RESUMEN
The properties of complex bodily fluids are linked to their biological functions through natural selection. Velvet worms capture their prey by ensnaring them with a proteinaceous fluid (slime). We examined the electrical conductivity of slime and found that dry slime is an insulator. However, its conductivity can increase by up to 106 times in its hydrated state, which can be further increased by an order in magnitude under acidic hydration (pH ≈ 2.3). The transient current measured using ion-blocking electrodes showed a continuous decay for up to 7 h, revealing slime's nature as a proton conducting material. Slime undergoes a spontaneous fibrilization process producing high aspect ratio ≈ 105 fibers that exhibit an average conductivity ≈2.4 ± 1.1 mS cm-1. These findings enhance our understanding of slime as a natural biopolymer and provide molecular-level guidelines to rationally design biomaterials that may be employed as hygroscopic conductors.
RESUMEN
Efforts to engineer high-performance protein-based materials inspired by nature have mostly focused on altering naturally occurring sequences to confer the desired functionalities, whereas de novo design lags significantly behind and calls for unconventional innovative approaches. Here, using partially disordered elastin-like polypeptides (ELPs) as initial building blocks this work shows that de novo engineering of protein materials can be accelerated through hybrid biomimetic design, which this work achieves by integrating computational modeling, deep neural network, and recombinant DNA technology. This generalizable approach involves incorporating a series of de novo-designed sequences with α-helical conformation and genetically encoding them into biologically inspired intrinsically disordered repeating motifs. The new ELP variants maintain structural conformation and showed tunable supramolecular self-assembly out of thermal equilibrium with phase behavior in vitro. This work illustrates the effective translation of the predicted molecular designs in structural and functional materials. The proposed methodology can be applied to a broad range of partially disordered biomacromolecules and potentially pave the way toward the discovery of novel structural proteins.
Asunto(s)
Materiales Biomiméticos , Elastina , Ingeniería de Proteínas , Elastina/química , Elastina/genética , Ingeniería de Proteínas/métodos , Materiales Biomiméticos/química , Péptidos/química , Biomimética/métodos , Modelos MolecularesRESUMEN
Biological systems can create materials with intricate structures and specialized functions. In comparison, precise control of structures in human-made materials has been challenging. Here we report on insect cuticle peptides that spontaneously form nanocapsules through a single-step solvent exchange process, where the concentration gradient resulting from the mixing of water and acetone drives the localization and self-assembly of the peptides into hollow nanocapsules. The underlying driving force is found to be the intrinsic affinity of the peptides for a particular solvent concentration, while the diffusion of water and acetone creates a gradient interface that triggers peptide localization and self-assembly. This gradient-mediated self-assembly offers a transformative pathway towards simple generation of drug delivery systems based on peptide nanocapsules.
RESUMEN
Coacervation, or liquid-liquid phase separation (LLPS) of biomacromolecules, is increasingly recognized to play an important role both intracellularly and in the extracellular space. Central questions that remain to be addressed are the links between the material properties of coacervates (condensates) and both the primary and the secondary structures of their constitutive building blocks. Short LLPS-prone peptides, such as GY23 variants explored in this study, are ideal model systems to investigate these links because simple sequence modifications and the chemical environment strongly affect the viscoelastic properties of coacervates. Herein, a systematic investigation of the structure/property relationships of peptide coacervates was conducted using GY23 variants, combining biophysical characterization (plate rheology and surface force apparatus, SFA) with secondary structure investigations by infrared (IR) and circular dichroism (CD) spectroscopy. Mutating specific residues into either more hydrophobic or more hydrophilic residues strongly regulates the viscoelastic properties of GY23 coacervates. Furthermore, the ionic strength and kosmotropic characteristics (Hofmeister series) of the buffer in which LLPS is induced also significantly impact the properties of formed coacervates. Structural investigations by CD and IR indicate a direct correlation between variations in properties induced by endogenous (peptide sequence) or exogenous (ionic strength, kosmotropic characteristics, aging) factors and the ß-sheet content within coacervates. These findings provide valuable insights to rationally design short peptide coacervates with programmable materials properties that are increasingly used in biomedical applications.
