RESUMEN
This article shows the results of experiments to grow Nitrogen incorporated ultrananocrystalline diamond (N-UNCD) films on commercial natural graphite (NG)/Cu anodes by hot chemical vapor deposition (HFCVD) using a gas mixture of Ar/CH4/N2/H2. The experiments focused on studying the effect of the pressure in the HFCVD chamber, filament-substrate distance, and temperature of the substrate. It was found that a substrate distance of 3.0 cm and a substrate temperature of 575 C were optimal to grow N-UNCD film on the graphite surface as determined by Raman spectroscopy, SEM, and TEM imaging. XPS analysis shows N incorporation through the film. Subsequently, the substrate surface temperature was increased using a heater, while keeping the substrate-filament distance constant at 3.0 cm. In this case, Raman spectra and SEM images of the substrate surface showed a major composition of graphite in the film as the substrate-surface temperature increased. Finally, the process pressure was increased to 10 Torr where it was seen that the growth of N-UNCD film occurred at 2.0 cm at a substrate temperature of 675 C. These results suggest that as the process pressure increases a smaller substrate-filament distance and consequently a higher substrate surface temperature can still enable the N-UNCD film growth by HFCVD. This effect is explained by a mean free path analysis of the main precursors H2 and CH3 molecules traveling from the filament to the surface of the substrate The potential impact of the process developed to grow electrically conductive N-UNCD films using the relatively low-cost HFCVD process is that this process can be used to grow N-UNCD films on commercial NG/Cu anodes for Li-ion batteries (LIBs), to enable longer stable capacity energy vs. charge/discharge cycles.
RESUMEN
Implant therapy using osseointegratable titanium (Ti) dental implants has revolutionized clinical dental practice and has shown a high rate of success. However, because a metallic implant is in contact with body tissues and fluids in vivo, ions/particles can be released into the biological milieu as a result of corrosion or biotribocorrosion. Ultrananocrystalline diamond (UNCD) coatings possess a synergistic combination of mechanical, tribological, and chemical properties, which makes UNCD highly biocompatible. In addition, because the UNCD coating is made of carbon (C), a component of human DNA, cells, and molecules, it is potentially a highly biocompatible coating for medical implant devices. The aim of the present research was to evaluate tissue response to UNCD-coated titanium micro-implants using a murine model designed to evaluate biocompatibility. Non-coated (n = 10) and UNCD-coated (n = 10) orthodontic Ti micro-implants were placed in the hematopoietic bone marrow of the tibia of male Wistar rats. The animals were euthanized 30 days post implantation. The tibiae were resected, and ground histologic sections were obtained and stained with toluidine blue. Histologically, both groups showed lamellar bone tissue in contact with the implants (osseointegration). No inflammatory or multinucleated giant cells were observed. Histomorphometric evaluation showed no statistically significant differences in the percentage of BIC between groups (C: 53.40 ± 13% vs. UNCD: 58.82 ± 9%, p > 0.05). UNCD showed good biocompatibility properties. Although the percentage of BIC (osseointegration) was similar in UNCD-coated and control Ti micro-implants, the documented tribological properties of UNCD make it a superior implant coating material. Given the current surge in the use of nano-coatings, nanofilms, and nanostructured surfaces to enhance the biocompatibility of biomedical implants, the results of the present study contribute valuable data for the manufacture of UNCD coatings as a new generation of superior dental implants.
RESUMEN
Although Ultrananocrystalline diamond (UNCD) has been proposed as a coating material for titanium biomedical implants, the biological effects and toxicity of UNCD particles that could eventually detach have not been studied to date. The biokinetics and biological effects of UNCD compared to titanium dioxide (TiO2 ) nanoparticles was evaluated in vivo using Wistar rats (n = 30) i.p. injected with TiO2 , UNCD or saline solution. After 6 months, blood, lung, liver, and kidney samples were histologically analyzed. Oxidative damage by membrane lipidperoxidation (thiobarbituric acid reactive substances-TBARS), generation of reactive oxygen species (superoxide anion- O2-), and antioxidant enzymes (superoxide dismutase-SOD, catalase-CAT) was evaluated in lung and liver. Histologic observation showed agglomerates of TiO2 or UNCD in the parenchyma of the studied organs, though there were fewer UNCD than TiO2 deposits. In addition, TiO2 caused areas compatibles with foci of necrosis in the liver and renal hyaline cylinders. Regarding UNCD, no membrane damage (TBARS) or mobilization of enzymatic antioxidants was observed either in lung or liver samples. No variations in O2- generation were observed in lung (Co: 35.1 ± 4.02 vs. UNCD: 48 ± 9.1, p > 0.05). Conversely, TiO2 exposure caused production of O2- in alveolar macrophages and consumption of catalase (p < 0.05). The studied parameters suggest that UNCD caused neither biochemical nor histological alterations, and therefore may prove useful as a surface coating for biomedical implants. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 2408-2415, 2017.
