Quasi-2D perovskites have attracted much attention in perovskite photovoltaics due to their excellent stability. However, their photoelectric conversion efficiency (PCE) still lags 3D counterparts, particularly with high short-circuit current (JSC) loss. The quantum confinement effect is pointed out to be the sole reason, which introduces widened bandgap and poor exciton dissociation, and undermines the light capture and charge transport. Here, the gradient incorporation of formamidinium (FA) cations into quasi-2D perovskite is proposed to address this issue. It is observed that FA prefers to incorporate into the larger n value phases near the film surface compared to the smaller n value phases in the bulk, resulting in a narrow bandgap and gradient structure within the film. Through charge dynamic analysis using in situ light-dark Kelvin probe force microscopy and transient absorption spectroscopy, it is demonstrated that incorporating 10% FA significantly facilitates efficient charge transfer between low n-value phases in the bulk and high n-value nearby film surface, leading to reduced charge accumulation. Ultimately, the device based on (AA)2(MA0.9FA0.1)4Pb5I16, where AA represents n-amylamine renowned for its exceptional environmental stability as a bulky organic ligand, achieves an impressive power conversion efficiency (PCE) of 18.58% and demonstrates enhanced illumination and thermal stability.
The orthogonal structure of the widely used hole transporting material (HTM) Spiro-OMeTAD imparts isotropic conductivity and excellent film-forming capability. However, inherently weak intra- and inter-molecular π-π interactions result in low intrinsic hole mobility. Herein, a novel arylamine derivative, termed FTPE-ST, with a twist conjugated dibenzo[g,p]chrysene core and coplanar 3,4-ethylenedioxythiophene (EDOT) as extended donor units, was designed to enhance intra- and inter-molecular π-π interactions, without compromising on solubility. The 3D configuration provides the material multi-direction charge transport as well as excellent solubility even in 2-methylanisole (2-MA), and its large conjugated delocalization backbone endows the HTM with a high hole mobility (7.2 × 10-4 cm2V-1s-1). Moreover, the sulfur donors in the EDOT units coordinate to lead ions on the perovskite surface, leading to stronger interfacial interactions and the suppression of defects at the perovskite/HTM interface. As a result, perovskite solar cells (PSCs) employing FTPE-ST as the HTM achieve a champion power conversion efficiency (PCE) of 25.21% with excellent long-time stability, which is one of the highest PCEs for non-spiro HTMs in n-i-p PSCs. In addition, the excellent film-forming capacity of the HTM enables the fabrication of FTPE-ST-based large-scale PSCs (1.0 cm2) and modules (29.0 cm2), which achieve PCEs of 24.21% (certificated 24.17%) and 21.27%, respectively. This article is protected by copyright. All rights reserved.
In perovskite solar cells (PSCs), defects in the interface and mismatched energy levels can damage the device performance. Improving the interface quality is an effective way to achieve efficient and stable PSCs. In this work, a multifunctional dye molecule, named ThPCyAc, was designed and synthesized to be introduced in the perovskite/HTM interface. On one hand, various functional groups on the acceptor unit can act as Lewis base to reduce defect density and suppress nonradiative combinations. On the other hand, the stepwise energy-level alignment caused by ThPCyAc decreases the accumulation of interface carriers for facilitating charge extraction and transmission. Therefore, based on the ThPCyAc molecule, the devices exhibit elevated open-circuit voltage and fill factor, resulting in the best power conversion efficiency (PCE) of 23.16%, outperforming the control sample lacking the interface layer (PCE = 21.49%). Excitingly, when attempting to apply it as a self-assembled layer in inverted devices, ThPCyAc still exhibits attractive behavior. It is worth noting that these results indicate that dye molecules have great potential in developing multifunctional interface materials to obtain higher-performance PSCs.
Cardiovascular disease stands as a leading global cause of mortality. Nucleotide-binding Oligomerization Domain-like Receptor Protein 3 (NLRP3) inflammasome is widely acknowledged as pivotal factor in specific cardiovascular disease progression, such as myocardial infarction, heart failure. Recent investigations underscore a close interconnection between autonomic nervous system (ANS) dysfunction and cardiac inflammation. It has been substantiated that sympathetic nervous system activation and vagus nerve stimulation (VNS) assumes critical roles withinNLRP3 inflammasome pathway regulation, thereby contributing to the amelioration of cardiac injury and enhancement of prognosis in heart diseases. This article reviews the nexus between NLRP3 inflammasome and cardiovascular disorders, elucidating the modulatory functions of the sympathetic and vagus nerves within the ANS with regard to NLRP3 inflammasome. Furthermore, it delves into the potential therapeutic utility of NLRP3 inflammasome to be targeted by VNS. This review serves as a valuable reference for further exploration into the potential mechanisms underlying VNS in the modulation of NLRP3 inflammasome.