RESUMEN
The molecular design of many peptide-based materials originates from structural proteins identified in living organisms. Prominent examples that have garnered broad interdisciplinary research interest (chemistry, materials science, bioengineering, etc.) include elastin, silk, or mussel adhesive proteins. The critical first steps in this type of research are to identify a convenient model system of interest followed by sequencing the prevailing proteins from which these biological structures are assembled. In our laboratory, the main model systems for many years have been the hard biotools of cephalopods, particularly their parrot-like tough beak and their sucker ring teeth (SRT) embedded within the sucker cuptions that line the interior surfaces of their arms and tentacles. Unlike the majority of biological hard tissues, these structures are devoid of biominerals and consist of protein/polysaccharide biomolecular composites (the beak) or, in the case of SRT, are entirely made of proteins that are assembled by supramolecular interactions.In this Account, we chronicle our journey into the discovery of these intriguing biological materials. We initially focus on their excellent mechanical robustness followed by the identification and sequencing of the structural proteins from which they are built, using the latest "omics" techniques including next-generation sequencing and high-throughput proteomics. A common feature of these proteins is their modular architecture at the molecular level consisting of short peptide repeats. We describe the molecular design of these peptide building blocks, highlighting the consensus motifs identified to play a key role in biofabrication and in regulating the mechanical properties of the macroscopic biological material. Structure/property relationships unveiled through advanced spectroscopic and scattering techniques, including Raman, infrared, circular dichroism, and NMR spectroscopies as well as wide-angle and small-angle X-ray scattering, are also discussed.We then present recent developments in exploiting the discovered molecular designs to engineer peptides and their conjugates for promising biomedical applications. One example includes short peptide hydrogels that self-assemble entirely under aqueous conditions and simultaneously encapsulate large macromolecules during the gelation process. A second example involves peptide coacervate microdroplets produced by liquid-liquid phase separation. These microdroplets are capable of recruiting and delivering large macromolecular therapeutics (genes, mRNA, proteins, peptides, CRISPR/Cas 9 modalities, etc.) into mammalian cells, which introduces exciting prospects in cancer, gene, and immune therapies.This Account also serves as a testament to how curiosity-driven explorations, which may lack an obvious practical goal initially, can lead to discoveries with unexpected and promising translational potential.
Asunto(s)
Decapodiformes , Conducta Exploratoria , Animales , Decapodiformes/genética , Péptidos/química , Seda , Sustancias Macromoleculares , MamíferosRESUMEN
Increasing carbon emissions have accelerated climate change, resulting in devastating effects that are now tangible on an everyday basis. This is mirrored by a projected increase in global energy demand of approximately 50% within a single generation, urging a shift from fossil-fuel-derived materials toward greener materials and more sustainable manufacturing processes. Biobased industrial byproducts, such as side streams from the food industry, are attractive alternatives with strong potential for valorization due to their large volume, low cost, renewability, biodegradability, and intrinsic material properties. Here, we demonstrate the reutilization of industrial chicken feather waste into proton-conductive membranes for fuel cells, protonic transistors, and water-splitting devices. Keratin was isolated from chicken feathers via a fast and economical process, converted into amyloid fibrils through heat treatment, and further processed into membranes with an imparted proton conductivity of 6.3 mS cm-1 using a simple oxidative method. The functionality of the membranes is demonstrated by assembling them into a hydrogen fuel cell capable of generating 25 mW cm-2 of power density to operate various types of devices using hydrogen and air as fuel. Additionally, these membranes were used to generate hydrogen through water splitting and in protonic field-effect transistors as thin-film modulators of protonic conductivity via the electrostatic gating effect. We believe that by converting industrial waste into renewable energy materials at low cost and high scalability, our green manufacturing process can contribute to a fully circular economy with a neutral carbon footprint.
