Morphological features of magnetorheological elastomer degradation under a natural weathering environment.

It is well known in the field of materials science that a substance's longevity is significantly influenced by its environment. Everything begins with the initial contact on a material's surface. This influence will then deteriorate and have an extended negative impact on the strength of the material. In this study, the effect of natural weathering in tropical climates on magnetorheological elastomer (MRE) was investigated through microstructural evaluation to understand the aging behavior of the environmentally exposed MRE. To understand and elucidate the process, MREs made of silicone rubber and 70 wt% micron-sized carbonyl iron particles were prepared and exposed to the natural weathering of a tropical climate for 90 days. The MRE samples were then mechanically tensile tested, which revealed that Young's modulus increased, while elongation at break decreased. Surface degradation due to weathering was suspected to be the primary cause of this condition. Using scanning electron microscopy (SEM), the degradation of MRE was investigated as a function of morphological evidence. Upon examination through SEM, it was noted that the weathering effects on the morphology of the exposed samples showed distinct characteristics on the degraded surfaces of the MRE, including numerous microvoids, cavities, and microcracks. While these features were not prominent for the MRE itself, they bear resemblance to the effects observed in similar materials like rubber and elastomer. An atomic force microscope (AFM) is used to investigate the surface topography and local degradation conditions. This observation revealed a distinctive degradation characteristic of the MRE in connection to natural weathering in tropical climates. The surface damage of the MRE samples became severe and inhomogeneous during the environmental aging process, and degradation began from the exposed MRE surface, causing the mechanical characteristics of the MRE to significantly change.

Magnetostriction Enhancement in Midrange Modulus Magnetorheological Elastomers for Sensor Applications.

Magnetorheological elastomer (MRE), which is capable of exhibiting magnetostriction in the presence of a magnetic field, has a great potential to be used for the development of sensor devices. Unfortunately, to date, many works focused on studying low modulus of MRE (less than 100 kPa) which can hamper their potential application in sensors due to short lifespan and low durability. Thus, in this work, MRE with storage modulus above 300 kPa is to be developed to enhance magnetostriction magnitude and reaction force (normal force). To achieve this goal, MREs are prepared with various compositions of carbonyl iron particles (CIPs), in particular, MRE with 60, 70 and 80 wt.% of CIP. It is shown that both the magnetostriction percentage and normal force increment are achieved as the concentration of CIPs increases. The highest magnetostriction magnitude of 0.075% is obtained with 80 wt.% of CIP, and this increment is higher than that of moderate stiffness MRE developed in the previous works. Therefore, the midrange range modulus MRE developed in this work can copiously produce the required magnetostriction value and potentially be implemented for the design of forefront sensor technology.

The effect of salt water ageing on the mechanical and rheological properties of magnetorheological elastomer.

This paper aims to investigate the mechanical and rheological properties of magnetorheological elastomer (MRE) in marine ecosystems. The prepared samples comprised silicone rubber (SR) and 70 wt% micron-sized carbonyl iron particles (CIPs), immersed in an artificial marine ecosystem using salt water (Natrium Chloride) for 30 days. The mechanical properties of MRE samples were evaluated using hardness and quasi-static tensile tests. While the rheometer was used to investigate the rheological properties of their storage modulus condition with magnetic field stimulation. Further analysis of the defects and damages caused by salt water ageing was done through morphological observation using scanning electron microscope (SEM) technology. The results showed that the hardness and tensile strength of MRE samples that were soaked in salt water were affected over time. Lower values of hardness and tensile strength were obtained after 30 days due to the presence of Na+ and Cl-, which acted as an accelerator to the hydrolyzation process of the MRE. The process then, enhanced the water ingress capability into the matrix to cause the molecular changes. Interestingly, for rheological properties, 30 days of salt water ageing allowed the water molecules to move the MRE matrix molecular chains apart, a process known as plasticization and thus increasing the MR effect. Furthermore, morphological evidence was established to determine the MRE changes during salt water ageing. The research findings should greatly contribute to a better understanding of the effect of salt water on the performance of MRE.

