Structural, luminescent and in vitro studies of europium-doped soda lime phosphate glasses.

In this article, we have reported the effect of varying concentration of europium (Eu) in (50 - x)% P2 O5 -25% Na2 O-24% CaO-% Eu2 O3 , where x = 1, 3, 5. The glass samples were synthesised via conventional melt-quench method. The impact of europium ion (Eu3+ ) on the structural, optical and luminescent properties of phosphate soda lime glasses has been studied using X-ray diffraction (XRD), Fourier-transformed infrared (FTIR) spectroscopy, ultraviolet-visible spectroscopy, scanning electron microscopy coupled with energy-dispersive spectroscopy and photoluminescent techniques. The amorphous nature of glass samples was confirmed by XRD patterns. FTIR confirmed the presence of various functional groups. The emission spectra of synthesised samples exhibited intense emission peaks corresponding to Eu3+ under excitation at 393 nm. Among all the peaks, the maximum intensity was observed for 5 D0 → 7 F2 transition. Judd-Ofelt (J-O) parameters (Ω2 , Ω4 ) and other radiative parameters such as band width, radiative transition probabilities, stimulated emission cross-sections and branching ratio were determined from emission spectra. The other photometric parameters such as CIE coordinates and colour purity were also determined. Furthermore, cytotoxic studies were carried out on normal cell line human embryonic kidney cells (HEK-293) using MTT assay. Results showed that the prepared samples significantly enhanced growth in glass sample-treated cells as compared to control cells. These findings suggest that synthesised glass samples are biocompatible in nature and have potential for applications in display devices and biomedical research area.

In-vitro bioactivity of silicate-phosphate glasses using agriculture biomass silica.

In the present work, silica extracted from the agricultural waste material; rice husk (RH) was utilized for the synthesis of biocompatible glass of general composition SiO2-P2O5-CaO-MgO-MoO3. In the synthesized glasses P2O5 (5%) and CaO (25%) was kept constant whereas MgO and MoO3 was varied from 10% to 20% and 0% to 5% respectively. The structural, morphological, elemental and functional properties of silica as well as the derived glasses were analyzed by X-Ray Diffraction (XRD), Field Emission Scanning Electron Microscopy (FE-SEM), Energy Dispersive X-ray spectroscopy (EDX) and Fourier Transform Infrared (FTIR) spectroscopy techniques. The effect of MoO3 on the structural and thermal properties of silicate phosphate glasses has been studied in details. The bioactivity of as-synthesized glass samples were further evaluated after immersion in Simulated Body Fluid (SBF) solution which shows bioactive properties thus enabling them to be used as scaffolds in implant materials.