RESUMEN
TiO2 nanocubes were synthesized via hydrolysis condensation of titanium tetra-isopropoxide (TTIP) in aqueous media, followed by hydrothermal treatment with ammonium salts. Various ammonium salts with different alkyl chain such as ammonium hydroxide (NH4OH), tetramethylammonium hydroxide (TMAH), tetraethylammonium hydroxide (TEAH) and tetrabutylammonium hydroxide (TBAH) were investigated. The crystalline phase, shape, and morphology of TiO2 nanocubes were studied by XRD, TEM, and SEM analysis. These TiO2 nanocubes were pure anatase phase and tended to assemble with well-ordered and close-packed domains. Both alkyl chain length of ammonium salts and hydrothermal duration affected the TiO2 nanocube formation process. The ammonium salts with longer alkyl chain formed TiO2 nanocubes in shorter hydrothermal time and offered the smallest particle size. The above TiO2 nanocubes were applied as photoanode materials in N719 anchored dye-sensitized solar cells and one of the cells exhibited the maximum power conversion efficiency of 7.85%.
RESUMEN
The surface modification of the TiO2 photoelectrode film is one of the promising ways to improve the photovoltaic performance of dye-sensitized solar cell (DSSC). In this work for the acid treatment of TiO2 powder, fluorine containing compounds such as trifluoroacetic acid was carried out to enhance the properties of photoanode. In order to investigate the effect of trifluoroacetyl group, the TiO2 nanopowders were also treated with different acids such as acetic acid, nitric acid, hydrochloric acid, and sulfuric acid and their properties were compared. The TiO2 powders treated with both acetic acid and TFA have possessed smooth surface morphologies as well as enhanced particle dispersions with reduced particle sizes. Photoelectrodes prepared for these two kinds of TiO2 powders accommodated high amounts of dye loading and exhibited excellent light transmittance (wavelength region of 400600 nm). Electrochemical impedance spectroscopy analysis showed the smallest radius of the semicircle which indicates the enhanced rate of electron transport for the cell based photoelectrode with trifluoroacetic acid treated TiO2 powder. The solar cell from the untreated TiO2 film showed the power conversion efficiency of 8.86% and the highest efficiency of 9.51% was achieved by the cell fabricated from trifluoroacetic acid treated TiO2 film.
RESUMEN
The vertically orientated TiO2 nanotube array (TNA) decorated with TiO2 nano-particles was successfully fabricated by electrochemically anodizing titanium (Ti) foils followed by Ti-precursor post-treatment and annealing process. The TNA morphology characterized by SEM and TEM was found to be filled with TiO2 nano-particles interior and exterior of the TiO2 nano-tubes after titanium (IV) n-butoxide (TnB) treatment, whereas TiO2 nano-particles were only found inside of TiO2 nano-tubes upon titanium tetrachloride (TiCl4) treatment. The efficiency in TNA-based DSSCs was improved by both TnB and TiCl4 treatment presumably due to the increase of dye adsorption.