Vertical nanoscale strain-induced electronic localization in epitaxial La2/3Sr1/3MnO3 films with ZrO2 nanopillar inclusions.

Unusual electrical transport properties associated with weak or strong localization are sometimes found in disordered electronic materials. Here, we report experimental observation of a crossover of electronic behavior from weak localization to enhanced weak localization due to the spatial influence of disorder induced by ZrO2 nanopillars in (La2/3Sr1/3MnO3)1-x:(ZrO2)x (x = 0, 0.2, and 0.3) nanocomposite films. The spatial strain regions, identified by scanning transmission electron microscopy and high-resolution x-ray diffraction, induce a coexistence of two-dimentional (2D) and three-dimentional (3D) localization and switches to typical 2D localization with increasing density of ZrO2 pillars due to length scale confinement, which interestingly accords with enhancing vertically interfacial strain. Based on the excellent agreement of our experimental results with one-parameter scaling theory of localization, the enhanced weak localization exists in metal range close to the fixed point. These films provide a tunable experimental model for studying localization in particular the transition regime by appropriate choice of the second epitaxial phase.

Twin-Domain Formation in Epitaxial Triangular Lattice Delafossites.

Twin domains are often found as structural defects in symmetry mismatched epitaxial thin films. The delafossite ABO2, which has a rhombohedral structure, is a good example that often forms twin domains. Although bulk metallic delafossites are known to be the most conducting oxides, high conductivity is yet to be realized in thin film forms. Suppressed conductivity found in thin films is mainly caused by the formation of twin domains, and their boundaries can be a source of scattering centers for charge carriers. To overcome this challenge, the underlying mechanism for their formation must be understood so that such defects can be controlled and eliminated. Here, we report the origin of structural twins formed in a CuCrO2 delafossite thin film on a substrate with hexagonal or triangular symmetries. A robust heteroepitaxial relationship is found for the delafossite film with the substrate, and the surface termination turns out to be critical to determine and control the domain structure of epitaxial delafossites. Based on such discoveries, we also demonstrate twin-free epitaxial thin films grown on high-miscut substrates. This finding provides an important synthesis strategy for growing single-domain delafossite thin films and can be applied to other delafossites for the epitaxial synthesis of high-quality thin films.

Understanding Substrate-Guided Assembly in van der Waals Epitaxy by in Situ Laser Crystallization within a Transmission Electron Microscope.

Understanding the bottom-up synthesis of atomically thin two-dimensional (2D) crystals and heterostructures is important for the development of new processing strategies to assemble 2D heterostructures with desired functional properties. Here, we utilize in situ laser-heating within a transmission electron microscope (TEM) to understand the stages of crystallization and coalescence of amorphous precursors deposited by pulsed laser deposition (PLD) as they are guided by 2D crystalline substrates into van der Waals (vdW) epitaxial heterostructures. Amorphous clusters of tungsten selenide were deposited by PLD at room temperature onto graphene or MoSe2 monolayer crystals that were suspended on TEM grids. The precursors were then stepwise evolved into 2D heterostructures with pulsed laser heating treatments within the TEM. The lattice-matching provided by the MoSe2 substrate is shown to guide the formation of large-domain, heteroepitaxial vdW WSe2/MoSe2 bilayers both during the crystallization process via direct templating and after crystallization by assisting the coalescence of nanosized domains through nonclassical particle attachment processes including domain rotation and grain boundary migration. The favorable energetics for domain rotation induced by lattice matching with the substrate were understood from first-principles calculations. These in situ TEM studies of pulsed laser-driven nonequilibrium crystallization phenomena represent a transformational tool for the rapid exploration of synthesis and processing pathways that may occur on extremely different length and time scales and lend insight into the growth of 2D crystals by PLD and laser crystallization.

Strain-Induced Atomic-Scale Building Blocks for Ferromagnetism in Epitaxial LaCoO3.

