação da clorexidina 2%. Os grupos foram fatiados (1,8 mm) em três porções (cervical, média e apical) e tiveram seus pinos deslocados pela máquina universal de ensaios mecânicos. A análise estatística foi feita pelos testes ANOVA e Post Hoc de Tukey (p = 0,05). A técnica autocondicionante obteve maiores valores em MPa, mostrando a não necessidade de condicionamento ácido para melhoria da resistência adesiva. Para a técnica com condicionamento ácido, com e sem clorexidina, os valores de resistência adesiva foram estatisticamente semelhantes nos três terços radiculares. Para a técnica autocondicionante, com e sem o uso da clorexidina, a região cervical exibiu os maiores valores de resistência adesiva. Em ambas as técnicas, convencional e autocondicionante, não houve diferença significativa nos valores imediatos de resistência adesiva ao uso da clorexidina (AU).


The aim of this research was to evaluate by the push up method the bonding strength of fiberglass pins cemented with dual resin cement associated to the Single Bond Universal adhesive system through different adhesive strategies. In 40 bovine incisors, a fiberglass pin (Whitepost DC nº3) was cemented with dual resin cement (RelyX ARC) and adhesive (Single Bond Universal). The teeth were divided in 4 groups (n = 10), according to the union strategy. In Group 1, no treatment of the dentin substrate was performed. Group 2 received conditioning with 37% phosphoric acid. Group 3 received 2% chlorhexidine and Group 4 received conditioning with 37% phosphoric acid and 2% chlorhexidine application. The groups were sliced (1.8 mm) in three portions (cervical, middle, and apical) and had their pins displaced by the universal machine of mechanical tests. Statistical analysis was performed by ANOVA and Tukey's Post Hoc tests (p = 0.05). The self-etching technique obtained higher values in MPa, showing no need of acid conditioning to improve the adhesive strength. For the acid-conditioning technique with and without chlorhexidine, adhesive strength values were statistically similar in the three-thirds root. For the self-etching technique with and without the use of chlorhexidine, the cervical region exhibited the highest values of adhesive strength. In both techniques, conventional and self-etching, there was no significant difference in the immediate values of adhesive resistance to the use of chlorhexidine (AU).


Assuntos
Animais , Bovinos , Tratamento do Canal Radicular/métodos , Resistência à Tração , Teste de Materiais/métodos , Adesivos Dentinários , Pinos Dentários , Brasil , Análise de Variância , Estatísticas não Paramétricas , Incisivo
8.
Rev. Cient. CRO-RJ (Online) ; 3(3): 56-61, Sept.-Dec. 2018.
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-1022027

RESUMO

Objective: The aim of this study was to evaluate the effect of different concentrations of a natural antioxidant (grape seed extract) on the bond strength of the restorative material to the bleached enamel. Methods: Forty fragments of healthy bovine incisors were randomly divided into four groups (n = 10): Group I: no bleaching; Group II: Bleaching with 35% hydrogen peroxide (HP) and without post-treatment; Group III: Bleaching with 35% HP + 5% grape seed extract; and Group IV: Bleaching with 35% HP + 10% grape seed extract. The bond strength at the adhesive interface was evaluated using the shear test (MPa). The data were analyzed by the analysis of variance (ANOVA) and Tukey test ( =0.05%). The fracture types were also analyzed and classified into: adhesive, cohesive or mixed. Results: Only Group III (bleached + 5% grape seed extract) had a significant increase (p<0.001) in bond strength values when compared to Group II bleached, without post- reatment). All groups showed a predominance of the adhesive type of fracture. Conclusion: It could be concluded that tooth bleaching decreases the bond strength to bleached enamel and 5% grape seed extract applied after dental bleaching improves the bond strength between the restorative material and the bleached enamel.


Objetivo: Este trabalho teve por objetivo avaliar in vitro o efeito de um antioxidante natural (extrato de semente de uva) em diferentes concentrações, na resistência de união do material restaurador ao esmalte clareado. Métodos: Quarenta fragmentos de incisivos bovinos hígidos, foram divididos aleatoriamente em quatro grupos (n=10): Grupo I: sem clareamento; Grupo II: clareado com peróxido de hidrogênio 35% (PH) e sem pós-tratamento; GIII: clareado PH 35% + extrato de semente de uva 5%; e Grupo IV: clareado com PH 35% + extrato de semente de uva 10%. A resistência de união da interface esmalte/material restaurador foi avaliada por meio do teste de cisalhamento (MPa). Os dados foram analisados pela análise de variância (ANOVA) e testes de Tukey ( =0,05%). Os tipos de fratura também foram analisados e classificados em: adesiva, coesiva ou mista. Resultados: Apenas o Grupo III (clareado + extrato de semente de uva 5%) apresentou aumento estatisticamente significante (p<0,001). dos valores de resistência de união comparado ao Grupo II (clareado e sem pós-tratamento). Todos os grupos mostraram um predomínio do tipo de fratura adesiva. Conclusão: O clareamento dental diminui significativamente a força de adesão ao esmalte dental clareado, e o extrato de semente de uva 5% aplicado após o clareamento dental melhora a resistência de união entre o material restaurador e o esmalte clareado.