Dopant-free hole transporting materials (HTMs) is significant to the stability of perovskite solar cells (PSCs). Here, we developed a novel star-shape arylamine HTM, termed Py-DB, with a pyrene core and carbon-carbon double bonds as the bridge units. Compared to the reference HTM (termed Py-C), the extension of the planar conjugation backbone endows Py-DB with typical intermolecular π-π stacking interactions and excellent solubility, resulting in improved hole mobility and film morphology. In addition, the lower HOMO energy level of the Py-DB HTM provides efficient hole extraction with reduced energy loss at the perovskite/HTM interface. Consequently, an impressive power conversion efficiency (PCE) of 24.33 % was achieved for dopant-free Py-DB-based PSCs, which is the highest PCE for dopant-free small molecular HTMs in n-i-p configured PSCs. The dopant-free Py-DB-based device also exhibits improved long-term stability, retaining over 90 % of its initial efficiency after 1000â h exposure to 25 % humidity at 60 °C. These findings provide valuable insights and approaches for the further development of dopant-free HTMs for efficient and reliable PSCs.
Perovskite solar cells (PSCs) are among the most promising photovoltaic technologies owing to their exceptional optoelectronic properties1,2. However, the lower efficiency, poor stability and reproducibility issues of large-area PSCs compared with laboratory-scale PSCs are notable drawbacks that hinder their commercialization3. Here we report a synergistic dopant-additive combination strategy using methylammonium chloride (MACl) as the dopant and a Lewis-basic ionic-liquid additive, 1,3-bis(cyanomethyl)imidazolium chloride ([Bcmim]Cl). This strategy effectively inhibits the degradation of the perovskite precursor solution (PPS), suppresses the aggregation of MACl and results in phase-homogeneous and stable perovskite films with high crystallinity and fewer defects. This approach enabled the fabrication of perovskite solar modules (PSMs) that achieved a certified efficiency of 23.30% and ultimately stabilized at 22.97% over a 27.22-cm2 aperture area, marking the highest certified PSM performance. Furthermore, the PSMs showed long-term operational stability, maintaining 94.66% of the initial efficiency after 1,000 h under continuous one-sun illumination at room temperature. The interaction between [Bcmim]Cl and MACl was extensively studied to unravel the mechanism leading to an enhancement of device properties. Our approach holds substantial promise for bridging the benchtop-to-rooftop gap and advancing the production and commercialization of large-area perovskite photovoltaics.
Perovskite solar cells with the formula FA1-xCsxPbI3, where FA is formamidinium, provide an attractive option for integrating high efficiency, durable stability and compatibility with scaled-up fabrication. Despite the incorporation of Cs cations, which could potentially enable a perfect perovskite lattice1,2, the compositional inhomogeneity caused by A-site cation segregation is likely to be detrimental to the photovoltaic performance of the solar cells3,4. Here we visualized the out-of-plane compositional inhomogeneity along the vertical direction across perovskite films and identified the underlying reasons for the inhomogeneity and its potential impact for devices. We devised a strategy using 1-(phenylsulfonyl)pyrrole to homogenize the distribution of cation composition in perovskite films. The resultant p-i-n devices yielded a certified steady-state photon-to-electron conversion efficiency of 25.2% and durable stability.
Perovskite crystal facets greatly impact the performance and stability of their corresponding photovoltaic devices. Compared to the (001) facet, the (011) facet yields better photoelectric properties, including higher conductivity and enhanced charge carrier mobility. Thus, achieving (011) facet-exposed films is a promising way to improve device performance. However, the growth of (011) facets is energetically unfavorable in FAPbI3 perovskites due to the influence of methylammonium chloride additive. Here, 1-butyl-4-methylpyridinium chloride ([4MBP]Cl) was used to expose (011) facets. The [4MBP]+ cation selectively decreases the surface energy of the (011) facet enabling the growth of the (011) plane. The [4MBP]+ cation causes the perovskite nuclei to rotate by 45° such that (011) crystal facets stack along the out-of-plane direction. The (011) facet has excellent charge transport properties and can achieve better-matched energy level alignment. In addition, [4MBP]Cl increases the activation energy barrier for ion migration, suppressing decomposition of the perovskite. As a result, a small-size device (0.06 cm2) and a module (29.0 cm2) based on exposure of the (011) facet achieved power conversion efficiencies of 25.24% and 21.12%, respectively.