The origin of strain-induced ferromagnetism, which is robust regardless of the type and degree of strain in LaCoO3 (LCO) thin films, is enigmatic despite intensive research efforts over the past decade. Here, by combining scanning transmission electron microscopy with ab initio density functional theory plus U calculations, we report that the ferromagnetism does not emerge directly from the strain itself but rather from the creation of compressed structural units within ferroelastically formed twin-wall domains. The compressed structural units are magnetically active with the rocksalt-type high-spin/low-spin order. Our study highlights that the ferroelastic nature of ferromagnetic structural units is important for understanding the intriguing ferromagnetic properties in LCO thin films.

Metal-insulator transition tuned by oxygen vacancy migration across TiO2/VO2 interface.

Oxygen defects are essential building blocks for designing functional oxides with remarkable properties, ranging from electrical and ionic conductivity to magnetism and ferroelectricity. Oxygen defects, despite being spatially localized, can profoundly alter global properties such as the crystal symmetry and electronic structure, thereby enabling emergent phenomena. In this work, we achieved tunable metal-insulator transitions (MIT) in oxide heterostructures by inducing interfacial oxygen vacancy migration. We chose the non-stoichiometric VO2-δ as a model system due to its near room temperature MIT temperature. We found that depositing a TiO2 capping layer on an epitaxial VO2 thin film can effectively reduce the resistance of the insulating phase in VO2, yielding a significantly reduced ROFF/RON ratio. We systematically studied the TiO2/VO2 heterostructures by structural and transport measurements, X-ray photoelectron spectroscopy, and ab initio calculations and found that oxygen vacancy migration from TiO2 to VO2 is responsible for the suppression of the MIT. Our findings underscore the importance of the interfacial oxygen vacancy migration and redistribution in controlling the electronic structure and emergent functionality of the heterostructure, thereby providing a new approach to designing oxide heterostructures for novel ionotronics and neuromorphic-computing devices.

Interfacial stabilization for epitaxial CuCrO2 delafossites.

ABO2 delafossites are fascinating materials that exhibit a wide range of physical properties, including giant Rashba spin splitting and anomalous Hall effects, because of their characteristic layered structures composed of noble metal A and strongly correlated BO2 sublayers. However, thin film synthesis is known to be extremely challenging owing to their low symmetry rhombohedral structures, which limit the selection of substrates for thin film epitaxy. Hexagonal lattices, such as those provided by Al2O3(0001) and (111) oriented cubic perovskites, are promising candidates for epitaxy of delafossites. However, the formation of twin domains and impurity phases is hard to suppress, and the nucleation and growth mechanisms thereon have not been studied for the growth of epitaxial delafossites. In this study, we report the epitaxial stabilization of a new interfacial phase formed during pulsed-laser epitaxy of (0001)-oriented CuCrO2 epitaxial thin films on Al2O3 substrates. Through a combined study using scanning transmission electron microscopy/electron-energy loss spectroscopy and density functional theory calculations, we report that the nucleation of a thermodynamically stable, atomically thick CuCr1-xAlxO2 interfacial layer is the critical element for the epitaxy of CuCrO2 delafossites on Al2O3 substrates. This finding provides key insights into the thermodynamic mechanism for the nucleation of intermixing-induced buffer layers that can be used for the growth of other noble-metal-based delafossites, which are known to be challenging due to the difficulty in initial nucleation.

Effect of indium alloying on the charge carrier dynamics of thick-shell InP/ZnSe quantum dots.

Thick-shell InP/ZnSe III-V/II-VI quantum dots (QDs) were synthesized with two distinct interfaces between the InP core and ZnSe shell: alloy and core/shell. Despite sharing similar optical properties in the spectral domain, these two QD systems have differing amounts of indium incorporation in the shell as determined by high-resolution energy-dispersive x-ray spectroscopy scanning transmission electron microscopy. Ultrafast fluorescence upconversion spectroscopy was used to probe the charge carrier dynamics of these two systems and shows substantial charge carrier trapping in both systems that prevents radiative recombination and reduces the photoluminescence quantum yield. The alloy and core/shell QDs show slight differences in the extent of charge carrier localization with more extensive trapping observed in the alloy nanocrystals. Despite the ability to grow a thick shell, structural defects caused by III-V/II-VI charge carrier imbalances still need to be mitigated to further improve InP QDs.