Assuntos
Bovinos , Clareamento Dental , Técnicas In Vitro , Esmalte Dentário , Extrato de Sementes de Uva , Antioxidantes
9.
Braz. j. oral sci ; 17: e18138, 2018. tab
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-963962

RESUMO

Aim: The objective of this study was to compare the efficiencies of different adhesive systems used to bond orthodontic brackets as well as the fracture pattern during debonding on bovine teeth. Methods: The sample included 45 specimens assigned to 3 groups according to the adhesive system applied: Group I: Transbond XT (3M Unitek®, Monrovia/CA -USA), Group II: Orthocem (FGM® Joinville/SC-BR), and Group III: Orthobond (Morelli®, Sorocaba/SP-BR). For this purpose, metal brackets were bonded to bovine teeth following the instructions from each manufacturer. The specimens were subjected to a shear test to assess bond strength (BS). Finally, after debonding, the adhesive remnant index (ARI) was estimated. Results: The average shear strength for a tooth bonded using the adhesive system Transbond XT was 16.39 MPa, while it was 18.08 Mpa for Orthocem and 7.28 Mpa for Orthobond; The Tukey test revealed no statistically significant differences between groups I and II (p < 0.01) and group III differed statistically from groups I and II. Conclusion: In conclusion, both adhesive systems Transbond XT and Orthocem attained higher bond strength values than Orthobond; the fracture pattern was similar for all adhesive systems applied


Assuntos
Animais , Bovinos , Colagem Dentária , Braquetes Ortodônticos , Esmalte Dentário , Resistência ao Cisalhamento
10.
Braz. dent. sci ; 21(4): 395-402, 2018. ilus, tab
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-965429

RESUMO

Objective: The aim of this study was to evaluate the shear bond strength (SBS) of two materials for bonding orthodontic brackets on dental enamel before and after thermocycling. Material and Methods: Forty bovine incisors were divided into four groups (n=10). All teeth were etched with 35% phosphoric acid (3M Espe). For bonding of the brackets, G1 and G2 received orthodontic composite resin (Fill Magic Ortodôntico) and G3 and G4, an adhesive (ScotchBond) was used before the orthodontic resin Transbond XT (3M Unitek). G1 and G3 were kept at 37ºC for 24h and G2 and G4 were submitted to thermocycling (5000 cycles, at 5ºC - 55ºC) prior to SBS testing, performed by a universal machine (EMIC) at 1 mm/min, with a 50kgf load cell. Results were analyzed with two-way ANOVA, followed by Tukey's test (p=0.05). Adhesive surfaces were evaluated through stereomicroscopy and classified according to the type of failure presented. Results: Surface treatment with dental adhesive presented higher SBS values, regardless thermocycling (G3: 12.01 MPa; G4: 12.36 MPa) and the lowest values occurred in G2 (8.89 MPa). For groups without adhesive and with thermocycling, a higher number of completely adhesive failures between composite and enamel were present. For groups in which dental adhesive was used, regardless thermocycling, the failures were mainly adhesive between composite and the bracket. Conclusion: Surface etching of enamel with 35% phosphoric acid with or without adhesive showed a positive effect on SBS. The application of adhesive on enamel surface contributed to the maintenance of SBS values after thermocycling (AU)


Objetivo: O objetivo desse estudo foi avaliar a resistência ao cisalhamento de dois materiais para fixação de braquetes ortodônticos ao esmalte dentário antes e após a termociclagem. Material e Métodos: Quarenta incisivos bovinos foram divididos em quatro grupos (n=10). Todos os dentes foram condicionados com ácido fosfórico a 35% (3M Espe). Para a fixação dos braquetes, G1 e G2 receberam a resina composta ortodôntica (Fill Magic Ortodôntico) e G3 e G4, um adesivo dentário (ScotchBond) foi usado antes da resina ortodôntica Transbond XT (3M Unitek). G1 e G3 foram mantidos a 37ºC por 24h e G2 e G4 foram submetidos à ciclagem térmica (5000 ciclos, de 5ºC - 55ºC) anterior ao teste de resistência ao cisalhamento, realizado por máquina universal (EMIC) a 1 mm/min, com célula de carga de 50kgf. Os resultados foram analisados com ANOVA 2-fatores, seguida do teste de Tukey (p=0,05). As superfícies adesivas foram avaliadas através de estereomicroscopia e classificadas de acordo com o tipo de falha presente. Resultados: O tratamento de superfície com adesivo dentário apresentou maiores valores de resistência ao cisalhamento, independente da termociclagem (G3: 12,01 MPa; G4: 12,36 MPa) e os menores valores ocorreram para G2 (8,89 MPa). Para os grupos sem adesivo e com termociclagem, o maior número de falhas predominantemente adesivas entre resina composta e esmalte estava presente. Para os grupos em que o adesivo dentário foi utilizado, independente da termociclagem, as falhas foram principalmente adesivas entre resina composta e o braquete. Conclusão: O condicionamento superficial do esmalte com ácido fosfórico a 35% com ou sem adesivo mostrou um efeito positivo sobre a resistência ao cisalhamento. A aplicação de adesivo na superfície do esmalte contribuiu para a manutenção dos valores de resistência ao cisalhamento após a termociclagem. (AU)


Assuntos
Animais , Bovinos , Envelhecimento , Braquetes Ortodônticos , Resinas Compostas , Resistência ao Cisalhamento
11.
Braz. dent. sci ; 21(1): 17-25, 2018. tab, ilus
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-881814

RESUMO

Objective: To evaluate the effect of 35% hydrogen peroxide (35% HP) combined to different concentrations of nanohydroxyapatite (nHA) on the effectiveness of dental bleaching (superficial enamel and deep dentin) and enamel bond strength. Material and Methods: Fifty bovine dental specimens (5x5x2mm) were divided into 5 groups, according to the treatments (n = 10): no bleaching (negative control); 35% HP (positive control); 35% HP+ 5% nHA; 35% HP + 10% nHa; and 35% HP + 15% nHA. Three in-office bleaching sessions were made. The color analysis was performed on the enamel surface and the opposite dentin, using a spectrophotometer. The results were expressed in the CIE L*a*b* system. After this, the adhesive system was applied to the tooth structure, and the dental specimens received a composite restoration. The microshear bond strength test was performed 24 h after the restoration. Data were submitted to ANOVA and Tukey's test (α=0.05). Results: For the enamel color analysis, all bleached groups differed statistically from the unbleached group, with increasing L* values and decreasing b* values. The addition of different concentrations of nHA did not interfere with the bleaching effectiveness for the enamel and opposite dentin. For microshear bond strength, no statistically significant differences were presented between groups. The adhesive failure rate of the 35% HP + 10% nHA group was lower than the 35% HP group and similar to the negative control. Conclusion: The addition of different concentrations of nHA in 35% of hydrogen peroxide did not interfere with the bleaching efficacy of enamel and deep dentin and did not affect the enamel bond strength after bleaching.(AU)


