Phase-pure crystalline Bi2Se3 and Bi2Te3 nanoparticles are formed in reactions of [C4C1Im]3[Bi3I12] (C4C1Im = 1-butyl-3-methylimidazolium) with [C4C1Pyr][ESiMe3] (E = Se or Te; C4C1Pyr = 1-butyl-1-methylpyrrolidinium) in the ionic liquid (IL) [C4C1Im]I. The resulting crystalline tetradymite-type nanoparticles exhibit stoichiometric Bi:E (E = Se or Te) molar ratios (2:3). Because all synthetic steps were performed under strict inert gas conditions, the surfaces of the Bi2Se3 and Bi2Te3 nanoparticles are free of metal oxide species. As proven by infrared and X-ray photoelectron spectroscopy analyses, the nanoparticle surfaces reveal only minor organic contamination from solvent residues ([C4C1Im]I). The nanomaterials show high Seebeck coefficients of -124 µV K-1 (Bi2Se3) and -155 µV K-1 (Bi2Te3) and feature high electrical conductivities (328 and 946 S cm-1, respectively) at the highest tested temperature (240 °C). The corresponding thermal conductivities (0.8 and 2.3 W m-1 K-1, respectively, at 30 °C) are comparable to those of single crystals and recently reported ab initio calculations, which is in remarkable contrast to typical findings of nanograined bulk materials obtained from compacted nanoparticles. These findings emphasize the low level of impurities, surface contamination, and, in general, defects produced by the synthetic approach reported here. The figure of merit in the in-plane direction of the compacted pellets reached peak values 0.45 for Bi2Se3 and 0.4 for Bi2Te3.
A systematic study on the microwave-assisted thermolysis of the single source precursor (Et2Sb)2Te (1) in different asymmetric 1-alkyl-3-methylimidazolium- and symmetric 1,3-dialkylimidazolium-based ionic liquids (ILs) reveals the distinctive role of both the anion and the cation in tuning the morphology and microstructure of the resulting Sb2Te3 nanoparticles as evidenced by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX), and X-ray photoelectron spectroscopy (XPS). A comparison of the electrical and thermal conductivities as well as the Seebeck coefficient of the Sb2Te3 nanoparticles obtained from different ILs reveals the strong influence of the specific IL, from which C4mimI was identified as the best solvent, on the thermoelectric properties of as-prepared nanosized Sb2Te3. This work provides design guidelines for ILs, which allow the synthesis of nanostructured thermoelectrics with improved performances.