RESUMEN
The tandem CO2 hydrogenation to hydrocarbons over mixed metal oxide/zeolite catalysts (OXZEO) is an efficient way of producing value-added hydrocarbons (platform chemicals and fuels) directly from CO2via methanol intermediate in a single reactor. In this contribution, two MAPO-18 zeotypes (M = Mg, Si) were tested and their performance was compared under methanol-to-olefins (MTO) conditions (350 °C, PCH3OH = 0.04 bar, 6.5 gCH3OH h-1 g-1), methanol/CO/H2 cofeed conditions (350 °C, PCH3OH/PCO/PH2 = 1:7.3:21.7 bar, 2.5 gCH3OH h-1 g-1), and tandem CO2 hydrogenation-to-olefin conditions (350 °C, PCO2/PH2 = 7.5:22.5 bar, 1.4-12.0 gMAPO-18 h molCO2-1). In the latter case, the zeotypes were mixed with a fixed amount of ZnO:ZrO2 catalyst, well-known for the conversion of CO2/H2 to methanol. Focus was set on the methanol conversion activity, product selectivity, and performance stability with time-on-stream. In situ and ex situ Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), solid-state nuclear magnetic resonance (NMR), sorption experiments, and ab initio molecular dynamics (AIMD) calculations were performed to correlate material performance with material characteristics. The catalytic tests demonstrated the better performance of MgAPO-18 versus SAPO-18 at MTO conditions, the much superior performance of MgAPO-18 under methanol/CO/H2 cofeeds, and yet the increasingly similar performance of the two materials under tandem conditions upon increasing the zeotype-to-oxide ratio in the tandem catalyst bed. In situ FT-IR measurements coupled with AIMD calculations revealed differences in the MTO initiation mechanism between the two materials. SAPO-18 promoted initial CO2 formation, indicative of a formaldehyde-based decarboxylation mechanism, while CO and ketene were the main constituents of the initiation pool in MgAPO-18, suggesting a decarbonylation mechanism. Under tandem CO2 hydrogenation conditions, the presence of high water concentrations and low methanol partial pressure in the reaction medium led to lower, and increasingly similar, methanol turnover frequencies for the zeotypes. Despite both MAPO-18 zeotypes showing signs of activity loss upon storage due to the interaction of the sites with ambient humidity, they presented a remarkable stability after reaching steady state under tandem reaction conditions and after steaming and regeneration cycles at high temperatures. Water adsorption experiments at room temperature confirmed this observation. The faster activity loss observed in the Mg version is assigned to its harder Mg2+-ion character and the higher concentration of CHA defects in the AEI structure, identified by solid-state NMR and XRD. The low stability of a MgAPO-34 zeotype (CHA structure) upon storage corroborated the relationship between CHA defects and instability.
RESUMEN
This work aims to produce poly(lactic acid) (PLA)/poly(alkylene furanoate)s (PAF)s fiber blends for textile applications and evaluates their microstructural, chemical, thermal, and mechanical properties. The work focuses on two PAFs with very different alkyl chain lengths, i.e., poly(ethylene 2,5-furandicarboxylate) (PEF) and poly(dodecamethylene 2,5-furandicarboxylate) (PDoF), which were blended in solution at various concentrations (in the range 2.5-10 wt %) with PLA, wet spun, and subsequently drawn. Light optical micrographs highlight that PLA/PEF blends present large and concentrate PEF domains, whereas PLA/PDoF blends show small and homogeneously distributed PDoF domains. The blends appear to be immiscible, which is confirmed also by scanning electron microscopy (SEM), Fourier-Transform Infrared (FT-IR) spectroscopy, and differential scanning calorimetry (DSC). Thermogravimetric analysis (TGA) highlights that the addition of the PAFs improves the thermal stability of the fibers. The drawing process, which was carried out at 80 °C with a heat setting step at 95 °C and at three draw ratios, improves the mechanical properties of the fibers upon the addition of the PAFs. The results obtained in this study are promising and may serve as a basis for future investigations on these novel bio-based fiber blends, which can contribute to increase the environmental sustainability of industrial textiles.
