RESUMEN
Portland cements (PCs) and cement blends are multiphase materials of different fineness, and quantitatively analysing their hydration pathways is very challenging. The dissolution (hydration) of the initial crystalline and amorphous phases must be determined, as well as the formation of labile (such as ettringite), reactive (such as portlandite) and amorphous (such as calcium silicate hydrate gel) components. The microstructural changes with hydration time must also be mapped out. To address this robustly and accurately, an innovative approach is being developed based on in situ measurements of pastes without any sample conditioning. Data are sequentially acquired by Mo Kα1 laboratory X-ray powder diffraction (LXRPD) and microtomography (µCT), where the same volume is scanned with time to reduce variability. Wide capillaries (2â mm in diameter) are key to avoid artefacts, e.g. self-desiccation, and to have excellent particle averaging. This methodology is tested in three cement paste samples: (i) a commercial PC 52.5 R, (ii) a blend of 80â wt% of this PC and 20â wt% quartz, to simulate an addition of supplementary cementitious materials, and (iii) a blend of 80â wt% PC and 20â wt% limestone, to simulate a limestone Portland cement. LXRPD data are acquired at 3â h and 1, 3, 7 and 28 days, and µCT data are collected at 12â h and 1, 3, 7 and 28 days. Later age data can also be easily acquired. In this methodology, the amounts of the crystalline phases are directly obtained from Rietveld analysis and the amorphous phase contents are obtained from mass-balance calculations. From the µCT study, and within the attained spatial resolution, three components (porosity, hydrated products and unhydrated cement particles) are determined. The analyses quantitatively demonstrate the filler effect of quartz and limestone in the hydration of alite and the calcium aluminate phases. Further hydration details are discussed.
RESUMEN
Despite a century of research, our understanding of cement dissolution and precipitation processes at early ages is very limited. This is due to the lack of methods that can image these processes with enough spatial resolution, contrast and field of view. Here, we adapt near-field ptychographic nanotomography to in situ visualise the hydration of commercial Portland cement in a record-thick capillary. At 19 h, porous C-S-H gel shell, thickness of 500 nm, covers every alite grain enclosing a water gap. The spatial dissolution rate of small alite grains in the acceleration period, â¼100 nm/h, is approximately four times faster than that of large alite grains in the deceleration stage, â¼25 nm/h. Etch-pit development has also been mapped out. This work is complemented by laboratory and synchrotron microtomographies, allowing to measure the particle size distributions with time. 4D nanoimaging will allow mechanistically study dissolution-precipitation processes including the roles of accelerators and superplasticizers.
RESUMEN
Reducing cement CO2 footprint is a societal need. This is being achieved mainly by replacing an increasing amount of Portland clinker by supplementary cementitious materials. However, this comes at a price: lower mechanical strengths at early ages due to slow pozzolanic reaction(s). This is being addressed by using accelerator admixtures. In this context, calcium silicate hydrate nucleation seeding seems to have a promising future, as it can accelerate cement and pozzolanic reactions at early ages, optimising their microstructures, without compromising late strength and durability performances. In fact, these features could even be improved. Moreover, other uses are low temperature concreting, precasting, shotconcrete, etc. Here, we focus on reviewing recent reports on calcium silicate hydrate seeding using commercially available admixtures. Current knowledge on the consequences of nucleation seeding on hydration reactions and on early and late mechanical strengths is discussed. It is noted that other features, in addition to the classic alite hydration acceleration, are covered here including the enhanced ettringite precipitation and the very efficient porosity refinement, which take place in the seeded binders. Finally, because the seeded binders seem to be denser, durability properties could also be enhanced although this remains to be properly established.