Objetivo: avaliar o efeito do peróxido de hidrogênio a 35% (HP 35%) associado a diferentes concentrações de nanohidroxiapatita (nHA) sobre a efetividade clareadora do esmalte superficial, dentina profunda e da força de adesão ao esmalte. Material e Métodos: Cinquenta espécimes bovinos (5x5x2mm) foram divididos 5 grupos (n = 10): sem clareamento (controle negativo); HP 35% (controle positivo); HP 35% + nHA 5%; HP 35% + nHA 10%; e HP 35% + nHA 15%. Três sessões de clareamento de consultório foram realizadas. A análise de cor foi realizada na superfície do esmalte e na dentina oposta e os resultados expressos no sistema CIE L*a*b*. Depois disso, os sistemas adesivos foram aplicados no esmalte, e os blocos receberam uma restauração em resina composta. O teste microcisalhamento foi realizado 24 h após a restauração. Os dados foram submetidos à ANOVA e ao teste de Tukey (α = 0,05). Resultados: Para a análise de cor do esmalte, todos os grupos clareados diferiram estatisticamente do grupo não clareado. A adição de diferentes concentrações de nHA não interferiu com a eficácia clareadora para o esmalte e dentina. Para o microcisalhamento, não houve diferença entre os grupos. A taxa de falha adesiva do grupo HP 35% + nHA 10% foi menor do que o grupo HP 35% e similar ao controle negativo. Conclusão: a adição de diferentes concentrações de nHA em PH 35% não interferiu na eficácia clareadora do esmalte e da dentina e não afetou a força de adesão do esmalte após o clareamento (AU)


Assuntos
Bovinos , Esmalte Dentário , Resistência ao Cisalhamento , Clareamento Dental
12.
Bauru; s.n; 2018. 132 p. tab, graf, ilus.
Tese em Inglês | LILACS, BBO - Odontologia | ID: biblio-906807

RESUMO

The objective of this study was to evaluate the antimicrobial and anti-caries effects of two plant extracts. The first chapter dealt with a review of the literature whose objective was to discuss the antimicrobial potential of Brazilian natural agents on the biofilm related to dental caries and gingivitis/periodontal disease. The research of the articles was carried out using PubMed. We found a total of 23 papers. Most of the studies were performed using planktonic microorganisms or under clinical trials. Nineteen articles were focused on cariogenic bacteria. From these nineteen articles, eleven were also about periodontopathogenic bacteria. Four studies addressed only periodontopathogenic bacteria. The most tested Brazilian natural agents were green propolis, essential oils of Lippia sidoides and Copaifera sp. Most of the tested agents showed similar results when compared to positive control (essential oils and extracts) or better effect than negative control (green propolis). More studies involving protocols closer to the clinical condition and the use of response variables that allows understanding the mechanism of action of natural agents are necessary before the incorporation of these natural agents into dental products. The second chapter aimed to test the effect of the hydroalcoholic extracts of Myracrodruon urundeuva All. and Qualea grandiflora Mart. leaves on the viability of the microcosm biofilm and on the prevention of enamel demineralization. The microcosm biofilm was produced on bovine enamel, using human saliva pool mixed with McBain saliva (0.2% sucrose) for 14 days. The biofilm was treated daily with the extracts for 1 min. M. urundeuva at 100, 10 and 0.1 µg/ml and Q. grandiflora at 100 and 0.1 µg/ml reduced cell viability similarly to the positive control and significantly more than negative control. M. urundeuva at 1000, 100 and 0.1 µg/ml were able to reduce the counting formation unit-CFU counting of lactobacilli sp. and Streptococcus mutans, while Q. grandiflora at 1000 and 1.0 µg/ml significantly reduced the S. mutans CFU counting. On the other hand, the natural extracts did not reduce the production of extracellular polyssacharides, lactic acid and the development of enamel caries lesions. The third chapter aimed to evaluate the effect of hydroalcoholic extracts of M. urundeuva and Q. grandiflora (alone or combined) on the viability of S. mutans biofilm and the prevention of enamel demineralization. S. mutans strain (ATCC 21175) was reactivated in BHI broth. Minimum inhibitory concentration, minimum bactericidal concentration, minimum biofilm inhibitory concentration and minimum biofilm eradication concentration were determined to choose the concentrations to be tested under the biofilm model. S. mutans biofilm (5x105 CFU/ml) was produced on bovine enamel using McBain saliva with 0.2% sucrose for 3 days. The biofilm was treated daily with the extracts for 1 min. M. urundeuva (isolated or combined) at concentrations equal or higher than 0.625 mg/ml was able to reduce the bacteria viability, whereas Q. grandiflora extract alone showed antimicrobial effect at 5 mg/ml only (p<0.05). On the other hand, none of the extracts was able to reduce the development of enamel caries lesions. Despite the tested natural extracts have antimicrobial effect; they are unable to prevent caries in enamel.(AU)