Asunto(s)
Materiales Biocompatibles Revestidos , Ensayo de Materiales , Nanodiamantes , Titanio , Animales , Materiales Biocompatibles Revestidos/química , Materiales Biocompatibles Revestidos/farmacocinética , Materiales Biocompatibles Revestidos/farmacología , Masculino , Nanodiamantes/química , Nanodiamantes/uso terapéutico , Especificidad de Órganos/efectos de los fármacos , Ratas , Ratas Wistar , Titanio/química , Titanio/farmacocinética , Titanio/farmacologíaRESUMEN
Unique functional materials provide a platform as scaffolds for cell/tissue regeneration. Investigation of cell-materials' chemical and biological interactions will enable the application of more functional materials in the area of bioengineering, which provides a pathway to the novel treatment for patients who suffer from tissue/organ damage and face the limitation of donation sources. Many studies have been made into tissue/organ regeneration. Development of new substrate materials as platforms for cell/tissue regeneration is a key research area. Studies discussed in this paper focus on the investigation of novel ultrananocrystalline diamond (UNCD) films as substrate/scaffold materials for developmental biology. Specially designed quartz dishes have been coated with different types of UNCD films and cells were subsequently seeded on those films. Results showed the cells' growth on UNCD-coated culture dishes are similar to cell culture dishes with little retardation, indicating that UNCD films have no or little inhibition on cell proliferation and are potentially appealing as substrate/scaffold materials. The mechanisms of cell adhesion on UNCD surfaces are proposed based on the experimental results. The comparisons of cell cultures on diamond-powder-seeded culture dishes and on UNCD-coated dishes with matrix-assisted laser desorption/ionization-time-of-flight mass spectroscopy (MALDI-TOF MS) and X-ray photoelectron spectroscopy (XPS) analyses provided valuable data to support the mechanisms proposed to explain the adhesion and proliferation of cells on the surface of the UNCD platform.
RESUMEN
A fast, simple, scalable technique is described for the controlled, solution-based, electrochemical synthesis of patterned metallic and semiconducting nanowires from reusable, nonsacrificial, ultrananocrystalline diamond (UNCD) templates. This enables the repeated fabrication of arrays of complex patterns of nanowires, potentially made of any electrochemically depositable material. Unlike all other methods of patterning nanowires, this benchtop technique quickly mass-produces patterned nanowires whose diameters are not predefined by the template, without requiring intervening vacuum or clean room processing. This technique opens a pathway for studying nanoscale phenomena with minimal equipment, allowing the process-scale development of a new generation of nanowire-based devices.
RESUMEN
This presentation focuses on reviewing research to develop two critical biocompatible film technologies to enable implantable biomedical devices, namely: 1) development of bioinert/biocompatible coatings for encapsulation of Si chips implantable in the human body (e.g., retinal prosthesis implantable in the human eye)-the coating involves a novel ultrananocrystalline diamond (UNCD) film or hybrid biocompatible oxide/UNCD layered films; and 2) development of biocompatible films with high-dielectric constant and microfabrication process to produce energy storage super-capacitors embedded in the microchip to achieve full miniaturization for implantation into the human bodynovel Al2O3/TiO2 nanolaminates exhibit abnormally high dielectric constant to enable super-capacitors with very high-capacitance.
Asunto(s)
Materiales Biocompatibles/química , Tecnología Biomédica , Equipos y Suministros , Prótesis e Implantes , Animales , Materiales Biocompatibles Revestidos/química , Electricidad , HumanosRESUMEN
Surfaces of materials that promote cell adhesion, proliferation, and growth are critical for new generation of implantable biomedical devices. These films should be able to coat complex geometrical shapes very conformally, with smooth surfaces to produce hermetic bioinert protective coatings, or to provide surfaces for cell grafting through appropriate functionalization. Upon performing a survey of desirable properties such as chemical inertness, low friction coefficient, high wear resistance, and a high Young's modulus, diamond films emerge as very attractive candidates for coatings for biomedical devices. A promising novel material is ultrananocrystalline diamond (UNCD) in thin film form, since UNCD possesses the desirable properties of diamond and can be deposited as a very smooth, conformal coating using chemical vapor deposition. In this paper, we compared cell adhesion, proliferation, and growth on UNCD films, silicon, and platinum films substrates using different cell lines. Our results showed that UNCD films exhibited superior characteristics including cell number, total cell area, and cell spreading. The results could be attributed to the nanostructured nature or a combination of nanostructure/surface chemistry of UNCD, which provides a high surface energy, hence promoting adhesion between the receptors on the cell surface and the UNCD films.
