1.
Rev. Odontol. Araçatuba (Impr.) ; 41(2): 34-39, maio-ago.2020. tab, graf
Artigo em Português | LILACS, BBO - Odontologia | ID: biblio-1102682

RESUMO

As resinas Bulk fill surgiram com o intuito de facilitar a restauração de cavidades profundas. A fotoativação adequada é extremamente importante para que a resina bulk fill ofereça propriedades mecânicas satisfatórias e, longevidade na restauração. Este estudo avaliou a influência da espessura do incremento na microdureza Knoop (KHN) de três resinas bulk fill (n = 5). Cinquenta amostras foram divididas de acordo com o material (Filtek Z250, Filtek One Bulk Fill e Filtek Bulk Fill Flow), espessura (2mm e 4 mm) e tempo de fotoativação (20 e 40s) - Z2502mm20s, Z2502mm40s, One2mm20s, One2mm40s, One4mm20s, One4mm40s, Flow2mm20s, Flow2mm40s, Flow4mm20s e Flow4mm40s. As análises KHN foram realizadas no topo e na base de cada amostra. Os dados foram submetidos à ANOVA a 1 critério e ao Teste de Tukey (p< 0,05). A média e desvio padrão (+/-) dos seguintes grupos foram (Z2502mm20s) 0,85 (+/- 0,01); (Z2502mm40s) 0,92 (+/- 0,01); (One2mm20s) 1,05 (+/- 0,08); (One2mm40s) 0,95 (+/- 0,04); (One4mm20s) 0,93 (+/- 0,04); (One4mm40s) 0,97 (+/ - 0,04); (Flow2mm20s) 0,92 (+/- 0,05); (Flow2mm40s) 0,89 (+/- 0,04); (Flow4mm20s) 0,79 (+/- 0,04) e (Flow4mm40s) 0,90 (+/- 0,03). Os grupos da Filtek One Bulk apresentaram um valor significativamente maior, demonstrando uma polimerização suficiente mesmo na base de incrementos com 4 mm. Concluiu-se que o aumento na espessura do incremento de resinas bulk fill não afetou negativamente a fotoativação(AU)


Bulk fill composites emerged, allowing the restoration of deep cavities easily. Appropriate lightcuring is crucial to bulk fill composite presents satisfactory mechanical properties and restoration longevity. This study evaluated the influence of thickness increment on Knoop microhardness (KHN) of three dental bulk fill composites (n=5). Fifty samples were divided according to composite (Filtek Z250, Filtek One Bulk Fill and Filtek Bulk Fill Flow), thickness (2mm and 4 mm) and time lightcuring (20 and 40 s) - Z2502mm20s, Z2502mm40s, One2mm20s, One2mm40s, One4mm20s, One4mm40s, Flow2mm20s, Flow2mm40s, Flow4mm20s e Flow4mm40s. KHN analysis were performed on the top and the base of each specimen. Data were subjected to one-way ANOVA and Tukey test (p< 0,05). The mean and standard deviation (+/-) of following groups were (Z2502mm20s) 0,85(+/-0,01); (Z2502mm40s) 0,92(+/- 0,01); (One2mm20s) 1,05(+/-0,08); (One2mm40s) 0,95(+/-0,04); (One4mm20s) 0,93 (+/-0,04); (One4mm40s) 0,97(+/-0,04); (Flow2mm20s) 0,92(+/- 0,05); (Flow2mm40s) 0,89(+/-0,04); (Flow4mm20s) 0,79(+/-0,04) e (Flow4mm40s) 0,90(+/-0,03) Filtek One Bulk groups present significantly higher value, demonstrating sufficient polymerization even on the base of 4 mm increments. It was concluded that the increase in the thickness increment of Bulk fill composites did not negatively affect the lightcure(AU)


Assuntos
Resinas Compostas , Testes de Dureza , Materiais Dentários , Polimerização
2.
Electron. j. biotechnol ; 41: 81-87, sept. 2019. tab, graf, ilus
Artigo em Inglês | LILACS | ID: biblio-1087242

RESUMO

Background: The search for innovative anti-tubercular agents has received increasing attention in tuberculosis chemotherapy because Mycobacterium tuberculosis infection has steadily increased over the years. This underlines the necessity for new methods of preparation for polymer-drug adducts to treat this important infectious disease. The use of poly(ethylene glycol)(PEG) is an alternative producing anti-tubercular derivatives. However, it is not yet known whether PEGylated isonicotinylhydrazide conjugates obtained by direct links with PEG are useful for therapeutic applications. Results: Here, we synthesized a PEGylated isoniazid (PEG-g-INH or PEG­INH) by gamma radiation-induced polymerization, for the first time. The new prodrugs were characterized using Raman and UV/Vis spectrometry. The mechanism of PEGylated INH synthesis was proposed. The in vitro evaluation of a PEGylated isonicotinylhydrazide macromolecular prodrug was also carried out. The results indicated that PEG­INH inhibited the bacterial growth above 95% as compared with INH, which showed a lower value (80%) at a concentration of 0.25 µM. Similar trends are observed for 0.1, 1, and 5 µM. Conclusions: In summary, the research suggests that it is possible to covalently attach the PEG onto INH by the proposed method and to obtain a slow-acting isoniazid derivative with little toxicity in vitro and higher antimycobacterial potency than the neat drug.


Assuntos
Polietilenoglicóis/química , Isoniazida/química , Mycobacterium tuberculosis/efeitos dos fármacos , Antituberculosos/química , Polietilenoglicóis/farmacologia , Polímeros , Análise Espectral Raman , Técnicas In Vitro , Pró-Fármacos , Polimerização , Raios gama , Isoniazida/farmacologia , Antituberculosos/farmacologia
3.
Rev. Asoc. Argent. Ortop. Traumatol ; 84(3): 296-308, jun. 2019.
Artigo em Espanhol | LILACS | ID: biblio-1020345

RESUMO

Una significativa cantidad de adultos jóvenes activos sufre lesiones condrales focales. Estas lesiones, si no se tratan, pueden progresar hacia la artrosis, que es una de las principales enfermedades musculoesqueléticas debilitantes y de gran carga económica que afectan a toda sociedad. Pese a los tratamientos quirúrgicos disponibles para la reparación de defectos condrales focales sintomáticos que mejoran la calidad de vida a mediano plazo, hay un mayor riesgo de progresión hacia la artrosis prematura. Los tratamientos biológicos (células madre, bioingeniería tisular) han avanzado a grandes pasos en los últimos años. La bioingeniería es un área que ha progresado en la regeneración de cartílago articular y que potencialmente podría progresar en el terreno de tratamientos articulares, promoviendo la regeneración y evitando la degeneración. Las células madre y los hidrogeles pueden proveer un tejido símil biológico de comportamiento dinámico-funcional equivalente que induce la regeneración tisular al ser degradado y reemplazado gradualmente. El abordaje consiste en colocar un hidrogel precursor o un biomaterial tridimensional impreso dentro del defecto condral por ocupar para inducir la regeneración. Esta revisión se focaliza en el uso actual y futuro de hidrogeles y bioimpresión tridimensional para la regeneración de cartílago articular en el tratamiento de lesiones condrales focales y proporciona datos preliminares de dos estudios piloto en animales. Nivel de Evidencia: V


A significant number of young active adults are affected by focal chondral lesions. These lesions, if left untreated, will progress to osteoarthritis (OA). OA is one of the main debilitating musculoskeletal diseases and leads to a high economic and social burden. Despite surgical cartilage repair for focal chondral lesions, which improve patient-reported outcomes at short- and mid-term, there is a risk of early OA progression. Biological treatments (i.e., stem-cell therapy, bioengineering) have made great progress in the last years. Tissue engineering is an evolving field for articular cartilage repair which could potentially be used for the treatment of focal chondral lesions, promoting regeneration and preventing joint surface degeneration. Stem cells and hydrogels may provide a functional, dynamic and biologically equivalent tissue that promotes tissue regeneration while being gradually degraded and replaced. The standard approach to tissue engineering consists in delivering cells within a hydrogel or a three-dimensional printed biomaterial scaffold into the chondral lesion to induce regeneration. This review focuses on the current and future use of hydrogels and tissue scaffold bioprinting for the treatment of focal chondral lesions, and provides preliminary data from two pilot animal studies. Level of Evidence: V