O objetivo foi avaliar os efeitos antimicrobiano e anti-cárie de dois extratos de plantas. O primeiro capítulo se referiu a uma revisão da literatura cujo objetivo foi discutir o potencial antimicrobiano dos agentes naturais brasileiros sobre o biofilme relacionado à cárie dentária e à gengivite/doença periodontal. A pesquisa dos artigos foi realizada usando o PubMed. Foram encontrados 23 trabalhos. A maioria dos estudos foi realizada utilizando microorganismos na fase planctônica ou ensaios clínicos. Dezenove artigos foram focados em bactérias cariogênicas. Dos dezenove artigos, onze também eram sobre bactérias periodontopatogênicas. Quatro estudos abordaram apenas bactérias periodontopatogênicas. Os agentes naturais brasileiros mais testados foram própolis verde, óleos essenciais de Lippia sidoides e Copaifera sp. Os agentes testados apresentaram resultados similares quando comparados ao controle positivo (óleos essenciais e extratos) ou melhor efeito que o controle negativo (própolis verde). Mais estudos próximos da condição clínica e o uso de variáveis de resposta que permitam entender o mecanismo de ação são necessários, para permitir a incorporação desses agentes naturais em produtos odontológicos. O segundo capítulo teve como objetivo testar o efeito dos extratos hidroalcoólicos de Myracrodruon urundeuva All. e Qualea grandiflora Mart. sobre a viabilidade do biofilme microcosmo e na prevenção da desmineralização do esmalte. O biofilme microcosmo foi produzido em esmalte bovino, utilizando pool de saliva humana misturada à saliva de McBain (0,2% de sacarose) durante 14 dias. O biofilme foi tratado diariamente com os extratos durante 1 min. M. urundeuva a 100, 10 e 0,1 µg/ml e Q. grandiflora a 100 e 0,1 µg/ml reduziram a viabilidade dos microrganismos de forma semelhante ao controle positivo e significativamente maior do que o controle negativo. M. urundeuva a 1000, 100 e 0,1 µg/ml foi capaz de reduzir a contagem de Unidade formadora de colônia-UFC para Lactobacilos totais e Streptococcus mutans, enquanto a Q. grandiflora a 1000 e 1,0 µg/ml reduziu significativamente a contagem de UFC para S. mutans. Os extratos naturais não conseguiram reduzir a produção de polissacarídeos extracelulares-PEC, ácido lático e o desenvolvimento da lesão cariosa em esmalte. O terceiro capítulo teve como objetivo avaliar o efeito dos extratos hidroalcoólicos de M. urundeuva. e Q. grandiflora (sozinhos ou combinados) sobre a viabilidade do biofilme de S. mutans e na prevenção da desmineralização do esmalte. Cepa de S. mutans (ATCC 21175) foi reativada em caldo BHI. Concentração inibitória mínima, concentração bactericida mínima, concentração inibitória mínima de biofilme e concentração de erradicação mínima de biofilme foram determinadas para escolher as concentrações a serem testadas sob o modelo de biofilme. O biofilme de S. mutans (5x105 CFU/ml) foi produzido em esmalte bovino, utilizando saliva de McBain com 0,2% de sacarose durante 3 dias. O biofilme foi tratado diariamente com os extratos durante 1 min. M. urundeuva (isolada ou combinada) nas concentrações iguais ou superiores a 0,625 mg/ml foi capaz de reduzir a viabilidade das bactérias, enquanto que o extrato da Q. grandflora apresentou efeito antimicrobiano somente a 5 mg/ml (p<0,05). Nenhum dos extratos reduziu o desenvolvimento da lesão da cárie. Apesar dos extratos naturais terem efeito antimicrobiano, são incapazes de prevenir o desenvolvimento da lesão cariosa em esmalte.(AU)


Assuntos
Humanos , Animais , Bovinos , Anacardiaceae/química , Anti-Infecciosos/farmacologia , Biofilmes/efeitos dos fármacos , Esmalte Dentário/microbiologia , Magnoliopsida/química , Extratos Vegetais/farmacologia , Desmineralização do Dente/prevenção & controle , Testes de Sensibilidade Microbiana , Microrradiografia , Reprodutibilidade dos Testes , Saliva/microbiologia , Streptococcus mutans/efeitos dos fármacos , Streptococcus mutans/crescimento & desenvolvimento , Fatores de Tempo
13.
Rio de janeiro; s.n; 2018. 80 p.
Tese em Português | LILACS, BBO - Odontologia | ID: biblio-1007463

RESUMO

O clareamento dental é considerado um procedimento muito seguro, de efeito rápido e agradável, tornando-se um dos procedimentos mais realizados na odontologia. Contudo, o mesmo apresenta alguns efeitos colaterais, sendo o principal deles a sensibilidade dental, que pode ser causada pela citotoxidade, pela desmineralização, pela geração de espécies reativas do oxigênio na polpa dental e pela degradação da região interprismática facilitando o estimulo nos túbulos dentinários. Diante disso, a presente pesquisa avaliou a desmineralização, a citotoxidade e o potencial clareador de géis clareadores experimentais baseados em peróxido de carbamida (PC) 15%, adicionados de 5% e 10% de nano partículas de hidroxiapatita (n-Hap). Para a avaliação cromática foram utilizados 36 incisivos bovinos divididos em 3 grupos: Grupo1 PC 15%, Grupo 2 PC 15% adicionado 5% nHap e grupo 3 PC 15% com 10% n-Hap, mensurando a cor antes e depois do procedimento terapêutico clareador com auxilio de um espectrofotômetro. As coordenadas do CIELAB foram analisadas para verificação da diferença de cor (ΔE) obtida entre os grupos e dentro do próprio grupo (L*) e, após a analise estatística, foi verificado que todos os géis foram capazes de clarear e não houve diferenças entre os grupos. A citotoxidade foi verificada através da absorbância das células viáveis após o tratamento com o MTT e 1:800 das preparações de agente clareador e gel contendo 5% e 10% de n-Hap aplicadas sobre células L929. Nesse caso os grupos foram desiguais estatisticamente, apresentando o PC 15% como o mais tóxico, seguido do PC 15% adicionado de 10% de n-Hap e o melhor resultado foi obtido pelo gel acrecido de 5% de n-Hap. A análise do conteúdo mineral foi realizada pela fluorescência de raios X por dispersão de energia, onde foi necessário o uso de 15 dentes bovinos, que tiveram seus terços médios seccionados, embutidos em resina epóxi e planificados, e foram dividos em grupos de 5 CPs. Cada CP foi aferido em 8 pontos diferentes antes e depois, nos mesmos pontos da terapia clareadora. Foi então verificado que os géis experimentais apresentaram menor perda de Ca e P. No entanto, não houve diferenças estatísticas entre os grupos 2 e 3. Diante das limitações do presente estudo in vitro é possível concluir que os géis experimentais contendo n-Hap foram eficazes em reduzir a citotoxidade e desmineralização sem perder a eficácia da terapia clareadora


