355 nm Nanosecond Ultraviolet Pulsed Laser Annealing Effects on Amorphous In-Ga-ZnO Thin Film Transistors.

Bottom-gate thin-film transistors (TFTs) with n-type amorphous indium-gallium-zinc oxide (a-IGZO) active channels and indium-tin oxide (ITO) source/drain electrodes were fabricated. Then, an ultraviolet (UV) nanosecond pulsed laser with a wavelength of 355 nm was scanned to locally anneal the active channel at various laser powers. After laser annealing, negative shifts in the threshold voltages and enhanced on-currents were observed at laser powers ranging from 54 to 120 mW. The energy band gap and work function of a-IGZO extracted from the transmittance and ultraviolet photoelectron spectroscopy (UPS) measurement data confirm that different energy band structures for the ITO electrode/a-IGZO channel were established depending on the laser annealing conditions. Based on these observations, the electron injection mechanism from ITO electrodes to a-IGZO channels was analyzed. The results show that the selective laser annealing process can improve the electrical performance of the a-IGZO TFTs without any thermal damage to the substrate.

Effects of Insertion of Ag Mid-Layers on Laser Direct Ablation of Transparent Conductive ITO/Ag/ITO Multilayers: Role of Effective Absorption and Focusing of Photothermal Energy.

From the viewpoint of the device performance, the fabrication and patterning of oxide-metal-oxide (OMO) multilayers (MLs) as transparent conductive oxide electrodes with a high figure of merit have been extensively investigated for diverse optoelectronic and energy device applications, although the issues of their general concerns about possible shortcomings, such as a more complicated fabrication process with increasing cost, still remain. However, the underlying mechanism by which a thin metal mid-layer affects the overall performance of prepatterned OMO ML electrodes has not been fully elucidated. In this study, indium tin oxide (ITO)/silver (Ag)/ITO MLs are fabricated using an in-line sputtering method for different Ag thicknesses on glass substrates. Subsequently, a Q-switched diode-pumped neodymium-doped yttrium vanadate (Nd:YVO4, λ = 1064 nm) laser is employed for the direct ablation of the ITO/Ag/ITO ML films to pattern ITO/Ag/ITO ML electrodes. Analysis of the laser-patterned results indicate that the ITO/Ag/ITO ML films exhibit wider ablation widths and lower ablation thresholds than ITO single layer (SL) films. However, the dependence of Ag thickness on the laser patterning results of the ITO/Ag/ITO MLs is not observed, despite the difference in their absorption coefficients. The results show that the laser direct patterning of ITO/Ag/ITO MLs is primarily affected by rapid thermal heating, melting, and vaporization of the inserted Ag mid-layer, which has considerably higher thermal conductivity and absorption coefficients than the ITO layers. Simulation reveals the importance of the Ag mid-layer in the effective absorption and focusing of photothermal energy, thereby supporting the experimental observations. The laser-patterned ITO/Ag/ITO ML electrodes indicate a comparable optical transmittance, a higher electrical current density, and a lower resistance compared with the ITO SL electrode.