The orthogonal structure of the widely used hole transporting material (HTM) 2,2',7,7'-tetrakis(N, N-di-p-methoxyphenylamino)-9,9'-spirobifluorene (Spiro-OMeTAD) imparts isotropic conductivity and excellent film-forming capability. However, inherently weak intra- and inter-molecular π-π interactions result in low intrinsic hole mobility. Herein, a novel HTM, termed FTPE-ST, with a twist conjugated dibenzo(g,p)chrysene core and coplanar 3,4-ethylenedioxythiophene (EDOT) as extended donor units, is designed to enhance π-π interactions, without compromising on solubility. The three-dimensional (3D) configuration provides the material multi-direction charge transport as well as excellent solubility even in 2-methylanisole, and its large conjugated backbone endows the HTM with a high hole mobility. Moreover, the sulfur donors in EDOT units coordinate with lead ions on the perovskite surface, leading to stronger interfacial interactions and the suppression of defects at the perovskite/HTM interface. As a result, perovskite solar cells (PSCs) employing FTPE-ST achieve a champion power conversion efficiency (PCE) of 25.21% with excellent long-time stability, one of the highest PCEs for non-spiro HTMs in n-i-p PSCs. In addition, the excellent film-forming capacity of the HTM enables the fabrication of FTPE-ST-based large-scale PSCs (1.0 cm2) and modules (29.0 cm2), which achieve PCEs of 24.21% (certificated 24.17%) and 21.27%, respectively.
As a leading contender to replace lead halide perovskites, tin-based perovskites have demonstrated ever increasing performance in solar cells and light-emitting diodes (LEDs). They tend to be processed with dimethyl sulfoxide (DMSO) solvent, which has been identified as a major contributor to the Sn(II) oxidation during film fabrication, posing a challenge to the further improvement of Sn-based perovskites. Herein, we use NMR spectroscopy to investigate the kinetics of the oxidation of SnI2, revealing that autoamplification takes place, accelerating the oxidation as the reaction progresses. We propose a mechanism consistent with these observations involving water participation and HI generation. Building upon these insights, we have developed low-temperature Sn-based perovskite LEDs (PeLEDs) processed at 60 °C, achieving enhanced external quantum efficiencies (EQEs). Our research underscores the substantial potential of low-temperature DMSO solvent processes and DMSO-free solvent systems for fabricating oxidation-free Sn-based perovskites, shaping the future direction in processing Sn-containing perovskite materials and optoelectronic devices.