Dental whitening is considered a very safe, quick and pleasant procedure, making it one of the most accomplished procedures in dentistry. However, it has some side effects, the main one being sensibility, which can be caused by cytotoxicity, demineralization, oxygen arrival in the dental pulp and the degradation of the interprismatic region facilitating the stimulation in the dentin tubes. Therefore, the present study evaluated the demineralization, cytotoxicity and bleaching potential of 15% carbamide peroxide-based (PC) based bleaching gels added with 5% and 10% nano-hydroxyapatite (n-Hap) particles. For the chromatic evaluation, 36 bovine incisors were divided into 3 groups: Group 1 PC 15%, Group 2 PC 15% added 5% nHap and group 3 PC 15% with 10% n-Hap, measuring the color before and after the the CIELAB coordinates were analyzed to verify the color difference (Δe) obtained between the groups and within the group (L *). After the statistical analysis it was verified that all the gels were able to lighten and there were no differences between the groups. Cytotoxicity was verified by optical density of viable cells after treatment with MTT and 1: 800 of the bleach and gel preparations containing 5% and 10% nHap applied in L929 cells. In this case, the groups were statistically unequal, presenting 15% PC as the most toxic, followed by PC 15% added with 10% n-Hap and the best result was obtained by the 5% n-Hap increased gel. The mineral content analysis was performed by X-ray Fluorescence by energy dispersion, where it was necessary to use 15 bovine teeth, which had their middle sections sectioned, embedded in epoxy resin and planned, and were divided into groups of 5 CPs, each CP was measured at 8 different points before and after, at the same points of the bleaching therapy, then it was verified that the experimental gels presented a lower loss of Ca and P, however there were no statistical differences between groups 2 and 3. On the face of the limitations of the present in vitro study, it is possible to conclude that the experimental gels were effective in reducing the cytotoxicity and demineralization without losing the effectiveness of the bleaching therapy.


Assuntos
Animais , Bovinos , Clareamento Dental/efeitos adversos , Durapatita/uso terapêutico , Clareadores Dentários/toxicidade , /uso terapêutico , Análise Estatística , Desmineralização do Dente , Sensibilidade da Dentina
14.
Braz. j. oral sci ; 17: e18924, 2018. ilus
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-970500

RESUMO

Aim: This study evaluated the effect of a sonic device on the bonding of fiberglass posts cemented with a self-etching adhesive combined with conventional cement or a self-adhesive cement to root dentin. Methods: Forty single-rooted bovine incisors were endodontically prepared using a step-back technique. Gutta-percha and AH Plus sealer were used for root canal filling, combined with a thermoplasticization technique. After 1 week, the post space was prepared and the roots were divided into four groups according to the following factors: adhesive system/resin cement (Ambar/ AllCem Core [FGM] and RelyX U200 [3M]) and application mode (manual or sonic). The posts were cemented and the roots were cut into discs and submitted to push-out bond strength (POBS) test. The failure mode was evaluated using a stereoscope at 25x magnification. The data were analyzed statistically using ANOVA and Tukey's post-hoc test (α = 0.05). Results: The sonically activated RelyX U200 group was superior to the other groups. RelyX U200 manually applicated showed similar results to those of sonically activated Âmbar/AllCem. These three groups outperformed the Âmbar/AllCem manually applicated group. Adhesive failure between dentin and resin cement was the most predominant pattern. Conclusion: Sonic application of self-etching adhesive and self-adhesive cement improved the POBS of fiber posts to the root canal


Assuntos
Animais , Bovinos , Colagem Dentária , Cimentos Dentários , Pinos Dentários , Cavidade Pulpar , Análise do Estresse Dentário
15.
Braz. j. oral sci ; 17: e18483, 2018. tab
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-970525

RESUMO

Aim: To evaluate crown and root discoloration promoted by different endodontic sealers after root canal filling. Methods: Eighty bovine incisors were prepared and filled with: Endofill, Sealer 26, AH Plus, and MTA Fillapex. Color was recorded using a spectrophotometer before endodontic treatment (T0) and at 24 hours (T1), seven days (T2), 30 days (T3), and 90 days (T4) after treatment. Analyses were performed on the middle and cervical regions of the crown, and on the cervical third of the root, immediately below the cementoenamel junction. The color alterations (ΔE) were calculated using Commission International de I'Eclairage (CIE) L*a*b parameters, and data were analyzed by analysis of variance (ANOVA) and Tukey's test (p<0.05). Results: All sealers induced color alterations. Sealer 26 resulted in the smallest changes in color (E = 5.32). The other materials did not present statistical differences (AH Plus E = 6.98; MTA Fillapex E = 6.88; Endofill E = 6.41). Of the three regions analyzed, the largest discoloration was observed at the cervical third of the root (E=10.67). In terms of time, the largest ΔE values (E=7.72) were observed at T4. Color changes at T1 (E=5.88), T2 (E=6.10), and T3 (E=5.89) were statistically similar. Conclusions: All endodontic sealers promoted discoloration on the tooth crown and root


Assuntos
Animais , Bovinos , Materiais Restauradores do Canal Radicular , Descoloração de Dente , Coroa do Dente , Endodontia
16.
Braz. j. oral sci ; 17: e18409, 2018. tab
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-970529

