RESUMEN
Dental materials are challenged by wear processes in the oral environment and should be evaluated in laboratory tests prior to clinical use. Many laboratory wear-testing devices are high-cost investments and not available for cross-centre comparisons. The 'Rub&Roll' wear machine enables controlled application of force, chemical and mechanical loading, but the initial design was not able to test against rigid antagonist materials. The current study aimed to probe the sensitivity of a new 'Rub&Roll' set-up by evaluating the effect of force and test solution parameters (deionized water; water + abrasive medium; acid + abrasive medium) on the wear behaviour of direct and indirect dental resin-based composites (RBCs) compared with human molars against 3D-printed rod antagonists. Molars exhibited greater height loss than RBCs in all test groups, with the largest differences recorded with acidic solutions. Direct RBCs showed significantly greater wear than indirect RBCs in the groups containing abrasive media. The acidic + abrasive medium did not result in increased wear of RBC materials. The developed method using the 'Rub&Roll' wear machine in the current investigation has provided a sensitive wear test method to allow initial screening of resin-based composite materials compared with extracted human molars under the influence of different mechanical and erosive challenges.
Asunto(s)
Resinas Compuestas , Materiales Dentales , Ensayo de Materiales , Humanos , Ensayo de Materiales/métodos , Resinas Compuestas/química , Diente Molar , Propiedades de SuperficieRESUMEN
Introduction: Pseudomonas aeruginosa is a leading cause of canine otitis externa. Enrofloxacin is often applied topically to treat this condition, although recalcitrant and recurring infections are common. There is evidence that exposure to blue light (400-470 nm) has a bactericidal effect on P. aeruginosa and other microorganisms. Methods: In the present study, we tested the biocidal effect of blue light (375-450 nm), alone or in combination with enrofloxacin, against six isolates of P. aeruginosa from dogs with otitis externa (5 of which were resistant to enrofloxacin). Results: Treatment of planktonic cell cultures with blue light resulted in significant (p < 0.5) reductions in Colony Forming Units (CFU) for all seven strains tested, in some cases below the limit of detection. The greatest bactericidal effect was observed following exposure to light at 405 nm wavelength (p < 0.05). Exposure to blue light for 20 min usually resulted in a greater reduction in Pseudomonas aeruginosa than enrofloxacin treatment, and combination treatment typically resulted in the largest reductions in CFU. Analysis of the genome sequences of these strains established that enrofloxacin resistance was likely the result of a S466F substitution in GyrB. However, there was no clear association between genotype and susceptibility to blue light treatment. Discussion: These results suggest that blue light treatment, particularly at 405 nm wavelength, and especially in combination with enrofloxacin therapy, could be an effective treatment for otherwise recalcitrant canine otitis externa caused by Pseudomonas aeruginosa. It may also provide a way of extending the usefulness of enrofloxacin therapy which would otherwise be ineffective as a sole therapeutic agent.
RESUMEN
OBJECTIVES: The study aimed to assess the impact of diphenyliodonium hexafluorophosphate (DPI) on the physicochemical properties of experimental resin composites (ECRs) featuring reduced concentrations of camphorquinone (CQ)/amine. METHODS: Five concentrations of CQ (0.125, 0.25, 0.5, 0.75, and 1 mol%) with dimethylaminoethyl amine benzoate (EDAB) in a 1:2 mol% ratio (CQ:EDAB) were incorporated into a 50:50 mass% monomer blend of bisphenol glycidyl methacrylate (BisGMA) and triethyleneglycol dimethacrylate (TEGDMA). An additional 5 groups with the same CQ:EDAB concentrations had 0.5 mol% DPI added. Each resin group contained 60 wt% of 0.7 µm barium-alumino-silicate glass. Light transmission (n = 3), real-time degree of polymerization (n = 3), temperature change during polymerization (n = 5), polymerization shrinkage strain (n = 3), flexural strength, and modulus (n = 12), as well as water sorption and solubility (n = 5), were evaluated. Data were analyzed using two-way ANOVA and Tukey's post-hoc test (α = 0.05). RESULTS: Light transmission was reduced in groups containing 0.125 and 0.25 mol% of CQ without DPI. DPI increased temperature, degree and rate of polymerization, despite the reduction in CQ/amine concentration. Additionally, there was an increase in polymerization shrinkage strain, flexural strength and modulus, and a reduction in water sorption and solubility in ECRs with DPI, even with lower concentrations of CQ/EDAB. SIGNIFICANCE: DPI improved the assessed properties of composites across various concentrations of CQ/EDAB, showing the benefit of reducing the quantity of CQ used without compromising the properties and curing of the resin composites.
