Conversion of waste cork to N-doped porous carbons by urea-assisted hydrothermal method for enhanced VOC capture.

Converting waste resources into porous carbon for pollutants capture is an effective strategy to achieve the environmental goal of "treating waste with waste". Cork is an ideal precursor of porous carbons due to its ordered honeycomb-like cell structure and layered composition distribution. Herein, N-doped porous carbons (PCs) were prepared via two steps of urea-assisted hydrothermal carbonization and chemical activation to mitigate volatile organic compounds (VOCs) pollution. Results indicated that the obtained PC4-800 exhibited remarkable features for adsorption including high total pore volume (0.97 cm3/g) and specific surface area (1864.89 m2/g), as well as abundant N-containing functional groups. The excellent pore structure was primarily owing to the corrosion of the carbon matrix by the gas produced from the reaction of K2CO3 and N-containing functional groups. The adsorption results showed that the PC4-800 have an outstanding toluene adsorption capacity (867.03 mg/g) that outperforming majority of adsorbents previously reported. There are substantial pores in N-doped PCs with a pore width of 1.71-2.28 nm, which is 3 to 4 times the molecular dynamic diameter of toluene, and plays a crucial role in the absorption process. Moreover, the promotional influence of N-functional groups on the toluene adsorption process was verified through DFT calculation by Gaussian imitating, where N-6 generated π-electron enrichment sites on the surface of N-doped PCs, facilitating π-π dispersion with the benzene ring in toluene. This study provides a new strategy to convert waste cork into high-performance adsorbents for VOCs removal.

Honeycomb-like cork activated carbon with ultra-high adsorption capacity for anionic, cationic and mixed dye: Preparation, performance and mechanism.

Herein, the cork activated carbon (CAC) with excellent adsorption performance for cationic dye, anionic dye, and mixed dye was obtained by a two-step pyrolysis method. The CAC exhibits a fluffy honeycomb structure consisted of porous carbon nanosheets (100-200 nm), ultra-high specific surface area (3402.68 m2/g), and well-developed hierarchical porous structure, which offers a great deal of adsorption sites and transport channels to dye molecules. The adsorption process of all the dyes onto CAC is better described by Langmuir isotherm model and pseudo-2nd-order kinetic model. The CAC shows ultra-high adsorption capacity for methylene blue (1283.99 mg/g), rhodamine B (4067.57 mg/g), methyl orange (2666.2 mg/g), and congo red (8920.61 mg/g), with an extremely low equilibrium adsorption time (∼10 min). Collectively, this study demonstrated the potential of converting waste cork into high value-added adsorbent for the efficient purification of dye wastewater.