RESUMO

Aim: Modifications in the mechanical properties of dentin may reduce the fracture resistance of tooth, especially after endodontic treatment. The aim of present study was to evaluate the effect of the irrigation with different root canal irrigants on the microhardness of root dentin. Methods: The coronal portion of 60 single-rooted bovine incisors was sectioned and the pulpal tissue removed using endodontic K-files. The roots were cut transversely to obtain 2 fragments, which were embedded in acrylic resin and randomly distributed into six groups (n=20) according to the irrigation protocol: distilled water (DW) (control); 2% chlorhexidine solution (CHX); 6% sodium hypochlorite (NaOCl); 6% calcium hypochlorite (Ca[OCl]2); QMix; and 6.5% grape seed extract solution (GSE). The solutions were kept in contact with the root dentin specimens for 30 min. After that, irrigation with 5 mL of DW was performed. The Vickers microhardness was determined by performing three indentations in all specimens, using 300-g load and 20-second dwell time. The first indentation was made 1.000 µm from the root canal entrance, and two other indentations were made at a distance of 200 µm from each other. The microhardness value for each specimen was obtained as the average of the results for the three indentations. Data were statistically analyzed using one-way ANOVA with 5% significance level. Results: All the tested irrigant solutions maintained the same microhardness level of the root dentin when compared to the control group, with no statistically significant differences between them (p<0.05) Conclusion: The tested irrigant solutions did not present ability to modify the microhardness of root dentin


Assuntos
Animais , Bovinos , Hipoclorito de Sódio , Clorexidina , Hipoclorito de Cálcio , Extrato de Sementes de Uva , Dureza
17.
Full dent. sci ; 9(34): 92-99, 2018. ilus, tab, graf
Artigo em Português | BBO - Odontologia | ID: biblio-988236

RESUMO

A restauração de dentes por sistemas adesivos é rotina em odontologia. O tratamento do esmalte inicia-se pela profilaxia e asperização dos prismas. A manobra é feita com brocas adaptadas à canetas de alta ou baixa rotação as quais devem ser lubrificadas frequentemente. Diversos fatores podem provocar falhas nas restaurações, entre eles a contaminação por oleosidade. A proposta do trabalho foi verificar a influência da lubrificação das pontas de alta rotação na adesão de resinas compostas ao esmalte. Foram confeccionados 30 corpos de provas, constituídos de cilindros de PVC, nos quais se incluiu fragmento da superfície vestibular de dente bovino em resina acrílica autopolimerizável, de maneira paralela ao solo, com área suficiente para a colagem de braquete de 9 mm2. A amostra foi dividida em três grupos de 10. No primeiro (A), cada braquete foi colado de maneira convencional com uma asperização prévia do esmalte realizada com caneta sem lubrificação. No segundo (B), foi realizada asperização com caneta lubrificada e pré-acionada por 30 segundos. E no terceiro (C), a asperização foi feita imediatamente após a lubrificação. Cada braquete foi submetido ao teste de tração. Todas as falhas foram coesivas, apresentando valores médios de 73,18N para o grupo A, 75,90N para o B e 91,45N para o C. O tratamento estatístico não mostrou diferença significativa entre os grupos. De acordo com o método instituído não houve influência da lubrificação das pontas de alta rotação na adesão de resinas compostas ao esmalte (AU).


The use of adhesive systems is a routine procedure in restorative dentistry. Enamel treatment starts with prophylaxis and abrasion of enamel prisms. This is performed using drills adapted to high or slow speed handpieces which must be frequently lubricated. Many factors may produce failure in tooth restoration, among them is the contamination by oil. The purpose of this study was to assess the influence of high speed handpiece lubrication in bond strength of composite resin to enamel. Thirty specimen were made constituted of PVC cylinders, in which were included fragments of the vestibular surface of the bovine tooth in self-polymerized acrylic resin parallel to the floor with sufficient area for bonding the 9 mm2 bracket. The samples were divided randomly into three groups of 10. In the first group (A), the bracket was bonded using the conventional way and enamel abrasion was previously performed with an unlubricated handpiece. In the second one (B), abrasion was performed with a lubricated handpiece which was run on air for 30 seconds and in the third group (C), abrasion was made immediately after lubrication. A tensile test was carried out for each bracket. All failures were cohesive with mean values of 73,18N (group A), 75,90N (group B) and 91,45N (group C). Statistical tests detected no significant differences between the groups. According to the established method, there was no influence of high speed handpiece lubrication on bond strength of composite resin to enamel (AU).


Assuntos
Animais , Bovinos , Adesividade , Resinas Compostas , Esmalte Dentário , Lubrificantes , Análise de Variância
18.
Rio de Janeiro; s.n; 2018. 68 p. ilus, tab.
Tese em Português | BBO - Odontologia | ID: biblio-1023198