RESUMEN
The stomatopod Odontodactylus scyllarus uses weaponized club-like appendages to attack its prey. These clubs are made of apatite, chitin, amorphous calcium carbonate, and amorphous calcium phosphate organized in a highly hierarchical structure with multiple regions and layers. We follow the development of the biomineralized club as a function of time using clubs harvested at specific times since molting. The clubs are investigated using a broad suite of techniques to unravel the biomineralization history of the clubs. Nano focus synchrotron x-ray diffraction and x-ray fluorescence experiments reveal that the club structure is more organized with more sub-regions than previously thought. The recently discovered impact surface has crystallites in a different size and orientation than those in the impact region. The crystal unit cell parameters vary to a large degree across individual samples, which indicates a spatial variation in the degree of chemical substitution. Energy dispersive spectroscopy and Raman spectroscopy show that this variation cannot be explained by carbonation and fluoridation of the lattice alone. X-ray fluorescence and mass spectroscopy show that the impact surface is coated with a thin membrane rich in bromine that forms at very initial stages of club formation. Proteomic studies show that a fraction of the club mineralization protein-1 has brominated tyrosine suggesting that bromination of club proteins at the club surface is an integral component of the club design. Taken together, the data unravel the spatio-temporal changes in biomineral structure during club formation. STATEMENT OF SIGNIFICANCE: Mantis shrimp hunt using club-like appendages that contain apatite, chitin, amorphous calcium carbonate, and amorphous calcium phosphate ordered in a highly hierarchical structure. To understand the formation process of the club we analyze clubs harvested at specific times since molting thereby constructing a club formation map. By combining several methods ranging from position resolved synchrotron X-ray diffraction to proteomics, we reveal that clubs form from an organic membrane with brominated protein and that crystalline apatite phases are present from the very onset of club formation and grow in relative importance over time. This reveals a complex biomineralization process leading to these fascinating biomineralized tools.
Asunto(s)
Apatitas , Biomineralización , Animales , Apatitas/química , Muda , Proteómica , Crustáceos , Carbonato de Calcio , Quitina , Difracción de Rayos XRESUMEN
CRISPR/Cas9-based genome editing tools have enormous potential for the development of various therapeutic treatments due to their reliability and broad applicability. A central requirement of CRISPR/Cas9 is the efficient intracellular delivery of the editing machinery, which remains a well-recognized challenge, notably to deliver Cas9 in its native protein form. Herein, a phase-separating peptide with intracellular redox-triggered release properties is employed to encapsulate and deliver all three forms of CRISRP-Cas9 editing machinery, namely, pDNA, mRNA/sgRNA, and the ribonucleoprotein complex. These modalities are readily recruited within peptide coacervates during liquid-liquid phase separation by simple mixing and exhibit higher transfection and editing efficiency compared to highly optimized commercially available transfection reagents currently used for genome editing.
Asunto(s)
Sistemas CRISPR-Cas , Edición Génica , Sistemas CRISPR-Cas/genética , ARN Guía de Sistemas CRISPR-Cas , Reproducibilidad de los Resultados , Péptidos/genética , Oxidación-ReducciónRESUMEN
Engineering liquid-liquid phase separation (LLPS) of proteins and peptides holds great promise for the development of therapeutic carriers with intracellular delivery capability but requires accurate determination of their assembly properties in vitro, usually with fluorescently labeled cargo. Here, we use mass spectrometry (MS) to investigate redox-sensitive coacervate microdroplets (the dense phase formed during LLPS) assembled from a short His- and Tyr-rich peptide. We can monitor the enrichment of a reduced peptide in dilute phase as the microdroplets dissolve triggered by their redox-sensitive side chain, thus providing a quantitative readout for disassembly. Furthermore, MS can detect the release of a short peptide from coacervates under reducing conditions. In summary, with MS, we can monitor the disassembly and cargo release of engineered coacervates used as therapeutic carriers without the need for additional labels.