RESUMEN
The acceleration of very early age cement hydration by C-S-H seeding is getting attention from scholars and field applications because the enhanced early age features do not compromise later age performances. This acceleration could be beneficial for several low-CO2 cements as a general drawback is usually the low very early age mechanical strengths. However, the mechanistic understanding of this acceleration in commercial cements is not complete. Reported here is a contribution to this understanding from the study of the effects of C-S-H gel seeding in one Portland cement and two belite cements at two widely studied water-cement ratios, 0.50 and 0.40. Two commercially available C-S-H nano-seed-based admixtures, i.e., Master X-Seed 130 and Master X-Seed STE-53, were investigated. A multi-technique approach was adopted by employing calorimetry, thermal analysis, powder diffraction (data analysed by the Rietveld method), mercury intrusion porosimetry, and mechanical strength determination. For instance, the compressive strength at 1 day for the PC (w/c = 0.50) sample increased from 15 MPa for the unseeded mortar to 24 and 22 MPs for the mortars seeded with the XS130 and STE53, respectively. The evolution of the amorphous contents was determined by adding an internal standard before recording the powder patterns. In summary, alite and belite phase hydrations, from the crystalline phase content evolutions, are not significantly accelerated by C-S-H seedings at the studied ages of 1 and 28 d for these cements. Conversely, the hydration rates of tetracalcium alumino-ferrate and tricalcium aluminate were significantly enhanced. It is noted that the degrees of reaction of C4AF for the PC paste (w/c = 0.40) were 10, 30, and 40% at 1, 7, and 28 days. After C-S-H seeding, the values increased to 20, 45, and 60%, respectively. This resulted in larger ettringite contents at very early ages but not at 28 days. At 28 days of hydration, larger amounts of carbonate-containing AFm-type phases were determined. Finally, and importantly, the admixtures yielded larger amounts of amorphous components in the pastes at later hydration ages. This is justified, in part, by the higher content of amorphous iron siliceous hydrogarnet from the enhanced C4AF reactivity.
RESUMEN
Cement hydration is a very complex set of processes. The evolution of the crystalline phases during hydration can be accurately followed by X-ray powder diffraction data evaluated by the Rietveld method. However, accurate measurements of some microstructural features, including porosity and amorphous content developments, are more challenging. Here, we combine laboratory X-ray powder diffraction and computed microtomography (µCT) to better understand the results of the µCT analyses. Two pastes with different water-cement ratios, 0.45 and 0.65, filled within capillaries of two sizes, Ï = 0.5 and 1.0 mm, were analysed at 50 days of hydration. It was shown that within the spatial resolution of the measured µCTs, ~2 µm, the water capillary porosity was segmented within the hydrated component fraction. The unhydrated part could be accurately quantified within 2 vol% error. This work is a first step to accurately determining selected hydration features like the hydration degree of amorphous phases of supplementary cementitious materials within cement blends.
RESUMEN
The effect of superplasticiser, borax and the water-to-cement ratio on BYF hydration and mechanical strengths has been studied. Two laboratory-scale BYF cements-st-BYF (with ß-C2S and orthorhombic C4A3S¯) and borax-activated B-BYF (with α'H-C2S and pseudo-cubic C4A3S¯)-have been used, and both show similar particle size distribution. The addition of superplasticiser and externally added borax to BYF pastes has been optimised through rheological measurements. Optimised superplasticiser contents (0.3, 0.4 and 0.1 wt % for st-BYF, B-BYF and st-BYF with externally added 0.25 wt % B2O3, respectively) result in low viscosities yielding homogeneous mortars. The calorimetric study revealed that st-BYF is more reactive than B-BYF, as the values of heat released are 300-370 J/g and 190-210 J/g, respectively, after 7 days of hydration; this fact is independent of the water-to-cement ratio. These findings agree with the higher degree of hydration at 28 days of ß-C2S in st-BYF (from 45 to 60%) than α'H-C2S in B-BYF (~20 to 30%). The phase assemblage evolution has been determined by LXRPD coupled with the Rietveld method and MAS-NMR. The formation of stratlingite is favoured by increasing the w/c ratio in both systems. Finally, the optimisation of fresh BYF pastes jointly with the reduction of water-to-cement ratio to 0.40 have allowed the achieving of mortars with compressive strengths over 40 MPa at 7 days in all systems. Moreover, the st-BYF mortar, where borax was externally added, achieved more than 70 MPa after 28 days. The main conclusion of this work does not support Lafarge's approach of adding boron/borax to the raw meal of BYF cements. This procedure stabilises the alpha belite polymorph, but its reactivity, in these systems, is lower and the associated mechanical strengths poorer.