Assuntos
Humanos , Regeneração , Cartilagem Articular/lesões , Cartilagem Articular/patologia , Hidrogel de Polietilenoglicol-Dimetacrilato/uso terapêutico , Engenharia Tecidual , Polimerização , Bioimpressão
4.
Braz. dent. sci ; 22(3): 371-377, 2019. tab
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-1009280

RESUMO

Objective: the aim of this study is to evaluate the microhardness and color change (∆E) of composite resins, that were light-cured with different LEDs, after being immersed in a staining drink. Material and Methods: Two composite resins with Lucerin-TPO (Tetric N-Ceram/ Vit-l-escence) and camphorquinone (Filtek Z350) were selected. The specimens (n=120) were prepared and lightcured with LED of monowave or polywave lightemitting diode (LED) devices. Microhardness and color evaluations were measured before and after immersion in staining drink. Microhardness data were evaluated by Kruskal-Wallis test, MannWhitney and Wilcoxon tests. Color changes were evaluated by two-way analysis of variance (ANOVA) and Tukey test (p ≤ 0.05). Results: No statistically significant difference between the two generations of LEDs was found for microhardness data. Regarding the ∆E, a statistical difference between the two LEDs was observed for Tetric NCeram and Filtek Z350. Conclusion: The compostion of composites appears to have more influence on analyses than the type of LEDs used. A decreased microhardness occurred to Vit-lescence for monowave and to Filtek Z350 for both LED devices. A clinically perceptible color change was observed for Tetric-N Ceram and Filtek Z350 when polywave LED were used. (AU)


Objetivo: o objetivo deste estudo foi aviliar a microdureza e alteração de cor (∆E) de resinas compostas, fotoativadas com diferentes LEDs, imergidas em bebidas pigmetadas. Material e métodos: Duas resinas compostas com Lucerina-TPO (Tetric N-Ceram/ VIt-l-essence) e canforoquinona (Filtek Z350) foram selecionadas. Os espécimes (n=120) foram preparados. Os mesmos foram fotopolimerizados com LED monowave ou polywave. Microdureza e cor foram avaliadas antes e após a imersão em bebidas pigmentadas. Os dados de microdureza foram avaliados pelos testes de Kruskal-Wallis, Mann-Whitney e Wilcoxon. As alterações de cor foram avaliadas por análise de variância a dois critérios (ANOVA) e Tukey (p ≤ 0,05). Resultados: Não foi encontrada diferença estatística entre as duas gerações de LEDs, para os dados da microdureza. Quanto ao ∆E, foi encontrada diferença estatisticamente significante entre os dois LEDs, sendo observadas na Tetric N-Ceram na FIltek Z350. Conclusão: A composição das resinas compostas parece ter mais influencia nas análises do que o tipo de LEDs. Uma redução na microdureza ocorreu para Vit-lescence para monowave e para Filtek Z350 para ambos os dispositivos LED. Uma mudança de cor clinicamente perceptível foi observada em Tetric-N Ceram para polywave e Filtek Z350 para ambos os dispositivos LED. (AU)


Assuntos
Resinas Compostas , Luzes de Cura Dentária , Fotoiniciadores Dentários , Polimerização
5.
Rev. Fac. Odontol. (B.Aires) ; 34(78): 49-55, 2019. tab, graf
Artigo em Espanhol | LILACS | ID: biblio-1116910

RESUMO

El objetivo de este estudio fue analizar el comportamiento, contracción volumétrica, de diferentes resinas compuestas de fotopolimerización, expuestas a variadas condiciones de incidencia lumínica. Se tomaron volúmenes estandarizados de 7 resinas compuestas (microhíbridas y nanohíbridas y nanoparticulados) que se colocaron sobre una línea de referencia en portaobjetos, cubriéndose luego con otro y aplicando una fuerza previamente establecida. Se midió luego con un calibre electrónico la variaciones en el diámetro de la muestra bajo tres situaciones diferentes: luz ambiente (natural), luz foco (halógena), luz artificial (tubos fluorescentes) y sus combinaciones. Resultados: Se observó la mayor variación porcentual al exponer a las muestras simultáneamente a la luz ambiente, artificial y operatoria, siendo los valores más altos de reducción para las resinas compuestas Brilliant NG Coltene (Dentina) y Miris 2 Coltene (Dentina) con -2.52% y -2.7% respectivamente. Conclusión: existieron modificaciones en el volumen de todos los materiales expuestos a las diferentes condiciones de luz y tiempo de exposición. Comparando los resultados con el estudio previo (2007) se pude inferir que los materiales usados en el presente estudio resultaron más fotosensibles, dado que a similar exposición, aumentaron y/redujeron su tamaño en mayor medida (AU)


Assuntos
Resinas Compostas/química , Luzes de Cura Dentária , Polimerização , Fatores de Tempo , Teste de Materiais , Análise Estatística , Análise de Variância , Propriedades Físicas e Químicas , Dentina , Luz
6.
Rev. odontol. UNESP (Online) ; 48: e20190103, 2019. tab, graf
Artigo em Português | LILACS, BBO - Odontologia | ID: biblio-1099185

RESUMO

Resumo Introdução As resinas de polimetilmetacrilato e as bisacrílicas são materiais amplamente utilizados para a confecção de restaurações provisórias; no entanto, ambas apresentam uma característica de exotermia durante a polimerização que deve ser investigada por causa de possíveis interferências no sucesso clínico. Objetivo Avaliar a variação de temperatura de polimerização da resina bisacrílica e de uma resina acrílica quimicamente ativada, em preparos classe V, pelo método direto. Material e método Para isso, vinte dentes incisivos inferiores bovinos foram divididos em dois grupos: RA (N=10) com dentes restaurados com resina acrílica e RB (N=10) com dentes restaurados com resina bisacrílica. As mensurações das variações térmicas foram realizadas através de termopares tipo J, ligados a um termômetro óptico, e analisadas por um computador equipado com o software específico. Os dados obtidos foram analisados e submetidos à análise de médias comparadas pelo teste de Tukey (significância de 5%). Resultado Foi possível observar que não houve diferença estatística significante entre ambos os grupos experimentais (p=0,0739), mesmo que aumento de temperatura de RA tenha apresentado média maior (0,52 °C) do que RB (0,44 °C). Conclusão Não existe diferença significativa experimental entre o calor emitido pela resina acrílica e pela resina bisacrílica durante seus processos de polimerização, não definindo a característica de escolha de uma destas para as restaurações provisórias diretas.


Abstract Introduction Polymethyl methacrylate and bis-acryl resins are materials widely used for temporary restorations, however, both have a characteristic of polymerization exotermia that should be investigated because of possible interferences in clinical success. Objective to evaluate the variation of the polymerization temperature of bis-acryl resin and a chemically activated acrylic resin in the temporary restoration by the direct method. Material and method Twenty bovine mandibular incisor teeth were divided into two groups: AR (N = 10) teeth restored with acrylic resin and BR (N = 10) teeth restored with bis-acryl resin. Measurements of thermal variations were performed using type J thermocouples, connected to an optical thermometer and analyzed by a computer equipped with specific software. The obtained data were analyzed and submitted to the analysis of means compared by Tukey test (significance of 5%). Result It was observed that there was no statistically significant difference between both experimental groups (p = 0.0739), even though AR temperature increase presented higher average (0.52ºC) than BR (0.44ºC). Conclusion There is no significant experimental difference between the heat emitted by acrylic resin and bis-acryl resin during their polymerization processes, not defining the factor that characterizes a choice of a material for temporary restorations.


