Application of near-infrared-to-blue upconversion luminescence for the polymerization of resin cements through zirconia discs.

OBJECTIVES: To investigate a near-infrared-to-blue luminescence upconversion curing method for polymerizing resin cements under zirconia discs. METHODS: Lava zirconia discs of different thicknesses (0.5-2.0 mm) were manufactured. First, the transmittances of the NIR and two blue lights (BLs) (LED and halogen lights) through these discs were measured. Second, NaYF4:Yb3+/Tm3+ upconversion phosphor (UP) powder was milled into 0.5-µm particle sizes. A light-curable resin cement VariolinkII base was chosen as the control (UP0), and an experimental cement (UP5) was prepared by adding 5 % UPs. These two cements were examined using multiphoton excitation microscopy for particle distribution. UP5 and UP0 were polymerized with or without zirconia shielding then subjected to a microhardness test. A multifold analysis was performed to examine the effects of zirconia thickness, curing protocols (pure BL or combined BL and NIR curing), and cement type. RESULTS: The transmittance of NIR was superior to that of BL through zirconia discs of all thicknesses. UP particles were homogeneously distributed in UP5 and emitted blue luminescence under 980-nm NIR excitation. UP5 showed higher microhardness values than UP0 under any curing protocol or zirconia shielding condition. The combination of 20-s BL and 40-s NIR curing yielded the highest microhardness in uncovered UP5. However, combining 40-s BL and 20-s NIR curing surpassed the other groups when the zirconia discs were thicker than 0.5 mm. SIGNIFICANCE: NIR exhibits higher transmission through zirconia than BL. UP particles work as strengthen fillers and photosensitizers in cements. NIR upconversion curing could be a new strategy for polymerizing resin cements under thick zirconia restorations.

Assessments of polymerization shrinkage by optical coherence tomography-based digital image correlation analysis-Part II: Effects of restorative composites.

OBJECTIVES: To examine the polymerization shrinkage of different resin-based composite (RBC) restorations using optical coherence tomography (OCT) image-based digital image correlation (DIC) analysis. METHODS: The refractive index (RI) of three RBCs, Filtek Z350XT (Z350), Z350Flowable (Z350F), and BulkFill Posterior (Bulkfill), was measured before and after polymerization to calibrate their axial dimensions under OCT. Class I cavities were prepared in bovine incisors and individually filled with these RBCs under nonbonded and bonded conditions. A series of OCT images of these restorations were captured during 20-s light polymerization and then input into DIC software to analyze their shrinkage behaviors. The interfacial adaptation was also examined using these OCT images. RESULTS: The RI of the three composites ranged from 1.52 to 1.53, and photopolymerization caused neglectable increases in the RI values. For nonbonded restorations, Z350F showed maximal vertical displacements on the top surfaces (-16.75 µm), followed by Bulkfill (-8.81 µm) and Z350 (-5.97 µm). In their bonded conditions, all showed increased displacements. High variations were observed in displacement measurements on the bottom surfaces. In the temporal analysis, the shrinkage of nonbonded Z350F and Bulkfill decelerated after 6-10 s. However, Z350 showed a rebounding upward displacement after 8.2 s. Significant interfacial gaps were found in nonbonded Z350 and Z350F restorations. SIGNIFICANCE: The novel OCT image-based DIC analysis provided a comprehensive examination of the shrinkage behaviors and debonding of the composite restorations throughout the polymerization process. The flowable composite showed the highest shrinkage displacements. Changes in the shrinkage direction may occur in nonbonded conventional composite restorations.

Assessments of polymerization shrinkage by optical coherence tomography-based digital image correlation analysis-Part I: Parameter identification.

