Biochar-MgO from Soursop Seeds in the Production of Biofuel Additive Intermediates.

The conversion of residual biomass from fruit seeds into biochar can be achieved using MgCl2 as an activating agent and calcining at 700 °C. The resulting MgO-biochars were employed in the aldol condensation reaction between furfural and acetone. This reaction is essential as the first step in the obtention of biofuels derived from biomass. The biochars were characterized through various physicochemical techniques, revealing that the presence of MgO nanoparticles deposited on the carbon surface modifies the structural and acidic-basic properties of the carbonaceous materials with a graphitic structure. The biochar with a surface content of MgO of 0.34 % w/w enables the achievement of 100 % of selectivity towards 4-(2-furanyl)-3-buten-2-one (I) with quantitative conversions under optimized conditions. This property highlights the potential of using this type of biochar, commonly used for CO2 capture, as a versatile acidic-basic catalyst, thereby introducing a novel approach to sustainable chemistry.

Effect of Metal Content on Ethanol Decomposition over Ni-Co Catalysts Supported on La-Ce Oxides.

The search for catalysts with features that can improve coke resistance and decrease byproduct formation is a current goal in H2 production from renewable sources. In this work, the effect of the presence of Ni nanoparticles over Co/La-Ce oxides on the ethanol decomposition reaction was studied. Catalysts were synthetized using as precursor a La0.8Ce0.2NixCo1-xO3 perovskite-type material to ensure a low segregation of phases and a high dispersion of metals. After reduction at 873 K, the perovskite structure was destroyed, and metal Co-Ni particles were supported over a lanthanum-cerium oxide. The materials were characterized by different techniques before and after reaction. Solids exhibited metal particle sizes between 5 and 15 nm demonstrating the advantages of the preparation method to obtain Ni-Co alloys. Although the results of adsorption of ethanol followed by diffuse reflectance infrared fourier transformed spectroscopy (DRIFTS) showed acetate species strongly adsorbed on the catalyst's surface, the material (Ni0.7Co0.3/La0.8Ce0.2) with the lowest particle size was the most stable system leading to the lowest amount of carbon deposits during ethanol decomposition. This catalyst showed the better performance, with a higher ethanol conversion (98.4%) and hydrogen selectivity (75%). All catalysts exhibited carbonaceous deposits, which were an ordered and disordered carbon phase mixture.