Effects of Surface Terminations of 2D Bi2WO6 on Photocatalytic Hydrogen Evolution from Water Splitting.

Two-dimensional (2D)-structured photocatalysts with atomically thin layers not only have the potential to enhance hydrogen generation efficiency but also allow more direct investigations of the effects of surface terminations on photocatalytic activity. Taking 2D Bi2WO6 as a model, we found that the configuration of bilayer Bi2O2 sandwiched by alternating WO4 layers enabled the thermodynamic driving potential for photocatalytic hydrogen evolution. Without Pt deposition, the H2 generation efficiency can reach to 56.9 µmol/g/h by 2D Bi2WO6 as compared with no activity of Bi2WO6 nanocrystals under simulated solar light. This configuration is easily functionalized by adsorption of Cl-/Br- to form Bi-Cl/Bi-Br bonds, which leads to the decrease of recombination in photogenerated charge carriers and narrower band gaps. This work highlights an effective way to design photocatalysts with efficient hydrogen evolution by tuning the surface terminations.

Role of shell composition and morphology in achieving single-emitter photostability for green-emitting "giant" quantum dots.

The use of the varied chemical reactivity of precursors to drive the production of a desired nanocrystal architecture has become a common method to grow thick-shell graded alloy quantum dots (QDs) with robust optical properties. Conclusions on their behavior assume the ideal chemical gradation and uniform particle composition. Here, advanced analytical electron microscopy (high-resolution scanning transmission electron microscopy coupled with energy dispersive spectroscopy) is used to confirm the nature and extent of compositional gradation and these data are compared with performance behavior obtained from single-nanocrystal spectroscopy to elucidate structure, chemical-composition, and optical-property correlations. Specifically, the evolution of the chemical structure and single-nanocrystal luminescence was determined for a time-series of graded-alloy "CdZnSSe/ZnS" core/shell QDs prepared in a single-pot reaction. In a separate step, thick (∼6 monolayers) to giant (>14 monolayers) shells of ZnS were added to the alloyed QDs via a successive ionic layer adsorption and reaction (SILAR) process, and the impact of this shell on the optical performance was also assessed. By determining the degree of alloying for each component element on a per-particle basis, we observe that the actual product from the single-pot reaction is less "graded" in Cd and more so in Se than anticipated, with Se extending throughout the structure. The latter suggests much slower Se reaction kinetics than expected or an ability of Se to diffuse away from the initially nucleated core. It was also found that the subsequent growth of thick phase-pure ZnS shells by the SILAR method was required to significantly reduce blinking and photobleaching. However, correlated single-nanocrystal optical characterization and electron microscopy further revealed that these beneficial properties are only achieved if the thick ZnS shell is complete and without large lattice discontinuities. In this way, we identify the necessary structural design features that are required for ideal light emission properties in these green-visible emitting QDs.

Two-Dimensional Palladium Diselenide with Strong In-Plane Optical Anisotropy and High Mobility Grown by Chemical Vapor Deposition.

Two-dimensional (2D) palladium diselenide (PdSe2 ) has strong interlayer coupling and a puckered pentagonal structure, leading to remarkable layer-dependent electronic structures and highly anisotropic in-plane optical and electronic properties. However, the lack of high-quality, 2D PdSe2 crystals grown by bottom-up approaches limits the study of their exotic properties and practical applications. In this work, chemical vapor deposition growth of highly crystalline few-layer (≥2 layers) PdSe2 crystals on various substrates is reported. The high quality of the PdSe2 crystals is confirmed by low-frequency Raman spectroscopy, scanning transmission electron microscopy, and electrical characterization. In addition, strong in-plane optical anisotropy is demonstrated via polarized Raman spectroscopy and second-harmonic generation maps of the PdSe2 flakes. A theoretical model based on kinetic Wulff construction theory and density functional theory calculations is developed and described the observed evolution of "square-like" shaped PdSe2 crystals into rhombus due to the higher nucleation barriers for stable attachment on the (1,1) and (1,-1) edges, which results in their slower growth rates. Few-layer PdSe2 field-effect transistors reveal tunable ambipolar charge carrier conduction with an electron mobility up to ≈294 cm2 V-1 s-1 , which is comparable to that of exfoliated PdSe2 , indicating the promise of this anisotropic 2D material for electronics.