RESUMEN
OBJECTIVE: This study investigated the influence of photoinitiator types on degree of conversion (DC), rate of polymerization (RP), flexural strength (FS), flexural modulus (FM), and light transmittance (LT) of filled and unfilled light-curable resin cements through different thicknesses and shades of lithium disilicate ceramics. METHODS: Lithium disilicate ceramic discs (IPS Emax Press, background [0.0], 0.5, 1.0, 2.0, 3.0, and 4.0 mm, shades A1 and BL3) were prepared. Experimental resin-based cements [TEGDMA/BisGMA (50/50 mass%)] were prepared using either camphorquinone (CQ)/amine (0.44/1.85 mol%) or TPO (0.44 mol%)], and a micro and nanofiller loads of nil (unfilled); 40/10 mass%; and 50/10 mass%). Resin cements (0.2 mm thick) were placed on the lower surface of the ceramic specimens and light-activated for 30 s from the upper surface using a Bluephase Style curing light (exitance at tip: 1236 mW/cm2 ± 1.20). LT and distribution of irradiance through the ceramics were measured using a UV-vis spectrometer and a beam profile camera, respectively (n = 3). The DC and RP were measured in real-time using mid infrared spectroscopy in attenuated total reflectance (ATR) mode (n = 3). FS and FM were measured using a universal testing machine (n = 5). Statistical analyses were performed on LT, DC, RP, FS, and FM data using a general linear model, and supplementary ANOVA and post hoc Tukey multiple comparison test were also performed (α = .05). RESULTS: Thicknesses, shades, photoinitiator type, and fillers load significantly influenced the optical and mechanical characteristics of the resin-based materials (p < 0.05). The BL3 shade ceramic provided higher values of DC, RP, FS, FM, and LT compared with the A1 shade (p < 0.05). Increasing ceramic thickness decreased the properties of the resin-based materials (p < 0.05). Generally, TPO improved mechanical properties of the resin cement compared with CQ (p < 0.05). SIGNIFICANCE: The luting process of indirect restorations may be improved by using high molar absorptivity, more reactive, and more efficient photoinitiators such as TPO, as opposed to conventional CQ. The use of such initiator may allow the placement of thicker and more opaque indirect restorations.
RESUMEN
OBJECTIVES: Quality control testing of dental materials requires a standard to enable the generation of reproducible and comparable data. Currently there are no standards for testing materials used for vital pulp therapy. The aim of this study was to develop a new standard to evaluate solubility of pulp preservation materials. METHODS: The solubility of three materials used for vital pulp therapy: Biodentine, TheraCal and Activa was evaluated using two international standards for dental materials ISO 4049:2019 (S1) and ISO 6876:2012 (S2). For both standards, a modified methodology was evaluated. This included changing the volume of the solution used (S1M, S2M), using Dulbecco's modified eagle medium (DMEM) as an alternative to water (S1D, S2D) and periodic solution change for the ISO 4049 method (S1P, S1MP). Materials were characterised before and after completion of solubility test using scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. RESULTS: The test materials exhibited different solubility values depending on the methodology used. Biodentine exhibited significantly lower solubility when lower volumes of solution were used when tested using both ISO methods (p ≤ 0.05). TheraCal and Activa showed negative solubility values after desiccation when tested using ISO 4049:2019. The Biodentine exhibited changes in its microstructure which was dependent on the method used to test solubility. CONCLUSIONS: The solubility values obtained were dependent on the method used. It is thus important to use methods that replicate the clinical environment for meaningful evaluations.
