Braz. j. oral sci ; 18: e191591, jan.-dez. 2019. tab
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-1095170

RESUMO

Aim: The yellowing effect is undesirable and can occur in the dental restoration margins when light-cured resin cements containing camphorquinone as photoinitiator is used. This study aimed to evaluate the effect of diphenyliodonium hexafluorphosphate (DPI) in photoinitiator systems that contained different concentrations of camphorquinone (CQ) and dimethylamino ethyl benzoate (EDAB) on resin cements. Methods: A base (1:1) of bisphenol A diglycidyl methacrylate (BisGMA) and triethylene glycol dimethacrylate (TEGDMA) was obtained, and 60wt% of glass fillers was added. Eight formulations were obtained: RC1 (0.5mol% CQ / 1mol% EDAB), RC2 (0.5mol% CQ / 2mol% EDAB), RC3 (1mol% CQ / 1mol% EDAB), RC4 (1mol% CQ / 2mol% EDAB), and RC5 to RC8, which contained the same bases plus 0.5mol% DPI. Experimental resin cements were evaluated by the degree of conversion (DC), L*a*b* color analysis, water sorption (WS) and solubility (S), flexural strength, and Elastic Modulus. The data were analyzed by three-way ANOVA, Tukey's and Mann-Whitney tests (α = 0.05). Results: The combination of DPI and 0.5mol% CQ increased DC in RC6 and L* in RC5 without increasing the WS and a* b* values. CQ at 1mol% showed higher values of b* and lower values of a*, except for RC3. Groups with 2mol% EDAB showed higher DC. Conclusion: The addition of DPI reduces CQ, generating a decreased yellowing effect, while maintaining adequate properties in the resin cements, especially with 2mol% EDAB


Assuntos
Polímeros , Cimentos de Resina , Fenômenos Físicos , Fotoiniciadores Dentários
2.
Ortho Sci., Orthod. sci. pract ; 12(46): 61-68, 2019. ilus, tab, graf
Artigo em Português | BBO - Odontologia | ID: biblio-1007629

RESUMO

Introdução: As características ideais dos braquetes ortodônticos são alto potencial anticorrosivo, baixa concentração de níquel, boa dureza, curvatura da base adequada, paredes das canaletas lisas e ainda se constituirem em monobloco. O objetivo deste trabalho foi analisar as características químicas, físicas e metalográficas do braquete Roth Max, a fim de verificar os seus benefícios na clínica ortodôntica. Métodos: Foram utilizados dois conjuntos de braquetes ortodônticos. A análise química foi realizada através de três métodos: espectrometria, combustão e leitura por meio de infravermelho e nitrogênio total. A análise metalográfica foi realizada por meio de microscopia óptica, força atômica e magnética e ferritoscopia. A análise física foi realizada por meio de microdureza vickers. Resultados: A análise química mostrou a seguinte composição: Cr- 17%; Mn- 10.8%; Mo- 3.2%; C- 0.65%; N- 0.18%; Cu- 0.1%; Ni- 0.1%; Al- 0.1%; Co- 0.016%; Zn- 0.003%; Pb- 0.004%; Ti- 0.004%; Sn- 0.005% e V- 0.007%. Na análise metalográfica foi observada ausência de solda, presença de poros, estrutura duplex (ferrita e austenita). Na análise física, as médias das microdurezas na secção longitudinal foram de 242 HV1 (base), 213 e 212 HV1 (aletas). Na secção frontal foi de 217 HV1 (base). Conclusões: O teor de carbono excedeu o limite máximo indicado para os aços duplex. Os teores de nitrogênio e molibdênio elevaram o potencial anticorrosivo. A microdureza foi considerada eficiente para a clínica ortodôntica. A análise metalográfica não encontrou presença de solda, mas evidenciou uma grande quantidade de poros e heterogeneidade na microestrutura entre as frações volumétricas de ferrita e austenita.(AU)


Introduction: Ideal characteristics of orthodontic brackets include high anti-corrosive potential, high nickel concentration, good hardness, adequate base curvature, smooth channel walls, and their monoblock form. The present study aimed to analyze the chemical, physical and metallographic characteristics of the Roth Max bracket to verify its benefits in orthodontic clinic. Methods: Two orthodontic bracket sets were used. Chemical analysis was performed using three methods: spectrometry, combustion, and scanning through infrared and total nitrogen. Metallographic analysis was performed by optical microscopy, atomic and magnetic force and ferrite measurement. Physical analysis was conducted using vickers microhardness. Results: Chemical analysis showed the following composition: Cr- 17%, Mn- 10.8%, Mo-3.2%, C- 0.65%, N- 0.18%, Cu- 0.1%, Ni- 0.1%, Al- 0.1%, Co- 0.016%, Zn- 0.003%, Pb- 0.004%, Ti- 0.004%, Sn- 0.005%, and V- 0.007%. Metallographic analysis presented absence of welding, the presence of pores, and a duplex structure (ferrite and austenite). In the physical analysis, microhardness averages in the longitudinal section were 242 HV1 (base), and 213 and 212 HV1 (flaps). In the front section, it was 217 HV1 (base). Conclusions: The carbon content exceeded the maximum limit indicated for duplex steels. Nitrogen and Molybdenum raised the anti-corrosive potential. Microhardness was considered efficient for orthodontics clinics. Metallographic analysis found no evidence of welding, but it did find a large quantity of pores and heterogeneity in the microstructure between the ferrite and austenite volumetric fractions.(AU)


Assuntos
Fenômenos Físicos , Fenômenos Químicos , Braquetes Ortodônticos , Corrosão , Microscopia
3.
Rev. bras. odontol ; 58(5): 300-304, set.-out. 2001. ilus
Artigo em Português | LILACS, BBO - Odontologia | ID: lil-302488

RESUMO

O propósito deste artigo é apresentar de maneira didática os principais conceitos envolvidos nos fenômenos de memória de forma e superelasticidade das ligas de Ni-Ti com aplicaçöes médicas ou odontológicas. Será dada maior ênfase aos aspectos metalúrgicos: transformaçöes cristalinas, temperaturas de transformaçäo e comportamento mecânico


Assuntos
Elasticidade , Engenharia Biomédica/tendências , Fios Ortodônticos/tendências , Fenômenos Físicos
4.
Rev. odontol. Univ. Säo Paulo ; 11(2): 93-7, abr.-jun. 1997. tab
Artigo em Português | LILACS, BBO - Odontologia | ID: lil-192836

RESUMO

Os autores pesquisaram três marcas comerciais de silicones acéticos de fabricaçäo nacional e os submeteram a testes de dureza "Shore A" e de resistência ao rasgamento, com o objetivo de verificar qual proporçäo desses materiais misturados ao silicone Silastic 4-4210 mais se aproximaria dos valores considerados ideiais para as propriedades físicas dos silicones. Concluíram que, à medida em que a quantidade de Silastic 4-4210 era aumentada, as características físicas dos silicones acéticos estudados pioravam. Estes, porém, possuem certas vantagens sobre os materiais "in natura", em funçäo da maior sensaçäo de textura de pele natural e da maior liberdade de escolha do profissional quanto às qualidades desejadas para a confecçäo de próteses faciais


Assuntos
Prótese Maxilofacial/reabilitação , Prótese Maxilofacial/tendências , Silicones/análise , Silicones/uso terapêutico , Testes de Dureza , Fenômenos Físicos