Asunto(s)
Técnicas de Cultivo de Célula/instrumentación , Diamante/química , Membranas Artificiales , Nanoestructuras/química , Nanoestructuras/ultraestructura , Ingeniería de Tejidos/instrumentación , Ingeniería Biomédica/instrumentación , Ingeniería Biomédica/métodos , Adhesión Celular , Técnicas de Cultivo de Célula/métodos , Proliferación Celular , Diseño de Equipo , Análisis de Falla de Equipo , Ensayo de Materiales , Propiedades de Superficie , Ingeniería de Tejidos/métodosRESUMEN
In this work, ultrananocrystalline diamond (UNCD) thin films were evaluated for use as hermetic and bioinert coatings for a retinal microchip. These films were deposited on highly conductive Si substrates at different temperatures (from 400 to 800 degrees C), using microwave plasma enhanced chemical vapor deposition with argon-rich Ar/CH4 gas mixtures and different relative amounts of hydrogen (0-20%). Scanning electron microscopy studies showed that all the films are dense and continuous. Results of cyclic voltammetry test revealed that when there was <2% of hydrogen in the plasma, the film obtained renders the surface electrochemically inactive, with very low leakage currents ( approximately 4 x 10(-7) A/cm2 at +/-5 V). In addition, in vivo tests of the UNCD-coated Si samples were performed by implanting them in the eyes of rabbits for 4-6 months within the eye physiological environment. According to all these results, it was concluded that UNCD is a promising candidate for use as the encapsulating coatings for implantable retinal microelectronic devices.
Asunto(s)
Materiales Biocompatibles Revestidos/química , Diamante , Electrónica Médica , Prótesis e Implantes , Retina , Animales , Implantes Experimentales , Microscopía Electrónica de Rastreo , Nanoestructuras , Conejos , Silicio , Propiedades de SuperficieRESUMEN
A hard, low-wear probe for contact-mode writing techniques, such as dip-pen nanolithography (DPN), was fabricated using ultrananocrystalline diamond (UNCD). Molding within anisotropically etched and oxidized pyramidal pits in silicon was used to obtain diamond tips with radii down to 30 nm through growth of UNCD films followed by selective etching of the silicon template substrate. The probes were monolithically integrated with diamond cantilevers and subsequently integrated into a chip body obtained by metal electroforming. The probes were characterized in terms of their mechanical properties, wear, and atomic force microscopy imaging capabilities. The developed probes performed exceptionally well in DPN molecular writing/imaging mode. Furthermore, the integration of UNCD films with appropriate substrates and the use of directed microfabrication techniques are particularly suitable for fabrication of one- and two-dimensional arrays of probes that can be used for massive parallel fabrication of nanostructures by the DPN method.
Asunto(s)
Materiales Biocompatibles Revestidos , Diamante , Oro/química , Microscopía de Fuerza Atómica/métodos , Nanoestructuras , Nanotecnología/métodos , Cristalización , Electroquímica/métodos , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Semiconductores , Silicio , Electricidad Estática , Propiedades de SuperficieRESUMEN
The surface functionalization of ultrananocrystalline diamond (UNCD) thin films via the electrochemical reduction of aryl diazonium cations is described. The one-electron-transfer reaction leads to the formation of solution-based aryl radicals, which in turn react with the UNCD surface forming stable covalent C-C bonds. Cyclic voltammetry (CV), X-ray photoelectron spectroscopy (XPS), ac impedance spectroscopy, and contact angle measurements have been employed to characterize the organic overlayer and estimate the surface coverage. The grafting of 3,5-dichlorophenyl groups renders the UNCD surface hydrophobic, whereas the attachment of 4-aminophenyl groups makes the surface relatively hydrophilic. The surface coverage, estimated from the electrochemical and XPS measurements, is as high as 70% of a compact monolayer. The aminophenyl terminated surface was obtained by electrochemical reduction of the tethered nitrophenyl groups. This two-step approach yields a UNCD surface with functional moieties available for the potential covalent coupling of a wide variety of biomolecules (e.g., DNA and proteins).
RESUMEN
Understanding the suppression of ferroelectricity in perovskite thin films is a fundamental issue that has remained unresolved for decades. We report a synchrotron x-ray study of lead titanate as a function of temperature and film thickness for films as thin as a single unit cell. At room temperature, the ferroelectric phase is stable for thicknesses down to 3 unit cells (1.2 nanometers). Our results imply that no thickness limit is imposed on practical devices by an intrinsic ferroelectric size effect.
RESUMEN
Diamond, because of its electrical and chemical properties, may be a suitable material for integrated sensing and signal processing. But methods to control chemical or biological modifications on diamond surfaces have not been established. Here, we show that nanocrystalline diamond thin-films covalently modified with DNA oligonucleotides provide an extremely stable, highly selective platform in subsequent surface hybridization processes. We used a photochemical modification scheme to chemically modify clean, H-terminated nanocrystalline diamond surfaces grown on silicon substrates, producing a homogeneous layer of amine groups that serve as sites for DNA attachment. After linking DNA to the amine groups, hybridization reactions with fluorescently tagged complementary and non-complementary oligonucleotides showed no detectable non-specific adsorption, with extremely good selectivity between matched and mismatched sequences. Comparison of DNA-modified ultra-nanocrystalline diamond films with other commonly used surfaces for biological modification, such as gold, silicon, glass and glassy carbon, showed that diamond is unique in its ability to achieve very high stability and sensitivity while also being compatible with microelectronics processing technologies. These results suggest that diamond thin-films may be a nearly ideal substrate for integration of microelectronics with biological modification and sensing.