RESUMEN
TiO2-based mixed oxide-carbon composite support for Pt electrocatalysts provides higher stability and CO tolerance under the working conditions of polymer electrolyte membrane fuel cells compared to traditional carbon supports. Non-traditional carbon materials like graphene nanoplatelets and graphite oxide used as the carbonaceous component of the composite can contribute to its affordability and/or functionality. Ti(1-x)MoxO2-C composites involving these carbon materials were prepared through a sol-gel route; the effect of the extension of the procedure through a solvothermal treatment step was assessed. Both supports and supported Pt catalysts were characterized by physicochemical methods. Electrochemical behavior of the catalysts in terms of stability, activity, and CO tolerance was studied. Solvothermal treatment decreased the fracture of graphite oxide plates and enhanced the formation of a reduced graphene oxide-like structure, resulting in an electrically more conductive and more stable catalyst. In parallel, solvothermal treatment enhanced the growth of mixed oxide crystallites, decreasing the chance of formation of Pt-oxide-carbon triple junctions, resulting in somewhat less CO tolerance. The electrocatalyst containing graphene nanoplatelets, along with good stability, has the highest activity in oxygen reduction reaction compared to the other composite-supported catalysts.
RESUMEN
The composites of transition metal-doped titania and carbon have emerged as promising supports for Pt electrocatalysts in PEM fuel cells. In these multifunctional supports, the oxide component stabilizes the Pt particles, while the dopant provides a co-catalytic function. Among other elements, Sn is a valuable additive. Stong metal-support interaction (SMSI), i.e., the migration of a partially reduced oxide species from the support to the surface of Pt during reductive treatment is a general feature of TiO2-supported Pt catalysts. In order to explore the influence of SMSI on the stability and performance of Pt/Ti0.8Sn0.2O2-C catalysts, the structural and catalytic properties of the as prepared samples measured using XRD, TEM, XPS and electrochemical investigations were compared to those obtained from catalysts reduced in hydrogen at elevated temperatures. According to the observations, the uniform oxide coverage of the carbon backbone facilitated the formation of Pt-oxide-C triple junctions at a high density. The electrocatalytic behavior of the as prepared catalysts was determined by the atomic closeness of Sn to Pt, while even a low temperature reductive treatment resulted in Sn-Pt alloying. The segregation of tin oxide on the surface of the alloy particles, a characteristic material transport process in Sn-Pt alloys after oxygen exposure, contributed to a better stability of the reduced catalysts.
RESUMEN
TiO2-based mixed oxide-carbon composite supports have been suggested to provide enhanced stability for platinum (Pt) electrocatalysts in polymer electrolyte membrane (PEM) fuel cells. The addition of molybdenum (Mo) to the mixed oxide is known to increase the CO tolerance of the electrocatalyst. In this work Pt catalysts, supported on Ti1-xMoxO2-C composites with a 25/75 oxide/carbon mass ratio and prepared from different carbon materials (C: Vulcan XC-72, unmodified and functionalized Black Pearls 2000), were compared in the hydrogen oxidation reaction (HOR) and in the oxygen reduction reaction (ORR) with a commercial Pt/C reference catalyst in order to assess the influence of the support on the electrocatalytic behavior. Our aim was to perform electrochemical studies in preparation for fuel cell tests. The ORR kinetic parameters from the Koutecky-Levich plot suggested a four-electron transfer per oxygen molecule, resulting in H2O. The similarity between the Tafel slopes suggested the same reaction mechanism for electrocatalysts supported by these composites. The HOR activity of the composite-supported electrocatalysts was independent of the type of carbonaceous material. A noticeable difference in the stability of the catalysts appeared only after 5000 polarization cycles; the Black Pearl-containing sample showed the highest stability.