Electroreduction of CO2 on Single-Site Copper-Nitrogen-Doped Carbon Material: Selective Formation of Ethanol and Reversible Restructuration of the Metal Sites.

It is generally believed that CO2 electroreduction to multi-carbon products such as ethanol or ethylene may be catalyzed with significant yield only on metallic copper surfaces, implying large ensembles of copper atoms. Here, we report on an inexpensive Cu-N-C material prepared via a simple pyrolytic route that exclusively feature single copper atoms with a CuN4 coordination environment, atomically dispersed in a nitrogen-doped conductive carbon matrix. This material achieves aqueous CO2 electroreduction to ethanol at a Faradaic yield of 55 % under optimized conditions (electrolyte: 0.1 m CsHCO3 , potential: -1.2 V vs. RHE and gas-phase recycling set up), as well as CO electroreduction to C2 -products (ethanol and ethylene) with a Faradaic yield of 80 %. During electrolysis the isolated sites transiently convert into metallic copper nanoparticles, as shown by operando XAS analysis, which are likely to be the catalytically active species. Remarkably, this process is reversible and the initial material is recovered intact after electrolysis.

Identification of catalytic sites in cobalt-nitrogen-carbon materials for the oxygen reduction reaction.

Single-atom catalysts with full utilization of metal centers can bridge the gap between molecular and solid-state catalysis. Metal-nitrogen-carbon materials prepared via pyrolysis are promising single-atom catalysts but often also comprise metallic particles. Here, we pyrolytically synthesize a Co-N-C material only comprising atomically dispersed cobalt ions and identify with X-ray absorption spectroscopy, magnetic susceptibility measurements and density functional theory the structure and electronic state of three porphyrinic moieties, CoN4C12, CoN3C10,porp and CoN2C5. The O2 electro-reduction and operando X-ray absorption response are measured in acidic medium on Co-N-C and compared to those of a Fe-N-C catalyst prepared similarly. We show that cobalt moieties are unmodified from 0.0 to 1.0 V versus a reversible hydrogen electrode, while Fe-based moieties experience structural and electronic-state changes. On the basis of density functional theory analysis and established relationships between redox potential and O2-adsorption strength, we conclude that cobalt-based moieties bind O2 too weakly for efficient O2 reduction.Nitrogen-doped carbon materials with atomically dispersed iron or cobalt are promising for catalytic use. Here, the authors show that cobalt moieties have a higher redox potential, bind oxygen more weakly and are less active toward oxygen reduction than their iron counterpart, despite similar coordination.

Metal-Doped Nitrogenated Carbon as an Efficient Catalyst for Direct CO2 Electroreduction to CO and Hydrocarbons.

This study explores the kinetics, mechanism, and active sites of the CO2 electroreduction reaction (CO2RR) to syngas and hydrocarbons on a class of functionalized solid carbon-based catalysts. Commercial carbon blacks were functionalized with nitrogen and Fe and/or Mn ions using pyrolysis and acid leaching. The resulting solid powder catalysts were found to be active and highly CO selective electrocatalysts in the electroreduction of CO2 to CO/H2 mixtures outperforming a low-area polycrystalline gold benchmark. Unspecific with respect to the nature of the metal, CO production is believed to occur on nitrogen functionalities in competition with hydrogen evolution. Evidence is provided that sufficiently strong interaction between CO and the metal enables the protonation of CO and the formation of hydrocarbons. Our results highlight a promising new class of low-cost, abundant electrocatalysts for synthetic fuel production from CO2 .

Noble-metal-free electrocatalysts with enhanced ORR performance by task-specific functionalization of carbon using ionic liquid precursor systems.

The synthesis and characterization of functionalized carbon using variable doping profiles are presented. The hybrids were obtained from nitrile-functionalized ionic precursors and a ferric chloride mediator. This way, novel nitrogen doped and nitrogen-sulfur, nitrogen-phosphorus, and nitrogen-boron codoped carbon hybrids with a morphology containing microporous nanometer-sized particles were obtained. As-prepared heteroatom doped carbons exhibited superior electrocatalytic activity toward the oxygen reduction reaction (ORR) in alkaline and acid electrolytes. In particular, both the heteroatom type and iron were found to play crucial roles in improving the catalytic activity of functionalized carbon. It is worth noting that sulfur-nitrogen codoped functionalized materials synthesized in the presence of ferric chloride showed higher activity and stability in comparison to those of the commercial state-of-the-art Pt catalyst in alkaline electrolyte. Moreover, in acid electrolyte, sulfur-nitrogen codoped catalyst rivaled the activity of Pt with a stability outperforming that of Pt. Our X-ray photoelectron spectroscopy (XPS) investigation revealed a distinctive atomic structure in nitrogen-sulfur codoped material in comparison to other codoped catalysts, most likely explaining its superior electrocatalytic activity. This work presents a novel toolbox for designing advanced carbon hybrids with variable heteroatom doping profiles which presents tunable and enhanced ORR performance.