RESUMO

Objetivo: verificar a ação de produtos lácteos contendo ou não probióticos sob associação de cepas de Streptococcus mutans (SM) e S salivarius (SS), a adesão desses produtos à superfície de bráquetes ortodônticos e avaliar a progressão da desmineralização em blocos de dente bovino ao redor de bráquetes ortodônticos após o esmalte ter sido exposto a produtos lácteos contendo probióticos. Materiais e métodos: pool de cepas ATCC de SM e SS foi formado e plaqueado sobre placa de Petri contendo meio de cultura brain heart infusion agar (BHI). Cada poço foi preenchido com 150µl dos produtos a serem testados, formando os grupos: L - Leite bovino; LP - Leite bovino com probiótico; LF - Leite fermentado e LFP - Leite fermentado com probiótico. Na sequência as placas foram incubadas por 48h, em estufa à 37ºC. Após isso foi feita a medição do halo formado entre o produto e o meio. Na outra avaliação foi formado biofilme sobre o disco de membrana com o mesmo pool de cepas. Após o tratamento foi feito de acordo com o grupo: P1 (água); P2 (L); P3 (LP); P4 (LFP), seguido pela diluição seriada, plaqueamento e a contagem total de microorganismos. Para a adesividade dos produtos lácteos, bráquetes ortodônticos foram submergidos em cada solução (L, LP, LF e LFP), as quais foram incubadas a 37ºC/24h. Posteriormente, cada bráquete foi transferido para um ependorf contendo solução salina estéril, que foi submetida a diluições seriadas, posteriormente incubadas a 37ºC/48h sob microaerofilia para contagem das UFC/mL. Na avaliação da desmineralização foram utilizados 42 dentes bovinos previamente cortados em blocos com 64 mm². Bráquetes foram colados na superfície do esmalte e divididos em 6 grupos aleatoriamente: G1 (controle negativo), G2 (controle positivo), G3 (L), G4 (LP), G5 (LF) e G6 (LFP). Com a exceção do G1, todos os outros foram colocados em BHI suplementado com 2% de sacarose com 1x106 células/ml de SM (ATCC 25175) e SS (ATCC 7073) durante 24 horas. Posteriormente, foram tratados diariamente com os produtos teste por 5 minutos por um total de 4 dias. Após o tratamento, foi avaliado os valores de microdureza superficial final, índice de perda mineral e microdureza interna. Resultados: não houve formação de halo de inibição entre os produtos e o meio de cultura (p<0.05); no disco de membrana não foram observadas diferenças estatísticas entre os grupos (p=0.679); o GLP e o GLFP apresentaram adesividade aos bráquetes ortodônticos (p=0.056). Todos os grupos G1, G2, G3, G4, G5 e G6, apresentaram perda mineral no final do experimento. Conclusões: não foi possível verificar a bacterioterapia a partir de produtos lácteos contendo probióticos em cepas de SM e SS, e não foi possível prevenir a progressão da cárie em torno dos bráquetes ortodônticos. (AU)


Aim: To verify the action of dairy products with or without probiotics on strains of Streptococcus mutans (SM) and S salivarius (SS), the adhesion of these products to the surface of orthodontic brackets and to evaluate the progression of demineralization in blocks of bovine teeth around orthodontic brackets after the enamel has been exposed to dairy products containing probiotics. Materials and methods: pool of SM and SS ATCC strains was formed and plated on Petri dish containing brain heart infusion agar (BHI) medium. Following the methodology of Antonniazzi et al. (2015) the well was filled with 150µl of the products to be tested, forming the following groups: L - Bovine milk; LP - Bovine milk with probiotic; LF - Fermented milk and LFP - Fermented milk with probiotic. The plates were then incubated for 48 h in an oven at 37 °C. After this the measurement of the halo formed between the product and the medium with millimeter ruler was made. Following the methodology of Antônio et al. (2012) biofilm was formed on the membrane disc with the same pool of strains. After the treatment was done according to the group: P1 (water); P2 (L); P3 (LP); P4 (LFP), followed by serial dilution, plating and total count of microorganisms. For the adhesiveness of the dairy products, orthodontic brackets were submerged in each solution (L, LP, LF and LFP), which were incubated at 37ºC / 24h. Subsequently, each bracket was transferred to an ependorf containing sterile saline solution, which was submitted to serial dilutions, then incubated at 37ºC / 48h under microaerophilia to count the CFU/mL. In the evaluation of the demineralization, 42 bovine teeth previously cut in blocks with 64 mm² were used. Bacteria were glued on the enamel surface and divided into 6 groups randomly: G1 (negative control), G2 (positive control), G3 (L), G4 (LP), G5 (LF) and G6 (LFP). With the exception of G1, all others were placed in BHI supplemented with 2% sucrose with 1x106 cells / ml SM (ATCC 25175) and SS (ATCC 7073) for 24 hours. Subsequently, they were treated daily for 5 minutes for a total of 4 days. After the treatment, the values of final surface microhardness, mineral loss index and internal microhardness were evaluated. Results: there was no inhibition halo formation between the products and the culture medium (p <0.05); in the membrane disc no statistical differences were observed between the groups (p = 0.679); GLP and GLFP showed adhesiveness to orthodontic brackets (p = 0.056). All groups G1, G2, G3, G4, G5 and G6 presented mineral loss at the end of the experiment. Conclusions: it was not possible to verify bacteriotherapy from dairy products containing probiotics in MS and SS strains, and it was not possible to prevent the progression of caries around orthodontic supports. (AU)


Assuntos
Bovinos , Desmineralização do Dente/prevenção & controle , Braquetes Ortodônticos/microbiologia , Probióticos/uso terapêutico , Produtos Fermentados do Leite/efeitos adversos , Leite/efeitos adversos , Streptococcus mutans/isolamento & purificação , Remineralização Dentária/métodos , Técnicas In Vitro
19.
Ortho Sci., Orthod. sci. pract ; 11(42): 45-51, 2018. ilus, tab
Artigo em Português | BBO - Odontologia | ID: biblio-908941

RESUMO

A correta seleção de materiais, especificamente os bráquetes, é requisito importante para o êxito da terapia ortodôntica. Esse estudo tem como objetivo avaliar a resistência ao cisalhamento empregando-se três grupos de bráquetes metálicos de marcas comerciais nacionais diferentes em dentes incisivos bovinos. Foi encaminhado ao Comitê de Ética no Uso de Animais (CEUA) e somente após sua aprovação iniciou-se os testes. Foram utilizados 24 dentes incisivos inferiores bovinos, divididos em três grupos aleatoriamente, contendo 8 dentes em cada grupo: 1) Morelli; 2) Orthometric e 3) Eurodonto. Os dentes foram limpos com curetas periodontais e armazenados em água destilada à temperatura de 4°C. Após a estocagem, os dentes foram inclusos em tubos de PVC, de maneira centralizada e com as faces vestibulares perpendiculares ao solo, utilizando como auxílio um esquadro justaposto à superfície de colagem. Em cada amostra foram feitas marcações nos tubos de PVC identificando os grupos e a sequência. As amostras foram submetidas à profilaxia, condicionamento ácido, aplicação do primer e resina fotopolimerizável Transbond XT. Os dentes foram novamente armazenados e toda a amostra submetida ao teste de cisalhamento em máquina de ensaio universal, com velocidade de 0,5 mm por minuto. Os resultados obtidos, após execução do teste, foram armazenados em uma planilha eletrônica (software Excel®) e, posteriormente, submetidos aos testes estatísticos ANOVA e Teste de Tukey. Concluiu-se que os bráquetes metálicos das marcas Morelli, Orthometric e Eurodonto não têm diferenças estatisticamente significativas (p = 0,317) e todas as marcas testadas estão situados em uma faixa de resistência mecânica que possibilite sua utilização clínica.(AU)


