RESUMEN
Wood-plastic composites (WPCs) are some of the most common modern composite materials for interior and exterior design that combine natural waste wood properties and the molding possibility of a thermoplastic polymer binder. The addition of reinforcing elements, binding agents, pigments, and coatings, as well as changes to the microstructure and composition, can all affect the quality of WPCs for particular purposes. To improve the properties, hybrid composite panels of WPCs with 30 wt. % and 40 wt. % of wood content and reinforced with one or three metal grid layers were prepared sequentially by extrusion and hot pressure molding. The results show an average 20% higher moisture absorption for composites with higher wood content. A high impact test (HIT) revealed that the absorbed energy of deformation increased with the number of metal grid layers, regardless of the wood content, around two times for all samples before water immersion and around ten times after water absorption. Also, absorbed energy increases with raised wood content, which is most pronounced in three-metal-grid samples, from 21 J to 26 J (before swelling) and from 15 J to 24 J (after swelling). Flexural tests follow the trends observed by HIT, indicating around 65% higher strength for samples with three metal grid layers vs. samples without a metal grid before water immersion and around 80% higher strength for samples with three metal grid layers vs. samples without a grid after water absorption. The synthesis route, double reinforcing (wood and metal), applied methods of characterization, and optimization according to the obtained results provide a WPC with improved mechanical properties ready for an outdoor purpose.
RESUMEN
Polymer-bonded magnets are a class of composite material that combines the magnetic properties of metal particles and the molding possibility of a polymeric matrix. This class of materials has shown huge potential for various applications in industry and engineering. Traditional research in this field has so far mainly focused on mechanical, electrical or magnetic properties of the composite, or on particle size and distribution. This examination of synthesized Nd-Fe-B-epoxy composite materials includes the mutual comparison of impact toughness, fatigue, and the structural, thermal, dynamic-mechanical, and magnetic behavior of materials with different content of magnetic Nd-Fe-B particles, in a wide range from 5 to 95 wt.%. This paper tests the influence of the Nd-Fe-B content on impacting the toughness of the composite material, as this relationship has not been tested before. The results show that impact toughness decreases, while magnetic properties increase, along with increasing content of Nd-Fe-B. Based on the observed trends, selected samples have been analyzed in terms of crack growth rate behavior. Analysis of the fracture surface morphology reveals the formation of a stable and homogeneous composite material. The synthesis route, the applied methods of characterization and analysis, and the comparison of the obtained results can provide a composite material with optimum properties for a specific purpose.
RESUMEN
Antibiotic containing polycaprolactone (PCL) fibers were produced by using three electrospinning methods: blend, emulsion and co-axial electrospinning (labeled as S1, S2 and S3, respectively). The profiles of drug release from three different systems were studied and antimicrobial properties of produced materials were evaluated. Morphology of the produced fibers was characterized and revealed that cefazolin-loaded PCL fibers had smaller diameter compared to neat PCL fibers, while the chemical interaction between the antibiotic and PCL showed that cefazolin neither had reacted with PCL phase, nor had degraded during the electrospinning process. The crystallinity and thermal characterization of fabricated fibers showed that the addition of cefazolin decreased the crystallinity of PCL. The results of the drug release behavior of the blend and co-axial electrospun fibers was on a higher level (~68% and ~43%, respectively) compared to the emulsion electrospun fibers (~5%), after a period of 30â¯days. The obtained data had the best fitting with the first order model and the Higuchi model, while the Korsmeyer-Peppas model showed a Pseudo-Fickian diffusion of the drug. Antibacterial evaluations showed that cefazolin-loaded PCL fibers had better effects on Staphylococcus aureus compared to Escherichia coli during the treatment period and that the effect of the emulsion fibers was notably weaker than the other two studied systems. The aim of the study was to test different systems for control drug release of different dynamics, which will be applied for prevent bacterial accumulation when indwelling urinary catheters, applied for different periods of time.