Asunto(s)
Compuestos de Calcio , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Silicatos , Solubilidad , Difracción de Rayos X , Silicatos/química , Compuestos de Calcio/química , Materiales Dentales/química , Compuestos de Aluminio/química , Materiales de Recubrimiento Pulpar y Pulpectomía/química , Óxidos/química , Combinación de MedicamentosRESUMEN
Harnessing the power of light and its photonic energy is a powerful tool in biomedical applications. Its use ranges from biomaterials processing and fabrication of polymers to diagnostics and therapeutics. Dental light curable materials have evolved over several decades and now offer very fast (≤ 10 s) and reliable polymerization through depth (4-6 mm thick). This has been achieved by developments on two fronts: (1) chemistries with more efficient light absorption characteristics (camphorquinone [CQ], ~30 L mol-1 cm1 [Êmax 470 nm]; monoacylphosphine oxides [MAPO], ~800 L mol-1 cm-1 [Êmax 385 nm]; bisacylphosphine oxide [BAPO], ~1,000 L mol-1 cm-1 [Êmax 385 nm]) as well mechanistically efficient and prolonged radical generation processes during and after light irradiation, and; (2) introducing light curing technologies (light emitting diodes [LEDs] and less common lasers) with higher powers (≤ 2 W), better spectral range using multiple diodes (short: 390-405 nm; intermediate: 410-450 nm; and long: 450-480 nm), and better spatial power distribution (i.e. homogenous irradiance). However, adequate cure of materials falls short for several reasons, including improper selection of materials and lights, limitations in the chemistry of the materials, and limitations in delivering light through depth. Photonic energy has further applications in dentistry which include transillumination for diagnostics, and therapeutic applications that include photodynamic therapy, photobiomodulation, and photodisinfection. Light interactions with materials and biological tissues are complex and it is important to understand the advantages and limitations of these interactions for successful treatment outcomes. This article highlights the advent of photonic technologies in dentistry, its applications, the advantages and limitations, and possible future developments.
RESUMEN
INTRODUCTION: Biological characterization of root canal sealers is important as it assesses the ability of the root canal sealer to exert antimicrobial properties thus avoiding treatment failures caused by microbial challenge and also assess the cytotoxic effect on the periapical tissues. Assessment of the biological testing of root canal sealers necessitates the sterilisation of the materials prior to evaluation. This study aims to analyse the influence of various sterilisation techniques conducted prior to biological testing on the microstructure and surface properties of endodontic sealers. Assessment of the initial microbial contamination on the material was also undertaken. METHODS: Four commercial sealers were investigated. The sealers were either prepared in a laminar flow cabinet or on a laboratory bench top under ambient conditions. Each group was further divided into 5 groups (n = 3) based on the sterilization technique:1) ethanol-10 mins, 2) ultraviolet-1 h, 3) ethanol-10 mins + ultraviolet-1 h, 4) autoclave, and 5) no sterilisation (control). Microbial levels in the materials were assessed by plate streaking technique. The materials were characterized by scanning electron microscopy and energy dispersive spectroscopy, and Fourier transform infrared spectroscopy, before and after sterilisation, to assess any changes in microstructure and chemical composition. RESULTS: All the materials did not exhibit contamination when prepared in laminar flow chamber in sterile conditions compared with sealers prepared on the bench top. Three of the commercial materials showed changes in microstructure while one (TotalFill) was not affected by the sterilisation. AH Plus and BioRoot RCS exhibited alterations in water and alcohol peaks in FT-IR while the single syringe sealers (TotalFill and BioRoot Flow) showed no changes. CONCLUSIONS: Sterilisation methods cause physical and chemical alterations to sealers. Material preparation should be performed in a laminar flow cabinet and a test for sterility should be performed prior to any biological testing being undertaken. If the materials are not sterile, assessment of the effects of the sterilization methods is recommended.
Asunto(s)
Materiales de Obturación del Conducto Radicular , Resinas Epoxi/química , Gutapercha/química , Espectroscopía Infrarroja por Transformada de Fourier , Cavidad Pulpar , Compuestos de Calcio/química , Ensayo de Materiales , Etanol , Silicatos/químicaRESUMEN
Photobiomodulation (PBM) is a therapeutic modality that has gained increasing interest in neuroscience applications, including acute traumatic brain injury (TBI). Its proposed mechanisms for therapeutic effect when delivered to the injured brain include antiapoptotic and anti-inflammatory effects. This systematic review summarizes the available evidence for the value of PBM in improving outcomes in acute TBI and presents a meta-analysis of the pre-clinical evidence for neurological severity score (NSS) and lesion size in animal models of TBI. A systematic review of the literature was performed, with searches and data extraction performed independently in duplicate by two authors. Eighteen published articles were identified for inclusion: seventeen pre-clinical studies of in vivo animal models and one clinical study in human patients. The available human study supports safety and feasibility of PBM in acute moderate TBI. For pre-clinical studies, meta-analysis for NSS and lesion size were found to favor intervention versus control. Subgroup analysis based on PBM parameter variables for these outcomes was performed. Favorable parameters were identified as: wavelengths in the region of 665 nm and 810 nm; time to first administration of PBM ≤4 h; total number of daily treatments ≤3. No differences were identified between pulsed and continuous wave modes or energy delivery. Mechanistic substudies within included in vivo studies are presented and were found to support hypotheses of antiapoptotic, anti-inflammatory, and pro-proliferative effects, and a modulation of cellular metabolism. This systematic review provides substantial meta-analysis evidence of the benefits of PBM on functional and histological outcomes of TBI in in vivo mammalian models. Study design and PBM parameters should be closely considered for future human clinical studies.