Correct selection of materials, specifically the brackets, is an important requirement for orthodontic therapy success. This study aims to evaluate the shear strength employing three metal brackets groups of different national trademarks in bovine teeth incisors. It was referred to the Ethics Committee on Animal Use (CEUA) and only after approval tests began. Twenty-four bovine mandibular incisor teeth were used and randomly divided into three groups containing 8 teeth in each one: 1) Morelli; 2) Orthometric and 3) Eurodonto. The teeth were cleaned with periodontal curettes and stored in distilled water at 4°C. After storage, the teeth were inserted in PVC tubes, centrally and with the buccal surfaces perpendicular to the ground, using as an aid a square juxtaposed to the bonding surface. In each sample signs were made in the PVC tubes identifying groups and sequence. The samples were submitted o prophylaxis, etching, primer application, and Transbond XT photopolymerizable resin. The teeth were stored again and the whole sample was submitted to the shear test in a universal testing machine with speed of 0.5 mm per minute. The results obtained after test execution were stored in a spreadsheet (Excel software), and then submitted to statistical tests ANOVA and Tukey test. It was concluded that metal brackets of the trademarks Morelli, Orthometric and Eurodonto have statistically significant differences (p = 0.317) and all trademarks tested are situated in a strength range which allows their clinical use.(AU)


Assuntos
Bovinos , Resinas Compostas , Resistência ao Cisalhamento , Braquetes Ortodônticos
20.
Belo Horizonte; s.n; 2018. 37 p. ilus, graf, tab.
Tese em Inglês, Português | BBO - Odontologia | ID: biblio-986892

RESUMO

Objetivo: Avaliar a reparação de defeitos ósseos em modelo animal de rato por meio da análise fractal e radiopacidade em imagens radiográficas. Metodologia: 120 ratos Wistar tiveram seu primeiro molar extraído e foram divididos em quatro grupos (n=6/grupo) de acordo com o material de enxertia utilizado para preencher o defeito ósseo: Osso bovino mineralizado (OBM); Osso bovino desmineralizado (OBD); Coágulo sanguíneo como controle negativo (CN); Osso bovino Bio-Oss® como controle positivo (BO). Os animais foram sacrificados após 1, 7, 14, 21 e 49 dias e submetidos à análise radiográfica por dimensão fractal em um único ROI de 30x30 pixels e níveis de radiopacidade em três pontos (apical, médio e coronal) de 5x5 pixels. A avaliação histológica foi realizada como padrão ouro por meio da histomorfometria da neoformação óssea e maturação da matriz óssea. Resultados: A avaliação histomorfométrica sugere que o grupo OBD apresenta deposição mineral acelerada e um osso estatisticamente mais maduro aos 49 dias em relação ao CN. O grupo OBM apresenta características similares ao BO, porém, com menor percentual de deposição óssea. Em relação à maturação óssea, não houve diferença com significância estatística em nenhum momento da análise. A análise de radiopacidade mostra diferença com significância estatística entre OBD e o CN aos 49 dias. A análise fractal não mostrou diferenças estatísticas, mas seguiu padrão semelhante. Conclusão: A análise da radiopacidade mostrou-se mais efetiva na quantificação do reparo ósseo em relação à análise fractal no grupo desmineralizado. Não houve diferença entre os dois métodos no grupo mineralizado, concluindo que os dois métodos tem efetividade semelhante.


The aim of this study was to evaluate bone repair of an osseous defect in a rat animal model through fractal analysis and radiopacity analysis in radiographic images. Materials and methods: 120 Wistar rats were subjected to extraction of their first molar and were divided into four groups (n=6/group) according to the material used for bone grafting: mineralized bovine bone (MBB), demineralized bovine bone (DBB), blood clot (BC; as a negative control) or Bio-Oss (BO®; as a positive control). The animals were sacrificed after 1, 7, 14, 21 and 49 days and subjected to radiographic evaluation. For fractal analysis (FA), a rectangular ROI of 30x30 pixels was used, and radiopacity was measured as the mean gray scale (MGS) value for three points of 5x5 pixels in the apical, medial and coronal regions of the defect. Histomorphometric evaluation was realized as the gold standard for measuring bone neo-formation and the maturation of the new osseous matrix. Results: the histomorphometric evaluation suggested that DBB showed faster mineralized deposition and resulted in more mature bone at the final time point of evaluation. MBB and BO presented similar results. The mineralized groups did not show significant differences in bone maturation. The radiopacity analysis revealed a significant difference (p<0.05) between the DBB and BC groups at the final time point. FA did not show any significant differences at the final time point. Conclusion: Radiopacity analysis seemed to be more effective for the quantification of bone repair than fractal analysis in the demineralized group in this animal model. The results for the mineralized groups did not reveal a significant difference, leading to the conclusion that both methods are effective


Assuntos
Animais , Bovinos , Materiais Biocompatíveis , Osso e Ossos , Regeneração Óssea , Radiografia , Radiografia Dentária , Osseointegração , Fractais , Dente Molar