Asunto(s)
Péptidos , Proteínas , Péptidos/química , Proteínas/química , Espectrometría de MasasRESUMEN
Rationally designed biomolecular condensates have found applications primarily as drug-delivery systems, thanks to their ability to self-assemble under physico-chemical triggers (such as temperature, pH, or ionic strength) and to concomitantly trap client molecules with exceptionally high efficiency (>99%). However, their potential in (bio)sensing applications remains unexplored. Here, we describe a simple and rapid assay to detect E. coli by combining phase-separating peptide condensates containing a protease recognition site, within which an aggregation-induced emission (AIE)-fluorogen is recruited. The recruited AIE-fluorogen's fluorescence is easily detected with the naked eye when the samples are viewed under UV-A light. In the presence of E. coli, the bacteria's outer membrane protease (OmpT) cleaves the phase-separating peptides at the encoded protease recognition site, resulting in two shorter peptide fragments incapable of liquid-liquid phase separation. As a result, no condensates are formed and the fluorogen remains non-fluorescent. The assay feasibility was first tested with recombinant OmpT reconstituted in detergent micelles and subsequently confirmed with E. coli K-12. In its current format, the assay can detect E. coli K-12 (108 CFU) within 2 h in spiked water samples and 1-10 CFU/mL with the addition of a 6-7 h pre-culture step. In comparison, most commercially available E. coli detection kits can take anywhere from 8 to 24 h to report their results. Optimizing the peptides for OmpT's catalytic activity can significantly improve the detection limit and assay time. Besides detecting E. coli, the assay can be adapted to detect other Gram-negative bacteria as well as proteases having diagnostic relevance.
Asunto(s)
Proteínas de Escherichia coli , Escherichia coli , Humanos , Péptidos/química , Péptido Hidrolasas , EndopeptidasasRESUMEN
Barnacles strongly attach to various underwater substrates by depositing and curing a proteinaceous cement that forms a permanent adhesive layer. The protein MrCP20 present within the calcareous base plate of the acorn barnacle Megabalanus rosa (M. rosa) was investigated for its role in regulating biomineralization and growth of the barnacle base plate, as well as the influence of the mineral on the protein structure and corresponding functional role. Calcium carbonate (CaCO3) growth on gold surfaces modified by 11-mercaptoundecanoic acid (MUA/Au) with or without the protein was followed using quartz crystal microbalance with dissipation monitoring (QCM-D), and the grown crystal polymorph was identified by Raman spectroscopy. It is found that MrCP20 either in solution or on the surface affects the kinetics of nucleation and growth of crystals and stabilizes the metastable vaterite polymorph of CaCO3. A comparative study of mass uptake calculated by applying the Sauerbrey equation to the QCM-D data and quantitative X-ray photoelectron spectroscopy determined that the final surface density of the crystals as well as the crystallization kinetics are influenced by MrCP20. In addition, polarization modulation infrared reflection-absorption spectroscopy of MrCP20 established that, during crystal growth, the content of ß-sheet structures in MrCP20 increases, in line with the formation of amyloid-like fibrils. The results provide insights into the molecular mechanisms by which MrCP20 regulates the biomineralization of the barnacle base plate, while favoring fibril formation, which is advantageous for other functional roles such as adhesion and cohesion.
Asunto(s)
Thoracica , Animales , Thoracica/química , Thoracica/metabolismo , Biomineralización , Cementos de Resina/metabolismo , Amiloide/metabolismoRESUMEN
The stomatopod is a fascinating animal that uses its weaponized appendage dactyl clubs for breaking mollusc shells. Dactyl clubs are a well studied example of biomineralized hierarchical structures. Most research has focused on the regions close to the action, namely the impact region and surface composed of chitin and apatite crystallites. Further away from the site of impact, the club has lower mineralization and more amorphous phases; these areas have not been as actively studied as their highly mineralized counterparts. This work focuses on the side of the club, in what is known as the periodic and striated regions. A combination of laboratory micro-computed tomography, synchrotron X-ray diffraction mapping and synchrotron X-ray fluorescence mapping has shown that the mineral in this region undergoes the transition from an amorphous to a crystalline phase in some, but not all, clubs. This means that this side region can be mineralized by either an amorphous phase, calcite crystallites or a mixture of both. It was found that when larger calcite crystallites form, they are organized (textured) with respect to the chitin present in this biocomposite. This suggests that chitin may serve as a template for crystallization when the side of the club is fully mineralized. Further, calcite crystallites were found to form as early as 1â week after moulting of the club. This suggests that the side of the club is designed with a significant safety margin that allows for a variety of phases, i.e. the club can function independently of whether the side region has a crystalline or amorphous mineral phase.
