RESUMEN
Ceramics are widely used as implant materials; however, they are brittle and may emit particles when used in these applications. To overcome this disadvantage, alumina foams, which represent a 3D cellular structure comparable to that of human trabecular bone structures, were sputter coated with platinum, tantalum or titanium and modified with fibronectin or collagen type I, components of the extracellular matrix (ECM). To proof the cell material interaction, the unmodified and modified materials were cultured with (a) mesenchymal stem cells being a perfect indicator for biocompatibility and releasing important cytokines of the stem cell niche and (b) with fibroblasts characterized as mediators of inflammation and therefore an important cellular component of the foreign body reaction and inflammation after implantation. To optimize and compare the influence of metal surfaces on cellular behavior, planar glass substrates have been used. Identified biocompatible metal surface of platinum, titanium and tantalum were sputtered on ceramic foams modified with the above-mentioned ECM components to investigate cellular behavior in a 3D environment. The cellular alumina support was characterized with respect to its cellular/porous structure and niche accessibility and coating thickness of the refractory metals; the average cell size was 2.3 mm, the average size of the cell windows was 1.8 mm, and the total foam porosity was 91.4%. The Pt, Ti and Ta coatings were completely dense covering the entire alumina foam surface. The metals titanium and tantalum were colonized very well by the stem cells without a coating of ECM components, whereas the fibroblasts preferred components of the ECM on the alumina foam surface.
RESUMEN
Alloys in the V-Si-B system are a new and promising class of light-weight refractory metal materials for high temperature applications. Presently, the main attention is focused on three-phase alloy compositions that consist of a vanadium solid solution phase and the two intermetallic phases V3Si and V5SiB2. Similar to other refractory metal alloys, a major drawback is the poor oxidation resistance. In this study, initial pack-cementation experiments were performed on commercially available pure vanadium and a three-phase alloy V-9Si-5B to achieve an oxidation protection for this new type of high temperature material. This advance in oxidation resistance now enables the attractive mechanical properties of V-Si-B alloys to be used for high temperature structural applications.
RESUMEN
The present study reports on the microstructural evolution and room temperature plasticity of V(Si)B alloys with respect to the V solid solution (VSS)V3B2 phase region. To investigate the occurring effects systematically, different binary VB and ternary VSiB alloys were produced by conventional arc melting. Scanning electron microscope (SEM) analyses and X-ray diffraction (XRD) measurements were used to characterize the resulting as-cast microstructures. For the first time, the eutectic composition was systematically traced from the binary VB domain to the ternary VSiB system. The observations discover that the binary eutectic trough (VSSV3B2) seems to reach into the ternary system up to an alloy composition of V5Si9B. Room temperature compression tests were carried out in order to study the impact of single-phase and multi-phase microstructures on the strength and plasticity of binary and ternary alloys. The results indicate that the VSS phase controls the plastic deformability in the VSSV3B2 eutectic microstructure whereas the intermetallic V3B2 acts as a strong hardening phase.