Establishment of a clinically relevant large animal model to assess the healing of metaphyseal bone.

Despite the high incidence of metaphyseal bone fractures in patients, the mechanisms underlying the healing processes are poorly understood due to the lack of suitable experimental animal models. Hence, the present study was conducted to establish and characterise a clinically relevant large-animal model for metaphyseal bone healing. Six female adult Merino sheep underwent full wedge-shaped osteotomy at the distal left femur metaphysis. The osteotomy was stabilised internally with a customised anatomical locking titanium plate that allowed immediate post-operative full-weight bearing. Bone healing was evaluated at 12 weeks post-fracture relative to the untouched right femur. Histological and quantitative micro-computed tomography results revealed an increased mineralised bone mass with a rich bone microarchitecture. New trabeculae healed by direct intramembranous ossification, without callus and cartilaginous tissue formation. Stiffness at the cortical and trabecular regions was comparable in both groups. Functional morphological analysis of the osteocyte lacunae revealed regularly arranged spherically shaped lacunae along with the canalicular network. Bone surface biochemical analysis using time-of-flight secondary-ion mass spectrometry showed high and homogeneously distributed levels of calcium and collagenous components. Ultrastructure imaging of the new trabeculae revealed a characteristic parallel arrangement of the collagen fibrils, evenly mineralised by the dense mineral substance. The specialised bone cells were also characterised by their unique structural features. Bone remodelling in the fractured femur was evident in the higher expression levels of prominent bone formation and resorption genes. In conclusion, the novel metaphyseal fracture model is beneficial for studying healing and treatment options for the enhancement of metaphyseal bone defects.

Analysis of microscopic bone properties in an osteoporotic sheep model: a combined biomechanics, FE and ToF-SIMS study.

The present study deals with the characterization of bone quality in a sheep model of postmenopausal osteoporosis. Sheep were sham operated ( n = 7), ovariectomized ( n = 6), ovariectomized and treated with deficient diet ( n = 8) or ovariectomized, treated with deficient diet and glucocorticoid injections ( n = 7). The focus of the study is on the microscopic properties at tissue level. Microscopic mechanical properties of osteoporotic bone were evaluated by a combination of biomechanical testing and mathematical modelling. Sample stiffness and strength were determined by compression tests and finite-element analysis of stress states was conducted. From this, an averaged microscopic Young's modulus at tissue level was determined. Trabecular structure as well as mineral and collagen distribution in samples of sheep vertebrae were analysed by micro-computed tomography and time-of-flight secondary ion mass spectrometry. In the osteoporotic sheep model, a disturbed fibril structure in the triple treated group was observed, but bone loss only occurred in form of reduced trabecular number and thickness and cortical decline, while quality of the residual bone was preserved. The preserved bone tissue properties in the osteoporotic sheep model allowed for an estimation of bone strength which behaves similar to the human case.

A novel and easy-to-prepare strontium(II) modified calcium phosphate bone cement with enhanced mechanical properties.

The aim of this study was to evaluate two different approaches to obtaining strontium-modified calcium phosphate bone cements (SrCPCs) without elaborate synthesis of Sr-containing calcium phosphate species as cement precursors that could release biologically effective doses of Sr(2+) and thus could improve the healing of osteoporotic bone defects. Using strontium carbonate as a strontium(II) source, it was introduced into a hydroxyapatite-forming cement either by the addition of SrCO3 to an α-tricalcium phosphate-based cement precursor mixture (A-type) or by substitution of CaCO3 by SrCO3 during precursor composition (S-type). The cements, obtained after setting in a water-saturated atmosphere, contained up to 2.2at.% strontium in different distribution patterns as determined by time-of-flight secondary ion mass spectrometry and energy-dispersive X-ray spectroscopy. The setting time of CPC and A-type cements was in the range of 6.5-7.5min and increased for substitution-type cements (12.5-13.0min). Set cements had an open porosity between 26 and 42%. Compressive strength was found to increase from 29MPa up to 90% in substituted S-type cements (58MPa). SrCPC samples released between 0.45 and 1.53mgg(-1) Sr(2+) within 21days and showed increased radiopacity. Based on these findings, the SrCPC developed in this study could be beneficial for the treatment of defects of systemically impaired (e.g. osteoporotic) bone.