Asunto(s)
Apatitas , Carbonato de Calcio , Animales , Microtomografía por Rayos X , Carbonato de Calcio/química , Quitina/químicaRESUMEN
The occurrence of modular peptide repeats in load-bearing (structural) proteins is common in nature, with distinctive peptide sequences that often remain conserved across different phylogenetic lineages. These highly conserved peptide sequences endow specific mechanical properties to the material, such as toughness or elasticity. Here, using bioinformatic tools and phylogenetic analysis, we have identified the GX8 peptide with the sequence GLYGGYGX (where X can be any residue) in a wide range of organisms. By simple mutation of the X residue, we demonstrate that GX8 can be self-assembled into various supramolecular structures, exhibiting vastly different physicochemical and viscoelastic properties, from liquid-like coacervate microdroplets to hydrogels to stiff solid materials. A combination of spectroscopic, electron microscopy, mechanical, and molecular dynamics studies is employed to obtain insights into molecular scale interactions driving self-assembly of GX8 peptides, underscoring that π-π stacking and hydrophobic interactions are the drivers of peptide self-assembly, whereas the X residue determines the extent of hydrogen bonding that regulates the macroscopic mechanical response. This study highlights the ability of single amino-acid polymorphism to tune the supramolecular assembly and bulk material properties of GX8 peptides, enabling us to cover a broad range of potential biomedical applications such as hydrogels for tissue engineering or coacervates for drug delivery.
Asunto(s)
Aminoácidos , Péptidos , Filogenia , Péptidos/química , Hidrogeles/química , MutaciónRESUMEN
Polymeric materials produced from fossil fuels have been intimately linked to the development of industrial activities in the 20th century and, consequently, to the transformation of our way of living. While this has brought many benefits, the fabrication and disposal of these materials is bringing enormous sustainable challenges. Thus, materials that are produced in a more sustainable fashion and whose degradation products are harmless to the environment are urgently needed. Natural biopolymersâwhich can compete with and sometimes surpass the performance of synthetic polymersâprovide a great source of inspiration. They are made of natural chemicals, under benign environmental conditions, and their degradation products are harmless. Before these materials can be synthetically replicated, it is essential to elucidate their chemical design and biofabrication. For protein-based materials, this means obtaining the complete sequences of the proteinaceous building blocks, a task that historically took decades of research. Thus, we start this review with a historical perspective on early efforts to obtain the primary sequences of load-bearing proteins, followed by the latest developments in sequencing and proteomic technologies that have greatly accelerated sequencing of extracellular proteins. Next, four main classes of protein materials are presented, namely fibrous materials, bioelastomers exhibiting high reversible deformability, hard bulk materials, and biological adhesives. In each class, we focus on the design at the primary and secondary structure levels and discuss their interplays with the mechanical response. We finally discuss earlier and the latest research to artificially produce protein-based materials using biotechnology and synthetic biology, including current developments by start-up companies to scale-up the production of proteinaceous materials in an economically viable manner.
Asunto(s)
Biotecnología , Proteómica , Industrias , Polímeros , Biología SintéticaRESUMEN
Chronic wounds are non-healing wounds characterized by a prolonged inflammation phase. Excessive inflammation leads to elevated protease levels and consequently to a decrease in growth factors at wound sites. Stem cell secretome therapy has been identified as a treatment strategy to modulate the microenvironment of chronic wounds via supplementation with anti-inflammatory/growth factors. However, there is a need to develop better secretome delivery systems that are able to encapsulate the secretome without denaturation, in a sustained manner, and that are fully biocompatible. To address this gap, a recombinant squid suckerin-spider silk fusion protein is developed with cell-adhesion motifs capable of thermal gelation at physiological temperatures to form hydrogels for encapsulation and subsequent release of the stem cell secretome. Freeze-thaw treatment of the protein hydrogel results in a modified porous cryogel that maintains slow degradation and sustained secretome release. Chronic wounds of diabetic mice treated with the secretome-laden cryogel display increased wound closure, presence of endothelial cells, granulation wound tissue thickness, and reduced inflammation with no fibrotic scar formation. Overall, these in vivo indicators of wound healing demonstrate that the fusion protein hydrogel displays remarkable potential as a delivery system for secretome-assisted chronic wound healing.