Morphological Effects of Strain Localization in the Elastic Region of Magnetorheological Elastomers.

Strain localization is a significant issue that poses interesting research challenges in viscoelastic materials because it is difficult to accurately predict the damage evolution behavior. Over time, the damage mechanism in the amorphous structure of viscoelastic materials leads to subsequent localization into a shear band, gradually jeopardizing the materials' elastic sustainability. The primary goal of this study is to further understand the morphological effects and the role of shear bands in viscoelastic materials precipitated by strain localization. The current study aims to consolidate the various failure mechanisms of a sample and its geometry (surface-to-volume ratio) used in torsional testing, as well as to understand their effects on stress relaxation durability performance. A torsional shear load stress relaxation durability test was performed within the elastic region on an isotropic viscoelastic sample made of silicon rubber and a 70% weight fraction of micron-sized carbonyl iron particles. Degradation was caused by a shear band of localized plasticity that developed microscopically due to stress relaxation durability. The failure pattern deteriorated as the surface-to-volume ratio decreased. A field-emission scanning electron microscope (FESEM) and a tapping-mode atomic force microscope (AFM) were used for further observation and investigation of the sample. After at least 7500 cycles of continuous shearing, the elastic sustainability of the viscoelastic materials microstructurally degraded, as indicated by a decline in stress performance over time. Factors influencing the formation of shear bands were observed in postmortem, which was affected by simple micromanipulation of the sample geometry, making it applicable for practical implementation to accommodate any desired performance and micromechanical design applications.

Natural Weathering Effects on the Mechanical, Rheological, and Morphological Properties of Magnetorheological Elastomer (MRE) in Tropical Climate.

Magnetorheological elastomer (MRE) materials have the potential to be used in a wide range of applications that require long-term service in hostile environments. These widespread applications will result in the emergence of MRE-specific durability issues, where durability refers to performance under in-service environmental conditions. In response, the outdoor tropical climatic environment, combined with the effects of weathering, will be the primary focus of this paper, specifically the photodegradation of the MRE. In this study, MRE made of silicone rubber (SR) and 70 wt% micron-sized carbonyl iron particles (CIP) were prepared and subjected to mechanical and rheological testing to evaluate the effects under natural weathering. Magnetorheological elastomer samples were exposed to the natural weathering conditions of a tropical climate in Kuala Lumpur, Malaysia, for 30 days. To obtain a comprehensive view of MRE degradation during natural weathering, mechanical testing, rheology, and morphological evaluation were all performed. The mechanical and rheological properties test results revealed that after 30 days of exposure and known meteorological parameters, Young's modulus and storage modulus increased, while elongation at break decreased. The degradation processes of MRE during weathering, which are responsible for their undesirable change, were given special attention. With the help of morphological evidence, the relationship between these phenomena and the viscoelastic properties of MRE was comprehensively defined and discussed.

Enhancement of Magneto-Induced Modulus by the Combination of Filler and Plasticizer Additives-Based Magnetorheological Elastomer.

Filler additive is used to provide superior bonding in rubber matrix to enhance the storage modulus of magnetorheological elastomer (MRE). However, the magneto-induced modulus is reduced as the initial storage modulus increases. Therefore, this paper aims to increase the magneto-induced modulus and maintain the initial storage modulus by combining filler and plasticizer additives. Both types of additives have different functions, where cobalt ferrite (CoFe2O4) is capable of enhancing the maximum storage modulus and silicone oil (SO) reduces the initial storage modulus. Thus, four MRE samples have been fabricated using (a) no additive, (b) CoFe2O4, (c) SO, and (d) a combination of CoFe2O4 and SO. The sample's hardness and magnetic properties were investigated via Durometer Shore A and Vibrating Sample Magnetometer (VSM), respectively. Furthermore, the rheological properties of MRE samples in terms of storage modulus were investigated upon the frequency and magnetic field sweep using a rheometer. The results demonstrated that the storage modulus of the MRE samples has increased with increasing the oscillation frequency from 0.1 to 50 Hz. Interestingly, the combination of additives has produced the largest value of magneto-induced modulus of 0.90 MPa as compared to other samples. Furthermore, their initial storage modulus was in between samples with SO (lowest) and without additive (highest). Therefore, fundamental knowledge in adding the combination of additives can offer solutions for a wide range of stiffness in MR device applications such as vibration and noise control devices, sensing devices, and actuators.