OBJECTIVE: To investigate the feasibility of optical coherence tomography (OCT)-based digital image correlation (DIC) analysis and to identify the experimental parameters for measurements of polymerization shrinkage. METHODS: Class I cavities were prepared on bovine incisors and filled with Filtek Z350XT Flowable (Z350F). One OCT image of the polymerized restoration was processed to generate virtually displaced images. In addition, the tooth specimen was physically moved under OCT scanning. A DIC software analyzed these virtual and physical transformation sets and assessed the effects of subset sizes on accuracy. The refractive index of unpolymerized and polymerized Z350F was measured via OCT images. Finally, different particles (70-80 µm glass beads, 150-212 µm glass beads, and 75-150 µm zirconia powder) were added to Z350F to inspect the analyzing quality. RESULTS: The analyses revealed a high correlation (>99.99%) for virtual movements within 131 pixels (639 µm) and low errors (<5.21%) within a 10-µm physical movement. A subset size of 51 × 51 pixels demonstrated the convergence of correlation coefficients and calculation time. The refractive index of Z350F did not change significantly after polymerization. Adding glass beads or zirconia particles caused light reflection or shielding in OCT images, whereas blank Z350F produced the best DIC analysis results. SIGNIFICANCE: The OCT-based DIC analysis with the experimental conditions is feasible in measuring polymerization shrinkage of RBC restorations. The subset size in the DIC analysis should be identified to optimize the analysis conditions and results. Uses of hyper- or hypo-reflective particles is not recommended in this method.

The influence of pontic distribution on the marginal and internal gaps of CAD/CAM five-unit anterior zirconia framework.

Background/purpose: Nowadays, zirconia-based framework has been used for longspan or full-arch fixed dental prostheses (FDPs). This study aimed to evaluate the effect of pontic distribution on marginal and internal gaps of five-unit anterior zirconiabased DPs. Materials and methods: Right maxillary central incisor and second premolar were selected as terminal abutments and three different edentulous conditions with one nonterminal abutment were simulated. Marginal and internal gaps in each zirconia-based samples(n = 10) were examined by computer-aided replica technique. Five regions, including marginal gaps at mesial or distal finishing line, internal gaps at the mesial or distal axial wall, and occlusal surface, were statistically analyzed (α = .05). Results: Most of marginal gaps and internal gaps at axial wall were clinically acceptable, but larger at occlusal surface. For the three experimental groups, clinically accepted percentage with qualified gaps were less than 30%.There were statistical differences at axial wall over pontic side and marginal gaps over non-pontic side between groups (P<0.05). For sum of gaps of all abutments in each group, statistical differences were found at marginal and axial wall (P < 0.05). As for those on terminal and non-terminal abutments, statistical differences were found on second premolar (P < 0.05). Conclusion: Except for occlusal surface, the overall marginal gaps and internal gaps at axial wall of five-unit anterior zirconia-based FDPs with different pontic distribution were clinically acceptable. However, the percentage with qualified gaps were low (<30%). Greater gaps were noted when adjacent pontic existed. Different pontic size and distribution with curvature had an influence on the gaps.

Simulating the shrinkage-induced interfacial damage around Class I composite resin restorations with damage mechanics.

OBJECTIVES: To investigate the shrinkage-induced damage at the composite-tooth interface by finite element analysis (FEA) using the cohesive zone model (CZM). METHODS: Axisymmetric models of Class I restorations were created to illustrate the interfacial damage around composite resin restorations of different dimensions, with polymerization shrinkage modeled analogously to thermal shrinkage. The damage to the adhesive interface was determined using a CZM based on the fracture strength and fracture energy. To show the effects of damage, conventional models with perfectly bonded composite resin restorations were created as controls. RESULTS: The results indicated interfacial damage at the butt-joint cavosurface margin, dentinoenamel junction, and internal line angle. The percentage of damaged interfacial area was found to increase with decreasing diameter for restorations of the same height. For a given diameter, the damage was more severe for restorations of greater depth. The effects of the damage were further illustrated in the model with a restoration of 2-mm diameter and height. The interfacial damage occurred primarily at the internal line angle (83.3 % of all the damaged interfacial area), leading to local stress relief (from 18.3 MPa to 12.8 MPa), but also higher stress at the damage fronts. Greater local shrinkage was found in composites adjacent to the damage. SIGNIFICANCE: The damage mechanics-based CZM is an essential refinement of the FEA to predict interfacial damage and its implications. The extent of damage was found to be greater around restorations with smaller diameters and greater depths. The entire simulation is available via an open-source platform to facilitate further applications in adhesive dentistry.