Colossal oxygen vacancy formation at a fluorite-bixbyite interface.

Oxygen vacancies in complex oxides are indispensable for information and energy technologies. There are several means to create oxygen vacancies in bulk materials. However, the use of ionic interfaces to create oxygen vacancies has not been fully explored. Herein, we report an oxide nanobrush architecture designed to create high-density interfacial oxygen vacancies. An atomically well-defined (111) heterointerface between the fluorite CeO2 and the bixbyite Y2O3 is found to induce a charge modulation between Y3+ and Ce4+ ions enabled by the chemical valence mismatch between the two elements. Local structure and chemical analyses, along with theoretical calculations, suggest that more than 10% of oxygen atoms are spontaneously removed without deteriorating the lattice structure. Our fluorite-bixbyite nanobrush provides an excellent platform for the rational design of interfacial oxide architectures to precisely create, control, and transport oxygen vacancies critical for developing ionotronic and memristive devices for advanced energy and neuromorphic computing technologies.

Vertically Aligned Single-Crystalline CoFe2O4 Nanobrush Architectures with High Magnetization and Tailored Magnetic Anisotropy.

Micrometer-tall vertically aligned single-crystalline CoFe2O4 nanobrush architectures with extraordinarily large aspect ratio have been achieved by the precise control of a kinetic and thermodynamic non-equilibrium pulsed laser epitaxy process. Direct observations by scanning transmission electron microscopy reveal that the nanobrush crystal is mostly defect-free by nature, and epitaxially connected to the substrate through a continuous 2D interface layer. In contrast, periodic dislocations and lattice defects such as anti-phase boundaries and twin boundaries are frequently observed in the 2D interface layer, suggesting that interface misfit strain relaxation under a non-equilibrium growth condition plays a critical role in the self-assembly of such artificial architectures. Magnetic property measurements have found that the nanobrushes exhibit a saturation magnetization value of 6.16 B/f.u., which is much higher than the bulk value. The discovery not only enables insights into an effective route for fabricating unconventional high-quality nanostructures, but also demonstrates a novel magnetic architecture with potential applications in nanomagnetic devices.

Low Energy Implantation into Transition-Metal Dichalcogenide Monolayers to Form Janus Structures.

Atomically thin two-dimensional (2D) materials face significant energy barriers for synthesis and processing into functional metastable phases such as Janus structures. Here, the controllable implantation of hyperthermal species from pulsed laser deposition (PLD) plasmas is introduced as a top-down method to compositionally engineer 2D monolayers. The kinetic energies of Se clusters impinging on suspended monolayer WS2 crystals were controlled in the <10 eV/atom range with in situ plasma diagnostics to determine the thresholds for selective top layer replacement of sulfur by selenium for the formation of high quality WSSe Janus monolayers at low (300 °C) temperatures and bottom layer replacement for complete conversion to WSe2. Atomic-resolution electron microscopy and spectroscopy in tilted geometry confirm the WSSe Janus monolayer. Molecular dynamics simulations reveal that Se clusters implant to form disordered metastable alloy regions, which then recrystallize to form highly ordered structures, demonstrating low-energy implantation by PLD for the synthesis of 2D Janus layers and alloys of variable composition.

Rotational polarization nanotopologies in BaTiO3/SrTiO3 superlattices.

Ferroelectrics are characterized by domain structures as are other ferroics. At the nanoscale though, ferroelectrics may exhibit non-trivial or exotic polarization configurations under proper electrostatic and elastic conditions. These polar states may possess emerging properties not present in the bulk compounds and are promising for technological applications. Here, the observation of rotational polarization topologies at the nanoscale by means of aberration-corrected scanning transmission electron microscopy is reported in BaTiO3/SrTiO3 superlattices grown on cubic SrTiO3(001). The transition from a highly homogeneous polarization state to the formation of rotational nanodomains has been achieved by controlling the superlattice period while maintaining compressive clamping of the superlattice to the cubic SrTiO3 substrate. The nanodomains revealed in BaTiO3 prove that its nominal tetragonal structure also allows rotational polar textures.