Asunto(s)
Diabetes Mellitus Experimental , Células Madre Mesenquimatosas , Ratones , Animales , Humanos , Hidrogeles/farmacología , Criogeles , Seda , Secretoma , Células Endoteliales de la Vena Umbilical HumanaRESUMEN
Liquid metal droplets, such as eutectic gallium-indium (EGaIn), are important in many research areas, such as soft electronics, catalysis, and energy storage. Droplet contact on solid surfaces is typically achieved without control over the applied force and without optimizing the wetting properties in different environments (e.g., in air or liquid), resulting in poorly defined contact areas. In this work, we demonstrate the direct manipulation of EGaIn microdroplets using an atomic force microscope (AFM) to generate repeated, on-demand making and breaking of contact on self-assembled monolayers (SAMs) of alkanethiols. The nanoscale positional control and feedback loop in an AFM allow us to control the contact force at the nanonewton level and, consequently, tune the droplet contact areas at the micrometer length scale in both air and ethanol. When submerged in ethanol, the droplets are highly nonwetting, resulting in hysteresis-free contact forces and minimal adhesion; as a result, we are able to create reproducible geometric contact areas of 0.8-4.5 µm2 with the alkanethiolate SAMs in ethanol. In contrast, there is a larger hysteresis in the contact forces and larger adhesion for the same EGaIn droplet in air, which reduced the control over the contact area (4-12 µm2). We demonstrate the usefulness of the technique and of the gained insights in EGaIn contact mechanics by making well-defined molecular tunneling junctions based on alkanethiolate SAMs with small geometric contact areas of between 4 and 12 µm2 in air, 1 to 2 orders of magnitude smaller than previously achieved.
RESUMEN
Structures made by scleractinian corals support diverse ocean ecosystems. Despite the importance of coral skeletons and their predicted vulnerability to climate change, few studies have examined the mechanical and crystallographic properties of coral skeletons at the micro- and nano-scales. Here, we investigated the interplay of crystallographic and microarchitectural organization with mechanical anisotropy within Porites skeletons by measuring Young's modulus and hardness along surfaces transverse and longitudinal to the primary coral growth direction. We observed micro-scale anisotropy, where the transverse surface had greater Young's modulus and hardness by â¼ 6 GPa and 0.2 GPa, respectively. Electron backscatter diffraction (EBSD) revealed that this surface also had a higher percentage of crystals oriented with the a-axis between ± 30-60∘, relative to the longitudinal surface, and a broader grain size distribution. Within a region containing a sharp microscale gradient in Young's modulus, nanoscale indentation mapping, energy dispersive spectroscopy (EDS), EBSD, and Raman crystallography were performed. A correlative trend showed higher Young's modulus and hardness in regions with individual crystal bases (c-axis) facing upward, and in crystal fibers relative to centers of calcification. These relationships highlight the difference in mechanical properties between scales (i.e. crystals, crystal bundles, grains). Observations of crystal orientation and mechanical properties suggest that anisotropy is driven by microscale organization and crystal packing rather than intrinsic crystal anisotropy. In comparison with previous observations of nanoscale isotropy in corals, our results illustrate the role of hierarchical architecture in coral skeletons and the influence of biotic and abiotic factors on mechanical properties at different scales. STATEMENT OF SIGNIFICANCE: Coral biomineralization and the ability of corals' skeletal structure to withstand biotic and abiotic forces underpins the success of reef ecosystems. At the microscale, we show increased skeletal stiffness and hardness perpendicular to the coral growth direction. By comparing nano- and micro-scale indentation results, we also reveal an effect of hierarchical architecture on the mechanical properties of coral skeletons and hypothesize that crystal packing and orientation result in microscale anisotropy. In contrast to previous findings, we demonstrate that mechanical and crystallographic properties of coral skeletons can vary between surface planes, within surface planes, and at different analytical scales. These results improve our understanding of biomineralization and the effects of scale and direction on how biomineral structures respond to environmental stimuli.
