RESUMEN
In this study, the deoxidation process for off-grade titanium (Ti) sponge using magnesium (Mg) metal with a wire mesh strainer type of crucible was developed. Ti hydride (TiH2) feedstock, which was prepared by hydrogenating off-grade Ti sponge, was deoxidized using Mg in a molten magnesium chloride-potassium chloride salt at 933 K under an argon and 20% hydrogen (H2) mixed gas atmosphere. After deoxidation, the residual Mg-containing salt was separated in situ from the crucible to investigate the feasibility of minimizing salt loss during the leaching and production of pure TiH2. The results showed that the presence of residual Mg-containing salt inside the crucible strongly influenced whether a mixture of Ti and TiH2 or pure TiH2 was produced. When the salt was not sufficiently separated, a mixture of Ti and TiH2 was obtained and its oxygen (O) concentration was 0.121 mass% under certain conditions. Meanwhile, pure TiH2 was obtained by increasing the H2 gas flow rate during deoxidation. Therefore, these results demonstrate that the decrease of O concentration to below 0.180 mass% and the minimal loss of the salt are feasible.
RESUMEN
The mechanically-enhanced urea-formaldehyde (UF) microcapsules are developed through a multi-step in situ polymerization method. Optical microscope (OM) and field emission scanning electron microscope (FE-SEM) prove that the microcapsules, 147.4 µm in diameter with a shell thickness of 600 nm, are well-formed. From 1H-nuclear magnetic resonance (1H-NMR) analysis, we found that dicyclopentadiene (DCPD), a self-healing agent encapsulated by the microcapsules, occupies ca. 40.3 %(v/v) of the internal volume of a single capsule. These microcapsules are mixed with EPDM (ethylene-propylene-diene-monomer) and Grubbs' catalyst via a solution mixing method, and universal testing machine (UTM) tests show that the composites with mechanically-enhanced microcapsules has ca. 47% higher toughness than the composites with conventionally prepared UF microcapsules, which is attributed to the improved mechanical stability of the microcapsule. When the EPDM/microcapsule rubber composites are notched, Fourier-transform infrared (FT-IR) spectroscopy shows that DCPD leaks from the broken microcapsule to the damaged site and flows to fill the notched valley, and self-heals as it is cured by Grubbs' catalyst. The self-healing efficiency depends on the capsule concentration in the EPDM matrix. However, the self-healed EPDM/microcapsule rubber composite with over 15 wt% microcapsule shows an almost full recovery of the mechanical strength and 100% healing efficiency.