Dentin Sialoprotein/Phosphophoryn (DSP/PP) as Bio-Inductive Materials for Direct Pulp Capping.

Conventional direct pulp capping, such as calcium hydroxide (Ca(OH)2) or silicate products, usually induces an inflammatory reaction to provoke pulp regeneration. Phosphophoryn (PP) and dentin sialoprotein (DSP), the two most abundant non-collagenous proteins in the dentin matrix, are responsible for dentin mineralization, pulp cell migration, and differentiation. Here we examined the PP and combined DSP/PP as bio-inductive pulp capping materials by in vitro and in vivo tests. Firstly, the effects of the PP dose on pulp cell migration and matrix protein expression were examined by an agarose bead test. Secondly, the role of recombinant DSP (recDSP) and recDSP/PP on stimulating DSP-PP transcript expression was examined by RT-PCR. DSPP mRNA was also knocked down by RNA interference (RNAi) to examine their functions on dentin matrix mineralization. Finally, we used ferret animal models to test PP and recDSP/PP acting as capping agents on in vivo pulp responses and reparative dentin formation. The result showed that intermediate-dose PP was the most effective to enhance cell migration and differentiation. RecDSP/PP strongly enhanced the DSP-PP transcript expression, while inhibition of DSPP mRNA expression by siRNAs partially or completely affected dental pulp cell mineralization. The in vivo results showed that intermediate-dose PP and recDSP/PP proteins induced less pulp inflammation and promoted reparative dentin formation. Contrarily, conventional calcium hydroxide induced severe pulp inflammation. With these findings, DSP and PP could serve as capping agents for pulp capping therapy.

Enhancing Resin Cement Adhesion to Zirconia by Oxygen Plasma-Aided Silicatization.

The combinations of alumina particle air abrasion (AA) and a 10-methacryloyloxyidecyl-dihyidrogenphosphate (MDP) primer and a tribochemical silica coating (TSC) and a silane-base primer are contemporary pre-cementation treatments for zirconia restorations for bonding with resin cements. However, the stability of zirconia resists the mechanical or chemical preparations. The purpose of this study was to develop an atmospheric-pressure oxygen plasma (OP)-aided silicatization method to enhance the adhesion of resin cements to zirconia. Zirconia discs were prepared to receive surface treatments of different combinations: (1) AA or TSC (2) with or without OP treatment, and (3) a chemical primer (no primer, silane, or a silane-MDP mixture). The surface morphology, hydrophilicity, and chemical compositions were characterized, and the resin-zirconia bond strengths were examined either after 24 h or a thermocycling test. The results indicated that the OP treatment after the TSC facilitated the homogeneous distribution of silane and crosslinking of silica particles, and effectively improved the hydrophilicity. The OP increased the O and Si and reduced the C elemental contents, while the combination of TSC, OP, and silane induced SiOx generation. Among the groups, only the TSC-OP-silane treatment effectively enhanced the bond strength and maintained the adhesion after thermocycling. With these results, the OP aided the silicatization protocol effectively, generated silane crosslinking, and resulted in superior resin-zirconia bond strength and durability compared to the current treatments.

Interaction of silane with 10-MDP on affecting surface chemistry and resin bonding of zirconia.