All-inorganic CsPbI3 perovskite solar cells (PSCs) with efficiencies exceeding 20% are ideal candidates for application in large-scale tandem solar cells. However, there are still two major obstacles hindering their scale-up: (i) the inhomogeneous solid-state synthesis process and (ii) the inferior stability of the photoactive CsPbI3 black phase. Here, we have used a thermally stable ionic liquid, bis(triphenylphosphine)iminium bis(trifluoromethylsulfonyl)imide ([PPN][TFSI]), to retard the high-temperature solid-state reaction between Cs4PbI6 and DMAPbI3 [dimethylammonium (DMA)], which enables the preparation of high-quality and large-area CsPbI3 films in the air. Because of the strong Pb-O contacts, [PPN][TFSI] increases the formation energy of superficial vacancies and prevents the undesired phase degradation of CsPbI3. The resulting PSCs attained a power conversion efficiency (PCE) of 20.64% (certified 19.69%) with long-term operational stability over 1000 hours. A record efficiency of 16.89% for an all-inorganic perovskite solar module was achieved, with an active area of 28.17 cm2.
Hole transport materials (HTMs) are a key component of perovskite solar cells (PSCs). The small molecular 2,2',7,7'-tetrakis(N,N-di-p-methoxyphenyl)-amine-9,9'-spirobifluorene (spiro-OMeTAD, termed "Spiro") is the most successful HTM used in PSCs, but its versatility is imperfect. To improve its performance, we developed a novel spiro-type HTM (termed "DP") by substituting four anisole units on Spiro with 4-methoxybiphenyl moieties. By extending the π-conjugation of Spiro in this way, the HOMO level of the HTM matches well with the perovskite valence band, enhancing hole mobility and increasing the glass transition temperature. DP-based PSC achieves high power conversion efficiencies (PCEs) of 25.24 % for small-area (0.06â cm2 ) devices and 21.86 % for modules (designated area of 27.56â cm2 ), along with the certified efficiency of 21.78 % on a designated area of 27.86â cm2 . The encapsulated DP-based devices maintain 95.1 % of the initial performance under ISOS-L-1 conditions after 2560â hours and 87 % at the ISOS-L-3 conditions over 600â hours.
The development of stable and efficient hole-transporting materials (HTMs) is critical for the commercialization of perovskite solar cells (PSCs). Herein, a novel spiro-type HTM was designed and synthesized where N-ethylcarbazole-terminated groups fully substituted the methoxy group of spiro-OMeTAD, named spiro-carbazole. The developed molecule exhibited a lower highest occupied molecular orbital level, higher hole mobility, and extremely high glass transition temperature (Tg =196 °C) compared with spiro-OMeTAD. PSCs with the developed molecule exhibited a champion power conversion efficiency (PCE) of 22.01 %, which surpassed traditional spiro-OMeTAD (21.12 %). Importantly, the spiro-carbazole-based device had dramatically better thermal, humid, and long-term stability than spiro-OMeTAD.
Despite the remarkable progress in power conversion efficiency of perovskite solar cells, going from individual small-size devices into large-area modules while preserving their commercial competitiveness compared with other thin-film solar cells remains a challenge. Major obstacles include reduction of both the resistive losses and intrinsic defects in the electron transport layers and the reliable fabrication of high-quality large-area perovskite films. Here we report a facile solvothermal method to synthesize single-crystalline TiO2 rhombohedral nanoparticles with exposed (001) facets. Owing to their low lattice mismatch and high affinity with the perovskite absorber, their high electron mobility and their lower density of defects, single-crystalline TiO2 nanoparticle-based small-size devices achieve an efficiency of 24.05% and a fill factor of 84.7%. The devices maintain about 90% of their initial performance after continuous operation for 1,400 h. We have fabricated large-area modules and obtained a certified efficiency of 22.72% with an active area of nearly 24 cm2, which represents the highest-efficiency modules with the lowest loss in efficiency when scaling up.
Organic halide salt passivation is considered to be an essential strategy to reduce defects in state-of-the-art perovskite solar cells (PSCs). This strategy, however, suffers from the inevitable formation of in-plane favored two-dimensional (2D) perovskite layers with impaired charge transport, especially under thermal conditions, impeding photovoltaic performance and device scale-up. To overcome this limitation, we studied the energy barrier of 2D perovskite formation from ortho-, meta- and para-isomers of (phenylene)di(ethylammonium) iodide (PDEAI2) that were designed for tailored defect passivation. Treatment with the most sterically hindered ortho-isomer not only prevents the formation of surficial 2D perovskite film, even at elevated temperatures, but also maximizes the passivation effect on both shallow- and deep-level defects. The ensuing PSCs achieve an efficiency of 23.9% with long-term operational stability (over 1000 h). Importantly, a record efficiency of 21.4% for the perovskite module with an active area of 26 cm2 was achieved.
