Grinding and chemical mechanical polishing process for micropore x-ray optics fabricated with deep reactive ion etching.

Silicon micropore optics using deep reactive ion etching of silicon wafers has been being developed for future x-ray astronomy missions. Sidewalls of the micropores through a thin wafer with a typical thickness of hundreds of micrometers and a pore width of ∼20 µm are used for x-ray mirrors. However, burr structures observed after etching with a typical height of a few micrometers at the micropore edges are known to significantly reduce x-ray reflectivity. A new grinding and chemical mechanical polishing process is introduced to remove the burr structures. Both sides of the silicon wafer were ground and precisely polished after etching. X-ray reflectivity measurements confirmed an increase of reflectivity by 2-15 times at incident angles of 0.8-0.2 deg. The surface microroughness worsened from 2.0±0.2 nm rms to 7.8-0.8+0.6 nm rms; however, an additional annealing recovered the smooth surface and the estimated surface microroughness was <1.4 nm rms. This new process enables not only removing the burr structures but also choosing a flat part of the sidewalls for better angular resolution.

Pt thermal atomic layer deposition for silicon x-ray micropore optics.

We fabricated a silicon micropore optic using deep reactive ion etching and coated by Pt with atomic layer deposition (ALD). We confirmed that a metal/metal oxide bilayer of Al2O3∼10 nm and Pt ∼20 nm was successfully deposited on the micropores whose width and depth are 20 µm and 300 µm, respectively. An increase of surface roughness of sidewalls of the micropores was observed with a transmission electron microscope and an atomic force microscope. X-ray reflectivity with an Al Kα line at 1.49 keV before and after the deposition was measured and compared to ray-tracing simulations. The surface roughness of the sidewalls was estimated to increase from 1.6±0.2 nm rms to 2.2±0.2 nm rms. This result is consistent with the microscope measurements. Post annealing of the Pt-coated optic at 1000°C for 2 h showed a sign of reduced surface roughness and better angular resolution. To reduce the surface roughness, possible methods such as the annealing after deposition and a plasma-enhanced ALD are discussed.