OBJECTIVE: To investigate the effect of silane contents on their chemical interaction with 10-methacryloyloxydecyl-dihydrogen phosphate (MDP), and affecting the bonding of MDP to zirconia by time-of-flight secondary ion mass spectrometry (TOF-SIMS) and solid-state nuclear magnetic resonance (SSNMR) spectroscopy. METHODS: Zirconia (Cercon ht, Dentsply) slabs were prepared and fully sintered. Experimental primers SE-5 and SE-10 were formulated by adding 5 wt% and 10 wt% γ-methacryloxypropyltrimethoxysilane to an MDP-based primer SE BOND (SE), respectively. SE, SE-5, and SE-10 were applied on the assigned zirconia slabs. The chemical compositions on the surface and adhesive interfaces were examined by TOF-SIMS in a depth-profiling mode. Hydrophilicity and resin affinity of treated zirconia were analyzed. The bond strengths to resin cylinder were examined either after 24-h storage or thermocycles. In addition, zirconia powders treated with three primers were assessed by SSNMR spectrometry for the adsorption of MDP. RESULTS: TOF-SIMS analysis showed that SE treatment generated the greatest amount of P-O-Zr related ions, which reduced in SE-5 and SE-10 groups. The 3D ion-images illustrated the generation of ZrO2(OH)- ions with silane contents. The SSNMR analysis revealed that the chemical bonding was mainly P-O-Zr ionic bonds in SE but shifted to P-OH-Zr hydrogen bonds in SE-5 and SE-10. SE-5 and SE-10 treated zirconia presented higher hydrophilicity and affinity to resin compared to Zr did. SE showed the highest initial bond strength which significantly decreased after thermocycling. SIGNIFICANCE: MDP adsorption onto zirconia via P-O-Zr ionic bond promotes bonding with resin. The silane enhances the hydroxylation of zirconia and impairs the adsorption of MDP, but does not adversely affect the bond durability.

Investigations of silane-MDP interaction in universal adhesives: A ToF-SIMS analysis.

OBJECTIVES: The purposes of this study were to investigate whether the presence of silane in universal adhesives affects the functions of 10-methacryloyloxydecyl dihydrogen phosphate (MDP) and adhesion to zirconia. METHODS: Two silane-containing universal adhesives (Scotchbond Universal (SBU) and Clearfil Universal-Bond (CUB)) and two silane-free adhesives (All-Bond Universal (ABU) and SE-Bond primer (SE)) were individually applied on zirconia disks. Time-of-flight secondary-ion-mass-spectrometry (ToF-SIMS) examined the distributions of MDP- and silane-related ions, as well as evidence of zirconium phosphate (ZrP) compounds, on the surface and interfacial regions using a depth profiling mode. The hydrophilicity and resin wettability of the treated zirconia were examined using a contact angle test. For the shear bond strength (SBS) test, the zirconia disks were air-blasted, treated with the assigned adhesives, and bonded with pre-cured composite cylinders using a resin cement. These resin-zirconia assemblies received a bond test after 24-h storage. RESULTS: Both SBU and CUB exhibited silane-related ions and ZrO2(OH)-, but fewer PO- ions in the interfacial regions. CUB had more siloxane-related ions. SE-treated zirconia had abundant PO- ions and particularly high PO3-- and ZrP- related ions in the interfacial regions. The silane-free adhesives exhibited a higher affinity to both water and adhesive liquids. SE showed significantly higher SBSs compared to ABU, while SBU and CUB were not statistically different. SIGNIFICANCE: The silane content may cause hydroxylation of zirconia and affect MDP adsorption. An acidic pH accelerated the condensation of silanol. The bond performance of the MDP-based adhesive could be influenced by the silane content and other components.

Novel Polymerization of Dental Composites Using Near-Infrared-Induced Internal Upconversion Blue Luminescence.