Asunto(s)
Lesiones Traumáticas del Encéfalo , Lesiones Encefálicas , Terapia por Luz de Baja Intensidad , Animales , Humanos , Lesiones Traumáticas del Encéfalo/radioterapia , Encéfalo , MamíferosRESUMEN
This paper discusses the historical development of dental education and research over the last 150 years from a Birmingham School of Dentistry perspective. The School opened its doors to students in 1858 and has seen many changes and developments in both education and research. Looking back throughout the history, one of our greatest abilities as dental professionals is to be adaptable and the future will bring plenty of opportunity for us to demonstrate this. We have seen how resilient dentistry has been over the COVID-19 pandemic, both in terms of education and research; the next 150 years will be a very exciting time to work in the field.
Asunto(s)
COVID-19 , Educación en Odontología , Humanos , Estudiantes de Odontología , Pandemias , COVID-19/epidemiología , Instituciones AcadémicasRESUMEN
OBJECTIVES: To develop a risk of bias tool for pre-clinical dental materials research studies that aims to support reporting of future investigations and improve assessment in systematic reviews. METHODS: A four-stage process following EQUATOR network recommendations was followed, which included project launch, literature review, Delphi process and the tool finalization. With the support of the European Federation of Conservative Dentistry (EFCD) and the Dental Materials Group of the International Association for Dental Research (DMG-IADR), a total of 26 expert stakeholders were included in the development and Delphi vote of the initial proposal. The proposal was built using data gathered from the literature review stage. During this stage, recent systematic reviews featuring dental materials research, and risk of bias tools found in the literature were comprehensively scanned for bias sources. The experts thus reached a consensus for the items, domains and judgement related to the tool, allowing a detailed guide for each item and corresponding signalling questions. RESULTS: The tool features nine items in total, spread between 4 domains, pertaining to the following types of bias: bias related to planning and allocation (D1), specimen preparation (D2), outcome assessment (D3) and data treatment and outcome reporting (D4). RoBDEMAT, as presented, features signalling questions and a guide that can be used for RoB judgement. Its use as a checklist is preferred over a final summary score. CONCLUSION: RoBDEMAT is the first risk of bias tool for pre-clinical dental materials research, supported and developed by a broad group of expert stakeholders in the field, validating its future use. CLINICAL SIGNIFICANCE: This new tool will contribute the study field by improving the scientific quality and rigour of dental materials research studies and their systematic reviews. Such studies are the foundation and support of future clinical research and evidence-based decisions.
Asunto(s)
Lista de Verificación , Publicaciones , Revisiones Sistemáticas como Asunto , Sesgo , Materiales DentalesRESUMEN
Apoptotic cell death within the brain represents a significant contributing factor to impaired post-traumatic tissue function and poor clinical outcome after traumatic brain injury. After irradiation with light in the wavelength range of 600-1200 nm (photobiomodulation), previous investigations have reported a reduction in apoptosis in various tissues. This study investigates the effect of 660 nm photobiomodulation on organotypic slice cultured hippocampal tissue of rats, examining the effect on apoptotic cell loss. Tissue optical Raman spectroscopic changes were evaluated. A significantly higher proportion of apoptotic cells 62.8±12.2% vs 48.6±13.7% (P<0.0001) per region were observed in the control group compared with the photobiomodulation group. After photobiomodulation, Raman spectroscopic observations demonstrated 1440/1660 cm-1 spectral shift. Photobiomodulation has the potential for therapeutic utility, reducing cell loss to apoptosis in injured neurological tissue, as demonstrated in this in vitro model. A clear Raman spectroscopic signal was observed after apparent optimal irradiation, potentially integrable into therapeutic light delivery apparatus for real-time dose metering.