RESUMEN
In situ research of materials under moderate pressures (hundreds of bar) is essential in many scientific fields. These range from gas sorption to chemical and biological processes. One industrially important discipline is the hydration of oil well cements. Existing capillary cells in this pressure range are static as they are easy to design and operate. This is convenient for the study of single-phase materials; however, powder diffraction quantitative analyses for multiphase systems cannot be performed accurately as a good powder average cannot be attained. Here, the design, construction and commissioning of a cost-effective spinning capillary cell for in situ powder X-ray diffraction is reported, for pressures currently up to 200â bar. The design addresses the importance of reducing the stress on the capillary by mechanically synchronizing the applied rotation power and alignment on both sides of the capillary while allowing the displacement of the supports needed to accommodate different capillaries sizes and to insert the sample within the tube. This cell can be utilized for multiple purposes allowing the introduction of gas or liquid from both ends of the capillary. The commissioning is reported for the hydration of a commercial oil well cement at 150â bar and 150°C. The quality of the resulting powder diffraction data has allowed in situ Rietveld quantitative phase analyses for a hydrating cement containing seven crystalline phases.
Asunto(s)
Difracción de Polvo/métodos , Presión , Sincrotrones , Temperatura , Diseño de EquipoRESUMEN
Oil and gas well cements are multimineral materials that hydrate under high pressure and temperature. Their overall reactivity at early ages is studied by a number of techniques including through the use of the consistometer. However, for a proper understanding of the performance of these cements in the field, the reactivity of every component, in real-world conditions, must be analysed. To date, in situ high energy synchrotron powder diffraction studies of hydrating oil well cement pastes have been carried out, but the quality of the data was not appropriated for Rietveld quantitative phase analyses. Therefore, the phase reactivities were followed by the inspection of the evolution of non-overlapped diffraction peaks. Very recently, we have developed a new cell specially designed to rotate under high pressure and temperature. Here, this spinning capillary cell is used for in situ studies of the hydration of a commercial oil well cement paste at 150 bars and 150 °C. The powder diffraction data were analysed by the Rietveld method to quantitatively determine the reactivities of each component phase. The reaction degree of alite was 90% after 7 h, and that of belite was 42% at 14 h. These analyses are accurate, as the in situ measured crystalline portlandite content at the end of the experiment, 12.9 wt%, compares relatively well with the value determined ex situ by thermal analysis, i.e., 14.0 wt%. The crystalline calcium silicates forming at 150 bars and 150 °C are also discussed.
RESUMEN
Mortars and concretes are ubiquitous materials with very complex hierarchical microstructures. To fully understand their main properties and to decrease their CO2 footprint, a sound description of their spatially resolved mineralogy is necessary. Developing this knowledge is very challenging as about half of the volume of hydrated cement is a nanocrystalline component, calcium silicate hydrate (C-S-H) gel. Furthermore, other poorly crystalline phases (e.g. iron siliceous hydrogarnet or silica oxide) may coexist, which are even more difficult to characterize. Traditional spatially resolved techniques such as electron microscopy involve complex sample preparation steps that often lead to artefacts (e.g. dehydration and microstructural changes). Here, synchrotron ptychographic tomography has been used to obtain spatially resolved information on three unaltered representative samples: neat Portland paste, Portland-calcite and Portland-fly-ash blend pastes with a spatial resolution below 100â nm in samples with a volume of up to 5 × 104â µm3. For the neat Portland paste, the ptychotomographic study gave densities of 2.11 and 2.52â gâ cm-3 and a content of 41.1 and 6.4â vol% for nanocrystalline C-S-H gel and poorly crystalline iron siliceous hydrogarnet, respectively. Furthermore, the spatially resolved volumetric mass-density information has allowed characterization of inner-product and outer-product C-S-H gels. The average density of the inner-product C-S-H is smaller than that of the outer product and its variability is larger. Full characterization of the pastes, including segmentation of the different components, is reported and the contents are compared with the results obtained by thermodynamic modelling.
