Compliant foams can be used to mitigate ground reaction forces. However, it is unknown how foam surfaces influence the modulation of leg muscle activity. Thus, the current study aimed to investigate how the neuromuscular system managed changes in expected loading due to various thickness of foam placed on the landing surface during a step down task. The surface electromyographic signal (sEMG) pre-activation duration and the root mean square (RMS) amplitude of tibialis anterior (TA), lateral gastrocnemius (LG), and vastus medialis (VM) of 10 active females were measured as they stepped-down with a single leg onto polyurethane foam slabs of varying thickness (0-50 mm). Pre-activation duration was not affected by the thickness of the foam padding. LG RMS amplitude was less in the foam conditions than the control (no- foam) condition, with the greatest reduction observed for the 50 mm foam condition. In some trials, the muscles remained active throughout the step-down task. In such instances, a sEMG onset time and thus a pre-activation duration could not be determined. All foam conditions significantly increased the odds of continuous muscle activity above that of the no-foam condition. The results indicate that foam surfaces may alter the modulation of muscle activity during step-down tasks.

Impact properties of thiol-ene networks.

In this study, a series of thiol-ene networks having glass transition temperatures ranging from -30 to 60 °C were synthesized utilizing several multifunctional thiols and two trifunctional alkenes. Thermomechanical properties were determined using dynamic mechanical analysis, and impact properties were determined using pendulum impact and drop impact testing protocols. The impact behavior was found to directly correlate to the glass transition temperature, except when the temperature at which the impact event occurs overlaps with the range of temperatures corresponding to the viscoelastic dissipation regime of the polymer. Additionally, we discuss insight into the spatial limitations of energy dissipation for thiol-ene network polymers and establish a platform for predictability in similar systems.