Asunto(s)
Lesiones Traumáticas del Encéfalo , Terapia por Luz de Baja Intensidad , Animales , Apoptosis , Encéfalo , Lesiones Traumáticas del Encéfalo/metabolismo , Hipocampo/metabolismo , Terapia por Luz de Baja Intensidad/métodos , Ratas , Espectrometría RamanRESUMEN
OBJECTIVE: Guided bone regeneration (GBR) techniques use barrier membranes to augment the alveolar ridge for the site-specific growth of bone defects. However, current approaches using cast metal substructures exhibit poor adaptation to the surgical site and increased risk of infection. This study aimed to fabricate multi-functional coatings with 3D-printed porous titanium-niobium (Ti-Nb) alloy meshes to maintain space, prevent the ingrowth of fibroblasts and inhibit the colonization of bacteria for GBR. METHODS: Ti-Nb alloy meshes were prepared by selective laser melting (SLM) and used as substrates for novel surface coatings. Porous chitosan (CS)/ gelatin (G)/ doxycycline (Dox) coatings were formed on the meshes using electrophoretic deposition (EPD) and freeze-drying. The process of EPD was characterized through Fourier transform infrared spectroscopy (FT-IR), zeta potential, and particle size analysis. The cytotoxicity of the coatings was evaluated through the culture of osteoblasts and immunostaining. The antibacterial activity of the coatings was tested using inhibition zone tests against Staphylococcus aureus (S. aureus) and scanning electron microscope (SEM). The inhibition of fibroblasts infiltration and nutrients transfer properties were analyzed using immunostaining and permeability tests. RESULTS: High yield strength (567.5 ± 3.5 MPa) and low elastic modulus (65.5 ± 0.2 GPa) were achieved in Ti-Nb alloy bulk samples. The data of zeta potential, FT-IR and SEM indicated that porous spongy coatings were chemically bonded following EPD. In vitro analysis of CSGDox1 (containing Dox at 1 mg·mL-1) coating revealed its antibacterial effect and biocompatibility. Moreover, the CSGDox1 coating was proved to be effective for preventing the ingrowth of fibroblasts, whilst allowing the infiltration of nutrients. SIGNIFICANCE: This study verified that the EPD of CSGDox coatings on the 3D-printed Ti-Nb meshes can maintain space, provide antibiotic release whilst maintaining a barrier against soft-tissue growth, which is essential for the success of GBR treatment.
Asunto(s)
Implantes Dentales , Titanio , Aleaciones/farmacología , Regeneración Ósea , Materiales Biocompatibles Revestidos/química , Materiales Biocompatibles Revestidos/farmacología , Niobio/química , Impresión Tridimensional , Espectroscopía Infrarroja por Transformada de Fourier , Staphylococcus aureus , Titanio/químicaRESUMEN
To determine the influence of light curing units (LCUs) and material viscosity on the degree of conversion (DC) of bulk-fill (BF) resin-based composites (RBCs) placed in deep cavity preparations. Four LCUs were tested: Valo cordless, Bluephase-G2, Poly wireless and Radii-cal. Light irradiance was determined at 0 mm and 6 mm distance to the reading sensor. The following RBCs were considered: Filtek BF, Filtek BF Flow, Opus BF, Opus BF Flow, Tetric N-Ceram BF and Surefil SDR Flow. Sirius-Z was used with the incremental technique. DC (n = 3) was evaluated by spectroscopy both at top and bottom regions of deep preparations with 6 mm depth. The data were submitted to ANOVA and Tukey's test (α = 0.05). Pearson's correlation (95%) was used to verify the relation between the LCUs and the curing potential of RBCs. The DC at 6 mm depth was reduced when Opus BF, Opus BF Flow and Tetric N-Ceram BF were activated with Radii-cal. There was a positive correlation between the LCU irradiance and the bottom/top conversion ratios. The materials' viscosities did not affect the curing potential. Bulk-fill composites did not present higher curing potential than the conventional composite used with the incremental technique; the most important aspect of the LCU was the irradiance ratio; and the materials' viscosity did not affect the curing potential as a function of depth. Radii-cal negatively impacted the degree of conversion at 6 mm depth for most bulk-fill resin composites. Depending on the brand, bulk-fill composites may present reduced curing potential due to the light source when placed in deep cavities. Dentists should avoid LCU with acrylic tips to photoactivate bulk-fill resin-based composites.