Assuntos
Resinas Acrílicas , Restauração Dentária Temporária , Polimerização , Polimetil Metacrilato , Temperatura Alta
7.
Rev. odontol. UNESP (Online) ; 48: e20190007, 2019. tab
Artigo em Português | LILACS, BBO - Odontologia | ID: biblio-991492

RESUMO

Resumo Introdução Os adesivos autocondicionantes apresentam técnica adesiva simplificada e diminuição na sensibilidade pós-operatória. Quando aplicados sobre a dentina, atuam sobre a smear layer, cuja efetiva remoção ainda constitui um desafio. Uma substância utilizada como pré-tratamento dentinário na ajuda da remoção da smear layer é o etilenodiamino tetracético dissódico (EDTA). Objetivo Avaliar os efeitos do EDTA em associação com sistemas adesivos autocondicionantes na resistência de união ao microcisalhamento. Material e método Foram seccionadas as superfícies oclusais de 72 terceiros molares humanos extraídos, para expor superfície dentinária plana. Os dentes preparados foram divididos em: dentina sem pré-tratamento; dentina tratada com EDTA 0,1M; dentina tratada com EDTA 0,5M. Cada grupo recebeu tratamento de três sistemas adesivos autocondicionantes: Single Bond Universal (SBU), AdheSE (AdheSE) e Clearfil SE Bond (CSEB). Foi delimitada a área adesiva e assim posicionada uma matriz transparente, para inserção com resina composta Z250XT seguida de polimerização por 40 segundos. Após 24 horas de armazenamento, os dentes foram submetidos ao ensaio de microcisalhamento. Os dados obtidos foram analisados estatisticamente, utilizando-se os testes Two-Way ANOVA e Bonferroni, e sendo considerado nível de significância de 5%. Resultado Não houve diferença estatística significante na resistência de união entre os pré-tratamentos dentinários (p=0,8353), porém houve diferença significativa entre os adesivos (p<0,05) CSEB e AdheSE, mostrando semelhança entre CSEB e SBU, e entre SBU e AdheSE. Conclusão O pré-tratamento dentinário com solução de EDTA não afetou a resistência de união com nenhum dos sistemas adesivos autocondicionantes utilizados.


Abstract Introduction Self-etching adhesives have simplified adhesive technique and decreased the postoperative sensitivity. When applied on dentin, it acts on the smear layer, but it is still a challenge in the effectiveness of this removal. A substance used as a pre-treatment for the removal of the smear layer is disodium ethylenediaminetetraacetic acid (EDTA). Objective To evaluate the effects of EDTA in association with self-etching adhesive systems on micro-shear bond strength. Material and method The occlusal surfaces of 72 extracted human third molars were sectioned to expose a flat dentin surface. The prepared teeth were divided into: dentin without pre-treatment; dentin treated with 0.1M EDTA; dentin treated with 0.5M EDTA. Each group received treatment of 3 self-etching adhesive systems: Single Bond Universal (SBU), AdheSE (AdheSE), and Clearfil SE Bond (CSEB). The adhesive area was delimited and positioned a transparent matrix for insertion with Z250XT composite resin followed by polymerization for 40 seconds. After 24h of storage, the teeth were submitted to the micro-shear test. The data were analyzed statistically using the Two-Way ANOVA and Bonferroni tests, considering a level of significance of 5%. Result There was no statistically significant difference in bond strength between dentin pre-treatments (p = 0.8353), but showed a significant difference between CSEB and AdheSE adhesives (p <0.05), showing similarity between CSEB and SBU, and between SBU and AdheSE. Conclusion Dentin pretreatment with EDTA solution did not affect bond strength with any of the self-etching adhesive systems used.


Assuntos
Tratamento Preliminar , Adesivos , Resultado do Tratamento , Ácido Edético , Dentina , Hipoclorito de Sódio , Eficácia , Resistência ao Cisalhamento , Sensibilidade da Dentina , Polimerização
8.
Braz. j. oral sci ; 18: e191451, jan.-dez. 2019. ilus
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-1087501

RESUMO

Aim The aim of this study is to evaluate the degree of conversion (DC) of resin cements polymerized under different thicknesses of feldspathic dental ceramic. Methods: Forty samples of RelyX ARC and RelyX Veneer resin cements were polymerized under Starlight feldspathic ceramic discs (DeguDent Gmbh) with 0.5 mm, 1.2 mm, 1.8 mm, and 2.4 mm in thickness. The control group was cured without the interposition of ceramic. The DC measurements were performed 10 minutes, 1 hour, and 24 hours after the light-activation in a Nexus 670 FTIR spectrophotometer. Data were analyzed by two-way repeated measure ANOVA and Fisher PLSD test. Results: The RelyX ARC showed higher DC for all ceramic thicknesses. There was significant decrease in DC related to an increase in ceramic thickness. For RelyX ARC, the values of DC obtained after 1 hour and 24 hours did not differ statistically between them, but they were higher than those analyzed after 10 minutes. For RelyX Veneer cement, there was gradual increase in the DC up to 24 hours. Conclusion: The higher the thicknesses of ceramic, the lower DC of the resin cement


Assuntos
Cerâmica , Cimentos de Resina , Polimerização
9.
Rev. ADM ; 75(4): 228-236, jul.-ago. 2018. ilus
Artigo em Espanhol | LILACS | ID: biblio-916343

RESUMO

Los trastornos temporomandibulares (TTM) constituyen un problema en la población en general cuyos signos y síntomas tienen un carácter multifactorial que debe ser abordado de manera interdisciplinaria para poder brindar una mejor oportunidad de éxito y estética en los tratamientos. Las guardas oclusales forman parte del tratamiento en los TTM, se deben conocer sus indicaciones, contraindicaciones, ventajas y desventajas, debido a que las guardas oclusales cumplen ciertas funciones y objetivos. La guarda oclusal elaborada por la técnica de polimerización en microondas (GOTMI) reduce signifi cativamente el tiempo de elaboración en el laboratorio, proporciona un aparato de alta calidad y baja porosidad. La GOTMI es un aparato que proporciona un método indirecto y no invasivo modifi cando la oclusión, recuperando el tejido u órganos dentales perdidos, reorganiza la actividad refl eja neuromuscular, relaja la musculatura, promueve el reposicionamiento del disco articular, protege los dientes, oclusión y estructuras de sostén periodontal, además de mejorar la estética y la autoestima del paciente. La GOTMI disminuye el dolor en la ATM y la neuromusculatura, proporciona alivio a las cefaleas tensionales, elimina las interferencias oclusales, es un distribuidor de fuerzas oclusales, además de provocar un mayor número de contactos de igual intensidad de fuerza contra la superfi cie oclusal en todos los dientes. Existen varios métodos para la confección de las guardas oclusales, en el presente trabajo se describe la elaboración de una guarda oclusal programada con los principios de oclusión orgánica. La técnica de polimerización por microondas es innovadora debido a que este proceso consiste en la generación de calor dentro de la resina mediante ondas electromagnéticas producidas por un generador llamado magnetrón. Las moléculas de metilmetacrilato son capaces de orientarse por el campo electromagnético a una frecuencia de 2,450 MHz, y cambian su dirección cinco billones de veces por segundo aproximadamente, lo que implica numerosas colisiones intermoleculares y causa una rápida polimerización (AU)


