RESUMEN
Abstract The desire of individuals to have whiter teeth increases the interest in tooth whitening products. Our aim was to in vitro study the whitening effect of hydrogen peroxide, blue covarine and active charcoal containing whitening toothpastes on human teeth. A total of 40 extracted human incisor teeth were used in the study. To measure the whitening effect of toothpastes, the teeth were divided into four subgroups and placed in the phantom tooth jaw model. Then, daily brushing was done with an electric toothbrush. The colors of the teeth were measured initially using the spectrophotometer (single point and bleached shade mode) and at the end of 7th, 14th and 28th days. Whitening effectiveness of toothpastes were studied according to CIEDE2000 formula (ΔE00) and shade guide units (SGU). One- way analysis of variance (ANOVA) and Tukey test were used in the statistical analysis of the data. (p0.05). Blue covarine containing toothpaste had statistically the lowest whitening effect (p<0.05). All toothpastes showed a whitening effect on the teeth after 7 days of use. Activated charcoal containing toothpaste showed more whitening effect after 28 days of use than hydrogen peroxide, blue covarine and traditional toothpaste.
Resumen El deseo de los individuos de tener unos dientes más blancos aumenta el interés por los productos de blanqueamiento dental. Nuestro objetivo fue estudiar el efecto blanqueador de las pastas dentales blanqueadoras que contienen peróxido de hidrógeno, covarina azul y carbón activo en dientes humanos in vitro. En el estudio se utilizaron un total de 40 dientes incisivos humanos extraídos. Para medir el efecto blanqueador de los dentífricos, los dientes se dividieron en cuatro subgrupos y se colocaron en el modelo de diente fantasma en mandíbula. A continuación, se realizó un cepillado diario con un cepillo eléctrico. El color de los dientes se midió inicialmente con un espectrofotómetro (modo de punto único y tono blanqueado) y al final de los días 7, 14 y 28. Se estudió la eficacia blanqueadora de los dentífricos según la fórmula CIEDE2000 (ΔE00) y las unidades de guía de color (SGU). En el análisis estadístico de los datos se utilizó el análisis de varianza de una vía (ANOVA) y la prueba de Tukey. (p0,05). El dentífrico que contiene covarina azul tuvo estadísticamente el menor efecto blanqueador (p<0,05). Todos los dentífricos mostraron un efecto blanqueador en los dientes después de 7 días de uso. Los dentífricos con carbón activado mostraron un mayor efecto blanqueador tras 28 días de uso que el peróxido de hidrógeno, la covarina azul y el dentífrico tradicional.
Asunto(s)
Blanqueamiento de Dientes , Dentífricos , Peróxido de Hidrógeno/análisisRESUMEN
Objective: Unlike traditional composite resins, bulk-fill composite resins could be polymerized as thicker layers. This study aims to contribute to the field by investigating the cytotoxic effects of various bulk-fill composite resins on L929 mouse fibroblast cells in vitro. Material and Methods: In our study, six bulk fill and one conventional composite resin were used. Composite resin samples (8×4 mm) were prepared in a sterile cabinet by using a glass mod and polymerizing with a led light device (DTE LUX E, Germany). Composite samples (n:3) of which surface area was calculated according to ISO 10993-12: 2012 standards (3 cm2/ml), were kept in media for 24 h and 72 h in 37 oC incubator, their extracts were filtered in 1:1 and 1:2 proportion and were added on L929 mouse fibroblast cells. Cell viability was examined by the MTT assay and cell death by the LDH test. Cell viability results were evaluated using one-way analysis of variance (ANOVA) test (p<0.05). Results: When the 1:1 extracts from 4 mm thick bulk-fill composite samples were applied on L929 mouse fibroblast cells, cell viability rates showed significant differences compared to the control group at the end of 24 h and 72 h (except for Estelite Bulk Fill Flow). Although the extracts of the tested composite samples at 1:1 and 1:2 ratio at the end of 72 hours caused a decrease in L929 mouse fibroblast cell viability, the cell viability rate of only PRG-containing bulk fill composite and conventional composite remained below the cell viability ratio (70%) specified in ISO standards. Bulk fill composites did not produce toxic effects (except Beautifil Bulk Restorative) according to the LDH test. Conclusions: Despite decreasing in general the cell viability, bulk-fill composite resins used in 4 mm thick layers provided cell viability rates over the acceptability level, except PRG-containing bulk fill composite (Beautifil Bulk Restorative), which was cytotoxic to L929 mouse fibroblasts. (AU)
