Effects of Structurally Different Tertiary Amines on the Properties of Quaternized Anionic Exchange Membranes Potentially Applicable for Water Electrolysis.

In this work, two structurally different monoamines (trimethylamine [TMA] and N-methylpiperidine [N-MPip]) are used for the amination of a g-VBC-15 graft copolymer, obtained by the functionalization of a mechanically robust, commercially available styrene-butadiene block copolymer (SB) with vinylbenzyl chloride (VBC) via solution free-radical polymerization. Results demonstrate that g-VBC-15-based membranes quaternized with TMA have superior electrochemical performance than N-MPip counterparts; while, the mechanical properties are good and only slightly inferior to those of N-MPip. Therefore, TMA is the selected monoamine to be alternatively mixed with two polyamines (tetramethyl-1,3-propanediamine [TMPDA] and N,N,N',N'',N''-pentamethyldiethylenetriamine [PMDETA]) into different proportions, in order to modulate the average functionality of the amination mixture in terms of number of amine functional groups available for the quaternization reaction of the membranes. g-VBC-15-based membranes derived therefrom are extensively characterized to assess their thermal, mechanical, and ex situ electrochemical properties. Results indicate that membranes quaternized with a TMA/PMDETA mixture (90:10 in mole) display the highest conductivity among all the investigated membranes aminated with polyamine-based mixtures. Moreover, they have comparable mechanical and electrochemical properties to those quaternized with TMA, while exhibiting a reduced water uptake.

Vinylbenzyl Chloride/Styrene-Grafted SBS Copolymers via TEMPO-Mediated Polymerization for the Fabrication of Anion Exchange Membranes for Water Electrolysis.

In this work, a commercial SBS was functionalized with the 2,2,6,6-tetramethylpiperidin-N-oxyl stable radical (TEMPO) via free-radical activation initiated with benzoyl peroxide (BPO). The obtained macroinitiator was used to graft both vinylbenzyl chloride (VBC) and styrene/VBC random copolymer chains from SBS to create g-VBC-x and g-VBC-x-co-Sty-z graft copolymers, respectively. The controlled nature of the polymerization as well as the use of a solvent allowed us to reduce the extent of the formation of the unwanted, non-grafted (co)polymer, thereby facilitating the graft copolymer's purification. The obtained graft copolymers were used to prepare films via solution casting using chloroform. The -CH2Cl functional groups of the VBC grafts were then quantitatively converted to -CH2(CH3)3N+ quaternary ammonium groups via reaction with trimethylamine directly on the films, and the films, therefore, were investigated as anion exchange membranes (AEMs) for potential application in a water electrolyzer (WE). The membranes were extensively characterized to assess their thermal, mechanical, and ex situ electrochemical properties. They generally presented ionic conductivity comparable to or higher than that of a commercial benchmark as well as higher water uptake and hydrogen permeability. Interestingly, the styrene/VBC-grafted copolymer was found to be more mechanically resistant than the corresponding graft copolymer not containing the styrene component. For this reason, the copolymer g-VBC-5-co-Sty-16-Q with the best balance of mechanical, water uptake, and electrochemical properties was selected for a single-cell test in an AEM-WE.