Weakly solvated EC-free linear alkyl carbonate electrolytes for Ni-rich cathode in rechargeable lithium battery.

Ethylene carbonate (EC) in the electrolyte is not stable in cells operated at high voltage (≥4.4V) or with Li metal anode, which greatly reduce the energy density and lifetime of the rechargeable lithium battery. Herein, an EC-free linear alkyl carbonate-based electrolyte is developed, which enables the high-voltage (≥4.4V) and low-temperature (-30°C) application of Ni-rich cathode (LiNi0.8Mn0.1Co0.1O2, NCM811). The EC-free system, consisting of LiPF6 and LiNO3 in ternary linear alkyl carbonates, possesses low viscosity, weakly solvated structure, and high interfacial stability with both the Ni-rich cathode and the Li metal anode to avoid continuous electrode/electrolyte side reactions and metal dissolution from the cathode. As a result, the Li||NCM811 cell delivers remarkable capacity retention of 93 ± 0.5% at the voltage of 4.4V and 88 ± 0.6% at 4.5V over 100 cycles. This study provides very encouraging perspective to develop EC-free carbonate-based electrolyte for high-voltage and low-temperature application in high-energy-density rechargeable lithium batteries.

Facile Electroless Plating Method to Fabricate a Nickel-Phosphorus-Modified Copper Current Collector for a Lean Lithium-Metal Anode.

The compatibility of current collectors with reactive Li is key to inducing stable Li cycling and prolonged cycle life of lean Li-metal batteries. Herein, a thin and uniform layer of Ni-P complex was built on the surface of a Cu current collector (NiP@Cu) via an efficient, controllable, and cost-effective electroless plating method. The thickness, morphology, composition, and roughness of the Ni-P deposition were successfully regulated. Lithiophilicity of the current collector was greatly improved by Ni-P deposition, which effectively reduced the Li nucleation overpotential and suppressed the Li dendrite growth. In addition, NiP@Cu promoted an inorganic LiF/Li3P-rich solid electrolyte interphase to facilitate interfacial charge transfer and eliminate excessive side reactions between Li and the electrolyte. As a result, the Coulombic efficiency of half-cells remained above 98.5% for more than 400 cycles at 0.5 mA/cm2 and 98.2% for more than 250 cycles at 1 mA/cm2. Full cells with NiP@Cu also showed superior performance compared to those with bare Cu. This work proposes a promising surface modification method to develop a stable, dendrite-free, and cost-effective anode current collector for high-energy-density lean Li-metal batteries.