Temporomandibular disorders (TMD) are a problem in the general population whose signs and symptoms have a multifactorial character that must be addressed by an interdisciplinary team to provide a better chance of success and aesthetic treatments. Occlusal guards are part of TMD treatment, you should know the indications, contraindications, advantages, and disadvantages, because the occlusal guards perform certain functions and objectives. The occlusal guard by Iztacala modifi cation provides an indirect and noninvasive method modifying occlusion, recovering the lost dental tissue or organs, reorganizes the neuromuscular refl ex activity, relaxes the muscles, promotes articular disc repositioning, protecting the teeth and supporting occlusion structures, it also improves aesthetics and self-esteem. The occlusal guard Iztacala modifi cation has the advantage of decreasing TMJ pain, provides relief to tension headaches, elimination of occlusal interferences, is a distributor of occlusal forces as well as causing a greater number of contacts equal intensity of force against the occlusal surface of all teeth. There are several methods for the fabrication of occlusal guards, in this paper the development of an occlusal guard programmed with the principles of organic occlusion is described, using as a basis a rigid acetate and acrylic for programming, in addition to providing your cosmetic use and function. The acquisition or denial of treatment with an occlusal splint depends on the choice, preparation, occlusal guard adjustment and patient cooperation (AU)


Assuntos
Humanos , Oclusão Dentária , Micro-Ondas , Placas Oclusais , Polimerização , Transtornos da Articulação Temporomandibular , Acetatos , Articuladores Dentários , Modelos Dentários , Polímeros
10.
Rev. cient. odontol ; 6(1): 29-38, ene.-jun. 2018. ilus, tab
Artigo em Espanhol | LILACS | ID: biblio-998742

RESUMO

Objetivo: Comparar, a las 48 horas, la microdureza superficial de las resinas para reconstrucción de muñones Luxa- core DMG America, Absolute Dentin Parkell y Z350 XT 3M. Materiales y métodos: El grupo de estudio estuvo conformado por 33 discos de resina, distribuidos en tres subgrupos: dos experimentales cada uno conformado por (n = 11), y uno control (n = 11). Los dos primeros grupos son resinas de foto activación y el tercero, una resina de activación dual. Estos fueron sometidos al instrumento microdurómetro Vickers, marca LG, en el laboratorio de ensayos mecánicos. Se aplicó una carga de 200 gramos fuerza por 10 segundos para cada indentación. El análisis estadístico se realizó con ayuda del programa SPSS versión 24 y se realizó la prueba de Anova y la prueba de comparación múltiple de Tukey. Resultados: Luego del ensayo de microdureza Vickers (VHN), los resul- tados fueron: para G1, el valor promedio para la variable microdureza fue 55,24 ± 1,7 VHN; el G2 arrojó un valor promedio de 54,34 ± 3,82 VHN, y para G3 fue de 75.66 ± 4.4 VHN. Conclusión: Las resinas compuestas foto activadas, como material de reconstrucción de muñones sometidos a la prueba de microdureza superficial, mostraron propiedades mecánicas mejoradas en comparación con las resinas duales evaluadas. (AU)


Objective: Compare the superficial microhardness at 48 hours of the core build-up resins Luxacore DMG America, Absolute Dentin PARKELL and Z350 XT 3M. Materials and methods: The study group consisted of 33 resin discs, distrib-uted in three sub-groups: two experi-mental groups (n = 11) and one control group (n = 11). The first two groups were photo activation resins and the third group was a dual activation resin, subjected to the Micro-Vickers Hardness Tester - LG Brand in the mechanical testing labo-ratory. A test force of 200 grams was applied for 10 seconds for each indenta-tion. Statistical analysis was conducted with the help of the SPSS version 24 program and the Anova test and Tukey multiple comparison test were performed. Results: Following the Vickers micro-hardness test (vhn), the mean results for the indentations are shown in Table 1 in vhn values. f or g1 the average microhardness variable was 55.24 ± 1.7 vhn. g2 exhibited an average value of 54.34 ± 3.82 vhn. the average micro-hardness value for G3 was 75.66 ± 4.4 vhn.Conclusions: Composite photo activated resins as a core build-up mate-rial subjected to surface microhardness testing displayed improved mechanical properties compared to the dual resins evaluated. (AU)


Assuntos
Cimentos Dentários , Polimerização , Dureza
11.
Rev. cient. odontol ; 6(1): 72-83, ene.-jun. 2018. ilus., tabs., grafs.
Artigo em Espanhol | LILACS | ID: biblio-998842

RESUMO

Objetivo: Comparar la resistencia a la microtensión entre dentina y resina de laboratorio Ceramage (Shofu) microa- renada, con óxido de aluminio de 25, 50 y 90 micrómetros, y un grupo sin microarenado. Materiales y métodos: Se utilizaron 12 terceros molares sanos, 3 por cada grupo. Se cortó la super- ficie de esmalte oclusal con un disco diamantado biactivo (BesQual) de 22 mm para exponer una superficie plana de dentina. Se fabricaron 12 bloques de resina de laboratorio Ceramage (Shofu) en un molde cilíndrico de teflón con un diámetro de 8 mm y una altura de 4 mm. Se tuvieron 4 grupos de estudio (3 bloques por grupo), a los que aleatoria- mente se aplicaron los siguientes trata- mientos de superficie: G1, sin microa- renar (grupo control); G2, con Al2O3 de 25 µm (Zhermack); G3, con Al2O3 de 50 µm (Bioart), y G4, con Al2O3 de 90 µm (Bioart). La cementación de los bloques a la dentina se realizó con el cemento resinoso autoadhesivo Maxcem Elite (Kerr). Se obtuvieron especímenes de aproximadamente 1 mm2 de área transversal (n = 26 especímenes por grupo) con una máquina de corte tipo IsoMet y se almacenaron en agua desti- lada por 24 horas a 37 °C. La prueba de microtensión se realizó haciendo uso de un microtensiómetro (Microtensile Tester - Bisco). Para el análisis estadís- tico se utilizaron las pruebas de Anova y Tukey, donde p < 0,001. Resultados: Los valores de la media y de la desviación estándar, para la variable resistencia a la microtensión de cada grupo, fueron las siguientes: para el G1 sin microarenado, 7,03 (± 2,94) Mpa; para el G2, microare- nado con 25 µm: 4,63 (± 1,28) Mpa; para el G3, microarenado con 50 µm: 4,56 (± 1,40) Mpa; y para el G4, microarenado con 90 µm: 5,93 (± 1,39) Mpa. Conclu- sión: La resistencia de unión entre el grupo que no recibió ningún tratamiento de superficie y el que empleó partículas de 90 µm es similar, razón por la cual se podría prescindir del microarenado como tratamiento de superficie. Además, la resistencia de unión del grupo que empleó partículas de 90 µm es superior a los grupos que emplearon 25 y 50 µm. (AU)


Objective: To compare the micro-tensile bond strength of dentine and the labora-tory composite "Ceramage" (Shofu), sand-blasted with 25, 50 and 90 micrometer aluminum oxide, and a control group not subjected to sandblasting. Materials and methods: 12 third molars were used, 3 in each group. The surface of the occlusal enamel was cut with a 22 mm bioac-tive diamond disc (BesQual), exposing a flat surface of dentin. 12 blocks of the laboratory composite Ceramage (Shofu) were manufactured in a cylin-drical Teflon mold with a diameter of 8 mm and a height of 4 mm. There were 4 study groups (3 blocks per group), upon which the following surface treatments were randomly performed: (g1): without sandblasting (c ontrol group); (g2): with 25 µm al2o3 (zhermack); (g3): with 50 µm al2o3 (bioart) and (g4): with 90 µm Al2O3 (Bioart). The cementation was made using Maxcem elite (Kerr) self-adhesive resin cement. Specimens of approximately 1 mm2 in cross-sectional area (n=26 specimens by group) were obtained using an IsoMet type cutting machine and stored in distilled water for 24 hours at 37°C. The micro-tensile test was performed using a Micro-tensile tester machine (Bisco). The Anova and Tukey tests were applied to the statis-tical analysis (p <0.001). Results: The mean and standard deviation values for the micro-tensile bond strength of each group were as follows: f or group 1 (g1) without sandblasting: 7.03 (+ 2.94) Mpa; for group 2 (G2) sandblasted with 25 µm: 4.63 (+ 1.28) Mpa; for group 3 (g3) sandblasted with 50 µm: 4.56 (+ 1.40) Mpa; and for group 4 (G4) sandblasted with 90 µm: 5.93 (+ 1.39) Mpa. Conclu-sions: The micro-tensile bond strength of the group which did not receive any surface treatment and the group subjected to 90 µm particles is similar, indicating that sandblasting could be dispensed with as a surface treatment. Also, the micro-tensile bond strength of the group subjected to 90 µm particles is superior to that of the groups subjected to 25 and 50 µm. (AU)