Blue light (BL) curing on dental resin composites results in gradient polymerization. By incorporating upconversion phosphors (UP) in resin composites, near-infrared (NIR) irradiation may activate internal blue emission and a polymerization reaction. This study was aimed to evaluate the competency of the NIR-to-BL upconversion luminance in polymerizing dental composites and to assess the appropriate UP content and curing protocol. NaYF4 (Yb3+/Tm3+ co-doped) powder exhibiting 476-nm blue emission under 980-nm NIR was adapted and ball-milled for 4-8 h to obtain different particles. The bare particles were assessed for their emission intensities, and also added into a base composite Z100 (3M EPSE) to evaluate their ability in enhancing polymerization under NIR irradiation. Experimental composites were prepared by dispensing the selected powder and Z100 at different ratios (0, 5, 10 wt% UP). These composites were irradiated under different protocols (BL, NIR, or their combinations), and the microhardness at the irradiated surface and different depths were determined. The results showed that unground UP (d50 = 1.9 µm) exhibited the highest luminescence, while the incorporation of 0.4-µm particles obtained the highest microhardness. The combined 20-s BL and 20-120-s NIR significantly increased the microhardness on the surface and internal depths compared to BL correspondents. The 5% UP effectively enhanced the microhardness under 80-s NIR irradiation but was surpassed by 10% UP with longer NIR irradiation. The combined BL-NIR curing could be an effective approach to polymerize dental composites, while the intensity of upconversion luminescence was related to specific UP particle size and content. Incorporation of 5-10% UP facilitates NIR upconversion polymerization on dental composites.

Evaluation of the efficacy of low-dose liraglutide in weight control among Taiwanese non-diabetes patients.

AIMS/INTRODUCTION: Obesity and metabolic syndrome are well-known to be associated with multiple chronic diseases. Currently, high-dose liraglutide has been used for weight control in non-diabetic patients. Considering incretin-based therapy is more effective in Asian populations, the effect of low-dose liraglutide in weight control among these non-diabetic groups has not been well evaluated. Our study aimed to evaluate the efficacy of low-dose liraglutide in weight control among Taiwan patients. MATERIALS AND METHODS: From July 2017 to December 2018, 46 non-diabetic patients with metabolic syndrome were included. They had received low-dose liraglutide at 0.6 or 1.2 mg per day for weight reduction for 12 weeks. After then, changes in bodyweight, waist and metabolic factors were examined. Overt bodyweight reduction was defined as a decrease of >5% within 12 weeks. RESULTS: With 12 weeks of medication use, both groups showed statistical weight reduction. Higher doses of liraglutide had better efficacy, and 44.4% of patients in the liraglutide 1.2 mg group reached overt weight reduction, whereas just 32.1% in the 0.6 mg group had achieved this. Young age was found to be a predictor factor for a positive finding (odds ratio 0.941, P = 0.037). Early responders with decreased bodyweight of >4.2% within the first 4 weeks indicated a better chance to achieve measurable weight reduction. CONCLUSIONS: Low-dose liraglutide still has high efficacy in weight reduction in Taiwanese people, especially for those of younger age.

Effects of Restorative Materials on Dental Pulp Stem Cell Properties.

INTRODUCTION: Dental pulp stem cells (DPSCs) are multipotent progenitors for biotechnological practices, but the influences of existing restorations on their viability and differentiation are not well-known. This study was aimed to investigate in vivo and in vitro responses of DPSCs to restorative materials. METHODS: Class I cavities were prepared on molars scheduled to be extracted and then restored with a resin-based composite (RBC), a glass ionomer cement, or zinc oxide eugenol. Intact teeth were used as controls. Twelve molars in each group were extracted on day 7 or day 30 after restorations to assess the early or intermediate pulp responses and were then cut in half. One half was processed for histopathological analysis, and the other was used to isolate DPSCs for a colony-forming unit assay and real-time polymerase chain reaction for NANOG, OCT4, and CD44 expression. RESULTS: All restored teeth showed pulp damage at various levels, whereas mild to moderate inflammation persisted in the RBC group until day 30. The existence of DPSCs in the pulp cores of all groups was revealed based on CD44 immunoreactivity. Glass ionomer cement and zinc oxide eugenol did not affect the relative percentages of DPSCs in either early or intermediate stages, whereas RBCs reduced the percentage. The colony-forming units in all restoration groups were comparable with those in the control. Nevertheless, the restorations significantly enhanced OCT4 expression, especially in RBC/day 30. CONCLUSIONS: Dental restorations cause mild pulp damage but do not affect DPSC viability. RBC decreases DPSC densities but might increase the stemness of surviving DPSCs through an inflammation-stimulation process.