Effect of Magnetorheological Grease's Viscosity to the Torque Performance in Magnetorheological Brake.

Recently, magnetorheological grease (MRG) has been utilized in magnetorheological (MR) brakes to generate a braking torque based on the current applied. However, the high initial viscosity of MRG has increased the off-state torque that led to the viscous drag of the brake. Therefore, in this study, the off-state viscosity of MRG can be reduced by the introduction of dilution oil as an additive. Three samples consist of pure MRG (MRG 1) and MRG with different types of dilution oil; hydraulic (MRG 2) and kerosene (MRG 3) were prepared by mixing grease and spherical carbonyl iron particles (CIP) using a mechanical stirrer. The rheological properties in the rotational mode were examined using a rheometer and the torque performances in MR brake were evaluated by changing the current of 0 A, 0.4 A, 0.8 A, and 1.2 A with fixed angular speed. The result shows that MRG 3 has the lowest viscosity which is almost 93% reduction while the viscosity of MRG 2 has lowered to 25%. However, the torque performances generated by MRG 3 were highest, 1.44 Nm, when 1.2 A of current was applied and followed by MRG 2 and MRG 1. This phenomenon indicated that the improvement of torque performances was dependent on the viscosity of MRG. By reducing the viscosity of MRG, the restriction on CIP to form chain formation has also decreased and strengthen the torque of MRG brake. Consequently, the utilization of dilution oil in MRG could be considered in MR brake in near future.

Temperature Dependent on Mechanical and Rheological Properties of EPDM-Based Magnetorheological Elastomers Using Silica Nanoparticles.

Temperature is one of the most influential factors affecting the performance of elastomer matrix in magnetorheological elastomer (MRE). Previous studies have utilized silica as a reinforcing filler in polymer composite and as a coating material in MRE to improve the thermal stability of the base material. However, the usage of silica as an additive in the thermal stability of MRE has not been explored. Thus, in this study, the effect of silica as an additive on the temperature-dependent mechanical and rheological properties of ethylene propylene diene monomer (EPDM)-based MREs was investigated by using 30 wt.% carbonyl iron particles (CIPs) as the main filler, with different contents of silica nanoparticles (0 to 11 wt.%). The microstructure analysis was examined by using field-emission scanning electron microscopy (FESEM), while the thermal characterizations were studied by using a thermogravimetric analyzer and differential scanning calorimetry. The tensile properties were conducted by using Instron Universal Testing Machine in the absence of magnetic field at various temperatures. Meanwhile, the rheological properties were analyzed under oscillatory loadings in the influence of magnetic field, using a rotational rheometer at 25 to 65 °C. The results revealed that the temperature has diminished the interfacial interactions between filler and matrix, thus affecting the properties of MRE, where the tensile properties and MR effect decrease with increasing temperature. However, the presence of silica capable improved the thermal stability of EPDM-based MRE by enhancing the interactions between filler and matrix, thus reducing the interfacial defects when under the influence of temperature. Consequently, the incorporation of silica nanoparticles as an additive in EPDM-based MRE requires more exploration, since it has the potential to sustain the properties of MRE devices in a variety of temperature conditions. Thus, the study on the temperature-dependent mechanical and rheological properties of MRE is necessary, particularly regarding its practical applications.

Field-Dependent Rheological Properties of Magnetorheological Elastomer with Fountain-Like Particle Chain Alignment.

