Synergic Effect of Isolated Ce3+ and Ptδ+ Species in UiO-66(Ce) for Heterogeneous Catalysis.

In this work, we have synthesized through an efficient electrostatic deposition a Pt single-atom catalyst (SAC) supported on a Ce-MOF. The basic solution employed in the impregnation process favors the deprotonation of the hydroxyl groups allocated on the clusters that can easily interact with the cationic Pt species. The resulting material, denoted as Pt/UiO-66(Ce), shows an increment of Ce3+ content, as demonstrated by UV-vis and Ce L3-edge XANES spectroscopy. These Ce3+ species and their corresponding oxygen vacancies are able to accommodate very disperse Pt single sites. Moreover, Pt L3-edge XANES and CO-FTIR spectroscopy confirm the cationic nature of the supported Ptδ+ (2+ < δ < 4+). For comparison purpose, we have synthesized and characterized a well-known Pt single-site catalyst supported on nanocrystalline ceria, denoted as Pt/nCeO2. Since the simultaneous presence of Ce3+ and Ptδ+ on the MOF clusters were able to activate the oxygen molecules and the CO molecule, respectively, we tested Pt/UiO-66(Ce) for the CO oxidation reaction. Interestingly, this catalyst showed ∼six-fold increment in activity in comparison with the traditional Pt/nCeO2 material. Finally, the characterization after catalysis reveals that the Pt nature is preserved and that the activity is maintained during 14 h at 100 °C without any evidence of deactivation.

Tailoring Lewis/Brønsted acid properties of MOF nodes via hydrothermal and solvothermal synthesis: simple approach with exceptional catalytic implications.

The Lewis/Brønsted catalytic properties of the Metal-Organic Framework (MOF) nodes can be tuned by simply controlling the solvent employed in the synthetic procedure. In this work, we demonstrate that Hf-MOF-808 can be prepared from a material with a higher amount of Brønsted acid sites, via modulated hydrothermal synthesis, to a material with a higher proportion of unsaturated Hf Lewis acid sites, via modulated solvothermal synthesis. The Lewis/Brønsted acid properties of the resultant metallic clusters have been studied by different characterization techniques, including XAS, FTIR and NMR spectroscopies, combined with a DFT study. The different nature of the Hf-MOF-808 materials allows their application as selective catalysts in different target reactions requiring Lewis, Brønsted or Lewis-Brønsted acid pairs.

Coordinatively Unsaturated Hf-MOF-808 Prepared via Hydrothermal Synthesis as a Bifunctional Catalyst for the Tandem N-Alkylation of Amines with Benzyl Alcohol.

The modulated hydrothermal (MHT) synthesis of an active and selective Hf-MOF-808 material for the N-alkylation reaction of aniline with benzyl alcohol under base-free mild reaction conditions is reported. Through kinetic experiments and isotopically labeled NMR spectroscopy studies, we have demonstrated that the reaction mechanism occurs via borrowing hydrogen (BH) pathway, in which the alcohol dehydrogenation is the limiting step. The high concentration of defective -OH groups generated on the metallic nodes through MHT synthesis enhances the alcohol activation, while the unsaturated Hf4+, which acts as a Lewis acid site, is able to borrow the hydrogen from the methylene position of benzyl alcohol. This fact makes this material at least 14 times more active for the N-alkylation reaction than the material obtained via solvothermal synthesis. The methodology described in this work could be applied to a wide range of aniline and benzyl alcohol derivates, showing in all cases high selectivity toward the corresponding N-benzylaniline product. Finally, Hf-MOF-808, which acts as a true heterogeneous catalyst, can be reused in at least four consecutive runs without any activity loss.