RESUMEN
Germanium-tin nanoparticles are promising materials for near- and mid-infrared photonics thanks to their tunable optical properties and compatibility with silicon technology. This work proposes modifying the spark discharge method to produce Ge/Sn aerosol nanoparticles during the simultaneous erosion of germanium and tin electrodes. Since tin and germanium have a significant difference in the potential for electrical erosion, an electrical circuit damped for one period was developed to ensure the synthesis of Ge/Sn nanoparticles consisting of independent germanium and tin crystals of different sizes, with the ratio of the atomic fraction of tin to germanium varying from 0.08 ± 0.03 to 0.24 ± 0.07. We investigated the elemental and phase composition, size, morphology, and Raman and absorbance spectra of the nanoparticles synthesized under different inter-electrode gap voltages and the presence of additional thermal treatment directly in a gas flow at 750 °C. The research shows that the in-flow thermal treatment of aerosol-agglomerated nanoparticles produced special individual bicrystalline Janus Ge/Sn nanoparticles with an average size of 27 nm and a decreasing absorption function with a changing slope at 700 nm.
RESUMEN
A cost-effective, scalable and versatile method of preparing nano-ink without hazardous chemical precursors is a prerequisite for widespread adoption of printed electronics. Precursor-free synthesis by spark discharge is promising for this purpose. The synthesis of platinum nanoparticles (PtNPs) using a spark discharge under Ar, N2, and air has been investigated to prepare highly conductive nano-ink. The size, chemical composition, and mass production rate of PtNPs significantly depended on the carrier gas. Pure metallic PtNPs with sizes of 5.5 ± 1.8 and 7.1 ± 2.4 nm were formed under Ar and N2, respectively. PtNPs with sizes of 18.2 ± 9.0 nm produced using air consisted of amorphous oxide PtO and metallic Pt. The mass production rates of PtNPs were 53 ± 6, 366 ± 59, and 490 ± 36 mg/h using a spark discharge under Ar, N2, and air, respectively. It was found that the energy dissipated in the spark gap is not a significant parameter that determines the mass production rate. Stable Pt nano-ink (25 wt.%) was prepared only on the basis of PtNPs synthesized under air. Narrow (about 30 µm) and conductive Pt lines were formed by the aerosol jet printing with prepared nano-ink. The resistivity of the Pt lines sintered at 750 °C was (1.2 ± 0.1)·10-7 Ω·m, which is about 1.1 times higher than that of bulk Pt.