Protecting the Nanoscale Properties of Ag Nanowires with a Solution-Grown SnO2 Monolayer as Corrosion Inhibitor.

The chemical reactivity and/or the diffusion of Ag atoms or ions during thermal processing can cause irreversible structural damage, hindering the application of Ag nanowires (NWs) in transparent conducting films and other applications that make use of the material's nanoscale properties. Here, we describe a simple and effective method for growing monolayer SnO2 on the surface of Ag nanowires under ambient conditions, which protects the Ag nanowires from chemical and structural damage. Our results show that Sn2+ and Ag atoms undergo a redox reaction in the presence of water. First-principle simulations suggest a reasonable mechanism for SnO2 formation, showing that the interfacial polarization of the silver by the SnO2 can significantly reduce the affinity of Ag to O2, thereby greatly reducing the oxidation of the silver. The corresponding values (for example, before coating: 17.2 Ω/sq at 86.4%, after coating: 19.0 Ω/sq at 86.6%) show that the deposition of monolayer SnO2 enables the preservation of high transparency and conductivity of Ag. In sharp contrast to the large-scale degradation of pure Ag-NW films including the significant reduction of its electrical conductivity when subjected to a series of harsh corrosion environments, monolayer SnO2 coated Ag-NW films survive structurally and retain their electrical conductivity. Consequently, the thermal, electrical, and chemical stability properties we report here, and the simplicity of the technology used to achieve them, are among the very best reported for transparent conductor materials to date.

Defect-Mediated Phase Transformation in Anisotropic Two-Dimensional PdSe2 Crystals for Seamless Electrical Contacts.

The failure to achieve stable Ohmic contacts in two-dimensional material devices currently limits their promised performance and integration. Here we demonstrate that a phase transformation in a region of a layered semiconductor, PdSe2, can form a contiguous metallic Pd17Se15 phase, leading to the formation of seamless Ohmic contacts for field-effect transistors. This phase transition is driven by defects created by exposure to an argon plasma. Cross-sectional scanning transmission electron microscopy is combined with theoretical calculations to elucidate how plasma-induced Se vacancies mediate the phase transformation. The resulting Pd17Se15 phase is stable and shares the same native chemical bonds with the original PdSe2 phase, thereby forming an atomically sharp Pd17Se15/PdSe2 interface. These Pd17Se15 contacts exhibit a low contact resistance of ∼0.75 kΩ µm and Schottky barrier height of ∼3.3 meV, enabling nearly a 20-fold increase of carrier mobility in PdSe2 transistors compared to that of traditional Ti/Au contacts. This finding opens new possibilities in the development of better electrical contacts for practical applications of 2D materials.

Defect-Tailoring Mediated Electron-Hole Separation in Single-Unit-Cell Bi3 O4 Br Nanosheets for Boosting Photocatalytic Hydrogen Evolution and Nitrogen Fixation.

Solar photocatalysis is a potential solution to satisfying energy demand and its resulting environmental impact. However, the low electron-hole separation efficiency in semiconductors has slowed the development of this technology. The effect of defects on electron-hole separation is not always clear. A model atomically thin structure of single-unit-cell Bi3 O4 Br nanosheets with surface defects is proposed to boost photocatalytic efficiency by simultaneously promoting bulk- and surface-charge separation. Defect-rich single-unit-cell Bi3 O4 Br displays 4.9 and 30.9 times enhanced photocatalytic hydrogen evolution and nitrogen fixation activity, respectively, than bulk Bi3 O4 Br. After the preparation of single-unit-cell structure, the bismuth defects are controlled to tune the oxygen defects. Benefiting from the unique single-unit-cell architecture and defects, the local atomic arrangement and electronic structure are tuned so as to greatly increase the charge separation efficiency and subsequently boost photocatalytic activity. This strategy provides an accessible pathway for next-generation photocatalysts.