The use of bio-based reagents for silver nanoparticle (AgNP) production has gained much attention among researchers as it has paved the way for environmentally friendly approaches at low cost for synthesizing nanomaterials while maintaining their properties. In this study, Stellaria media aqueous extract was used for silver nanoparticle phyto-synthesis, and the resulting treatment was applied to textile fabrics to test its antimicrobial properties against bacteria and fungi strains. The chromatic effect was also established by determining the L*a*b* parameters. For optimizing the synthesis, different ratios of extract to silver precursor were tested using UV-Vis spectroscopy to observe the SPR-specific band. Moreover, the AgNP dispersions were tested for their antioxidant properties using chemiluminescence and TEAC methods, and the phenolic content was evaluated by the Folin-Ciocâlteu method. For the optimal ratio, values of average size, 50.11 ± 3.25 nm, zeta potential, -27.10 ± 2.16 mV, and polydispersity index, 0.209, were obtained via the DLS technique and zeta potential measurements. AgNPs were further characterized by EDX and XRD techniques to confirm their formation and by microscopic techniques to evaluate their morphology. TEM measurements revealed cvasi-spherical particles with sizes in the range of 10-30 nm, while SEM images confirmed their uniform distribution on the textile fiber surface.
The present study aims to bring an addition to biomass resources valorization for environmental-friendly synthesis of nanoparticles. Thus, the green synthesis of silver nanoparticles (AgNPs) was performed, using a novel and effective reducing agent, Primula officinalis extract. The synthesis was optimized by monitoring the characteristic absorption bands, using UV−Vis spectroscopy, and by evaluating the size and physical stability. The phenolic consumption was established using Folin-Ciocâlteu method (1.40 ± 0.42 mg, representing ~5% from the total amount of poly--phenols) and the antioxidant activity was evaluated using chemiluminescence and TEAC methods. The optimum ratio extract to Ag ions was 1:3, for which the AgNPs presented a zeta potential value of −29.3 ± 1.2 mV and particles size of 5−30 nm. For characterization, EDS and XRD techniques were used, along with microscopy techniques (TEM). The AgNPs dispersions were applied on natural textile samples (cotton and wool), as a novel antimicrobial treatment for textile preservation. The treated fabrics were further characterized in terms of chromatic parameters and antimicrobial effect against Escherichia coli, Staphylococcus aureus, Bacillus subtilis, and Penicillium hirsutum strains. The high percentages of bacterial reduction, >99%, revealed that the AgNPs produced are a good candidate for textiles preservation against microbial degradation.