Magnetorheological elastomer (MRE) consists of magnetic particles known as carbonyl iron (CIPs), which have been locked in a silicone-based matrix, in various alignments. However, current MRE exhibits inadequate rheological properties due to several issues such as particle alignments. Therefore, in this study, a new approach of the particle alignment of CIPs in MRE, namely fountain-like structure, is introduced. It is expected that this kind of MRE exhibits enhancement rheological responses, in off- and on-state conditions. This work includes the development of a new mold that can produce various directions of magnetic flux lines in order to have fountain-like structures of CIPs in MRE, during the curing process. Three types of particle alignments in MRE, namely isotropic, fountain-like and inverted fountain-like, are fabricated. The rheological properties of MRE in terms of storage modulus and MR effect are measured in an oscillatory shear mode using a rheometer. The results have revealed that fountain-like MRE exhibits higher storage modulus than the isotropic MRE, approximately 0.6 MPa of increment in the strain sweep test, in an on-state condition. Furthermore, it has been demonstrated from strain, frequency and the current sweep test that the rheological properties of fountain-like MRE related to storage modulus and magnetorheological (MR) effect are higher compared to the inverted fountain-like MRE.

Non-parametric multiple inputs prediction model for magnetic field dependent complex modulus of magnetorheological elastomer.

This study introduces a novel platform to predict complex modulus variables as a function of the applied magnetic field and other imperative variables using machine learning. The complex modulus prediction of magnetorheological (MR) elastomers is a challenging process, attributable to the material's highly nonlinear nature. This problem becomes apparent when considering various possible fabrication parameters. Furthermore, traditional parametric modeling methods are limited when applied to solve larger-scale cases involving large databases. Consequently, the application of non-parametric modeling such as machine learning has gained increasing attraction in recent years. Therefore, this work proposes a data-driven approach for predicting multiple input-dependent complex moduli using feedforward neural networks. Besides excitation frequency and magnetic flux density as operating conditions, the inputs consider compositions and curing conditions represented by magnetic particle weight percentage and the curing magnetic field, respectively. Extreme learning machines and artificial neural networks were used to train the models. The simulation results obtained at various curing conditions and other inputs confirm that the predicted complex modulus has high accuracy with an R2 of about 0.997, as compared to the experimental results. Furthermore, the predicted complex modulus pattern and magnetorheological effect agree with the experimental data using both the learned and unlearned data.

Lightweight Glass Fiber-Reinforced Polymer Composite for Automotive Bumper Applications: A Review.

The enhancement of fuel economy and the emission of greenhouse gases are the key growing challenges around the globe that drive automobile manufacturers to produce lightweight vehicles. Additionally, the reduction in the weight of the vehicle could contribute to its recyclability and performance (for example crashworthiness and impact resistance). One of the strategies is to develop high-performance lightweight materials by the replacement of conventional materials such as steel and cast iron with lightweight materials. The lightweight composite which is commonly referred to as fiber-reinforced plastics (FRP) composite is one of the lightweight materials to achieve fuel efficiency and the reduction of CO2 emission. However, the damage of FRP composite under impact loading is one of the critical factors which affects its structural application. The bumper beam plays a key role in bearing sudden impact during a collision. Polymer composite materials have been abundantly used in a variety of applications such as transportation industries. The main thrust of the present paper deals with the use of high-strength glass fibers as the reinforcing member in the polymer composite to develop a car bumper beam. The mechanical performance and manufacturing techniques are discussed. Based on the literature studies, glass fiber-reinforced composite (GRP) provides more promise in the automotive industry compared to conventional materials such as car bumper beams.

The Effect of Graphite Additives on Magnetization, Resistivity and Electrical Conductivity of Magnetorheological Plastomer.