RESUMEN
The identification and quantification of amorphous components and nanocrystalline phases with very small crystal sizes, smaller than ~3 nm, within samples containing crystalline phases is very challenging. However, this is important as there are several types of systems that contain these matrices: building materials, glass-ceramics, some alloys, etc. The total scattering synchrotron pair distribution function (PDF) can be used to characterize the local atomic order of the nanocrystalline components and to carry out quantitative analyses in complex mixtures. Although the resolution in momentum transfer space has been widely discussed, the resolution in the interatomic distance space has not been discussed to the best of our knowledge. Here, we report synchrotron PDF data collected at three beamlines in different experimental configurations and X-ray detectors. We not only discuss the effect of the resolution in Q-space, Qmax ins of the recorded data and Qmax of the processed data, but we also discuss the resolution in the interatomic distance (real) space. A thorough study of single-phase crystalline nickel used as standard was carried out. Then, selected cement-related samples including anhydrous tricalcium and dicalcium silicates, and pastes derived from the hydration of tricalcium silicate and ye'elimite with bassanite were analyzed.
RESUMEN
Human aldose reductase (hAR, AKR1B1) has been explored as drug target since the 1980s for its implication in diabetic complications. An activated form of hAR was found in cells from diabetic patients, showing a reduced sensitivity to inhibitors in clinical trials, which may prevent its pharmacological use. Here we report the conversion of native hAR to its activated form by X-ray irradiation simulating oxidative stress conditions. Upon irradiation, the enzyme activity increases moderately and the potency of several hAR inhibitors decay before global protein radiation damage appears. The catalytic behavior of activated hAR is also reproduced as the KM increases dramatically while the kcat is not much affected. Consistently, the catalytic tetrad is not showing any modification. The only catalytically-relevant structural difference observed is the conversion of residue Cys298 to serine and alanine. A mechanism involving electron capture is suggested for the hAR activation. We propose that hAR inhibitors should not be designed against the native protein but against the activated form as obtained from X-ray irradiation. Furthermore, since the reactive species produced under irradiation conditions are the same as those produced under oxidative stress, the described irradiation method can be applied to other relevant proteins under oxidative stress environments.
Asunto(s)
Aldehído Reductasa/genética , Inhibidores Enzimáticos/farmacología , Estrés Oxidativo/efectos de la radiación , Alanina/genética , Aldehído Reductasa/antagonistas & inhibidores , Aldehído Reductasa/efectos de la radiación , Catálisis/efectos de los fármacos , Catálisis/efectos de la radiación , Microambiente Celular/efectos de la radiación , Activación Enzimática/efectos de la radiación , Inhibidores Enzimáticos/efectos de la radiación , Humanos , Oxidación-Reducción , Estrés Oxidativo/genética , Serina/genética , Rayos XRESUMEN
Tricalcium silicate, the main constituent of Portland cement, hydrates to produce crystalline calcium hydroxide and calcium-silicate-hydrates (C-S-H) nanocrystalline gel. This hydration reaction is poorly understood at the nanoscale. The understanding of atomic arrangement in nanocrystalline phases is intrinsically complicated and this challenge is exacerbated by the presence of additional crystalline phase(s). Here, we use calorimetry and synchrotron X-ray powder diffraction to quantitatively follow tricalcium silicate hydration process: i) its dissolution, ii) portlandite crystallization and iii) C-S-H gel precipitation. Chiefly, synchrotron pair distribution function (PDF) allows to identify a defective clinotobermorite, Ca11Si9O28(OH)2.8.5H2O, as the nanocrystalline component of C-S-H. Furthermore, PDF analysis also indicates that C-S-H gel contains monolayer calcium hydroxide which is stretched as recently predicted by first principles calculations. These outcomes, plus additional laboratory characterization, yielded a multiscale picture for C-S-H nanocomposite gel which explains the observed densities and Ca/Si atomic ratios at the nano- and meso- scales.
RESUMEN
Macromolecular crystallography (MX) and small-angle X-ray scattering (SAXS) studies on proteins at synchrotron light sources are commonly limited by the structural damage produced by the intense X-ray beam. Several effects, such as aggregation in protein solutions and global and site-specific damage in crystals, reduce the data quality or even introduce artefacts that can result in a biologically misguiding structure. One strategy to reduce these negative effects is the inclusion of an additive in the buffer solution to act as a free radical scavenger. Here the properties of uridine as a scavenger for both SAXS and MX experiments on lysozyme at room temperature are examined. In MX experiments, upon addition of uridine at 1â M, the critical dose D1/2 is increased by a factor of â¼1.7, a value similar to that obtained in the presence of the most commonly used scavengers such as ascorbate and sodium nitrate. Other figures of merit to assess radiation damage show a similar trend. In SAXS experiments, the scavenging effect of 40â mM uridine is similar to that of 5% v/v glycerol, and greater than 2â mM DTT and 1â mM ascorbic acid. In all cases, the protective effect of uridine is proportional to its concentration.