The emerging CsPbI3 perovskites are highly efficient and thermally stable materials for wide-band gap perovskite solar cells (PSCs), but the doped hole transport materials (HTMs) accelerate the undesirable phase transition of CsPbI3 in ambient. Herein, a dopant-free D-π-A type HTM named CI-TTIN-2F has been developed which overcomes this problem. The suitable optoelectronic properties and energy-level alignment endow CI-TTIN-2F with excellent charge collection properties. Moreover, CI-TTIN-2F provides multisite defect-healing effects on the defective sites of CsPbI3 surface. Inorganic CsPbI3 PSCs with CI-TTIN-2F HTM feature high efficiencies up to 15.9 %, along with 86 % efficiency retention after 1000â h under ambient conditions. Inorganic perovskite solar modules were also fabricated that exhibiting an efficiency of 11.0 % with a record area of 27â cm2 . This work confirms that using efficient dopant-free HTMs is an attractive strategy to stabilize inorganic PSCs for their future scale-up.
Perovskite solar cells (PSCs) emerging as a promising photovoltaic technology with high efficiency and low manufacturing cost have attracted the attention from all over the world. Both the efficiency and stability of PSCs have increased steadily in recent years, and the research on reducing lead leakage and developing eco-friendly lead-free perovskites pushes forward the commercialization of PSCs step by step. This review summarizes the main progress of PSCs in 2020 and 2021 from the aspects of efficiency, stability, perovskite-based tandem devices, and lead-free PSCs. Moreover, a brief discussion on the development of PSC modules and its challenges toward practical application is provided.
A series of hole transporting materials (HTMs) with fused tetraphenylethylene cores (9,9'-bifluorenylidene and dibenzo[g,p]chrysene) as well as different substitution positions of arylamine side arms has been designed and synthesized. A reference HTM with a non-fused tetraphenylethylene core is also prepared for a comparative study. It is noted that fused tetraphenylethylene molecules show a bathochromic spectral shift, electronegative character, and lower reorganization energies than the non-fused ones. Furthermore, the molecules with side arms located on the meta-position on the tetraphenylethylene core in terms of a double bond exhibit a deeper highest occupied molecular orbital level than those of the para-position-based ones whether tetraphenylethylene is fused or not. Moreover, the reorganization energies of fused meta-position-based HTMs are lower than those of para-position-based HTMs. Fused tetraphenylethylene HTMs own a better hole-extraction capability than the non-fused ones. When used in perovskite solar cells, all devices with fused tetraphenylethylene HTMs display better performance than those of the non-fused ones. The HTMs based on dibenzo[g,p]chrysene exhibit better performance than those of bifluorenylidene. Moreover, the devices with HTMs with side arms located on the meta-position on the tetraphenylethylene core display higher power conversion efficiency than those of the para-position-based ones. The results give some new insight and reference to develop ideal HTMs for perovskite solar cells.
The developed ammonium salt-containing hole transporting material could passivate perovskite defects and transport holes, and exhibits better performance compared with the non-ammonium salt counterpart.
The tandem pn-type dye-sensitized solar cells (pn-DSCs) have received much attention in the field of photovoltaic technologies because of their great potential to overcome the Shockley-Queisser efficiency limitation that applies to single junction photovoltaic devices. However, factors governing the short-circuit current densities (Jsc) of pn-DSC remain unclear. It is typically believed that Jsc of the pn-DSC is limited to the highest one that the two independent photoelectrodes can achieve. In this paper, however, we found that the available Jsc of pn-DSC is always determined by the larger Jsc that the photoanode can achieve but not by the smaller one in the photocathode. Such experimental findings were verified by a simplified series circuit model, which shows that a breakdown will occur on the photocathode when the photocurrent goes considerably beyond its threshold voltage, thus leading to an abrupt increase in Jsc of the circuit. The simulation results also suggest that a higher photoconversion efficiency of the pn-DSCs can be only achieved when an almost equivalent photocurrent is achieved for the two photoelectrodes.
The emerging inorganic CsPbI3 perovskites are promising wide-bandgap materials for application in tandem solar cells, but they tend to transit from a black α phase to a yellow δ phase in ambient conditions. Herein, a gradient grain-sized (GGS) CsPbI3 bilayer is developed to stabilize the α phase via a single-step film deposition process. The spontaneously upward migration of (adamantan-1-yl)methanammonium (ADMA) based on the hot-casting technique causes self-assembly of the hierarchical morphology for the perovskite layers. Due to the strong steric effect of the surficial ADMA cation, a self-assembly tiny grain-sized CsPbI3 layer is in situ formed at the surface site, which exhibits notably enhanced phase stability by its high surface energy. Meanwhile, a large grain-sized CsPbI3 layer is obtained at the bottom site with high charge mobility and low trap density of states, which benefits from the regulated growth rates by the interaction between ADMA and perovskites. The perovskite solar cell (PSC) based on the GGS CsPbI3 bilayer shows an efficiency of 15.5% and operates stably for 1000 h under ambient conditions. This work confirms that redistributing the surface energy of perovskite films is a facile strategy to stabilize metastable PSCs without the cost of efficiency loss.