The development of low-cost and eco-friendly materials for the removal of pollutants from water is one of the main modern challenges. For this purpose, molecularly imprinted polymers were prepared under optimized conditions starting from chitosan (CS), chemically or ionically modified with glycidyl methacrylate (GMA) or itaconic acid (ITA), respectively. 2,4-Dichlorophenoxyacetic acid (2,4-D) was used as a template, obtaining the CS_GMA and CS_ITA series. The influence of the template concentration on the MIPs' (molecularly imprinted polymers) morphology, thermal behaviour and swelling ability, as well as on the 2,4-D removal capacity, were analyzed. The amount of the template used for the imprinting, together with the different permeability of the matrices, were the key factors driving the analyte uptake process. Despite the good performance shown by the non-imprinted CS_GMA sample, the best results were obtained when CS_GMA was imprinted with the highest amount (5%) of template (CS_GMA_5). This system was also more efficient when consecutive adsorption experiments were carried out. In addition, CS_GMA_5 had a desorption efficiency of 90-100% when a low pesticide concentration was used. These findings suggest that the presence of imprinted cavities could be useful in improving the performance of sorbent materials making CS_GMA_5 a possible candidate for 2,4-D removal.
Asunto(s)
Quitosano , Herbicidas , Impresión Molecular , Impresión Molecular/métodos , Polímeros Impresos Molecularmente , Adsorción , Fenoxiacetatos , Ácido 2,4-DiclorofenoxiacéticoRESUMEN
Bioremediation with immobilized enzymes has several advantages, such as the enhancement of selectivity, activity, and stability of biocatalysts, as well as enzyme reusability. Laccase has proven to be a good candidate for the removal of a wide range of contaminants. In this study, naked or modified MnFe2O4 magnetic nanoparticles (MNPs) were used as supports for the immobilization of laccase from Trametes versicolor. To increase enzyme loading and stability, MNPs were coated with chitosan both after the MNP synthesis (MNPs-CS) and during their formation (MNPs-CSin situ). SEM analysis showed different sizes for the two coated systems, 20 nm and 10 nm for MNPs-CS and MNPs-CSin situ, respectively. After covalent immobilization of laccase by glutaraldehyde, the MNPs-CSin situ-lac and MNPs-CS-lac systems showed a good resistance to temperature denaturation and storage stability. The most promising system for use in repeated batches was MNPs-CSin situ-lac, which degraded about 80% of diclofenac compared to 70% of the free enzyme. The obtained results demonstrated that the MnFe2O4-CSin situ system could be an excellent candidate for the removal of contaminants.