Asunto(s)
Luces de Curación Dental , Ensayo de Materiales , Polimerizacion , Propiedades de Superficie , ViscosidadRESUMEN
This study investigated the accuracy of sixteen models of commercial dental radiometers (DR) in measuring the output of thirty-eight LED light curing units (LCUs) compared with a 'gold standard' laboratory-grade spectrometer integrating-sphere (IS) assembly. Nineteen Type I (fiber-bundle light guide) and nineteen Type II (light source in head) LED LCUs were tested, some using different output modes and light guides, resulting in 61 test subsets per radiometer. Gold standard (GS) output measurements (n = 3) were taken using the IS and confirmed with two types of laboratory-grade power meter (PowerMax-Pro 150 HD and PM10-19C; Coherent). One DR (Bluephase Meter II, Ivoclar; BM II) allowed power (mW) as well as irradiance (mW/cm2) recordings. Irradiance readings (n = 3) for each DR/LCU were compared with the IS derived irradiance. Individual LCU irradiance values were normalized against IS data. The GS method yielded reproducible data with a 0.4% pooled coefficient of variation for the LCUs. Mean power values ranged from 0.19 W to 2.40 W. Overall power values for the laboratory-grade power meters were within 5% of GS values. Individual LCU/DR normalized irradiance values ranged from 7% to 535% of the GS; an order of magnitude greater than previous reports. BM II was the only radiometer to average within 20% of normalized pooled GS irradiance values, whereas other radiometers differed by up to 85%. Ten radiometers failed to provide any reading for 1 LCU. When tested with the PowerMax-Pro in high speed (20 kHz) mode, eight LCUs demonstrated pulsing outputs undetectable at the standard (10 Hz) data acquisition rate. Sufficient light exposure is critical for the successful curing of dental resin-based materials. Substantial discrepancies may occur between actual and estimated radiometric data using current DRs. More accurate DRs need to be developed. Manufacturers' accuracy claims for DRs should specify compatible LCUs and testing parameters.
Asunto(s)
Luces de Curación Dental/normas , Radiometría/instrumentación , Radiometría/normas , Reproducibilidad de los ResultadosRESUMEN
The direct application of light for photo-disinfection potentially provides a safe and novel modality to inhibit or eliminate cariogenic bacteria residing upon and within dentine. This study aimed to both; characterize the pattern of transmission of 405 nm light through molar dentine at different tooth locations, as well as, determine the irradiation parameters that are antibacterial for Streptococcus mutans under various growth conditions, including lawns, planktonic cultures, and biofilms. To determine the amount of light (405 nm) transmitted at different anatomical tooth locations; irradiance values were recorded after blue light (470-4054 mW/cm2) had traversed through occlusal, oblique, and buccal dentine sections; and three thicknesses - 1, 2 and 3 mm were investigated. To determine tubular density; scanning electron micrographs from 2 mm outer (dentine-enamel junction) and inner (pulp) dentine sections were analysed. For photo-disinfection studies; S. mutans was irradiated using the same 405 nm wavelength light at a range of doses (110-1254 J/cm2) in both biofilm and planktonic cultures. The inhibitory effect of the irradiation on bacterial lawns was compared by measuring zones of inhibition; and for planktonic cultures both spectrophotometric and colony forming unit (CFU) assays were performed. A live/dead staining assay was utilised to determine the effect of irradiation on bacterial viability in mature biofilms. Data indicated that increasing dentine thickness decreased light transmission significantly irrespective of its orientation. Occlusal and oblique samples exhibited higher transmission compared with buccal dentine. Oblique dentine 405 nm light transmission was comparable with that of occlusal dentine independent of section thickness. An increased tubule density directly positively correlated with light transmission. Irradiation at 405 nm inhibited S. mutans growth in both biofilm and planktonic cultures and a dose response relationship was observed. Irradiation at doses of 340 and 831 J/cm2 led to significant reductions in bacterial growth and viability; as determined by CFU counting and live/dead staining. Data suggests that phototherapy approaches utilising a 405 nm wavelength have therapeutic potential to limit cariogenic bacterial infections both at the surface and within dentine.