Promoting porcelain-zirconia bonding using different atmospheric pressure gas plasmas.

OBJECTIVES: To evaluate the effects of different atmospheric-pressure plasma (APP) on the physicochemical properties of yttria-stabilized zirconia, and promoting the adhesion of veneering porcelain. METHODS: Cercon base zirconia disks were prepared to receive different treatments: as-polished, three APPs (oxygen, OP; argon, AP; and CF4, CP), and grit-blasted (GB). Their surface roughness and hydrophilicity were measured, and surface morphology was examined either after treatments, after simulated porcelain firing, or additional thermal etching. X-ray photoelectron spectroscopy (XPS) analysis characterized the surface chemical compositions. Shear bond strength (SBS) tests examined the adhesion between veneering porcelain and zirconia either before or after thermocycling. The layered ceramic disks were also sectioned to inspect the porcelain-zirconia interfaces. Statistical analysis was performed with one-way ANOVA and post hoc Duncan's test. RESULTS: Grit-blasting caused surface damage and increased roughness. All APP-treated disks exhibited deeper grain boundaries and enlarged grain sizes after thermal etching, while CP disks revealed additional particle dispersions. Three APPs rendered the zirconia surface superhydrophilic. XPS spectra of three APP groups revealed increased hydroxyl groups and reduced C-C contents, and CP group especially showed the existence of Z-F bonds. CP exhibited the highest SBS both before and after thermocycling, while AP and GB also showed improved SBSs compared to the as-polished. OP presented reduced SBS, and its cross-sections showed increased microporosities in the veneering porcelain. SIGNIFICANCE: APP did not change surface morphology but enhanced wettability. CP and AP improved porcelain-zirconia SBSs, primarily through surface hydroxylation. OP induced the microporosities in porcelain and adversely affected the adhesion.

Effects of silane- and MDP-based primers application orders on zirconia-resin adhesion-A ToF-SIMS study.

OBJECTIVE: To evaluate the 3-methacryloyloxypropyltrimethoxysilane (MPS)- and 10-methacryloyloxydecyl-dihydrogen-phosphate (MDP)-base primers, in their single or sequential applications, with regard to modifying zirconia surfaces and improving resin-zirconia adhesion. METHODS: Zirconia disks received different treatments: without primer (Zr), MPS-base primer (S), MDP-base primer (M), MPS/MDP mixture (SMmix), MPS followed by MDP (SM), and MDP followed by MPS (MS). The compositions and chemical interactions of the coatings to zirconia were analyzed using time-of-flight secondary ion mass spectrometry (ToF-SIMS) and reconstructed 3D ion images. Surface wettability of these coatings to water and resin adhesive was assessed. The shear bond strength (SBS) between resin and the treated zirconia was also examined before and after thermocycling. RESULTS: Groups S and MS presented substantial OH- ions in the coatings and zirconia substrate. PO2- and PO3- fragments existed in all MDP-treatment groups with various proportions and distributions, while groups M and SM showed higher proportions of PO3- and the zirconium phosphate related ions. In 3D ion images, PO3- in groups M and SM was denser and segregated to the interface, but was dispersed or overlaid above PO2- in SMmix and MS. All the primers increased the surface wettability to water and resin, with M and SM presenting superhydrophilic surfaces. All MDP-treatment groups showed improved SBS before thermocycling, while M and SM retained higher SBS after this. SIGNIFICANCE: The MDP-base primer shows a relevant function in facilitating POZr bonding and enhancing resin-zirconia bonding. The co-treated MPS impairs the chemical activity of MDP, especially if it is the final coat.

Shrinkage behaviors of dental composite restorations-The experimental-numerical hybrid analysis.

