Aliphatic Polybenzimidazoles: Synthesis, Characterization and High-Temperature Shape-Memory Performance.

A series of aliphatic polybenzimidazoles (PBIs) with methylene groups of varying length were synthesized by the high-temperature polycondensation of 3,3'-diaminobenzidine (DAB) and the corresponding aliphatic dicarboxylic acid in Eaton's reagent. The influence of the length of the methylene chain on PBIs' properties was investigated by solution viscometry, thermogravimetric analysis, mechanical testing and dynamic mechanical analysis. All PBIs exhibited high mechanical strength (up to 129.3 ± 7.1 MPa), glass transition temperature (≥200 °C) and thermal decomposition temperature (≥460 °C). Moreover, all of the synthesized aliphatic PBIs possess a shape-memory effect, which is a result of the presence of soft aliphatic segments and rigid bis-benzimidazole groups in the macromolecules, as well as strong intermolecular hydrogen bonds that serve as non-covalent crosslinks. Among the studied polymers, the PBI based on DAB and dodecanedioic acid has high adequate mechanical and thermal properties and demonstrates the highest shape-fixity ratio and shape-recovery ratio of 99.6% and 95.6%, respectively. Because of these properties, aliphatic PBIs have great potential to be used as high-temperature materials for application in different high-tech fields, including the aerospace industry and structural component industries.

Fabrication of Conductive Tissue Engineering Nanocomposite Films Based on Chitosan and Surfactant-Stabilized Graphene Dispersions.

Chitosan (CS)/graphene nanocomposite films with tunable biomechanics, electroconductivity and biocompatibility using polyvinylpyrrolidone (PVP) and Pluronic F108 (Plu) as emulsion stabilizers for the purpose of conductive tissue engineering were successfully obtained. In order to obtain a composite solution, aqueous dispersions of multilayered graphene stabilized with Plu/PVP were supplied with CS at a ratio of CS to stabilizers of 2:1, respectively. Electroconductive films were obtained by the solution casting method. The electrical conductivity, mechanical properties and in vitro and in vivo biocompatibility of the resulting films were assessed in relation to the graphene concentration and stabilizer type and they were close to that of smooth muscle tissue. According to the results of the in vitro cytotoxicity analysis, the films did not release soluble cytotoxic components into the cell culture medium. The high adhesion of murine fibroblasts to the films indicated the absence of contact cytotoxicity. In subcutaneous implantation in Wistar rats, we found that stabilizers reduced the brittleness of the chitosan films and the inflammatory response.

Unsaturated and thiolated derivatives of polysaccharides as functional matrixes for tissue engineering and pharmacology: A review.

This review examines investigations into the functionalization of polysaccharides by substituents containing multiple (CC) bonds and thiol (SH) groups that are prone to (co)polymerization in the presence of thermal, redox and photoinitiators or Michael addition reactions. A comparative analysis of the approaches to grafting the mentioned substituents onto the polysaccharide macromolecules was conducted. The use of the modified polysaccharides for the design of the 3D structures, including for the development of the pore bearing matrixes of cells or scaffolds utilized in regenerative medicine was examined. These modified polymers were also examined toward the design of excipient matrixes in pharmacological compositions, including with controllable release of active pharmaceuticals, as wel as of antibacterial and antifungal agents and others. In addition, a few examples of the use of modified derivatives in other areas are given.

Hydrothermal Synthesis of N-Doped Graphene for Supercapacitor Electrodes.

N-doped graphene based on graphene oxide and 3,3',4,4'-tetraaminodiphenyl oxide (TADPO) was obtained using a one-step hydrothermal process. The resulting materials were fully characterized using elemental analysis, infrared spectroscopy, Raman spectroscopy, thermogravimetric analysis, X-ray diffraction, scanning electron micrographs, and transmission electron microscopy. The findings reveal that benzimidazole rings were formed during the reaction, and the mass content of nitrogen in the obtained material varied from 12.3% to 14.7%, depending on the initial concentration of TADPO. Owing to the redox activity of benzimidazole rings, the new N-doped graphene materials demonstrated a high specific capacitance, reaching 340 F g-1 at 0.1 A g-1, which was significantly higher than that of the sample of reduced graphene oxide obtained under similar conditions without the use of TADPO (169 F g-1 at 0.1 A g-1). The resulting material also exhibited good cyclic stability after 5000 cycles.