Asunto(s)
Dentina/efectos de la radiación , Desinfección/métodos , Luz , Adulto , Color , Dentina/microbiología , Femenino , Humanos , Masculino , Viabilidad Microbiana/efectos de la radiación , Streptococcus mutans/fisiología , Streptococcus mutans/efectos de la radiación , Adulto JovenRESUMEN
The chemistry of resin-based dental adhesives is critical for its interaction with dental tissues and long-term bonding stability. Changes in dental adhesives composition influences the materials' key physical-chemical properties, such as rate and degree of conversion, water sorption, solubility, flexural strength and modulus, and cohesive strength and improves the biocompatibility to dental tissues. Maintaining a suitable reactivity between photoinitiators and monomers is important for optimal properties of adhesive systems, in order to enable adequate polymerisation and improved chemical, physical and biological properties. The aim of this article is to review the current state-of-the-art of dental adhesives, and their chemical composition and characteristics that influences the polymerisation reaction and subsequent materials properties and performance.
Asunto(s)
Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Adhesivos , Resinas Compuestas , Cementos Dentales , Dentina , Ensayo de Materiales , Cementos de ResinaRESUMEN
OBJECTIVE: To evaluate the influence of different co-initiators (diphenyliodonium hexafluorophosphate - DPI - and bis(4-methyl phenyl)iodonium hexafluorophosphate - BPI) on chemical and mechanical properties of resins. METHODS: Nine experimental resins (50% Bis-GMA and 50% TEGDMA, w/w) with 60 wt% filler particles were formulated. The initiating system used was camphorquinone (CQ-1 mol%) and ethyl dimethylaminobenzoate (EDAB-2 mol%). Experimental groups were established according to DPI and BPI quantities (0.25, 0.5, 0.75, and 1 mol%). The control group was a resin containing only CQ-EDAB. Light transmission through the resin during polymerisation was analysed with a UV-vis spectrophotometer. Real-time polymerisation of the systems was evaluated using an FTIR spectrometer. Real-time polymerisation shrinkage strain was evaluated, and the flexural strength and modulus of materials were obtained by 3-point bending. Experimental groups were statistically analysed by Analysis of Variance and Tukey's test (α = 0.05). Dunnett's test was applied to compare experimental groups with control. RESULTS: Light transmission rapidly increased initially for resins containing DPI or BPI. After 30 s cure, the irradiance on the lower surface of resin specimens was similar for all groups. After 10 s of light irradiation, groups containing DPI and BPI had higher conversion than the control. However, conversion after 120 s post-irradiation was similar for all groups. The rate of polymerisation, shrinkage strain, and the maximum strain rate were higher for groups containing DPI/BPI. The use of iodonium salts increased the flexural strength and flexural moduli of resins. SIGNIFICANCE: DPI and BPI increased resin reactivity similarly. Increased rate of polymerization influenced light transmission through the resin in the first seconds of polymerisation and increased resin shrinkage and rate of shrinkage, as well as flexural strength and moduli.
Asunto(s)
Compuestos de Bifenilo , Compuestos Onio , Bisfenol A Glicidil Metacrilato , Alcanfor/análogos & derivados , Resinas Compuestas , Ensayo de Materiales , Metacrilatos , Polietilenglicoles , Polimerizacion , Ácidos PolimetacrílicosRESUMEN
OBJECTIVE: The structure of the polymer phase of dental resin-based-composites is highly sensitive to photo-polymerisation variables. The objective of this study was to understand how different polymer structures, generated with different photo-polymerisation protocols, respond to thermal perturbation. METHODS: Experimental resins were prepared from a series of Bis-GMA/TEGDMA blends (40/60, 50/50 and 60/40 wt.%), with either Camphorquinone/DMAEMA or Lucirin TPO as the photo-initiator system. Resins were photo-polymerised, in a disc geometry, at either relatively 'high' (3000 mW cm-2 for 6 s) or 'low' (300 mW cm-2 for 60 s) irradiances ensuring matched radiant exposures (18 J cm-2). Specimens were heated, from 20-160 °C at a rate of 5 °C min-1, whilst simultaneous synchrotron X-ray scattering measurements were taken at 5 °C increments to determine changes in polymer chain segment extension and medium-range order as a function of temperature. For each unique resin composition (n = 3), differential scanning calorimetry was used to measure glass transition temperatures using the same heating protocol. A paired t-test was used to determine significant differences in the glass transition temperature between irradiance protocols and photo-initiator chemistry at É = 0.05. RESULTS: Resins pre-polymerised through the use of TPO and or high irradiances demonstrated a reduced rate of chain extension indicative of lower thermal expansion and a larger decrease in relative order when heated below the glass transition temperature. Above the transition temperature, differences in the rate of chain extension were negligible, but slower converted systems showed greater relative order. There was no significant difference in the glass transition temperature between different photo-initiator systems or irradiance protocols. SIGNIFICANCE: The evolution of chain extension and medium-range order during heating is dependent on the initial polymer structure which is influenced by photo-polymerisation variables. Less ordered systems, generated at faster rates of reactive group conversion displayed reduced chain extension below the glass transition temperature and maintained lower order throughout heating.