Assuntos
Cimentos de Resina , Dentina , Óxido de Alumínio , Polimerização
12.
Rev. Cient. CRO-RJ (Online) ; 3(1): 72-76, Jan.-Apr. 2018.
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-1021265

RESUMO

Introdution: Recently, composite resins that have low shrinkage and low polymerization stress have been released, the so-called Bulk-Fill composites. These offer the dental surgeon the possibility of inserting increments of up to 4 mm, making the restorative procedure faster. Objective : to report a clinical case of a posterior tooth restoration with discolored dentin substrate using a medium viscosity Bulk-Fill composite resin associated with an opacifying agent. Case report: upon clinical and radiographic examination, a 50-year-old male patient was informed about the need to replace the defective silver amalgam restoration on the occlusal surface of tooth 16. The unsatisfactory restoration was removed and then the bonding technique was performed to restore the cavity using a two-step self-etching adhesive (AdheSE, Ivoclar Vivadent, Schann, Liechtenstein). Due to the discolored dentin substrate, an opacifying agent (IPS Empress Direct Opaque, Ivoclar Vivadent, Schann, Liechtenstein) was applied to the bottom of the cavity, and then was photoactivated for 40 s. The restoration was performed with a single increment of Bulk-Fill resin composite (Tetric N-Ceram Bulk-Fill IVB, Ivoclar Vivadent, Schann, Liechtenstein) that was photoactivated for 40 s. The finishing and polishing procedures were performed using abrasive rubbers. Result: at the end, an aesthetically satisfactory restoration was obtained with the aid of the opacifying agent. Conclusion: it is possible to perform restorations faster with medium viscosity Bulk-Fill composites. However, as it is an essentially translucent material, the use of an opacifying agent in discolored tooth substrate is recommended, in order to obtain an aesthetically satisfactory result.


Introdução: Recentemente, foram lançadas no mercado resinas compostas que apresentam baixa contração e baixa tensão de polimerização, as chamadas resinas compostas Bulk-Fill. Estas oferecem ao cirurgião-dentista a possibilidade de inserir incrementos de até 4 mm, tornando o procedimento restaurador mais rápido. Objetivo: relatar um caso clínico de restauração de um dente posterior com substrato escurecido utilizando uma resina composta Bulk-Fill de média viscosidade associada a um agente opacificador. Relato do caso: após exame clínico e radiográfico, um paciente do sexo masculino com 50 anos de idade foi informado sobre a necessidade de substituição de uma restauração de amálgama de prata insatisfatória na superfície oclusal do dente 16. A restauração foi removida e, em seguida, foi realizada a técnica adesiva para a restauração da cavidade utilizando-se um sistema adesivo autocondicionante de dois passos clínicos (AdheSE, Ivoclar Vivadent, Schann, Liechtenstein). Devido ao substrato dentinário escurecido, foi aplicado no fundo da cavidade um agente opacificador (IPS Empress Direct Opaque, Ivoclar Vivadent, Schann, Liechtenstein) e este, então, fotoativado por 40 s. A restauração foi executada com uma resina composta Bulk-Fill (Tetric N-Ceram Bulk-Fill IVB, Ivoclar Vivadent, Schann, Liechtenstein) em incremento único que foi fotoativado por 40 s. Acabamento e polimento foram realizados com auxílio de borrachas abrasivas. Resultado: ao final, obteve-se, com o auxílio do agente opacificador, uma restauração esteticamente satisfatória. Conclusão: é possível executar restaurações de maneira mais rápida com resina composta Bulk-Fill de média viscosidade. Entretanto, por se tratar de um material essencialmente translúcido, é recomendado o uso de um agente opacificador em dentes com substrato escurecido a fim de se obter um resultado esteticamente satisfatório.


Assuntos
Dentística Operatória , Resinas Compostas , Restauração Dentária Permanente , Polimerização
13.
Braz. dent. j ; 29(1): 76-81, Jan.-Feb. 2018. tab, graf
Artigo em Inglês | LILACS | ID: biblio-888717

RESUMO

Abstract The aim of this study was to evaluate Knoop hardness of different shades of a resin cement light-cured directly or through ceramic discs, measured 15 min or 24 h after light exposure, and at different depths. Specimens of a commercial resin cement (Variolink Veneer) in seven shades, were fabricated in an elastomeric mold, covered with a mylar strip, a 0.7 mm thick ceramic disc (IPS e.max Press) was placed and the cement was light-activated for 20 s using a blue LED (Radii-Cal). The cured resin cement specimens were transversely wet-flattened to their middle portion and microhardness (Knoop) values were recorded at 15 min after light exposure and after deionized water storage at 37 ºC for 24 h. Five indentations were made in the cross-sectional area at 100 and 700 μm depths from the top surface. Ten specimens were made for each test conditions. Data were submitted to ANOVA split-plot design (shade, post-cure time, mode of activation and depth), followed by Tukey post hoc test (α=0.05). Significant differences for shade (p<0.0001), mode of activation (p<0.001), post-cure time (p<0.0001) and depth (p<0.0001) were detected. No significant interactions (p>0.05) were found, except for shade x post-cure time (p<0.0045) and mode of activation x post-cure time (p<0.0003). Resin cement shade has a significant effect on Knoop hardness. Indirect activation through a ceramic material reduced significantly Knoop hardness. Hardness Knoop significantly increased after 24 h in all cements shades compared to values obtained after 15 min. Resin cement depth significantly reduced Knoop hardness.


Resumo O objetivo deste estudo foi avaliar a dureza Knoop de diferentes cores de um cimento resinoso fotoativado diretamente ou através da interposição de um disco de cerâmica, medindo 15 min ou 24 h após exposição à luz, em diferentes profundidades. Amostras do cimento resinoso (Variolink Veneer) em sete cores foram fabricados num molde de elastômero, coberto com tira de poliéster, seguido de um disco cerâmico (IPS e.max Press) com 0.7 mm de espessura e fotoativado por 20 s com o aparelho LED (IPS e.max Press). O cimento resinoso fotoativado foi transversalmente desgastado na porção média e os valores de microdureza Knoop foram obtidos após 15 min após exposição à luz e após armazenagem em água deionizada à 37 °C por 24 h. Cinco penetrações foram feitas na secção transversal à 100 e 700 μm da superfície de topo. Dez amostras foram confeccionadas para cada condição de teste. Os dados foram submetidos à Análise de Variância em esquema de parcelas subdivididas (cor, tempo pós-ativação, modo de ativação e profundidade), seguido pelo teste de Tukey post hoc (α=0,05). Diferença significante para a cor (p<0,0001), modo de ativação (p<0,001), tempo pós-ativação (p<0,0001) e profundidade (p<0,0001) foi detectada. Nenhuma interação significante foi encontrada (p>0,05), exceto para a interação cor x tempo pós-ativação (p<0,0045) e modo de ativação x tempo pós-ativação (p<0,0003). A cor do cimento resinoso teve significante efeito na dureza Knoop. A ativação indireta através do material cerâmico reduziu significativamente a dureza Knoop. A dureza Knoop aumentou significativamente após 24 h em todas as cores do cimento comparados aos valores obtidos após 15 min. A profundidade do cimento resinoso reduziu significativamente os valores de dureza Knoop.