Common sensors in many applications are in the form of rigid devices that can react according to external stimuli. However, a magnetorheological plastomer (MRP) can offer a new type of sensing capability, as it is flexible in shape, soft, and responsive to an external magnetic field. In this study, graphite (Gr) particles are introduced into an MRP as an additive, to investigate the advantages of its electrical properties in MRPs, such as conductivity, which is absolutely required in a potential sensor. As a first step to achieve this, MRP samples containing carbonyl iron particles (CIPs) and various amounts of of Gr, from 0 to 10 wt.%, are prepared, and their magnetic-field-dependent electrical properties are experimentally evaluated. After the morphological aspect of Gr-MRP is characterized using environmental scanning electron microscopy (ESEM), the magnetic properties of MRP and Gr-MRP are evaluated via a vibrating sample magnetometer (VSM). The resistivities of the Gr-MRP samples are then tested under various applied magnetic flux densities, showing that the resistivity of Gr-MRP decreases with increasing of Gr content up to 10 wt.%. In addition, the electrical conductivity is tested using a test rig, showing that the conductivity increases as the amount of Gr additive increases, up to 10 wt.%. The conductivity of 10 wt.% Gr-MRP is found to be highest, at 178.06% higher than the Gr-MRP with 6 wt.%, for a magnetic flux density of 400 mT. It is observed that with the addition of Gr, the conductivity properties are improved with increases in the magnetic flux density, which could contribute to the potential usefulness of these materials as sensing detection devices.

Declining Performance of Silicone-Based Magnetorheological Elastomers after Accelerated Weathering.

Magnetorheological elastomers (MRE)-based products are usually located in an area directly exposed to sunlight and rain. However, there is no specific research on the behavior of MRE after accelerated weathering. Therefore, in this study, the changes to the chemical and rheological properties of both isotropic and anisotropic MRE after accelerated weathering were examined. Treated and untreated specimens were compared. MRE specimens with 40% by weight CIP were prepared with no current excitation and another sample was prepared with 1.5 T of magnetic flux density. Each specimen was treated in an accelerated weathering machine, Q-Sun Xe-1 Xenon Test Chamber, under a UV light exposure cycle and water spray. A material characterization was carried out using FTIR and a rheometer to determine the changes to the chemical and rheological properties. The morphological analysis results showed that after the weather treatment, the surface was rough and more cavities occurred. The rheometer test results showed a significant decrease in the storage modulus of each treated MRE specimen, unlike the untreated MRE specimens. The decrease in the storage modulus value with currents of 0, 1, 2, and 3 Amperes was 66.67%, 78.9%, 85.2%, and 80.5%, respectively. Meanwhile, FTIR testing showed a change in the wave peak between the untreated and treated MRE specimens. Thermogravimetric analysis (TGA) also showed a decrease in MRE weight for each specimen. However, for both treated and untreated MRE specimens, the decrease in TGA was not significantly different. In all the tests carried out on the MRE samples, weather acceleration treatment caused significant changes. This is an important consideration for developers who choose silicone as the MRE matrix.

Effects of Petroleum-Based Oils as Dispersing Aids on Physicochemical Characteristics of Magnetorheological Elastomers.

This paper investigated the effects of petroleum-based oils (PBOs) as a dispersing aid on the physicochemical characteristics of natural rubber (NR)-based magnetorheological elastomers (MREs). The addition of PBOs was expected to overcome the low performance of magnetorheological (MR) elastomers due to their inhomogeneous dispersion and the mobility of magnetic particles within the elastomer matrix. The NR-based MREs were firstly fabricated by mixing the NR compounds homogeneously with different ratios of naphthenic oil (NO), light mineral oil (LMO), and paraffin oil (PO) to aromatic oil (AO), with weight percentage ratios of 100:0, 70:30, 50:50, and 30:70, respectively. From the obtained results, the ratios of NO mixed with low amounts of AO improved the material physicochemical characteristics, such as thermal properties. Meanwhile, LMO mixed the AO led to the best results for curing characteristics, microstructure observation, and magnetic properties of the MREs. We found that the LMO mixed with a high content of AO could provide good compatibility between the rubber molecular and magnetic particles due to similar chemical structures, which apparently enhance the physicochemical characteristics of MREs. In conclusion, the 30:70 ratio of LMO:AO is considered the preferable dispersing aid for MREs due to structural compounds present in the oil that enhance the physicochemical characteristics of the NR-based MREs.

Dual Properties of Polyvinyl Alcohol-Based Magnetorheological Plastomer with Different Ratio of DMSO/Water.