Asunto(s)
Dispersión del Ángulo Pequeño , Sincrotrones , Uridina/química , Proteínas/química , Difracción de Rayos XRESUMEN
We report the synthesis, structural characterization, and functionality (framework interconversions together with proton conductivity) of an open-framework hybrid that combines Ca(2+) ions and the rigid polyfunctional ligand 5-(dihydroxyphosphoryl)isophthalic acid (PiPhtA). Ca2[(HO3PC6H3COOH)2]2[(HO3PC6H3(COO)2H)(H2O)2]·5H2O (Ca-PiPhtA-I) is obtained by slow crystallization at ambient conditions from acidic (pH ≈ 3) aqueous solutions. It possesses a high water content (both Ca coordinated and in the lattice), and importantly, it exhibits water-filled 1D channels. At 75 °C, Ca-PiPhtA-I is partially dehydrated and exhibits a crystalline diffraction pattern that can be indexed in a monoclinic cell with parameters close to the pristine phase. Rietveld refinement was carried out for the sample heated at 75 °C, Ca-PiPhtA-II, using synchrotron powder X-ray diffraction data, which revealed the molecular formula Ca2[(HO3PC6H3COOH)2]2[(HO3PC6H3(COO)2H)(H2O)2]. All connectivity modes of the "parent" Ca-PiPhtA-I framework are retained in Ca-PiPhtA-II. Upon Ca-PiPhtA-I exposure to ammonia vapors (28% aqueous NH3) a new derivative is obtained (Ca-PiPhtA-NH3) containing 7 NH3 and 16 H2O molecules according to elemental and thermal analyses. Ca-PiPhtA-NH3 exhibits a complex X-ray diffraction pattern with peaks at 15.3 and 13.0 Å that suggest partial breaking and transformation of the parent pillared structure. Although detailed structural identification of Ca-PiPhtA-NH3 was not possible, due in part to nonequilibrium adsorption conditions and the lack of crystallinity, FT-IR spectra and DTA-TG analysis indicate profound structural changes compared to the pristine Ca-PiPhtA-I. At 98% RH and T = 24 °C, proton conductivity, σ, for Ca-PiPhtA-I is 5.7 × 10(-4) S·cm(-1). It increases to 1.3 × 10(-3) S·cm(-1) upon activation by preheating the sample at 40 °C for 2 h followed by water equilibration at room temperature under controlled conditions. Ca-PiPhtA-NH3 exhibits the highest proton conductivity, 6.6 × 10(-3) S·cm(-1), measured at 98% RH and T = 24 °C. Activation energies (Ea) for proton transfer in the above-mentioned frameworks range between 0.23 and 0.4 eV, typical of a Grothuss mechanism of proton conduction. These results underline the importance of internal H-bonding networks that, in turn, determine conductivity properties of hybrid materials. It is highlighted that new proton transfer pathways may be created by means of cavity "derivatization" with selected guest molecules resulting in improved proton conductivity.
Asunto(s)
Fosfatos de Calcio/química , Cristalización , Cristalografía por Rayos X , Protones , Soluciones , Espectroscopía Infrarroja por Transformada de FourierRESUMEN
Stoichiometric dicalcium silicate, Ca2SiO4, displays a well-known polymorphism with temperature. When this phase is doped by a range of elements, belite, one of the main phases of cements, is generated. Here, we thoroughly study the aluminum doping of dicalcium silicate. This type of study is important for cement characterization and also from a basic point of view. Ca2Si(1-2x)Al(2x)O(4-x)â¡(x) (x = 0, 0.010, 0.014, 0.03) has been prepared and studied by X-ray powder diffraction and the Rietveld method. The limiting composition has been established as Ca2Si0.972Al0.028O3.986â¡0.014. The (27)Al MAS NMR band located close to ~-70 ppm is ascribed to tetrahedral environments, in agreement with the proposed aliovalent Si/Al atomic substitution mechanism. Thermal analysis measurements under a wet atmosphere indirectly confirm the increase of oxygen vacancies as the amount of incorporated protons increases with the aluminium content. A thorough electrical characterization has been carried out including overall conductivity measurements under wet and dry atmospheres and conductivity as a function of the oxygen partial pressure. The samples show oxide anion conductivity with a small p-type electronic contribution under oxidizing conditions. These compounds display a very important proton contribution to the overall conductivities under humidified atmospheres.
