Contribution of the Sub-Surface to Electrocatalytic Activity in Atomically Precise La0.7 Sr0.3 MnO3 Heterostructures.

Electrocatalytic reactions are known to take place at the catalyst/electrolyte interface. Whereas recent studies of size-dependent activity in nanoparticles and thickness-dependent activity of thin films imply that the sub-surface layers of a catalyst can contribute to the catalytic activity as well, most of these studies consider actual modification of the surfaces. In this study, the role of catalytically active sub-surface layers was investigated by employing atomic-scale thickness control of the La0.7 Sr0.3 MnO3 (LSMO) films and heterostructures, without altering the catalyst/electrolyte interface. The activity toward the oxygen evolution reaction (OER) shows a non-monotonic thickness dependence in the LSMO films and a continuous screening effect in LSMO/SrRuO3 heterostructures. The observation leads to the definition of an "electrochemically-relevant depth" on the order of 10 unit cells. This study on the electrocatalytic activity of epitaxial heterostructures provides new insight in designing efficient electrocatalytic nanomaterials and core-shell architectures.

Regulating Te Vacancies through Dopant Balancing via Excess Ag Enables Rebounding Power Factor and High Thermoelectric Performance in p-Type PbTe.

Thermoelectric properties are frequently manipulated by introducing point defects into a matrix. However, these properties often change in unfavorable directions owing to the spontaneous formation of vacancies at high temperatures. Although it is crucial to maintain high thermoelectric performance over a broad temperature range, the suppression of vacancies is challenging since their formation is thermodynamically preferred. In this study, using PbTe as a model system, it is demonstrated that a high thermoelectric dimensionless figure of merit, zT ≈ 2.1 at 723 K, can be achieved by suppressing the vacancy formation via dopant balancing. Hole-killer Te vacancies are suppressed by Ag doping because of the increased electron chemical potential. As a result, the re-dissolution of Na2 Te above 623 K can significantly increase the hole concentration and suppress the drop in the power factor. Furthermore, point defect scattering in material systems significantly reduces lattice thermal conductivity. The synergy between defect and carrier engineering offers a pathway for achieving a high thermoelectric performance by alleviating the power factor drop and can be utilized to enhance thermoelectric properties of thermoelectric materials.