The paper describes a comparative study of swelling processes in free-standing graphene oxide (GO) membranes and GO laminates encapsulated with epoxy glue. For free-standing graphene oxide membranes, a huge variation in d-spacing in the range of 8-12 Å depending on the ambient humidity and from 12 to >30 Å depending on the electrolyte type and its concentration was revealed using direct in situ and in operando XRD studies. Limited swelling at various humidity levels as well as in electrolyte solution with low constriction/expansion of epoxy-encapsulated GO is counterposed to that of free-standing graphene oxides. The swelling suppression was explained by both physical constriction and the intercalation of amines into GO laminates, which was proved by local EDX studies. This results in ion diffusivity variation for over 2 orders of magnitude in free-standing and constrained graphene oxide membranes and provides factual evidence for tunable sieving of ions with confined graphene oxides.
RESUMEN
In this study, we report the influence of carbon-based spacer-oxidized derivatives of fullerenes (fullerenols) C60(OH)26−32 and graphene oxide nanoribbons on the performance and pressure stability of graphene-oxide-based composite membranes. The impact of the intercalant shape and composition on the permeance of the selective layers for water vapors has been studied under pressure gradients. It is shown that the insertion of ball-shaped fullerenols between graphene oxide nanoflakes allows a suppression in irreversible permeance loss to 2−4.5% and reversible permeance loss to <25% (at 0.1 MPa), while retaining large H2O/N2 selectivities of up to ~30,000. The demonstrated approach opens avenues for the highly effective stabilization of GO membranes at elevated pressures for industrial-scale dehumidification.