Atomic layer deposited films of Al2O3 on fluorine-doped tin oxide electrodes: stability and barrier properties.

Al2O3 layers were deposited onto electrodes by atomic layer deposition. Solubility and electron-transport blocking were tested. Films deposited onto fluorine-doped tin oxide (FTO, F:SnO2/glass) substrates blocked electron transfer to redox couples (ferricyanide/ferrocyanide) in aqueous media. However, these films were rapidly dissolved in 1 M NaOH (≈100 nm/h). The dissolution was slower in 1 M H2SO4 (1 nm/h) but after 24 h the blocking behaviour was entirely lost. The optimal stability was reached at pH 7.2 where no changes were found up to 24 h and even after 168 h of exposure the changes in the blocking behaviour were still minimal. This behaviour was also observed for protection against direct reduction of FTO.

All-printed planar photoelectrochemical cells with digitated cathodes for the oxidation of diluted aqueous pollutants.

A novel outline of a planar photoelectrochemical cell consisting of a semiconductor layer topped by subsequent layers of a digitated insulator and counter electrode is introduced. The use of vertically separated electrodes represents a major development in reducing the footprint (inactive areas) of planar electrochemical cells. The cells, consisting of a nanoparticular titania photoanode and a digitated, metallic cathode, were fabricated by a strictly additive process employing material printing as the exclusive deposition and patterning tool. Transparent conductive oxide-coated glass and polyethyleneterepthalate sheets were used as substrates; nanocrystalline titania dispersion bonded by a novel organosilica binder was used for the fabrication of the photoanode and gold or carbon inks for the fabrication of the digitated cathodes. Due to the digitated shaping of the cathode, photoelectrochemical response was not suffering from iR drop down to low electrolyte ionic strengths. The printed cells were used for electroassisted photocatalytic degradation experiments with aqueous solutions of coumarin. Considerable acceleration of the coumarin degradation rate compared to the plain photocatalytic mode was observed.

Properties and Application Perspective of Hybrid Titania-Silica Patterns Fabricated by Inkjet Printing.

A hybrid titania-silica cold-setting sol has been developed that can be deposited onto a wide variety of surfaces without the need for high-temperature fixing and that is suitable for material printing deposition. Thin hybrid titania-silica coatings were patterned onto glass and PET substrates by inkjet printing. Well-defined hybrid titania-silica patterns, with thicknesses ranging from 40 to 400 nm, were fabricated by overprinting 1 to 10 layers. Excellent mechanical, optical, and photocatalytic properties were observed, making the reported material well suited for the fabrication of transparent self-cleaning coatings both on mineral and organic substrates. The printed patterns exhibit photoelectrochemical activity that can be further improved by thermal or photonic curing. A concept of fully printed interdigitated photoelectrochemical cells on flexible PET substrates utilizing the reported hybrid photocatalyst is disclosed as well.