RESUMEN
Two new families of divalent metal hybrid derivatives from the aromatic tetraphosphonic acids 1,4- and 1,3-bis(aminomethyl)benzene-N,N'-bis(methylenephosphonic acid), (H2O3PCH2)2-N-CH2C6H4CH2-N(CH2PO3H2)2 (designated herein as p-H8L and m-H8L) have been synthesized by crystallization at room temperature and hydrothermal conditions. The crystal structures of M[(HO3PCH2)2N(H)CH2C6H4CH2N(H)(CH2PO3H)2(H2O)2]·2H2O (M = Mg, Co, and Zn), M-(p-H6L), and M[(HO3PCH2)2N(H)CH2C6H4CH2N(H)(CH2PO3H)2]·nH2O (M = Ca, Mg, Co, and Zn and n = 1-1.5), M-(m-H6L), were solved ab initio by synchrotron powder diffraction data using the direct methods and subsequently refined using the Rietveld method. The crystal structure of the isostructural M-(p-H6L) is constituted by organic-inorganic monodimensional chains where the phosphonate moiety acts as a bidentate chelating ligand bridging two metal octahedra. M-(m-H6L) compounds exhibit a 3D pillared open-framework with small 1D channels filled with water molecules. These channels are formed by the pillaring action of the organic ligand connecting adjacent layers through the phosphonate oxygens. Thermogravimetric and X-ray thermodiffraction analyses of M-(p-H6L) showed that the integrity of their crystalline structures is maintained up to 470 K, without significant reduction of water content, while thermal decomposition takes place above 580 K. The utility of M-(p-H6L) (M = Mg and Zn) hybrid materials in corrosion protection was investigated in acidic aqueous solutions. In addition, the impedance data indicate both families of compounds display similar proton conductivities (σ â¼ 9.4 × 10(-5) S·cm(-1), at 98% RH and 297 K), although different proton transfer mechanisms are involved.
RESUMEN
Multifunctional materials, especially those combining two or more properties of interest, are attracting immense attention due to their potential applications. MOFs, metal organic frameworks, can be regarded as multifunctional materials if they show another useful property in addition to the adsorption behavior. Here, we report a new multifunctional light hybrid, MgH(6)ODTMP·2H(2)O(DMF)(0.5) (1), which has been synthesized using the tetraphosphonic acid H(8)ODTMP, octamethylenediamine-N,N,N',N'-tetrakis(methylenephosphonic acid), by high-throughput methodology. Its crystal structure, solved by Patterson-function direct methods from synchrotron powder X-ray diffraction, was characterized by a 3D pillared open framework containing cross-linked 1D channels filled with water and DMF. Upon H(2)O and DMF removal and subsequent rehydration, MgH(6)ODTMP·2H(2)O (2) and MgH(6)ODTMP·6H(2)O (3) can be formed. These processes take place through crystalline-quasi-amorphous-crystalline transformations, during which the integrity of the framework is maintained. A water adsorption study, at constant temperature, showed that this magnesium tetraphosphonate hybrid reversibly equilibrates its lattice water content as a function of the water partial pressure. Combination of the structural study and gas adsorption characterization (N(2), CO(2), and CH(4)) indicates an ultramicroporous framework. High-pressure CO(2) adsorption data are also reported. Finally, impedance data indicates that 3 has high proton conductivity σ = 1.6 × 10(-3) S cm(-1) at T = 292 K at ~100% relative humidity with an activation energy of 0.31 eV.