Asunto(s)
Antozoos , Ecosistema , Animales , Anisotropía , Módulo de Elasticidad , DurezaRESUMEN
Nanoscopic structural control with long-range ordering remains a profound challenge in nanomaterial fabrication. The nanoarchitectured egg cases of elasmobranchs rely on a hierarchically ordered latticework for their protective functionâserving as an exemplary system for nanoscale self-assembly. Although the proteinaceous precursors are known to undergo intermediate liquid crystalline phase transitions before being structurally arrested in the final nanolattice architecture, their sequences have so far remained unknown. By leveraging RNA-seq and proteomic techniques, we identified a cohort of nanolattice-forming proteins comprising a collagenous midblock flanked by domains typically associated with innate immunity and network-forming collagens. Structurally homologous proteins were found in the genomes of other egg-case-producing cartilaginous fishes, suggesting a conserved molecular self-assembly strategy. The identity and stabilizing role of cross-links were subsequently elucidated using mass spectrometry and in situ small-angle X-ray scattering. Our findings provide a new design approach for protein-based liquid crystalline elastomers and the self-assembly of nanolattices.
Asunto(s)
Cristales Líquidos , Tiburones , Animales , Colágeno , Humanos , Cristales Líquidos/química , Transición de Fase , ProteómicaRESUMEN
Eutectic gallium-indium (EGaIn) is increasingly employed as an interfacial conductor material in molecular electronics and wearable healthcare devices owing to its ability to be shaped at room temperature, conductivity, and mechanical stability. Despite this emerging usage, the mechanical and physical mechanisms governing EGaIn interactions with surrounding objectsâmainly regulated by surface tension and interfacial adhesionâremain poorly understood. Here, using depth-sensing nanoindentation (DSN) on pristine EGaIn/GaOx surfaces, we uncover how changes in EGaIn/substrate interfacial energies regulate the adhesive and contact mechanic behaviors, notably the evolution of EGaIn capillary bridges with distinct capillary geometries and pressures. Varying the interfacial energy by subjecting EGaIn to different chemical environments and by functionalizing the tip with chemically distinct self-assembled monolayers (SAMs), we show that the adhesion forces between EGaIn and the solid substrate can be increased by up to 2 orders of magnitude, resulting in about a 60-fold increase in the elongation of capillary bridges. Our data reveal that by deploying molecular junctions with SAMs of different terminal groups, the trends of charge transport rates, the resistance of monolayers, and the contact interactions between EGaIn and monolayers from electrical characterizations are governed by the interfacial energies as well. This study provides a key understanding into the role of interfacial energy on geometrical characteristics of EGaIn capillary bridges, offering insights toward the fabrication of EGaIn junctions in a controlled fashion.
RESUMEN
The slime of velvet worms (Onychophora) is a strong and fully biodegradable protein material, which upon ejection undergoes a fast liquid-to-solid transition to ensnare prey. However, the molecular mechanisms of slime self-assembly are still not well understood, notably because the primary structures of slime proteins are yet unknown. Combining transcriptomic and proteomic studies, the authors have obtained the complete primary sequences of slime proteins and identified key features for slime self-assembly. The high molecular weight slime proteins contain cysteine residues at the N- and C-termini that mediate the formation of multi-protein complexes via disulfide bonding. Low complexity domains in the N-termini are also identified and their propensity for liquid-liquid phase separation is established, which may play a central role in slime biofabrication. Using solid-state nuclear magnetic resonance, rigid and flexible domains of the slime proteins are mapped to specific peptide domains. The complete sequencing of major slime proteins is an important step toward sustainable fabrication of polymers inspired by the velvet worm slime.