Polyvinyl alcohol (PVA)-based magnetorheological plastomer (MRP) possesses excellent magnetically dependent mechanical properties such as the magnetorheological effect (MR effect) when exposed to an external magnetic field. PVA-based MRP also shows a shear stiffening (ST) effect, which is very beneficial in fabricating pressure sensor. Thus, it can automatically respond to external stimuli such as shear force without the magnetic field. The dual properties of PVA-based MRP mainly on the ST and MR effect are rarely reported. Therefore, this work empirically investigates the dual properties of this smart material under the influence of different solvent compositions (20:80, 40:60, 60:40, and 80:20) by varying the ratios of binary solvent mixture (dimethyl sulfoxide (DMSO) to water). Upon applying a shear stress with excitation frequencies from 0.01 to 10 Hz, the storage modulus (G') for PVA-based MRP with DMSO to water ratio of 20:40 increases from 6.62 × 10-5 to 0.035 MPa. This result demonstrates an excellent ST effect with the relative shear stiffening effect (RSTE) up to 52,827%. In addition, both the ST and MR effect show a downward trend with increasing DMSO content to water. Notably, the physical state of hydrogel MRP could be changed with different solvent ratios either in the liquid-like or solid-like state. On the other hand, a transient stepwise experiment showed that the solvent's composition had a positive effect on the arrangement of CIPs within the matrix as a function of the external magnetic field. Therefore, the solvent ratio (DMSO/water) can influence both ST and MR effects of hydrogel MRP, which need to be emphasized in the fabrication of hydrogel MRP for appropriate applications primarily with soft sensors and actuators for dynamic motion control.

Effect of Mould Orientation on the Field-Dependent Properties of MR Elastomers under Shear Deformation.

In this study, magnetorheological elastomer (MRE) was fabricated using an electromagnetic device with a new configuration mold at the orientation of 0°, 45° and 90°. This new curing concept enhanced the alignment of carbonyl iron particles (CIPs) within the silicone matrix in the presence of silicone oil (SO) during solidifying, by eliminating air gaps to prevent magnetic flux losses. Using a mold made of steel, which is a magnetic material, the mold functions as a guide for concentrated magnetic flux of 0.315 T to pass through the MRE sample. Scanning electron microscopy (SEM) was used to observe the surface morphology of the fabricated MRE samples particularly the alignment of the CIPs. The field-dependent dynamic properties of the MREs were measured using a rheometer. The analysis implied that the effectiveness of the MRE operating under shear deformation with this curing concept provided the highest magneto-induced modulus of 1.01 MPa when a 45° orientation mold is used, with relative magnetorheological (MR) effect value up to 918%, followed by 0° mold orientation with 0.79 MPa magneto-induced modulus and 646% relative MR effect. The high modulus properties offered by this MRE are believed to be potentially useful in industrial applications where a high range of stiffness is required particularly in the shear direction.

Loss Factor Behavior of Thermally Aged Magnetorheological Elastomers.

Polymer composites have been widely used as damping materials in various applications due to the ability of reducing the vibrations. However, the environmental and surrounding thermal exposure towards polymer composites have affected their mechanical properties and lifecycle. Therefore, this paper presents the effect of material-temperature dependence on the loss factor and phase shift angle characteristics. Two types of unageing and aging silicone-rubber-based magnetorheological elastomer (SR-MRE) with different concentrations of carbonyl iron particles (CIPs), 30 and 60 wt%, are utilized in this study. The morphological, magnetic, and rheological properties related to the loss factor and phase shift angle are characterized using a low-vacuum scanning electron microscopy, and vibrating sample magnetometer and rheometer, respectively. The morphological analysis of SR-MRE consisting of 30 wt% CIPs revealed a smoother surface area when compared to 60 wt% CIPs after thermal aging due to the improvement of CIPs dispersion in the presence of heat. Nevertheless, the rheological analysis demonstrated inimitable rheological properties due to different in-rubber structures, shear deformation condition, as well as the influence of magnetic field. No significant changes of loss factor occurred at a low CIPs concentration, whilst the loss factor increased at a higher CIPs concentration. On that basis, it has been determined that the proposed changes of the polymer chain network due to the long-term temperature exposure of different concentrations of CIPs might explain the unique rheological properties of the unaged and aged SR-MRE.