Objetivo: Ao contrário das resinas compostas tradicionais, as resinas compostas bulk-fill podem ser polimerizadas como camadas mais espessas. Este estudo visa investigar in vitro os efeitos citotóxicos de várias resinas compostas bulk-fill em células de fibroblastos de camundongo L929.Material e Métodos: Em nosso estudo, seis resinas tipo bulk fill e uma resina composta convencional foram usadas. Amostras de resina composta (8 × 4 mm) foram preparadas em gabinete estéril usando um molde de vidro e polimerizado com um dispositivo de luz LED (DTE LUX E, Alemanha). Amostras compostas (n=3) cuja área de superfície foi calculada de acordo com os padrões ISO 10993-12:2012 (3cm2/ml), foram mantidas em meio e incubadas por 24 h e 72 h a 37 ºC, seus extratos foram filtrados na Proporção de 1:1 e 1:2 e foram acondicionados em cultura de células de fibroblastos de camundongo L929. A viabilidade celular foi examinada pelo ensaio MTT e a morte celular pelo teste LDH. Os resultados de viabilidade celular foram avaliados usando o teste de análise de variância (ANOVA) um fator (p <0,05). Resultados: Quando os extratos foram plaqueados na proporção 1:1 de amostras de compósito bulk-fill de 4 mm de espessura com as células de fibroblastos de camundongo L929, as taxas de viabilidade celular mostraram diferenças significativas em comparação com o grupo controle no final de 24 h e 72 h (exceto para Estelite Bulk Fluxo de enchimento). Embora os extratos das amostras compostas testadas na proporção de 1:1 e 1:2 ao final de 72 horas tenham causado uma diminuição na viabilidade das células de fibroblastos de camundongo L929, a taxa de viabilidade celular apenas do compósito de preenchimento total contendo PRG e o compósito convencional permaneceram abaixo a taxa de viabilidade celular (70%) especificada nas normas ISO. Os compósitos de preenchimento a granel não produziram efeitos tóxicos (exceto Beautifil Bulk Restorative) de acordo com o teste de LDH. Conclusão: Apesar de diminuir em geral a viabilidade celular, as resinas compostas bulk-fill usadas em camadas de 4 mm de espessura forneceram taxas de viabilidade celular acima do nível aceitável, exceto o compósito bulk fill contendo PRG (Beautifil Bulk Restorative), que foi citotóxico para fibroblastos de camundongos L929 (AU)
Asunto(s)
Animales , Ratones , Resinas Compuestas , Toxicidad , FibroblastosRESUMEN
Objective: Dental composites developed by using nanotechnology in the field of dentistry are widely used in the treatment of anterior and posterior teeth. This study aimed to investigate the cytotoxic effects of dental composites of different particle size on L929 mouse fibroblast cell line by extract test method in vitro. Material and Methods: Composite samples of 8 x 2 mm diameter were prepared by polymerizing with led light device by using glass mod in a sterile cabinet. Composite samples of which surface areas were calculated according to ISO standards (3 cm2 / ml), were incubated for 24 and 72 hours, at 37 o C. cell viability was assessed by 3-[4,5-dimethylthiazole-2- yl]-2,5-diphenyltetrazolium bromide (MTT) assay and cell death was evaluated by the lactate dehydrogenase (LDH) leakage assay. Results: The 1:1 extracts of the composites at the end of 24 hours (except for nanoceramic composite) showed no toxic effect. When the cell viability results of the 1:1 extracts of the composite samples at the end of 72 hours were statistically analyzed, significant differences were found comparing to the control group (p < 0.05). Conclusion: It was observed that the type and size of the filler were effective on the toxicity of the composites, and the composites containing Bis-GMA, TEGDMA, UDMA and Bis EMA monomers in their organic matrix showed acceptable cell viability (70%) as specified by ISO. However, the composites with PEGDMA and BPA monomers in their organic matrix showed poor cell viability, which is below the acceptable level of 70%, and were found to have a toxic effect. (AU)
Objetivo: As resinas compostas desenvolvidas pela nanotecnologia no campo da odontologia são amplamente utilizadas no tratamento de dentes anteriores e posteriores. Este estudo teve como objetivo investigar os efeitos citotóxicos de resinas compostas de diferentes tamanhos de partículas na linha celular de fibroblastos de camundongos L929 pelo método de teste de extrato in vitro. Material e Métodos: Amostras compostas de 8 x 2 mm de diâmetro foram preparadas por polimerização com dispositivo de luz led usando um molde de vidro em um gabinete estéril. Amostras de resinas cujas áreas de superfície foram calculadas de acordo com os padrões ISO (3 cm2 / ml), foram incubadas por 24 e 72 horas, a 37 o C. A viabilidade celular foi avaliada pelo ensaio de brometo de 3- [4,5-dimetiltiazol-2- il] -2,5-difeniltetrazólio (MTT) e a morte celular foi avaliada pelo ensaio de infiltração de lactato desidrogenase (LDH). Resultados: Os extratos 1: 1 dos compósitos ao final de 24 horas (exceto o composto nanocerâmico) não apresentaram efeito tóxico. Quando os resultados de viabilidade celular dos extratos 1: 1 das amostras compostas ao final de 72 horas foram analisados, estatisticamente, foram encontradas diferenças significativas em relação ao grupo controle (p < 0,05). Conclusão: Observou-se que o tipo e tamanho da carga foram eficazes na toxicidade dos compósitos, e os compósitos contendo os monômeros Bis-GMA, TEGDMA, UDMA e Bis EMA em sua matriz orgânica apresentaram viabilidade celular aceitável (70%) como especificado pela ISO. No entanto, os compósitos com monômeros PEGDMA e BPA em sua matriz orgânica apresentaram baixa viabilidade celular, que está abaixo do nível aceitável de 70%, e foram encontrados como tendo um efeito tóxico. (AU)