Assuntos
Cerâmica , Cor , Dureza , Cimentos de Resina , Luzes de Cura Dentária , Polimerização
14.
Araçatuba; s.n; 2018. 110 p. graf, tab, ilus.
Tese em Português | LILACS, BBO - Odontologia | ID: biblio-1009517

RESUMO

O objetivo desse estudo foi avaliar a influência de diferentes ciclos e métodos de polimerização da resina acrílica (RA) branca de próteses oculares sobre a biocompatibilidade de células da conjuntiva humana e resposta inflamatória do tecido subcutâneo de ratos. Para isso, foram confeccionados corpos de prova em RA termopolimerizados em água aquecida (RNAA), por energia de microondas (RNTM) e quimicamente ativados (RNQA). Para a análise in vivo, a resposta inflamatória desses 3 grupos (n=20/grupo) foi avaliada no tecido subcutâneo de 20 ratos Wistar por 7, 15, 30 e 60 dias (d). Células inflamatórias foram contadas no tecido adjacente ao corpo de prova após coloração com hematoxilina e eosina. A análise imunohistoquímica foi realizada para a detecção de IL-1ß, IL-6, TNFα, IL-17 e CCL20. Para a análise in vitro, diferentes ciclos de polimerização para cada método citado foram avaliados, totalizando 11 grupos (n=8/grupo). Foram realizadas análises de grau de conversão (GC), MTT, Alamar Blue, ELISA, RT-PCR em tempo real e dupla marcação de Anexina V e iodeto de propídio. Dados quantitativos foram submetidos à Análise de Variância e ao teste de Tukey com significância de 5%. Os resultados qualitativos foram comparados visualmente. Na análise in vivo, houve infiltrado inflamatório moderado para os grupos RNTM e RNQA e leve para o grupo RNAA após 7 d. O infiltrado inflamatório e a imunomarcação dos alvos testados diminuiu gradativamente ao longo dos 60 d. O grupo RNTM exibiu mais células inflamatórias, com exceção do grupo RNAA, que apresentou mais eosinófilos e linfócitos após 15 d, e do grupo RNQA, onde foi observado mais macrófagos em 15 d e neutrófilos em 60 d. Os grupos RNAA e RNQA apresentaram maior imunomarcação de IL-1ß após 7 d. O grupo RNQA apresentou maior imunomarcação de IL-1ß (15 e 30 d), IL-6 (30 e 60 d), IL-17 (15 e 30 d) e TNF-α (7 d). Os grupos RNAA e RNTM apresentaram maior imunomarcação de TNF-α nos períodos de 15 e 30 d, enquanto o grupo RNTM, aos 60 d. Na análise in vitro, todos os grupos apresentaram proliferação celular maior que 75%. O ciclo longo de polimerização em microondas apresentou menor GC e percentual de proliferação celular no MTT e resultou em grande liberação de IL-2. No ensaio de Alamar Blue, esse grupo apresentou baixo percentual de proliferação celular, assim como o grupo que recebeu ciclo longo de polimerização em água aquecida e grupos submetidos à ativação química. Maior liberação de IL-6 foi observada nos grupos submetidos à ativação química e de IL-23 para o ciclo curto de polimerização em microondas. Maior expressão gênica de TGF ß1 ocorreu para o grupo que recebeu ciclo longo de polimerização em água aquecida seguido de 30 min de armazenamento em água. Maior expressão gênica de CASP9 ocorreu para o grupo ativado quimicamente sobre a bancada. Pode-se concluir que os métodos de polimerização por meio de energia de microondas (ciclos longo e curto) e por ativação química desencadearam uma resposta inflamatória mais intensa. Dentre os métodos de polimerização recomendados pelo fabricante, a polimerização em água aquecida apresentou resultados mais satisfatórios(AU)


The aim of this study was to evaluate the influence of different cycles and methods of white color acrylic resin (AR) for ocular prosthesis on the biocompatibility of human conjunctival cells and on the inflammatory response of rat subcutaneous tissue. For this, AR specimens were prepared in water bath (NRWB), by microwave energy (NRME), and chemically activated (ANR). For in vivo analysis, the inflammatory response of these 3 groups (n=20/group) was assessed in subcutaneous tissue of 20 Wistar rats at 7, 15, 30 and 60 days (d). Inflammatory cells were counted in the tissue adjacent to specimen after staining with hematoxylin and eosin. The immunohistochemical analysis was performed for the detection of IL-1ß, IL-6, TNFα, IL-17, and CCL20. For in vitro analysis, different cycles of polymerization for each method were evaluated, with a total of 11 groups (n=8/group). The degree of conversion (DC), MTT, ELISA, real-time RT-PCR and Annexin V and propidium iodide assays were performed. Quantitative data were submitted to Analysis of Variance and Tukey test with a 5% significance. Qualitative data were submitted to visual comparison. In in vivo analysis, there was a moderate inflammatory infiltrate for groups NRME and ANR, and a light infiltrate for the group NRWB after 7 d. The inflammatory infiltrate and the immunolabeling of tested targets decreased gradually during the 60 d. The group NRME exhibited the highest number of inflammatory cells, except for the group NRWB, which presented a higher number of eosinophils and lymphocytes after 15 d, and for the group ANR, where a higher number of macrophages and neutrophils were observed at 15 d and at 60 d, respectively. Groups NRWB and ANR showed higher IL-1ß immunolabeling after 7 d. The group ANR had the highest immunolabeling of IL-1ß (15 and 30 d), IL-6 (30 and 60 d), IL-17 (15 and 30 d), and TNF-α (7 d). Groups NRWB and NRME showed greater immunolabeling in the periods of 15 and 30 d, while the group NRME had also high results at 60 d. In in vitro analysis, all groups showed cell proliferation higher than 75%. The long cycle of polymerization using microwave energy resulted in lower DC and lower percentage of cell proliferation in the MTT assay and in large release of IL-2. In the Alamar Blue assay, this group had a low percentage of cell proliferation, as well as the group that received a long cycle of polymerization in water bath and groups submitted to chemical activation. A higher release of IL-6 was observed in groups submitted to chemical activation and of IL-23, for the short cycle of polymerization in microwave. Higher TGF ß1 gene expression occurred for the group that received long cycle of polymerization in water bath followed by 30 min of storage in water. Higher CASP 9 gene expression occurred for the chemically activated group on bench. It can be concluded that the polymerization by microwave energy (long and short cycles) and by chemical activation resulted in higher inflammatory response. Among methods recommended by the manufacturer, the water bath polymerization showed more satisfactory results(AU)


Assuntos
Resinas Acrílicas , Teste de Materiais , Olho Artificial , Materiais Biocompatíveis , Ratos Wistar , Citotoxicidade Imunológica , Polimerização
15.
Araçatuba; s.n; 2018. 63 p. ilus, tab.
Tese em Português | LILACS, BBO - Odontologia | ID: biblio-1009562

RESUMO

Os reembasadores resilientes têm sido amplamente utilizados em pacientes portadores de próteses totais para melhorar a adaptação da base de resina ao rebordo. Esses apresentam dois métodos de polimerização, um feito diretamente na boca do paciente e outro feito indiretamente em laboratório. Não há estudos na literatura que avaliem a percepção dos pacientes com relação a esse tratamento. Portanto o objetivo desse trabalho foi avaliar a satisfação a qualidade de vida, força de mordida e halitose de pacientes desdentados que tiveram suas próteses totais mandibulares reembasadas com material resiliente (Ufi Gel SC, Voco, Alemanha). Foram selecionados 20 pacientes desdentados seguindo critérios de inclusão e exclusão predefinidos para terem suas próteses mandibulares reembasadas. Estes foram divididos aleatoriamente nos grupos de reembasamento direto ou indireto (n=10). Os ensaios clínicos verificaram a qualidade de vida (OHIP Edent), a satisfação com o reembasamento, a força de mordida e também presença e etiologia de halitose. Os testes clínicos foram realizados inicialmente com as próteses totais sem intervenção, após o reembasamento, aos 30, 60, 90 e 180 dias após o reembasamento. A análise de variância ANOVA (significância de 5%) demonstrou que houve uma diferença estatisticamente significante para o fator tempo para todos os testes, mas a técnica de reembasamento não. Observamos que a qualidade de vida, a satisfação, a força de mordida e halitose melhoraram após o reembasamento. A halitose foi influenciada pelo reembasamento e pela higiene bucal dos pacientes. Apesar de não ter demonstrado diferença estatisticamente entre os métodos de polimerização, foi um resultado favorável tanto para o clínico como para o paciente. Portanto, se não houver diferença entre os métodos de polimerização a longo prazo, não há porque submeter o paciente ao reembasamento indireto. Independentemente do método de polimerização escolhido, o reembasamento com material resiliente a base de silicone demonstrou ser uma alternativa viável para melhorar os aspectos funcionais e a satisfação em pacientes que apresentem dificuldades em utilizar próteses totais mandibulares(AU)