Rheological Performance of Magnetorheological Grease with Embedded Graphite Additives.

The use of highly viscous grease as a medium in magnetorheological grease (MRG) provides the benefit of avoiding sedimentation from occurring. However, it limits the expansion of yield stress in the on-state condition, thus reducing the application performance during operation. Therefore, in this study, the improvement in the rheological properties of MRG was investigated through the introduction of graphite as an additive. MRG with 10 wt % graphite (GMRG) was fabricated, and its properties were compared to a reference MRG sample. The microstructure of GMRG was characterized using an environmental scanning electron microscope (ESEM). The rheological properties of both samples, including apparent viscosity, yield stress, and viscoelasticity, were examined using a shear rheometer in rotational and oscillatory modes. The results demonstrated a slight increase in the apparent viscosity in GMRG and a significant improvement in yield stress by 38.8% at 3 A with growth about 32.7% higher compared to MRG from 0 to 3 A. An expansion of the linear viscoelastic region (LVE) from 0.01% to 0.1% was observed for the GMRG, credited to the domination of the elastic properties on the sample. These obtained results were confirmed based on ESEM, which described the contribution of graphite to constructing a more stable chain structure in the GMRG. In conclusion, the findings highlight the influence of the addition of graphite on improving the rheological properties of MRG. Hence, the addition of graphite in MRG shows the potential to be applied in many applications in the near future.

The Effect of Microparticles on the Storage Modulus and Durability Behavior of Magnetorheological Elastomer.

This paper presents the effect of the micro-sized particles on the storage modulus and durability characteristics of magnetorheological elastomers (MREs). The initial phase of the investigation is to determine any associations among the microparticles' weight percent fraction (wt%), structure arrangement, and the storage modulus of MRE samples. In order to carry out this, both isotropic and anisotropic types of MRE samples consisting of the silicone rubber matrix and 50, 60, 70, 75, and 80 wt% microparticles of carbonyl iron fractions are prepared. It is identified from the magneto-rheometer that the increase in storage modulus and decrease in linear viscoelastic region limit are observed in varying consistency depending on wt% and particle arrangement. The consistency of this dependency feature is highlighted by superimposing all of the graphs plotted to create the proposed the samples' behavior model. In response to increasing magnetic stimulation, a sample of 70 wt% microparticles with an isotropic arrangement is found to be significant and stable. The experimentally defined fraction is then used for the durability test as the second phase of the investigation. During this phase, the durability evaluation is subjected to stress relaxation for an extended period of time. After undergoing durability testing, storage modulus performance is decreased by 0.7-13% at various magnetic stimulation levels. This result directly indicates that the storage modulus characteristics of different forms of MRE are sensitive to the different iron particle fractions' and microparticles' alignment. Therefore, important treatments to alter the storage modulus can be undertaken before the practical implementation to accommodate any desired performance of MRE itself and MRE application systems.

An Insight into Amorphous Shear Band in Magnetorheological Solid by Atomic Force Microscope.

Micro mechanism consideration is critical for gaining a thorough understanding of amorphous shear band behavior in magnetorheological (MR) solids, particularly those with viscoelastic matrices. Heretofore, the characteristics of shear bands in terms of formation, physical evolution, and response to stress distribution at the localized region have gone largely unnoticed and unexplored. Notwithstanding these limitations, atomic force microscopy (AFM) has been used to explore the nature of shear band deformation in MR materials during stress relaxation. Stress relaxation at a constant low strain of 0.01% and an oscillatory shear of defined test duration played a major role in the creation of the shear band. In this analysis, the localized area of the study defined shear bands as varying in size and dominantly deformed in the matrix with no evidence of inhibition by embedded carbonyl iron particles (CIPs). The association between the shear band and the adjacent zone was further studied using in-phase imaging of AFM tapping mode and demonstrated the presence of localized affected zone around the shear band. Taken together, the results provide important insights into the proposed shear band deformation zone (SBDZ). This study sheds a contemporary light on the contentious issue of amorphous shear band deformation behavior and makes several contributions to the current literature.