Highly Self-Healable Polymeric Coating Materials Based on Charge Transfer Complex Interactions with Outstanding Weatherability.

In this study, we prepare highly self-healable polymeric coating materials using charge transfer complex (CTC) interactions. The resulting coating materials demonstrate outstanding thermal stability (1 wt% loss thermal decomposition temperature at 420 °C), rapid self-healing kinetics (in 5 min), and high self-healing efficiency (over 99%), which is facilitated by CTC-induced multiple interactions between the polymeric chains. In addition, these materials exhibit excellent optical properties, including transmittance over 91% and yellow index (YI) below 2, and show enhanced weatherability with a ΔYI value below 0.5 after exposure to UV light for 72 h. Furthermore, the self-healable coating materials developed in this study show outstanding mechanical properties by overcoming the limitations of conventional self-healing materials.

Highly Self-Healable Polymeric Coating Materials with Enhanced Mechanical Properties Based on the Charge Transfer Complex.

Polymeric coating materials (PCMs) are promising candidates for developing next-generation flexible displays. However, PCMs are frequently subjected to external stimuli, making them highly susceptible to repeated damage. Therefore, in this study, a highly self-healing PCM based on a charge transfer complex (CTC) was developed, and its thermal, self-healing, and mechanical properties were examined. The self-healing material demonstrated improved thermal stability, fast self-healing kinetics (1 min), and a high self-healing efficiency (98.1%) via CTC-induced multiple interactions between the polymeric chains. In addition, it eliminated the trade-off between the mechanical strength and self-healing capability that is experienced by typical self-healing materials. The developed PCM achieved excellent self-healing and superior bulk (in-plane) and surface (out-of-plane) mechanical strengths compared to those of conventional engineering plastics such as polyether ether ketone (PEEK), polysulfone (PSU), and polyethersulfone (PES). These remarkable properties are attributed to the unique intermolecular structure resulting from strong CTC interactions. A mechanism for the improved self-healing and mechanical properties was also proposed by comparing the CTC-based self-healing PCMs with a non-CTC-based PCM.

A Heterocyclic Polyurethane with Enhanced Self-Healing Efficiency and Outstanding Recovery of Mechanical Properties.

A functional polyurethane based on the heterocyclic group was synthesized and its self-healing and mechanical properties were examined. To synthesize a heterocyclic polyurethane, a polyol and a heterocyclic compound with di-hydroxyl groups at both ends were blended and the blended solution was reacted with a crosslinker containing multiple isocyanate groups. The heterocyclic polyurethane demonstrates better self-healing efficiency than the conventional polyurethane with no heterocyclic groups. Furthermore, unlike the conventional self-healing materials, the heterocyclic polyurethane examined in this study shows an outstanding recovery of the mechanical properties after the self-healing process. These results are attributed to the unique supramolecular network resulting from the strong hydrogen bonding interaction between the urethane group and the heterocyclic group in the heterocyclic polyurethane matrix.