Resilient reliners have been widely used for patients wearing complete dentures to improve the adaptation of the base. They present two polymerization methods, one done directly in the patient's mouth and another done indirectly in the laboratory. There are no studies in the literature that assess the perception of patients regarding this treatment. Therefore, the purpose of this paper was to assess, the satisfaction, quality of life of edentulous patients who had their total mandibular prostheses rebased with resilient material (Ufi Gel SC, Voco, Germany). 20 edentulous patients were selected according to predefined inclusion and exclusion criteria. These were randomly divided into the direct or indirect soft reline groups (n = 10). The clinical trial evaluated the quality of life (OHIP Edent), the satisfaction regarding the treatment, the bite force and presence and prevalence of halitosis. The assays were performed in six phases during the treatment: initially with the total prostheses without intervention, after the reline procedure, 30, 60, 90 and 180 days after the reline. The analysis of variance ANOVA (5% significance) demonstrated a statistically significant difference for period in all parameters, but the technique did not influence any of the parameters (P ≤ 0.05). We observed that the QoL, satisfaction, bite force and halitosis increased after the reline. The halitosis was influenced by patients' oral hygiene and the reline procedure. Although it has not demonstrated a statistical difference between polymerization methods, it was a favorable result for both clinicians and patients. The direct polymerization method is simpler, less time consuming and less costly for the patient. Therefore, if there is no long-term difference between polymerization methods, there is no need to perform an indirect procedure. Regardless of the method of polymerization chosen, relining with resilient silicone-based material is a viable alternative to improve the quality of life, satisfaction, bite force and halitosis in patients who have difficulties wearing mandibular dentures(AU)


Assuntos
Humanos , Masculino , Feminino , Qualidade de Vida , Prótese Total , Reembasadores de Dentadura , Força de Mordida , Polimerização , Halitose
16.
Braz. oral res. (Online) ; 32: e008, 2018. tab
Artigo em Inglês | LILACS | ID: biblio-889493

RESUMO

Abstract This study aimed to evaluate the in situ degree of conversion, contact angle, and immediate and long-term bond strengths of a commercial primer and an experimental adhesive containing indomethacin- and triclosan-loaded nanocapsules (NCs). The indomethacin- and triclosan-loaded NCs, which promote anti-inflammatory and antibacterial effects through controlled release, were incorporated into the primer at a concentration of 2% and in the adhesive at concentrations of 1, 2, 5, and 10%. The in situ degree of conversion (DC, n=3) was evaluated by micro-Raman spectroscopy. The contact angle of the primer and adhesive on the dentin surface (n = 3) was determined by an optical tensiometer. For the microtensile bond strength µTBS test (12 teeth per group), stick-shaped specimens were tested under tensile stress immediately after preparation and after storage in water for 1 year. The data were analyzed using two-way ANOVA, three-way ANOVA and Tukey's post hoc tests with α=0.05. The use of the NC-loaded adhesive resulted in a higher in situ degree of conversion. The DC values varied from 75.07 ± 8.83% to 96.18 ± 0.87%. The use of NCs in only the adhesive up to a concentration of 5% had no influence on the bond strength. The contact angle of the primer remained the same with and without NCs. The use of both the primer and adhesive with NCs (for all concentrations) resulted in a higher contact angle of the adhesive. The longitudinal μTBS was inversely proportional to the concentration of NCs in the adhesive system, exhibiting decreasing values for the groups with primer containing NCs and adhesives with increasing concentrations of NCs. Adhesives containing up to 5% of nanocapsules and primer with no NCs maintained the in situ degree of conversion, contact angle, and immediate and long-term bond strengths. Therefore, the NC-loaded adhesive can be an alternative method for combining the bond performance and therapeutic effects. The use of an adhesive with up to 5% nanocapsules containing indomethacin and triclosan and a primer with no nanocapsules maintained the long-term bond performance.


Assuntos
Animais , Bovinos , Colagem Dentária/métodos , Indometacina/química , Nanocápsulas/química , Cimentos de Resina/química , Triclosan/química , Análise de Variância , Falha de Restauração Dentária , Dentina/efeitos dos fármacos , Teste de Materiais , Transição de Fase/efeitos dos fármacos , Polimerização/efeitos dos fármacos , Valores de Referência , Reprodutibilidade dos Testes , Análise Espectral Raman , Propriedades de Superfície/efeitos dos fármacos , Resistência à Tração , Fatores de Tempo
17.
Braz. dent. sci ; 21(2): 172-176, 2018. tab
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-906066

RESUMO

Polymer networks are considered to be largely affected by water and chemical absorption from environment. Objective: The aim of this study was to evaluate the hygroscopic expansion of bulk-fill composite. Material and Methods: Fifteen disks (5 in each group) with different thickness(4mm/2mm) of Tetric N-Ceram Bulk Fill composite(TB) and Tetric N-Ceram composite(TN) were made according to the manufacturer's instruction and stored in deionized water. The length of each specimen was recorded using a digital micrometer at baseline and at the end of 24 h, 1, 2, 4, 12 weeks intervals. Repeated measure ANOVA and Tukey HSD were used to determine the effect of variables. At 12 weeks, the mean hygroscopic expansion after water immersion ranged between 0. 33±0.09mm for TN to 0.41±0.07mm for TB with 2mm thickness. Repeated measure ANOVA revealed a significant increase in hygroscopic expansion over time (P <0.05). Results: The results indicated that at 24hours and 2weeks there was a significant difference among TN and TB with 4mm thickness (p=0.007 and p=0.023, respectively). The other differences were not significant. Hygroscopic expansion affected by the type of composite and the passing of time. Conclusion: The results showed that the time taken to reach stabilization in hygroscopic expansion was shorter for TN in comparison with TB. For 2mm thickness equilibrium was attained earlier. (AU)


Considera-se que as redes de ligações intrínsecas de polímeros são amplamente afetadas pela absorção de água e produtos químicos do meio ambiente. Objetivo: O objetivo deste estudo foi avaliar a expansão higroscópica do compósito bulk-fill. Material e Métodos: Quinze discos (5 em cada grupo) com diferentes espessuras (4mm / 2mm) de compósito Tetric N-Ceram Bulk Fill (TB) e Tetric N-Ceram (TN) foram confeccionados de acordo com as instruções do fabricante e armazenados em água deionizada. O comprimento de cada espécime foi registrado usando um micrômetro digital no início e no final de 24 h, 1, 2, 4, 12 semanas de intervalo. O teste de medidas repetidas ANOVA e Tukey foram usados para determinar o efeito das variáveis. Às 12 semanas, a expansão higroscópica média após imersão em água variou entre 0,33 ± 0,09mm para NT a 0,41 ± 0,07mm para TB com 2mm de espessura. ANOVA revelou um aumento significativo na expansão higroscópica ao longo do tempo (P <0,05). Resultados: Os resultados indicaram que às 24h e 2 semanas houve diferença significativa entre TN e TB com 4mm de espessura (p=0,007 e p=0,023, respectivamente). As outras diferenças não foram significativas. A expansão higroscópica foi afetada pelo tipo de compósito e pelo tempo. Conclusão: Os resultados mostraram que o tempo necessário para alcançar a estabilização na expansão higroscópica foi menor para TN em comparação com TB. Para 2 mm de espessura o equilíbrio foi atingido mais cedo. (AU)