Asunto(s)
Reactivos de Enlaces Cruzados/química , Magnesio/química , Compuestos Organometálicos/química , Ácidos Fosforosos/química , Protones , Conductividad Eléctrica , Modelos Moleculares , Compuestos Organometálicos/síntesis química , Porosidad , Difracción de Polvo , Propiedades de Superficie , TemperaturaRESUMEN
In this paper we report the synthesis and structural characterization of the 2D layered coordination polymer Mg(BPMGLY)(H(2)O)(2) (BPMGLY = bis-phosphonomethylglycine, (HO(3)PCH(2))(2)N(H)COO(2-)). The Mg ion is found in a slightly distorted octahedral environment formed by four phosphonate oxygens and two water molecules. The carboxylate group is deprotonated but noncoordinated. This compound is a useful starting material for a number of topotactic transformations. Upon heating at 140 °C one (of the two) Mg-coordinated water molecule is lost, with the archetype 2D structure maintaining itself. However, the octahedral Mg in Mg(BPMGLY)(H(2)O)(2) is now converted to trigonal bipyramidal in Mg(BPMGLY)(H(2)O). Upon exposure of the monohydrate Mg(BPMGLY)(H(2)O) compound to ammonia, one molecule of ammonia is inserted into the interlayer space and stabilized by hydrogen bonding. The 2D layered structure of the product Mg(BPMGLY)(H(2)O)(NH(3)) is still maintained, with Mg now acquiring a pseudo-octahedral environment. All of these topotactic transformations are also accompanied by changes in hydrogen bonding between the layers.
Asunto(s)
Amoníaco/química , Glicina/química , Magnesio/química , Compuestos Organometálicos/química , Cristalografía por Rayos X , Glicina/análogos & derivados , Modelos Moleculares , Estructura Molecular , Compuestos Organometálicos/síntesis química , Espectroscopía Infrarroja por Transformada de Fourier , Temperatura , Agua/químicaRESUMEN
A new flexible ultramicroporous solid, La(H(5)DTMP)·7H(2)O (1), has been crystallized at room temperature using the tetraphosphonic acid H(8)DTMP, hexamethylenediamine-N,N,N',N'-tetrakis(methylenephosphonic acid). Its crystal structure, solved by synchrotron powder X-ray diffraction, is characterised by a 3D pillared open-framework containing 1D channels filled with water. Upon dehydration, a new related crystalline phase, La(H(5)DTMP) (2) is formed. Partial rehydration of 2 led to La(H(5)DTMP)·2H(2)O (3). These new phases contain highly corrugated layers showing different degrees of conformational flexibility of the long organic chain. The combination of the structural study and the gas adsorption characterization (N(2) and CO(2)) suggests an ultramicroporous flexible framework. NO isotherms are indicative of a strong irreversible adsorption of NO within the pores. Impedance data indicates that 1 is a proton-conductor with a conductivity of 8 × 10(-3) S cm(-1) at 297 K and 98% of relative humidity, and an activation energy of 0.25 eV.
RESUMEN
A family of M-VP (M = Ni, Co, Cd, Mn, Zn, Fe, Cu, Pb; VP = vinylphosphonate) and M-PVP (M = Co, Cd; PVP = phenylvinylphosphonate) materials have been synthesized by hydrothermal methods and characterized by FT-IR, elemental analysis, and thermogravimetric analysis (TGA). Their structures were determined either by single crystal X-ray crystallography or from laboratory X-ray powder diffraction data. The crystal structure of some M-VP and M-PVP materials is two-dimensional (2D) layered, with the organic groups (vinyl or phenylvinyl) protruding into the interlamellar space. However, the Pb-VP and Cu-VP materials show dramatically different structural features. The porous, three-dimensional (3D) structure of Pb-VP contains the Pb center in a pentagonal pyramid. A Cu-VP variant of the common 2D layered structure shows a very peculiar structure. The structure of the material is 2D with the layers based upon three crystallographically distinct Cu atoms; an octahedrally coordinated Cu(2+) atom, a square planar Cu(2+) atom and a Cu(+) atom. The latter has an unusual co-ordination environment as it is 3-coordinated to two oxygen atoms with the third bond across the double bond of the vinyl group. Metal-coordinated water loss was studied by TGA and thermodiffractometry. The rehydration of the anhydrous phases to give the initial phase takes place rapidly for Cd-PVP but it takes several days for Co-PVP. The M-VP materials exhibit variable dehydration-rehydration behavior, with most of them losing crystallinity during the process.