Photoluminescence characteristics of novel Sm3+ ions-doped La1.4 Al22.6 O36 phosphor for n-UV w-LED.

The combustion procedure was used to synthesize La1.4 Al22.6 O36 :Sm3+ phosphors. The X-ray diffraction (XRD) patterns and morphological and photoluminescence properties were investigated. The XRD patterns consisted of a hexagonal crystal structure. At 405 nm, the maximum excitation intensity was obtained. Following 405 nm excitation, three different emission peaks at 573, 604, and 651 nm were seen. Concentration quenching occurred at 1.5 mol% Sm3+ ions. The Commission Internationale de l'éclairage coordinates for the La1.4 Al22.6 O36 phosphor with Sm3+ doping were 604 nm (x = 0.644, y = 0.355) falling in the red region. The findings implied that the prepared phosphor may be used to develop w-light-emitting diodes.

Wet chemical synthesis of BiPO4 :Eu3+ phosphor for w-LED application.

The synthesis of BiPO4 :Eu3+ phosphors has been achieved via a wet chemical process. X-ray diffraction patterns show that the phase of the as-prepared samples matches very well with the standard BiPO4 structure. At 395 nm, the highest excitation intensity was observed. Following 395 nm excitation, two characteristic emission peaks at 592 nm and 616 nm were shown. At 0.5 mol% of Eu3+ ions, concentration quenching occurred. The particle size is within the micrometre range, according to the scanning electron microscope magnification. The chromaticity coordinates for wavelengths 592 nm and 616 nm are (x = 0.586, y = 0.412) and (x = 0.682, y = 0.317), respectively. The findings imply that the prepared phosphor may be used to create white light-emitting diodes.