Assuntos
Resinas Compostas , Polimerização , Água
18.
Braz. oral res. (Online) ; 32: e15, 2018. tab, graf
Artigo em Inglês | LILACS | ID: biblio-889485

RESUMO

Abstract This study evaluated the shear bond strength (SBS) of self-adhesive resin cements (SARCs) to dentin and their physical-chemical properties. Five commercial SARCs were evaluated [SmartCem®2 - DENTSPLY (SC2); BisCem® - Bisco (BC); SeT PP® − SDI (SeT); Relyx U100® - 3M ESPE (U100) and YCEM® SA - Yller (YCEM)]. The SARCs were evaluated for SBS to dentin (n = 10) after 24 h, 6 months, and 12 months. The dentin demineralization caused by acidic monomers was observed by SEM, and pH-neutralization of eluate was observed for 24 h. Degree of conversion (DC), rate of polymerization (Rp), flexural strength (FS), and elastic modulus (E) were evaluated. Immediate SBS of SC2, SET, U100, and YCEM were statistically higher than that of BC (p < 0.001). After 12 months, all SARCs showed reduced SBS values and U100 showed values similar to those of SET and YCEM, and higher than those of BC and SC2 (p = 0.001). Demineralization pattern of SARCs was similar. At 24h, all SARCs showed no differences in the pH-value, except BC and U100 (p < 0.001). YCEM showed the highest Rp. U100, YCEM, and SC2 showed statistically higher FS (p<0.001) and E (p < 0.001) when compared with SET and BC. U100 and YCEM showed the best long-term bonding irrespective of the storage period. A significant reduction in SBS was found for all groups after 12 months. SBS was not shown to be correlated with physical-chemical properties, and appeared to be material-dependent. The polymerization profile suggested that an increased time of light activation, longer than that recommended by manufacturers, would be necessary to optimize DC of SARCs.


Assuntos
Resinas Compostas/química , Cimentos de Resina/química , Dentina/efeitos dos fármacos , Cura Luminosa de Adesivos Dentários/métodos , Valores de Referência , Propriedades de Superfície/efeitos dos fármacos , Fatores de Tempo , Teste de Materiais , Microscopia Eletrônica de Varredura , Reprodutibilidade dos Testes , Análise de Variância , Maleabilidade , Resistência ao Cisalhamento , Dentina/química , Transição de Fase/efeitos dos fármacos , Módulo de Elasticidade , Polimerização
19.
Braz. oral res. (Online) ; 32: e17, 2018. tab, graf
Artigo em Inglês | LILACS | ID: biblio-889495

RESUMO

Abstract: Bulk-fill composites are claimed to be restorative materials used in deep preparations and effectively photoactivated in layers up to 4 mm. The aim of the present study was to evaluate the degree of conversion, post-gel volumetric shrinkage, and cytotoxicity of six bulk-fill and two conventional composites. Degree of conversion was determined by FTIR spectroscopy; post-gel volumetric shrinkage was determined using the strain gauge method; and cytotoxicity in human fibroblasts was evaluated indirectly by the MTT assay. Data were subjected to one-way ANOVA/Tukey's test (α = 0.05). All materials, including bulk-fill and conventional composites, were classified as non-toxic, with cell viability higher than 70%. Bulk-fill composites exhibited volumetric shrinkage similar to or lower (1.4 to 0.4%) than that of conventional composites (1.7-2.1%). However, only four of the bulk-fill composites were able to sustain a homogeneous conversion at the 4-mm depth. Despite their non-toxicity and shrinkage similar to that of conventional materials, not all commercial bulk-fill materials were able to maintain a conversion as high as 80% of the superficial layer, at the 4-mm depth, indicating some failure in the bulk-fill design of some commercial brands. Therefore, the use of bulk-fill materials in dental practice is advantageous, but special attention should be given to the selection and correct use of the materials.


Assuntos
Humanos , Resinas Compostas/toxicidade , Resinas Compostas/química , Polimerização , Valores de Referência , Propriedades de Superfície , Fatores de Tempo , Teste de Materiais , Sobrevivência Celular/efeitos dos fármacos , Reprodutibilidade dos Testes , Análise de Variância , Espectroscopia de Infravermelho com Transformada de Fourier , Transição de Fase , Processos Fotoquímicos , Fibroblastos/efeitos dos fármacos
20.
Braz. dent. j ; 28(5): 632-637, Sept.-Oct. 2017. tab, graf
Artigo em Inglês | LILACS | ID: biblio-888679

RESUMO

Abstract This study aimed to evaluate the effect of the composite shade and distance from the light-curing unit (LCU) tip on the irradiance reaching the bottom of composite disks and on the depth of polymerization. Composites of three shades (opaque - OXDC, bleach - BXL, and A2) were inserted into molds with 3-mm of thickness positioned over a spectrometer and photo-activated with the LCU (Bluephase) tip placed at 0 or 1 cm from the composite surface. The mean irradiance reaching the bottom of composite was recorded during the entire photo-activation (30 s). Specimens (2 x 2 x 4 mm) were polymerized and used to map the degree of conversion achieved in different depths from irradiated surface. Specimens were sectioned into slices that were positioned over the platform of the infra-red microscope connected to the spectrometer to map the conversion. The conversion was measured in eight different depths every 500-µm. Increasing the distance of LCU tip reduced the irradiance only for A2. Interposing OXDC disks resulted in lowest values of irradiance and A2 the highest one. A tendency to decrease the conversion was observed towards the bottom of specimens for all experimental conditions, and the slope was more accentuated for OXDC. Differences among shades and distances from LCU tip were evident only beyond 1.5-2.0 mm of depth. In conclusion, both composite shade and distance from LCU tip might affect the light-transmission and depth of polymerization, while the effect of last was more pronounced.


Resumo Este estudo objetivou avaliar o efeito da cor do compósito e da distância da ponta do aparelho fotopolimerizador (AFP) na irradiância alcançando a base do disco de compósito e na profundidade de polimerização. Compósitos de três cores (opaca - OXDC, clareado - BXL, e A2) foram inseridos em moldes com 3 mm de espessura posicionados sobre um espectrômetro e fotoativados com a ponta do AFP (Bluephase) colocada a 0 ou 1 cm da superfície do compósito. A irradiância média alcançando a base do compósito foi registrada durante toda a fotoativação (30 s). Amostras (2 x 2 x 4 mm) de compósito polimerizado também foram confeccionadas e usada para mapear o grau de conversão obtido em diferentes profundidades da superfície irradiada. As amostras foram seccionadas em fatias que foram posicionadas sobre a plataforma de um microscópio infra-vermelho conectado ao espectrômetro para mapear a conversão. A conversão foi mensurada em oito diferentes profundidades com 500-µm entre elas. Aumentando a distância da ponta do AFP reduziu a irradiância apenas para A2. Interpondo discos de OXDC resultou em menores valores de irradiância e A2 nos maiores. Uma tendência de redução na conversão foi observada em direção a base das amostras para todas as condições experimentais, com uma redução mais acentuada para OXDC. Diferenças entre as cores e distâncias da ponta do AFP foram evidentes apenas a partir de 1,2-2,0 mm de profundidade. Como conclusão, tanto a cor do compósito como a distância da ponta do AFP podem afetar a transmissão de luz e a profundidade de polimerização, enquanto que o efeito do último foi mais pronunciado.


Assuntos
Resinas Compostas/química , Luzes de Cura Dentária , Propriedades de Superfície , Técnicas In Vitro , Polimerização