Asunto(s)
Resinas Compuestas , Resinas Sintéticas , Bisfenol A Glicidil Metacrilato , Ensayo de Materiales , Polietilenglicoles , Polimerizacion , Ácidos Polimetacrílicos , Resinas de Plantas , TemperaturaRESUMEN
Photobiomodulation (PBM) describes the application of light at wavelengths ranging from 400-1100 nm to promote tissue healing, reduce inflammation and promote analgesia. Traditionally, red and near-infra red (NIR) light have been used therapeutically, however recent studies indicate that other wavelengths within the visible spectrum could prove beneficial including blue and green light. This review aims to evaluate the literature surrounding the potential therapeutic effects of PBM with particular emphasis on the effects of blue and green light. In particular focus is on the possible primary and secondary molecular mechanisms of PBM and also evaluation of the potential effective parameters for application both in vitro and in vivo. Studies have reported that PBM affects an array of molecular targets, including chromophores such as signalling molecules containing flavins and porphyrins as well as components of the electron transport chain. However, secondary mechanisms tend to converge on pathways induced by increases in reactive oxygen species (ROS) production. Systematic evaluation of the literature indicated 72% of publications reported beneficial effects of blue light and 75% reported therapeutic effects of green light. However, of the publications evaluating the effects of green light, reporting of treatment parameters was uneven with 41% failing to report irradiance (mW cm-2) and 44% failing to report radiant exposure (J cm-2). This review highlights the potential of PBM to exert broad effects on a range of different chromophores within the body, dependent upon the wavelength of light applied. Emphasis still remains on the need to report exposure and treatment parameters, as this will enable direct comparison between different studies and hence enable the determination of the full potential of PBM.
RESUMEN
To evaluate the effects of Type I and Type II photoinitiator systems on curing efficiency, degree of conversion (DC) and chemico-physical properties of resin based materials. A comonomer base containing 50%wt 2.2-bis[4-(2-hydroxy-3-methacryloxypropoxy)phenyl]propane (bis-GMA) and 50%wt triethyleneglycol dimethacrylate (TEGDMA) was formulated with either 0.5 or 1mol% of Type II camphoroquinone (CQ), Type I monoacylphosphine oxide (MAPO) or bis-acylphosphine oxide (BAPO) photoinitiators. The Type II system was either a binary (1: 2 CQ:amine) or ternary system (1: 2 CQ:amine + 0.5 mol% DPI). Degree and rate of polymerization was measured by Fourier Transform Infrared Spectroscopy (FTIR). Knoop micro-hardness prior to and following ethanol immersion was assessed. Flexural strength and modulus was measured under three-point bend test. Water sorption and solubility was also evaluated. The photoinitiator absorption spectra and the total absorbed energy per unit volume (Eabs) for 0.5mol% photoinitiator in each material was calculated. Despite the reduced total absorbed energy per unit volume for CQ based systems, ternary Type II system significantly improved curing efficiency (Pâ¯<â¯0.05) compared to both Type I photoinitiators and degree of conversion compared to MAPO only, whilst exhibiting comparable mechanical and physical properties compared to both Type I based materials at equivalent molar concentrations of photoinitiator (Pâ¯>â¯0.05). Ternary Type II systems is an efficient alternative to improve the polymerization of resin materials, promoting similar or even better properties than Type I initiators. DPI can increase the reactivity of CQ systems and promote polymerization rates superior than Type I photoinitiators.