RESUMEN
Delamination, a form of composite failure, is a significant concern in laminated composites. The increasing use of out-of-autoclave manufacturing techniques for automotive applications, such as compression moulding and thermoforming, has led to increased interest in understanding the delamination resistance of carbon-fibre-reinforced thermoplastic (CFRTP) composites compared to traditional carbon-fibre-reinforced thermosetting (CFRTS) composites. This study evaluated the mode I (opening) interlaminar fracture toughness of two non-crimp fabric (NCF) biaxial (0/90°) carbon/thermoplastic composite systems: T700/polyamide 6.6 and T700/polyphenylene sulphide. The mode I delamination resistance was determined using the double cantilever beam (DCB) specimen. The results were analysed and the Mode I interlaminar fracture toughness was compared. Additionally, the fractographic analysis (microstructure characterisation) was conducted using a scanning electron microscope (SEM) to examine the failure surface of the specimens.
RESUMEN
There has been a lot of interest in understanding the low-velocity impact (LVI) response of thermoplastic composites. However, little research has focussed on studying the impact behaviour of non-crimp fabric (NCF)-based fibre reinforced thermoplastic composites. The purpose of this study was to evaluate the LVI responses of two types of non-crimp fabric (NCF) carbon fibre reinforced thermoplastic laminated composites that have been considered attractive in the automotive and aerospace industry: (i) T700/polyamide 6.6 (PA6.6) and (ii) T700/polyphenylene sulphide (PPS). Each carbon/thermoplastic type was impacted at three different energy levels (40, 100 and 160 J), which were determined to achieve three degrees of penetrability, i.e., no penetration, partial penetration and full penetration, respectively. Two distinct non-destructive evaluation (NDE) techniques ((i) ultrasonic C-scanning and (ii) X-ray tomography) were used to assess the extent of damage after impact. The laminated composite plates were subjected to an out-of-plane, localised impact using an INSTRON® drop-weight tower with a hemispherical impactor measuring 16 mm in diameter. The time histories of force, deflection and velocity are reported and discussed. A nonlinear finite element model of the LVI phenomenon was developed using a finite element (FE) solver LS-DYNA® and validated against the experimental observations. The extent of damage observed and level of impact energy absorption calculated on both the experiment and FE analysis are compared and discussed.
RESUMEN
A dynamic tensile experiment was performed on a rectangular specimen of a non-crimp fabric (NCF) thermoplastic composite T700 carbon/polyamide 6.6 specimens using a split Hopkinson pressure (Kolsky) bar (SHPB). The experiment successfully provided useful information on the strain-rate sensitivity of the NCF carbon/thermoplastic material system. The average tensile strength at three varying strain rates: 700, 1400, and 2100/s was calculated and compared to the tensile strength measured from a standardized (quasi-static) procedure. The increase in tensile strength was found to be 3.5, 24.2, and 45.1% at 700, 1400, and 2100/s strain rate, respectively. The experimental findings were used as input parameters for the numerical model developed using a commercial finite element (FE) explicit solver LS-DYNA®. The dynamic FE model was validated against experimental gathering and used to predict the composite system's behavior in various engineering applications under high strain-rate loading conditions. The SHPB tension test detailed in this study provided the enhanced understanding of the T700/polyamide 6.6 composite material's behavior under different strain rates and allowed for the prediction of the material's behavior under real-world, dynamic loading conditions, such as low-velocity and high-velocity impact.