RESUMEN
Mixed-cation perovskite solar cells (PSCs) have attracted much attention because of the advantages of suitable bandgap and stability. It is still a challenge to rationally design and modify the perovskite/tin oxide (SnO2) heterogeneous interface for achieving highly efficient and stable PSCs. Herein, a strategy of one-stone-for-three-birds is proposed to achieve multi-functional interface regulation via introducing N-Chlorosuccinimide (NCS) into the solution of SnO2: i) CâO functional group in NCS can induces strong binding affinity to uncoordinated defects (oxygen vacancies, free lead ions, etc) at the buried interface and passivate them; ii) incomplete in situ hydrolysis reactions can occur spontaneously and adjust the pH value of the SnO2 solution to achieve a more matchable energy level; iii) effectively releasing the residual stress of the underlying perovskite. As a result, a champion power conversion efficiency (PCE) of 24.74% is achieved with a device structure of ITO/SnO2/Perovskite/Spiro-OMeTAD/Ag, which is one of the highest values for cesium-formamidinium-methylammonium (CsFAMA) triple cation PSCs. Furthermore, the device without encapsulation can sustain 94.6% of its initial PCE after the storage at room temperature and relative humidity (RH) of 20% for 40 days. The research provides a versatile way to manipulate buried interface for achieving efficient and stable PSCs.
RESUMEN
With the rapid rise in perovskite solar cells (PSCs) performance, it is imperative to develop scalable fabrication techniques to accelerate potential commercialization. However, the power conversion efficiencies (PCEs) of PSCs fabricated via scalable two-step sequential deposition lag far behind the state-of-the-art spin-coated ones. Herein, the additive methylammonium chloride (MACl) is introduced to modulate the crystallization and orientation of a two-step sequential doctor-bladed perovskite film in ambient conditions. MACl can significantly improve perovskite film quality and increase grain size and crystallinity, thus decreasing trap density and suppressing nonradiative recombination. Meanwhile, MACl also promotes the preferred face-up orientation of the (100) plane of perovskite film, which is more conducive to the transport and collection of carriers, thereby significantly improving the fill factor. As a result, a champion PCE of 23.14% and excellent long-term stability are achieved for PSCs based on the structure of ITO/SnO2/FA1-xMAxPb(I1-yBry)3/Spiro-OMeTAD/Ag. The superior PCEs of 21.20% and 17.54% are achieved for 1.03 cm2 PSC and 10.93 cm2 mini-module, respectively. These results represent substantial progress in large-scale two-step sequential deposition of high-performance PSCs for practical applications.
RESUMEN
Perovskite solar cells (PSCs) have emerged as one of the most promising and competitive photovoltaic technologies, and doctor-blading is a facile and robust deposition technique to efficiently fabricate PSCs in large scale, especially matching with roll-to-roll process. Herein, it demonstrates the encouraging results of one-step, antisolvent-free doctor-bladed methylammonium lead iodide (CH3 NH3 PbI3, MAPbI3 ) PSCs under a wide range of humidity from 45% to 82%. A synergy strategy of ionic-liquid methylammonium acetate (MAAc) and molecular phenylurea additives is developed to modulate the morphology and crystallization process of MAPbI3 perovskite film, leading to high-quality MAPbI3 perovskite film with large-size crystal, low defect density, and ultrasmooth surface. Impressive power conversion efficiency (PCE) of 20.34% is achieved for doctor-bladed PSCs under the humidity over 80% with a device structure of ITO/SnO2 /MAPbI3 /Spiro-OMeTAD/Ag. It is the highest PCEs for one-step solution-processed MAPbI3 PSCs without antisolvent assistance. The research provides a facile and robust large-scale deposition technique to fabricate highly efficient and stable PSCs under a wide range of humidity, even with the humidity over 80%.
RESUMEN
Perovskite solar cells (PSCs) are being developed rapidly and exhibit greatly potential commercialization. Herein, it is found that the device performance can be improved by manipulating the migration of iodine ions via reverse-biasing, for example, at -0.4 V for 3 min in dark. Characterizations suggest that reverse bias can increase the charge recombination resistance, improve carrier transport, and enhance built-in electric field. Iodine ions including iodine interstitials in perovskites are confirmed to migrate and accumulate at the SnO2 /perovskite interface under reverse-basing, which fill iodine vacancies at the interface and interact with SnO2 . First-principles calculations suggest that the SnO2 /perovskite interface with less iodine vacancies has a stronger interaction and higher charge transfer, leading to larger built-in electric field and improved charge transport. Iodine ions that may pass through the SnO2 /perovskite interface are also confirmed to be able to interact with Sn4+ and passivate oxygen vacancies on the surface of SnO2 . Consequently, an efficiency of 23.48% with the open-circuit voltage (Voc ) of 1.16 V is achieved for PSCs with reverse-biasing, as compared with the initial efficiency of 22.13% with a Voc of 1.10 V. These results are of great significance to reveal the physics mechanism of PSCs under electric field.
RESUMEN
The B-site doped CsPbI3 has been demonstrated to be very promising for photovoltaics owing to its low black phase transition temperature. Though B-site doped black-CsPbI3 perovskites have been successfully achieved by solution-processing, it is unclear whether these systems are available by other methods such as vacuum deposition. In this work, heterovalent doped CsPb1-xBixI3 is targeted. To incorporate Bi3+ into the final film via vacuum deposition, the solid solution precursor Pb1-xBixI2 (0.01 ≤ x ≤ 0.04) is developed. However, these coevaporated films not only are dominated by another hexagonal perovskite phase but also fail to decrease the black phase transition temperature. The role of Bi3+ in the formation of the black phase is further studied by solution methods with different types of precursors. It is demonstrated that the key factor in the low-temperature black phase transition is small grain size, as well as the colloid size within the precursor solution, rather than simple substitution of Pb2+ with Bi3+.
RESUMEN
Flexible perovskite solar cells (f-PSCs) have been attracting tremendous attention due to their potentially commercial prospects in flexible energy system and mobile energy system. Reducing the energy barriers and charge extraction losses at the interfaces between perovskite and charge transport layers is essential to improve both efficiency and stability of f-PSCs. Herein, 4-trifluoromethylphenylethylamine iodide (CF3 PEAI) is introduced to form a 2D perovskite at the interface between perovskite and hole transport layer (HTL). It is found that the 2D perovskite plays a dual-functional role in aligning energy band between perovskite and HTL and passivating the traps in the 3D perovskite, thus reducing energy loss and charge carrier recombination at the interface, facilitating the hole transfer from perovskite to the Spiro-OMeTAD. Consequently, the photovoltaic performance of f-PSCs is significantly improved, leading to a power conversion efficiency (PCE) of 21.1% and a certified PCE of 20.5%. Furthermore, the long-term stability of f-PSCs is greatly improved through the protection of 2D perovskite layer to the underlying 3D perovskite. This work provides an excellent strategy to produce efficient and stable f-PSCs, which will accelerate their potential applications.