OBJECTIVES: To investigate the effects of light curing protocols on the shrinkage behaviors, contraction stress, and microleakage in composite restorations by an experimental-numerical hybrid analysis. METHODS: Three groups of human molars were collected to receive different light-curing protocols: vertical or oblique curing at regular intensity, and vertical curing at reduced intensity. For each tooth, the composite fillings were consecutively placed under unbonded and bonded states, and their shrinkage behaviors were examined with a digital image correlation (DIC) technique. The strains of the unbonded restorations were input into two finite element analysis (FEA) models with settings of the composite as either homogeneous or hardened along polymerization gradients. The preliminary solutions were verified by their individual deformations in the bonded restorations. The interfacial microleakage of restorations was also determined by micro-CT scanning and compared with the FEA results. RESULTS: The bonded restorations showed centripetal shrinkage patterns with greater downward displacements than their unbonded restorations. Vertical curing at regular intensity caused the greatest shrinkage strain, contraction stress, and microleakage among the three protocols. Low-intensity curing reduced overall shrinkage strain and displacements at cervical margin, but did not prevent the formation of microleakage. Oblique curing caused asymmetric shrinkage with the tooth-shielded side revealing less deformation. Setting the polymerization-dependent elastic moduli of the composite enhanced the reliability of FEA. SIGNIFICANCE: This hybrid analysis comprehensively examined the polymerization shrinkage behaviors. Both the light intensity and direction affect the shrinkages and contraction stress. Oblique curing decreases shrinkage due to the attenuated irradiation by tooth-shielding rather than modulations of shrinkage direction.

Characterization of the elastic and viscoelastic properties of dentin by a nanoindentation creep test.

Dentin is the main supporting structure of teeth, but its mechanical properties may be adversely affected by pathological demineralization. The purposes of this study were to develop a quantitative approach to characterize the viscoelastic properties of dentin after de- and re-mineralization, and to examine the elastic properties using a nanoindentation creep test. Dentin specimens were prepared to receive both micro- and nano-indentation tests at wet and dry states. These tests were repeatedly performed after demineralization (1% citric acid for 3 days) and remineralization (artificial saliva immersion for 28 days). The nanoindentation test was executed in a creep mode, and the resulting displacement-time responses were disintegrated into primary (transient) and secondary (viscous) creep. The structural changes and mineral densities of dentin were also examined under SEM and microCT, respectively. The results showed that demineralization removed superficial minerals of dentin to the depth of 400 µm, and affected its micro- and nano-hardness, especially in the hydrate state. Remineralization only repaired the minerals at the surface layer, and partially recovered the nanohardness. Both the primary the secondary creep increased in the demineralized dentin, while the hydration further enhanced creep deformation of untreated and remineralized dentin. Remineralization reduced the primary creep of dentin, but did not effectively increase the viscosity. In conclusion, water plasticization increases the transient and viscous creep strains of demineralized dentin and reduces load sustainability. The nanoindentation creep test is capable of analyzing the elastic and viscoelastic properties of dentin, and reveals crucial information about creep responses.

Evaluation of dentinal fluid flow behaviours: a fluid-structure interaction simulation.

This study uses the fluid-structure interaction (FSI) method to investigate the fluid flow in dental pulp. First, the FSI method is used for the biomechanical simulation of dental intrapulpal responses during force loading (50, 100 and 150 N) on a tooth. The results are validated by comparison with experimental outcomes. Second, the FSI method is used to investigate an intact tooth subjected to a mechanical stimulus during loading at various loading rates. Force loading (0-100 N) is applied gradually to an intact tooth surface with loading rates of 125, 62.5, 25 and 12.5 N/s, respectively, and the fluid flow changes in the pulp are evaluated. FSI analysis is found to be suitable for examining intrapulpal biomechanics. An external force applied to a tooth with a low loading rate leads to a low fluid flow velocity in the pulp chamber, thus avoiding tooth pain.

An investigation of dentinal fluid flow in dental pulp during food mastication: simulation of fluid-structure interaction.

