Carboxylated nanocellulose for wound healing applications - Increase of washing efficiency after chemical pre-treatment and stability of homogenized gels over 10 months.

To commercialize a biomedical product as a medical device, reproducibility of production and time-stability are important parameters. Studies of reproducibility are lacking in the literature. Additionally, chemical pre-treatments of wood fibres to produce highly fibrillated cellulose nanofibrils (CNF) seem to be demanding in terms of production efficiency, being a bottleneck for industrial upscaling. In this study, we evaluated the effect of pH on the dewatering time and washing steps of 2,2,6,6-Tetramethylpiperidinyloxy (TEMPO)-mediated oxidized wood fibres when applying 3.8 mmol NaClO/g cellulose. The results indicate that the method does not affect the carboxylation of the nanocelluloses, and levels of approximately 1390 µmol/g were obtained with good reproducibility. The washing time of a Low-pH sample was reduced to 1/5 of the time required for washing a Control sample. Additionally, the stability of the CNF samples was assessed over 10 months and changes were quantified, the most pronounced were the increase of potential residual fibre aggregates, reduction of viscosity and increase of carboxylic acid content. The cytotoxicity and skin irritation potential were not affected by the detected differences between the Control and Low-pH samples. Importantly, the antibacterial effect of the carboxylated CNFs against S. aureus and P. aeruginosa was confirmed.

Characterization and Antibacterial Properties of Autoclaved Carboxylated Wood Nanocellulose.

Cellulose nanofibrils (CNFs) were obtained by applying a chemical pretreatment consisting of autoclaving the pulp fibers in sodium hydroxide, combined with 2,2,6,6-tetramethylpiperidinyl-1-oxyl-mediated oxidation. Three levels of sodium hypochlorite were applied (2.5, 3.8, and 6.0 mmol/g) to obtain CNF qualities (CNF_2.5, CNF_3.8, and CNF_6.0) with varying content of carboxyl groups, that is, 1036, 1285, and 1593 µmol/g cellulose. The cytotoxicity and skin irritation potential (indirect tests) of the CNFs were determined according to standardized in vitro testing for medical devices. We here demonstrate that autoclaving (121 °C, 20 min), which was used to sterilize the gels, caused a modification of the CNF characteristics. This was confirmed by a reduction in the viscosity of the gels, a morphological change of the nanofibrils, by an increase of the ultraviolet-visible absorbance maxima at 250 nm, reduction of the absolute zeta potential, and by an increase in aldehyde content and reducing sugars after autoclaving. Fourier-transform infrared spectroscopy and wide-angle X-ray scattering complemented an extensive characterization of the CNF gels, before and after autoclaving. The antibacterial properties of autoclaved carboxylated CNFs were demonstrated in vitro (bacterial survival and swimming assays) on Pseudomonas aeruginosa and Staphylococcus aureus. Importantly, a mouse in vivo surgical-site infection model on S. aureus revealed that CNF_3.8 showed pronounced antibacterial effect and performed as good as the antiseptic Prontosan wound gel.

Micro-structural characterisation of homogeneous and layered MFC nano-composites.

The complementary capabilities of various characterisation methods for micro-structural assessment are demonstrated. The assessed structures were composed of unbleached microfibrillated cellulose (MFC) in combination with bleached and 2,2,6,6-tetramethylpiperidinyl-1-oxyl (TEMPO) pre-treated MFC materials. The biodegradable nano-composites were thus characterised in detail, including laser profilometry, scanning electron microscopy (SEM) in high and low vacuum modes, and field-emission SEM. The distribution of the unbleached MFC materials was assessed by staining the unbleached MFC with osmium tetroxide (OsO(4)), which reacts with C=C double bonds encountered in lignin. In addition, some properties of the MFC nano-composite films were tested, i.e. tensile properties, water wettability and oxygen permeability. In general, the group of characteristics of the nano-composite MFC films was better than the properties of the films made of the neat MFC qualities. This indicates that mixing complementary MFC qualities could give synergetic effects that are not exploited completely when using the MFC qualities separately. The study thus confirms the suitability of unbleached MFC materials as a component in multilayer structures, for example biodegradable packaging applications.

Screening analyses of pinosylvin stilbenes, resin acids and lignans in Norwegian conifers.

The content and distribution of stilbenes and resin acids in Scots pine (Pinus sylvestris) and spruce (Picea abies), sampled in central Norway, have been examined. The contents of pinosylvin stilbenes in pine heartwood/living knots were 0.2-2/2-8 %(w/w). No stilbenes could be detected in spruce (Picea abies). The resin acid contents of pine sapwood/heartwood and knots were 1-4 and 5-10 % (w/w), respectively. Minor amounts of resin acids (<0.2/<0.04 %w/w) were identified in spruce wood/knots. The lignan content in knots of Norwegian spruce was 6.5 % (w/w). Diastereomerically pure hydroxymatairesinol (HMR, 84 % of total lignans) was readily isolated from this source since only minor quantities (2.6 % of total lignans) of the allo-HMR diastereomer was detected. Insignificant amounts of lignans were present in the sapwood. Lignans could not be detected in the sapwood or knots of Norwegian sallow (Salix caprea), birch(Betula pendula) or juniper (Juniperus communis).