This study uses fluid-structure interaction (FSI) simulation to investigate the relationship between the dentinal fluid flow in the dental pulp of a tooth and the elastic modulus of masticated food particles and to investigate the effects of chewing rate on fluid flow in the dental pulp. Three-dimensional simulation models of a premolar tooth (enamel, dentine, pulp, periodontal ligament, cortical bone, and cancellous bone) and food particle were created. Food particles with elastic modulus of 2,000 and 10,000 MPa were used, respectively. The external displacement loading (5 µm) was gradually directed to the food particle surface for 1 and 0.1 s, respectively, to simulate the chewing of food particles. The displacement and stress on tooth structure and fluid flow in the dental pulp were selected as evaluation indices. The results show that masticating food with a high elastic modulus results in high stress and deformation in the tooth structure, causing faster dentinal fluid flow in the pulp in comparison with that obtained with soft food. In addition, fast chewing of hard food particles can induce faster fluid flow in the pulp, which may result in dental pain. FSI analysis is shown to be a useful tool for investigating dental biomechanics during food mastication. FSI simulation can be used to predict intrapulpal fluid flow in dental pulp; this information may provide the clinician with important concept in dental biomechanics during food mastication.

Riboflavin-ultraviolet-A-induced collagen cross-linking treatments in improving dentin bonding.

OBJECTIVES: To evaluate the collagen cross-linkers, riboflavin-ultraviolet-A (RF/UVA) and glutaraldehyde, with regard to their efficacy in cross-linking the dentinal collagen and improving dentin bonding. METHODS: Glutaraldehyde and different RF/UVA protocols (0.1%RF/1-minUV, 0.1%RF/2-minUV, and 1%RF/1-minUV) were first evaluated by gel electrophoresis to determine their abilities of collagen cross-linking. The mechanical properties of acid-etched dentin receiving these cross-linking treatments were examined in either dry or wet condition by a nanoindentation test. Fifteen teeth with exposed occlusal dentin received the microtensile bond strength (µTBS) test. The teeth were primed either with RF/UVA or glutaraldehyde, followed by adhesive treatment and composite restorations, and then cut into resin-dentin microbeams. Half of the microbeams received the µTBS test after 24h, and the other half received test after 5000 thermocycles. Nanoleakage at the bond interface was examined under TEM. The alignments of collagen fibrils in the hybrid layers were also defined by an image analysis. RESULTS: Gel electrophoresis showed that glutaraldehyde induced strong collagen gelation, while RF/UVA generated milder collagen cross-linking. Glutaraldehyde, 0.1%RF/2-min-UVA, and 1%RF/1-minUV showed higher stiffness compared to untreated and 0.1%RF/1-minUV in wet condition. All the crosslinking treatments improved early µTBS, but 0.1%RF/2-minUVA treatment maintained high µTBS after theromocycles. Under TEM, glutaraldehyde-treated dentin showed dense and enclosed collagen network on the adhesive interface. 0.1%RF/2-minUVA showed the least nanoleakage, and this could be associated with the suspended collagen fibrils in the hybrid layer. SIGNIFICANCE: 0.1%RF/2-minUVA treatment enhanced resin-dentin bond possibly through enhancing the stiffness and maintaining the expanding collagen matrix in the hybrid layer.

Capillary-tube-based micro-plasma system for disinfecting dental biofilm.

PURPOSE: A low-temperature low-energy capillary-tube-based argon micro-plasma system was applied to disinfect Streptococcus mutans-containing biofilm. MATERIALS AND METHODS: The micro-plasma system uses a hollow inner electrode that is ignited by a radio-frequency power supply with a matching network. The energy content was analyzed using optical emission spectroscopy. The micro-plasma-induced effect on a biofilm cultured for 24 or 48 h with a working distance of ≈3 mm at low temperature was evaluated. The morphologies of the treated live/dead bacteria and the produced polysaccharides after micro-plasma treatment were examined. RESULTS: Scanning electron microscopy images and staining results show that most of the S. mutans on the treated biofilm were acutely damaged within a micro-plasma treatment time of 300 s. CONCLUSIONS: The number of living bacteria underneath the treated biofilm greatly decreased with treatment time. The proposed micro-plasma system can thus disinfect S. mutans on/in biofilms.